CN201566396U - UV curing colored PVC decorative sheet - Google Patents

UV curing colored PVC decorative sheet Download PDF

Info

Publication number
CN201566396U
CN201566396U CN2009202777211U CN200920277721U CN201566396U CN 201566396 U CN201566396 U CN 201566396U CN 2009202777211 U CN2009202777211 U CN 2009202777211U CN 200920277721 U CN200920277721 U CN 200920277721U CN 201566396 U CN201566396 U CN 201566396U
Authority
CN
China
Prior art keywords
ultraviolet
pvc decorative
decorative board
paint
curing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN2009202777211U
Other languages
Chinese (zh)
Inventor
李树森
谭昊涯
陈伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009202777211U priority Critical patent/CN201566396U/en
Application granted granted Critical
Publication of CN201566396U publication Critical patent/CN201566396U/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

The utility model belongs to the field of decorative materials, and particularly relates to a UV curing colored PVC decorative sheet the surface of which is coated with UV curing paint. The surface of the base body of the PVC decorative sheet is coated with UV curing colored paint, the surface of the UV curing colored paint coat is coated with UV curing finish paint, and the surface of the UV curing finish paint coat is further stuck with a polypropylene or polyethylene protective film. The UV curing PVC decorative sheet has the advantages of high strength of sheet materials, good weather resistance, good environmental protection property, rich colors, full paint film, high hardness, scratch resistance, easy cleaning and the like, and compared with the existing commonly used PVC decorative sheets, the utility model has better decorative effect and protective effect.

Description

The ultraviolet curing chromatic PVC decorative board
Technical field
The utility model belongs to decoration material field, and particularly the surface is by ultraviolet curing chromatic polyvinyl chloride (PVC) decorative panel of application ultraviolet-curing paint (being called for short UV coating) production.
Background technology
PVC decorative board has characteristics such as lightweight, heat insulation, insulation, moistureproof, fire-retardant, easy construction.The specification of PVC decorative board, color, pattern are various, are rich in ornamentally, can be applicable to the decoration of room interior wall and furred ceiling, are one of ornament materials that is most widely used in the plastic materials.But traditional PVC decorative board just prints the coating of patterns such as one deck such as decorative pattern at polyvinyl chloride (PVC) substrate surface, and then makees one deck protection varnish, or directly makees one deck protection varnish at the PVC substrate surface.
Summary of the invention
The purpose of this utility model provides a kind of rich color, the ornamental and strong ultraviolet curing chromatic PVC decorative board of protectiveness.
Ultraviolet curing chromatic PVC decorative board of the present utility model is the multiple modification that the polyvinyl chloride matrix surfaces such as (PVC) at colour carries out color and pattern once more; simultaneously carry out the external coating protective layer again, reach abundant colors and surface protection effect more with this.
Ultraviolet curing chromatic PVC decorative board of the present utility model is that the external coating at the PVC decorative board matrix has ultraviolet cured colored paint, at the external coating of ultraviolet cured colored paint coating the ultraviolet light polymerization finish paint is arranged.
The surface of described ultraviolet light polymerization topcoat further post be used for that protective finish is avoided scratching, abrasive polypropylene or polyethylene protective film.
Described ultraviolet cured colored paint coating further is the compound enamelled coating (can obtain abundant colors more) of 2 layers of ultraviolet cured colored paint coating.
Described ultraviolet light polymerization finish paint can adopt the technology application of roller coat, showering or spraying, and the thickness of coating is 10~150um, and the gloss of coating is that 10~100 degree (60 degree gloss meter) are adjustable.
Described ultraviolet cured colored paint can adopt the technology application of roller coat or blade coating, and when application one deck ultraviolet cured colored paint coating, the thickness of coating is 1~50um; When two layers of ultraviolet cured colored paint coating of application, the gross thickness of the compound enamelled coating that obtains is 1~50um
Described ultraviolet cured colored paint is ultraviolet light polymerization solid-shade paint or ultraviolet light polymerization metal flash paint.
Described PVC decorative board matrix is colored PVC plate, white PVC plate or colourless PVC plate etc.
