DD210526A3 - METHOD FOR ONE OR MULTI-STAGE DRAWING OF METALLIC FORMING GOODS - Google Patents
METHOD FOR ONE OR MULTI-STAGE DRAWING OF METALLIC FORMING GOODS Download PDFInfo
- Publication number
- DD210526A3 DD210526A3 DD81231604A DD23160481A DD210526A3 DD 210526 A3 DD210526 A3 DD 210526A3 DD 81231604 A DD81231604 A DD 81231604A DD 23160481 A DD23160481 A DD 23160481A DD 210526 A3 DD210526 A3 DD 210526A3
- Authority
- DD
- German Democratic Republic
- Prior art keywords
- lubricant
- pressure
- solid lubricant
- liquid
- film
- Prior art date
Abstract
Die Erfindung bezieht sich auf das Gebiet der Metallurgie und ist anwendbar beim Ziehen von strangfoermigem Umformgut. Das Ziel der Erfindung besteht in der Schaffung von Voraussetzungen fuer eine Steigerung der Produktivitaet des Ziehprozesses. Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren zum ein- oder mehrstufigen Ziehen mittels Druckduesen zu entwickeln, bei dem mit einfachen Massnahmen und moeglichst unter Vermeidung eines Schmiermitteltraegers ein fuer die Gewaehrleistung hydrodynamischer Schmierungsverhaeltnisse ausreichender Druck in der Druckduese erzielt wird. Diese Aufgabe ist mit einem Verfahren, bei dem auf das Umformgut zur Erzielung eines festhaftenden homogenen Festschmierstoffilms ein fluessiges Schmiermittel aufgetragen und getrocknet wird, welches in einer fluessigen Substanz einen Festschmierstoff enthaelt, dadurch geloest, dass zur Erzielung des notwendigen Schmierstoffdruckes in den Druckduesen das Ziehgut durch Einlaufduesen zugefuehrt wird, deren Bohrungsdurchmesser jeweils 0,01 bis 0,06mm groesser als der einlaufende Ziehgutdurchmesser ist, und dass die Groesse des Schmierstoffdruckes im Druckraum mittels der Konsistenz und/oder der Dicke des Festschmierstoffilms eingestellt wird.The invention relates to the field of metallurgy and is applicable when pulling strandform Umformgut. The object of the invention is to create conditions for increasing the productivity of the drawing process. The invention has for its object to develop a method for single or multi-stage drawing by Druckduesen, which is achieved with simple measures and most possible while avoiding a Schmierstoffraegers sufficient to ensure hydrodynamic Schmierierungsverhaeltnisse pressure in the Druckduese. This object is achieved by a method in which a liquid lubricant is applied to the material to be molded to obtain a firmly adhering homogeneous solid lubricant film and dried, which contains a solid lubricant in a liquid substance, thereby solving that to achieve the necessary lubricant pressure in the Druckduesen the stock by Inlet diameter is supplied, the bore diameter is in each case 0.01 to 0.06 mm larger than the incoming Ziehgutdurchmesser, and that the size of the lubricant pressure in the pressure chamber by means of the consistency and / or the thickness of the solid lubricant film is adjusted.
Description
Verfahren zum ein- oder mehrstufigen Ziehen von metallischem UmformgutMethod for single or multi-stage drawing of metal forming material
Anwendungsgebiet der ErfindungField of application of the invention
Die Erfindung bezieht sich auf das Gebiet der Metallurgie und ist anwendbar beim Ziehen von st rangförmigem Umformgut, wie Draht, Stangen und Rohren, insbesondere zum Ziehen unter hydrodynamischen Schmierungsverhältnissen«The invention relates to the field of metallurgy and is applicable to the drawing of stangförmigem forming material, such as wire, rods and tubes, especially for pulling under hydrodynamic lubrication conditions «
Charakteristik der bekannten technischen LösungenCharacteristic of the known technical solutions
Für das Ziehen von Draht ist die Verwendung von Ziefiwerkzeugen in Form von Druckdüsen bekannt, mit denen weitestgehend hydrodynamische Schmierverhältnisse realisierbar sind» Die Druckdüsen bestehen meist aus einem Arbeitsziehstein und einer davor angeordneten einlaufdüse, wobei dazwischen ein Druckraum ausgebildet ist» Beim Ziehen wird zusammen mit dem umzuformenden Draht durch die Sinlaufdüse hindurch ein Schmiermittel in den Druckraum gefördert, wodurch dort ein Schmiermitteldruck aufgebaut wird, der das Schmiermittel zwischen den Draht und die Arbeitsflächen des Arbeitsziehsteins drückt. Als Schmiermittel werden dabei feste, pastenförmige und flüssige Substanzen eingesetzt, wobei vor dem Aufbringen des Schmiermittels auf dem Draht vielfach eine Trägerschicht aus chemischen Verbindungen der rietallen mittels einer aufwendigen Oberflächenbehandlung, wie Kalken, Phosphatieren, Oxalatierer., Soraxen, Verkupfern oder Verzinnen erzeugt werden muli« Als Festschmierstoffe werdenFor the drawing