Ultraviolet curing chromatic PVC decorative board of the present utility model can prepare by the following method:
(1). the matrix preparation: batching, extrude; Matrix surface is handled: base solvent wiping, and the dust of removing matrix surface;
(2). at the matrix surface application ultraviolet cured colored paint of step (1);
(3). photocuring;
(4). application ultraviolet cured colored paint again on the surface of the ultraviolet cured colored paint of step (3);
(5). photocuring;
(6). at the application ultraviolet light polymerization finish paint on the surface that 2 times ultraviolet cured colored paints are housed that is coated with of step (5);
(7). infrared levelling or natural levelling;
(8). photocuring;
(9). check;
(10). pasting protective film;
(11). packing.
Or
(1). the matrix preparation: batching, extrude; Matrix surface is handled: base solvent wiping, and the dust of removing matrix surface;
(2). at the matrix surface application ultraviolet cured colored paint of step (1);
(3). photocuring;
(4). application ultraviolet light polymerization finish paint on the ultraviolet cured colored paint of step (3);
(5). infrared levelling or natural levelling;
(6). photocuring;
(7). check;
(8). pasting protective film;
(9). packing.
At matrix surface application ultraviolet cured colored paint:
The application mode can adopt the mode of roller coat or blade coating, and the thickness of coating is 1~50 μ m (if 2 times ultraviolet cured colored paints of application, the thickness of described coating is that 1~50 μ m is 2 times a gross thickness).
Photocuring:
Photocuring adopts ultraviolet light polymerization, be coated with the workpiece that installs and enter the ultraviolet tube (high-pressure sodium lamp) that 1~6 3~20kw is housed, carry out illumination in the photo solidification machine of the metal halogen fluorescent tube of 0~3 3~20kw (Iodine gallium light, iron lamp, dysprosium lamp etc.), make light solidifying coating solidify 5~50 meters/minute of speed.
External coating ultraviolet light polymerization finish paint at ultraviolet cured colored paint:
The application mode can adopt the mode of roller coat, showering or spraying, and the thickness of coating is 10~150 μ m, and the gloss of coating is that 10~100 degree (60 degree gloss meter) are adjustable.
Infrared levelling or natural levelling:
Infrared levelling transfers to 20~80 ℃ with infrared ray leveling machine temperature, and flow time 0.1~10 minute makes coating surface smooth, and makes that solvent fully volatilizees in the coating; The nature levelling then will be coated with the workpiece that installs and put under field conditions (factors) 1~30 minute, make coating surface smooth, and make that solvent fully volatilizees in the coating.
Photocuring:
Photocuring adopts ultraviolet light polymerization, be coated with the workpiece that installs and enter the ultraviolet tube (high-pressure sodium lamp) that 1~6 3~20kw is housed, carry out illumination in the photo solidification machine of the metal halogen fluorescent tube of 0~3 3~20kw (Iodine gallium light, iron lamp, dysprosium lamp etc.), make light solidifying coating solidify 5~50 meters/minute of speed.
Coating such as employed ultraviolet cured colored paint, ultraviolet light polymerization finish paint in the utility model.By weight percentage, ultraviolet cured colored paint is made up of acrylic ester prepolymer 10~80%, acrylate monomer 5~50%, light trigger 1~10%, auxiliary agent 0~2% and 2~50% of pigment usually; The ultraviolet light polymerization finish paint is made up of acrylic ester prepolymer 10~80%, acrylate monomer 5~60%, light trigger 1~6%, auxiliary agent 0~2% and 0~50% of filler.
Wherein acrylic ester prepolymer is selected from least a in the group that epoxy acrylate, fluorine-containing epoxy acrylate, urethane acrylate, fluorochemical urethane acrylate, polyester acrylate, fluorine-containing polyester acrylate, amino acrylates, fluorine-containing amino acrylates, acrylate copolymer, fluoro-acrylate copolymer form.
Wherein acrylate monomer is: 1. single functionality monomer, as butyl acrylate, cyclohexyl acrylate, Isooctyl acrylate monomer (EHA), hydroxy-ethyl acrylate (HEA), hydroxyethyl methacrylate (MHEA), acrylic acid trifluoro ethyl ester, trifluoroethyl methacrylate, acrylic acid hexafluoro butyl ester, methacrylic acid hexafluoro butyl ester, dodecafluorhe-ptylacrylate or methacrylic acid ten difluoro heptyl esters etc.; 2. two functionality monomer, as tri (propylene glycol) diacrylate (TPGDA), propylene glycol diacrylate (DPGDA), neopentylglycol diacrylate (NPGDA), the third oxidation neopentylglycol diacrylate (PO-NPGDA), two (diethylene glycol) diacrylates (PDDA) of phthalic acid or 1,6 hexanediyl ester (HDDA) etc.; 3. polyfunctionality monomer, as trimethylolpropane triacrylate (TMPTA), ethoxyquin trimethylolpropane triacrylate (EO-TMPTA), the third oxidation trimethylolpropane triacrylate (PO-TMPTA), pentaerythritol triacrylate (PETA) or dipentaerythritol acrylate (DPHA) etc., common at least a in the group of being formed with above-mentioned acrylate monomer etc. as application.
Described light trigger is selected from see at least a in the group that oxygen compound photoinitiator, benzoic ether photoinitiator and reactive amine aided initiating formed of benzoin ether photoinitiator, benzil ketals photoinitiator, acetophenones light trigger, anthraquinone photoinitiator, thioxanthone photoinitiator, Benzophenones light trigger, acyl group.
Described benzoin ether photoinitiator is selected from least a in the group that benzoin methyl ether, benzoin ethylether, benzoin isopropyl ether etc. are formed.
Described benzil ketals photoinitiator is a benzil dimethyl ketal etc.
Described acetophenones light trigger is selected from acetophenone, 2,2-dimethoxy-2-phenyl acetophenone, 2,2-diethoxy-2-phenyl acetophenone, 1, the 1-dichloroacetophenone, the 1-hydroxy acetophenone, 1-hydroxy-cyclohexyl phenyl ketone, 2-hydroxy-2-methyl-1-phenyl-1-acetone, 1-(4-isopropyl phenyl)-2-hydroxy-2-methyl-1-acetone, 1-[4-(2-hydroxyl-oxethyl) phenyl]-2-hydroxy-2-methyl-1-acetone, 2-methyl isophthalic acid-[4-(methyl mercapto) phenyl]-2-morpholinyl-1-acetone, at least a in the 2-benzyl-2-dimethylamino-1-group that (4-morpholinyl phenyl)-1-butanone etc. is formed.
Described anthraquinone photoinitiator is selected from least a in the group that 2-tert-butyl group anthraquinone, 1-chloroanthraquinone, 2-amyl anthraquinone etc. are formed.
Described thioxanthone photoinitiator is selected from 2,4-dimethyl thia anthrone, 2,4-diethyl thioxanthone, 2-isopropyl thioxanthone, 4-isopropyl thioxanthone, 2-chloro thioxanthone, 2, at least a in the group that 4-diisopropyl thioxanthone etc. is formed.
Described Benzophenones light trigger is selected from benzophenone, 4-chlorobenzophenone, at least a in methyldiphenyl ketone, the group that 4-benzoyl-4 '-dimethyl diphenyl sulfide etc. is formed.
The described acyl group oxygen compound photoinitiator of seeing is selected from 2; 4; 6-trimethylbenzoyl diphenyl phosphine oxide, two (2; 4, the 6-trimethylbenzoyl)-phenyl phosphine oxide, two (2, the 6-dimethylbenzoyl)-2; 4; 4-tri-methyl-amyl phosphine oxide, 2,4, at least a in the group that 6-trimethylbenzoyl phenyl ethoxy phosphine oxide etc. is formed.
Described benzoic ether photoinitiator is benzoylbenzoic acid methyl esters, methyl o-benzoylbenzoate or their mixture etc.
Described reactive amine aided initiating is tertiary amine, response type tertiary amine acrylate or their mixture etc.