of wire, the use of Ziefiwerkzeugen in the form of pressure nozzles is known with which largely hydrodynamic lubrication ratios are feasible »The pressure nozzles are usually made of a Arbeitsziehstein and arranged upstream inlet nozzle, with a pressure chamber is formed in between» When pulling together with the To be formed by the wire through the Sinlaufdüse a lubricant in the pressure chamber, whereby there is a lubricant pressure is built up, which presses the lubricant between the wire and the working surfaces of the puller. As a lubricant while solid, paste-like and liquid substances are used, before the application of the lubricant on the wire often a carrier layer of chemical compounds Rietallen by means of a complex surface treatment, such as limestone, phosphating, Oxalatierer., Soraxen, copperplating or tinning are generated "Being solid lubricants
vorzugsweise Stearate, wie Calciumstearat und Zinkstearat, verwendet, die in Pulverform verarbeitet werden, indem der Draht vor dem Eintritt in die Druckdüse durch einen Kasten geführt wird, der das Schmierstoffpulver enthält. Auf Grund der mehr oder weniger losen Haftung des so auf die Oberfläche des Drahtes aufgebrachten Schmierstoffpulvers läßt sich der für schwierige Umformbedingungen (hochlegierte Werkstoffe, große Ziehgeschwindigkeiten, hohe Umformgrade) große Schmierstoffdruck im Druckraum nicht realisieren, da das Schmierstoffpulver abgestriffen wird und so den Ringspalt zwischen Draht und Düsenbohrung nicht ausreichend abdichtet*Preferably, stearates, such as calcium stearate and zinc stearate, are used which are processed in powder form by passing the wire through a box containing the lubricant powder prior to entering the pressure nozzle. Due to the more or less loose adhesion of the applied so to the surface of the wire lubricant powder for difficult forming conditions (high alloyed materials, high drawing speeds, high degrees of deformation) large lubricant pressure in the pressure chamber can not be realized because the lubricant powder is stripped and thus the annular gap between Wire and nozzle bore insufficiently sealed *
Ss ist auch bereits bekannt, vor dem Aufbringen des ßchmierstoffpulvers die Ziegutoberflache derart aufzurauhen, daß scharf randige Vertiefungen entstehen, in denen das Pulver haften kann. Gleichzeitig werden dabei Druckdüsen angewandt, deren Einlaufdüsenbohrung 2 bis 3 % größer als der Durchmesser des zugeführten Ziehgutes ist. Auch mit dieser Verfahrensweise werden die obengenannten Probleme nicht grundlegend beseitigt» Damit sind der Umformung von hochfesten Werkstoffen bzw» der Erhöhung der Ziehgeschwindigkeit und des Umformgrades Grenzen gesetzt. Insbesondere treten diese Probleme auf, wenn Draht mit kleinem Durchmesser von unter 1 mm gezogen werden soll. Die genannten Grenzen lassen sich auch mit der Verwendung pastöser oder flüssiger Schmierstoffilme aus beispielsweise Wachsen, flüssigen Seifen, ölen oder Graphit/MoS-Mischungen nicht überschreiten, da die dynamische Viskosität dieser Schmiermittel geringer als die der Festschmierstoffe ist, Es ist auch ein flüssiges Schmiermittel vorgeschlagen worden, das aus einem organischen Lösungsmittel mit darin enthaltenen Festschmierstoffen und Tensiden besteh";» Dieses Schmiermittel besitzt nur eine relativ geringe Druckfestigkeit und ist hygroskopisch , so daß es für schwe rum formbare u'erkstoffe und für sine Druckdüsenanwendung nicht in Betracht kommt.It is also already known to roughen the surface of the goat skin before applying the lubricating powder in such a way that sharp edge depressions are formed, in which the powder can adhere. At the same time pressure nozzles are used, the inlet nozzle bore is 2 to 3 % larger than the diameter of the supplied drawn material. Even with this procedure, the above-mentioned problems are not fundamentally eliminated »This limits the forming of high-strength materials or the increase of the drawing speed and the degree of deformation. In particular, these problems occur when small diameter wire of less than 1 mm is to be pulled. The above limits can not be exceeded even with the use of pasty or liquid lubricant films such as waxes, liquid soaps, oils or graphite / MoS mixtures, since the dynamic viscosity of these lubricants is lower than that of the solid lubricants, It is also proposed a liquid lubricant which consists of an organic solvent with solid lubricants and surfactants contained therein ";" This lubricant has only a relatively low compressive strength and is hygroscopic, so that it is for rum rum formbare u'erkstoffe and for sine pressure nozzle application is not eligible.