Wherein auxiliary agent is the defoamer (as BYK052, BYK055 or their mixture etc.) of the levelling agent (as BYK306, BYK358 or their mixture etc.) of German Bi Ke chemical company, German Bi Ke chemical company and/or the wetting dispersing agent (as Disperbyk 103, Disperbyk163 or their mixture etc.) of German Bi Ke chemical company.
Wherein pigment is that inorganic pigment, organic pigment, bronze (copper powder), silver powder (aluminium powder), pearl essence, fluorescent material, illusion-colour pigment, reflective pigment etc. have at least a in the group that special effect pigments etc. formed.
Described inorganic pigment is at least a in the group formed such as titanium dioxide, carbon black, iron oxide.
Described organic pigment is at least a in green, the brown chrome yellow of phthalocyanine blue, the phthalein mountain valley with clumps of trees and bamboo, the group of being formed such as bright red.
Wherein filler is powder body materials such as flatting silica.
Check:
Whether the colored PVC decorative board that check is made is qualified.
Pasting protective film:
Be used for protective finish at colored PVC decorative board surface subsides polypropylene through being up to the standards or polyethylene etc. and avoid scuffing, abrasive film, the surface light solidified coating of colored PVC decorative board is protected.
Packing:
According to the specification of product and require to finished product packing.
Described PVC decorative board is a decorative boards commonly used in this area, can be used for making various ornament materials.
Ultraviolet curing chromatic PVC decorative board of the present utility model, the surface is by first application ultraviolet cured colored paint, application ultraviolet light polymerization finish paint again; Or first application ultraviolet cured colored paint, application ultraviolet cured colored paint, application ultraviolet light polymerization finish paint more again.
Colored PVC decorative board by said method production has the timber intensity height, good weatherability, and the feature of environmental protection is good; rich color, paint film is plentiful, the hardness height; scratch resistance, advantage easy to clean has better decorative effect and protection effect than the PVC decorative board that generally uses at present.
The preparation method of ultraviolet curing chromatic PVC decorative board of the present utility model has that required production site is little, and equipment investment is low, production efficiency height, less energy consumption, free of contamination advantage.
Description of drawings
Fig. 1. the structural representation of the ultraviolet curing chromatic PVC decorative board of the utility model embodiment 1,2,3.
Fig. 2. the structural representation of the ultraviolet curing chromatic PVC decorative board of the utility model order embodiment 4,5.
Reference numeral
1.PVC decorative panel matrix 2. ultraviolet cured colored paints 3. ultraviolet cured colored paints (double-colored flower)
4. ultraviolet light polymerization finish paint 5. diaphragms
The specific embodiment
Embodiment 1. orange PVC decorative board for wall
See also Fig. 1.Earlier extrude orange PVC sheet material by mould with extruder; dust with 1 usefulness acetone wiping of PVC decorative board matrix and removing surface; be the orange ultraviolet cured colored paint 2 of 1um at PVC decorative board matrix surface roller coat one layer thickness again; enter 2 9.6kw uviol lamps (high-pressure sodium lamp) are housed; transmission speed is 24 meters/minute a photo solidification machine; after the curing; surperficial showering one layer thickness at orange ultraviolet cured colored paint is 150um again; gloss is the ultraviolet light polymerization finish paint 4 of 100 degree (60 degree gloss meter); levelling is 1 minute under the infrared ray of 60 ℃ of temperature; enter 1 13KW Iodine gallium light is housed, 2 13kw uviol lamps (high-pressure sodium lamp), transmission speed is 24 meters/minute a photo solidification machine; after the curing; reach criterion of acceptability through test rating, paste polypropylene diaphragm 5, promptly get orange PVC decorative board finished product.
The percentage by weight of orange ultraviolet cured colored paint consists of: epoxy acrylate 40%, polyester acrylate 20%, TMPTA 16%, palm fibre chrome yellow toner 5%, titanium dioxide 10%, bright red toner 2.5%, acetophenones initator 3%, thioxanthone photoinitiator 3%, BYK 052 0.2%, Disperbyk 1630.3%.
The percentage by weight of ultraviolet light polymerization finish paint consists of: fluorine-containing epoxy acrylate 35%, and urethane acrylate 30%, TPGDA 10%, and EO-TMPTA 20%, acetophenones initator 4.5%, BYK055 0.2%, and Disperbyk 103 0.3%.
Embodiment 2. blue PVC decorative board for wall
See also Fig. 1.Earlier extrude blue PVC sheet material by mould with extruder; dust with 1 usefulness acetone wiping of PVC decorative board matrix and removing surface; be the blue ultraviolet cured colored paint 2 of 50um at PVC decorative board matrix surface roller coat one layer thickness again; enter 2 11kw uviol lamps (high-pressure sodium lamp) are housed; transmission speed is 30 meters/minute a photo solidification machine; after the curing; surface roller coating one layer thickness of the blue ultraviolet cured colored paint after sanding is 10um again; gloss is the ultraviolet light polymerization finish paint 4 of 50 degree (60 degree gloss meter); levelling is 3 minutes under the infrared ray of 60 ℃ of temperature; enter 2 11kw uviol lamps (high-pressure sodium lamp) are housed, 1 11KW Iodine gallium light, transmission speed is 30 meters/minute a photo solidification machine; after the curing; reach criterion of acceptability through test rating, paste polypropylene diaphragm 5, promptly get blue PVC decorative board finished product.
The percentage by weight of blue ultraviolet cured colored paint consists of: epoxy acrylate 33.5%, urethane acrylate 20%, EO-TMPTA 16%, phthalocyanine blue toner 10%, titanium dioxide 10%, thioxanthone photoinitiator 2.5%, acetophenones light trigger 3%, tertiary amine 4.5%, BYK 055 0.2%, Disperbyk 163 0.3%.
The percentage by weight of ultraviolet light polymerization finish paint consists of: epoxy acrylate 15%, urethane acrylate 35%, TMPTA20%, PO-NPGDA 10%, flatting silica 15%, acetophenones light trigger 4.5%, BYK 052 0.2%, Disperbyk 103 0.3%.
Embodiment 3. red PVC decorative boards
See also Fig. 1.Earlier extrude red PVC sheet material by mould with extruder; dust with 1 usefulness acetone wiping of PVC decorative board matrix and removing surface; be the red ultraviolet cured colored paint 2 of 50um at PVC decorative board matrix surface roller coat one layer thickness again; enter 2 13kw uviol lamps (high-pressure sodium lamp) are housed; transmission speed is 30 meters/minute a photo solidification machine; after the curing; spraying a layer thickness on the surface of red ultraviolet cured colored paint again is 40um; gloss is 100 degree (60 degree gloss meter) ultraviolet light polymerization finish paints 4; levelling is 2 minutes under the infrared ray of 60 ℃ of temperature; enter 2 13kw uviol lamps (high-pressure sodium lamp) are housed, 2 13KW Iodine gallium lights, transmission speed is 30 meters/minute a photo solidification machine; after the curing; reach criterion of acceptability through test rating, paste polypropylene diaphragm 5, promptly get red PVC decorative board finished product.
The percentage by weight of red ultraviolet cured colored paint consists of: epoxy acrylate 40%, and polyester acrylate 23%, TMPTA 10%, red 18%, thioxanthone photoinitiator 1%, acetophenones light trigger 1%, tertiary amine 5.5%; BYK 052 1.2%, Disperbyk 163 0.3%.
The percentage by weight of ultraviolet light polymerization finish paint consists of: fluorine-containing epoxy acrylate 35%, and urethane acrylate 30%, TPGDA 10%, and EO-TMPTA 20%, acetophenones light trigger 4.5%, BYK 055 0.2%, Disperbyk 103 0.3%.