Ziel der ErfindungObject of the invention
Das Ziel der Erfindung besteht in der Schaffung von Voraussetzungen für eine Steigerung der Produktivität des Ziehprozesses, insbesondere bezüglich der Erhöhung des Umformgrades und der Ziehgeschwindigkeit, speziell bei der Umformung hochlegierter Werkstoffe* Gleichzeitig sollen die Kosten für die Vorbehandlung des Umformgutes wesentlich verringert werden,The aim of the invention is to create conditions for an increase in the productivity of the drawing process, in particular with regard to increasing the degree of deformation and the drawing speed, especially in the transformation of high-alloy materials * At the same time, the cost of pretreatment of the formed material should be substantially reduced
Darlegung des Wesens der ErfindungExplanation of the essence of the invention
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren zum ein- oder mehrstufigen Ziehen von metallischem Umformgut mittels Druckdüsen zu entwickeln, bei dem mit einfachen Maßnahmen und möglichst unter Vermeidung eines Schmiermittelträgers ein für die Gewährleistung hydrodynamischer Schmierungsverhältnisse ausreichender Druck im Druckraum der Druckdüse erzielt wird, und zwar auch beim Ziehen hochlegierter Werkstoffe, bei großen Ziehgeschivindigkeiten, bei hohen Umformgraden und bei Abmessungen unter 1 mm Durchmesser»The invention has for its object to develop a method for single or multi-stage drawing of metallic Umformgut by means of pressure nozzles, which is achieved by simple measures and preferably while avoiding a lubricant carrier sufficient to ensure hydrodynamic lubrication conditions pressure in the pressure chamber of the pressure nozzle, and even when drawing high-alloyed materials, with large drawing speeds, with high degrees of deformation and with dimensions of less than 1 mm diameter »
Diese Aufgabe ist mit einem Verfahren, bei dem auf das Umformgut zur Erzielung eines festhaftenden homogenen Fest- -schmierstof films ein flüssiges Schmiermittel, welches in einer flüssigen Substanz einen Festschmierstoff dispergiert oder gelöst enthält, aufgebracht und getrocknet wird, erfindungsgemäß dadurch gelöst, daß zur Erzielung des notwendigen Schmierstoffdruckes in den Dpuckdüsen das Ziehgut durch Einlaufdüsen zugeführt wird, deren Bohrungsdurchinesser jeweils O,C1 bis O,05 mm größer als der einlaufende Ziehgutdurchmesser ist, wobei die Größe des Schmierstoffdruckes im Druckraum mittels der Konsistenz und/oder dar Dicke des Festschnierstoffilms eingestellt v/ird.This object is achieved with a method in which applied to the Umformgut to achieve a firmly adhering homogeneous solid lubricant film, a liquid lubricant containing a solid lubricant dispersed or dissolved in a liquid substance applied and dried, according to the invention achieved that to achieve the necessary lubricant pressure in the Dpuckdüsen the drawn material is fed through inlet nozzles whose Bohrendurchdurchinesser each O, C1 to O, 05 mm greater than the incoming Ziehgutdurchmesser, the size of the lubricant pressure in the pressure chamber by means of the consistency and / or thickness of the Festschnierstoffilms set v / ill.
Der Schmierstoff wird dabei zweckmäßig mittels eines mit dem Druckraum verbundenen, einstellbaren Überdruckventils begrenzt. Die Dicke des Fest Schmierstoff iirns kann vorteilhaft mittels der Konzentration des Festschmierstoffe in der flüssigen Substanz, der Temperatur des flüssigen Schmiermittels The lubricant is expediently limited by means of an adjustable overpressure valve connected to the pressure chamber. The thickness of the solid lubricant can be advantageously determined by the concentration of the solid lubricants in the liquid substance, the temperature of the liquid lubricant
oder einem Abstreifer gesteuert werden»or a scraper can be controlled »
Bei dem erfindungsgemäßen Verfahren werden mittels einfacher Maßnahmen und in überraschender Weise ausgezeichnete Schmierungsverhältnisse in den Druckdüsen gewährleistet* Im Zusammenwirken mit der Funktionsweise der Kammern ermöglichen diese Schmierungsverhältnisse gegenüber dem Stand der Technik eine wesentliche Steigerung der Produktivität des Ziehprozesses hinsichtlich der Erhöhung des Umformgrades und der Ziehgeschwindigkeit sowie eine problemlosere Umformung hochlegierter Werkstoffe und dünner Drähte. Außerdem werden durch den beim erfindungsgemäßen Verfahren erzielten Wegfall der üblichen Trägerschicht die technologischen und die i-iaterialaufwendungen beträchtlich verringert,In the method according to the invention excellent lubrication conditions are ensured in the pressure nozzles by simple measures and in a surprising manner * In conjunction with the functioning of the chambers, these lubrication ratios compared to the prior art, a substantial increase in the productivity of the drawing process in terms of increasing the degree of deformation and the drawing speed and a smoother transformation of high-alloyed materials and thin wires. In addition, the technological and i-iaterialaufwendungen are considerably reduced by eliminating the usual carrier layer achieved in the process according to the invention,
Ausführungsbeispielembodiment
Draht der Stahlmarke X5CrNil3#10 mit einem Ausgangsdurchmesser von 1,6 mm, auf dem schmiermittelträgerlos ein homogener, festhaftender Festschmierstoffilm aus Calciumstearat aufgebracht worden ist, wird auf einer Mehrfachziehmaschine in 6 Stufen auf eine Hndabmessung von O1S mm mittels Druckdüsen gezogen« Mit den in den Druckdüsen enthaltenen Arbeitszieh-,steinen wird die nachfolgende Ziehfolge realisiert: 1,25/ 1,06/ 0,92/ 0,35/ 0,30 mm» Die vor den Arbeitsziehsteinen in den Druckdüsen angeordneten Sinlaufdüsen bestehen aus Ziehsteinen, deren Bohrungsdurchmesser zwischen 0,02 und 0,04 mm größer bemessen ist, als der Durchmesser des in die jeweilige Druckdüse einlaufenden Drahtes, Der umgeformte Dpaht läuft unmittelbar nach seinem Austritt aus den Arbeitsziehsteinen durch jeweils eine Kammer, deren Ausgang mit einem Ziehstein abgeschlossen ist# Der Bohrungsdurchmesser dieser Ziehsteine ist bis zu 0,1 mm größer bemessen, als der aohrungsdurchmesser des davor angeordneten Arbeitszishsteines» Die nach den Arbeitsziehsteinen angeordneten Kammern werden mit einer Flüssigkeit gespeist, die aus Trichlorethylen besteht, in dem Calciuiiistearat mit erhöhten Hetailoxidanteii enthalten ist» Dabei wird mittels der am Ausgang der Kammern befind-Wire of steel brand X5CrNil3 # 10 with a starting diameter of 1.6 mm, on which a homogeneous, firmly adhering solid lubricant film of calcium stearate has been applied is drawn on a multiple drawing machine in 6 stages to a final dimension of O 1 S mm by means of pressure nozzles The drawing sequence contained in the pressure nozzles is the following: 1.25 / 1.06 / 0.92 / 0.35 / 0.30 mm »The squeeze nozzles located in the pressure nozzles in front of the workholding blocks consist of drawing dies whose bore diameters The formed diameter runs immediately after its exit from the drawing dies by a respective chamber whose output is completed with a drawing die # The bore diameter These dies are sized up to 0.1 mm larger than the diameter of the hole in front of them The working chambers are supplied with a fluid consisting of trichlorethylene, containing calciuiistine stearate with increased hetal oxide content. The chamber is located at the exit of the chambers.
lichen Ziehsteine die Dicke des Flüssigkeitsfilms kalibriert. Infolge der im Draht vorhandenen Uraformwärme verdunstet das Trichloräthylen in sehr kurzer Zeit und es entsteht ein trockener, homogener, festhaftender Festschmierstoffilm aus Calciumstearat mit erhöhtem Metalloxidanteil für die nachfolgende Umformung«The thickness of the liquid film is calibrated by means of drawing dies. As a result of the uranium heat present in the wire, the trichlorethylene evaporates in a very short time and produces a dry, homogeneous, firmly adhering solid lubricant film of calcium stearate with an increased metal oxide content for subsequent forming «
Sofern eine Umformung über mehrere Stufen unter Ausnutzung des Schmierstoff-Restfilms realisierbar ist, werden die entsprechenden Kammern nicht mit der Flüssigkeit betrieben« Das Betreiben der letzten Kammer entfällt stets dann, wenn eine Schmierstoffbeschichtung des umgeformten Drahtes für Weiterverarbeitungsvorgänge nicht erforderlich ist.If a conversion over several stages using the residual lubricant film is feasible, the corresponding chambers are not operated with the liquid. "The operation of the last chamber is eliminated whenever a lubricant coating of the formed wire for further processing operations is not required.
Claims (1)