Embodiment 4. yellow pearly-lustre PVC decorative boards
See also Fig. 2.Earlier extrude yellow PVC sheet material by mould with extruder, dust with 1 usefulness acetone wiping of PVC decorative board matrix and removing surface, be the yellow ultraviolet cured colored paint 2 of 40um at PVC decorative board matrix surface roller coat one layer thickness again, enter 2 10kw uviol lamps (high-pressure sodium lamp) are housed, transmission speed is 35 meters/minute a photo solidification machine, after the curing, surface roller coating one layer thickness of the yellow ultraviolet cured colored paint after sanding is the ultraviolet cured colored paint (opalescent lacquers) 3 of 10um again, forms the double-colored flower lacquer of ultraviolet light polymerization thus; Enter 2 12kw uviol lamps (high-pressure sodium lamp) are housed; transmission speed is 35 meters/minute a photo solidification machine; after the curing; be the ultraviolet light polymerization finish paint 4 of 30um at ultraviolet curing pearl lacquer surface roller coating one layer thickness again; gloss is 80 degree (60 degree gloss meter) levellings 1 minute under the infrared ray of 50 ℃ of temperature; enter 1 12KW Iodine gallium light is housed; 3 12kw uviol lamps (high-pressure sodium lamp); transmission speed is 35 meters/minute a photo solidification machine; after the curing; reach criterion of acceptability through test rating, paste polypropylene diaphragm 5, promptly get yellow pearly-lustre PVC decorative board finished product.
The percentage by weight of yellow ultraviolet cured colored paint consists of: epoxy acrylate 40%, and polyester acrylate 30%, TMPTA 6%, palm fibre chrome yellow powder 17%, acetophenones initator 3%, thioxanthone photoinitiator 3.5%, BYK 055 0.2%, Disperbyk 163 0.3%.
The percentage by weight of ultraviolet curing pearl lacquer consists of: epoxy acrylate 28%, and polyester acrylate 20%, TPGDA 20%, and NPGDA 10%, pearl essence 15%, acetophenones light trigger 3.5%, the acyl group oxygen compound photoinitiator 3% of seeing; BYK 055 0.2%, Disperbyk 163 0.3%.
The percentage by weight of ultraviolet light polymerization finish paint consists of: epoxy acrylate 20%, fluorochemical urethane acrylate 40%, polyester acrylate 10%, PETA 10%, and HDDA 10%, flatting silica 6%, acetophenones light trigger 3%, BYK 052 0.2%, Disperbyk 163 0.8%.
Embodiment 5. ancient wood grain look PVC decorative board for wall
See also Fig. 2.Earlier extrude wooden look PVC sheet material by mould with extruder; dust with 1 usefulness acetone wiping of PVC decorative board matrix and removing surface; be the wooden look ultraviolet cured colored paint 2 of 30um again at PVC decorative board matrix surface roller coat one layer thickness; enter 2 12kw uviol lamps (high-pressure sodium lamp) are housed; transmission speed is 25 meters/minute a photo solidification machine; after the curing; surface roller coating one layer thickness at wooden look ultraviolet cured colored paint is the ultraviolet cured colored paint (coffee-like decorative pattern colored paint) 3 of 8um again; enter 2 12kw uviol lamps (high-pressure sodium lamp) are housed; transmission speed is 25 meters/minute a photo solidification machine; after the curing; spraying a layer thickness on the surface of the coffee-like decorative pattern lacquer of ultraviolet light polymerization is 50um; gloss is 80 degree (60 degree gloss meter) ultraviolet light polymerization finish paints 4; levelling is 3 minutes under the infrared ray of 60 ℃ of temperature; enter 2 12KW Iodine gallium lights are housed; 3 12kw uviol lamps (high-pressure sodium lamp); transmission speed is 25 meters/minute a photo solidification machine; after the curing; reach criterion of acceptability through test rating; paste polypropylene diaphragm 5, promptly get ancient wood grain look PVC decorative board finished product.
The percentage by weight of wood look ultraviolet cured colored paint consists of: epoxy acrylate 32%, polyester acrylate 20%, TPGDA 16%, bright red toner 3.5%, brown chrome yellow powder 10%, titanium dioxide 12%, acetophenones initator 3%, thioxanthone photoinitiator 3%, BYK 055 0.2%, Disperbyk 1630.3%.
The percentage by weight of the coffee-like colored paint of ultraviolet light polymerization consists of: fluorine-containing epoxy acrylate 30%, urethane acrylate 15%, TPGDA 15.5%, and EO-TMPTA 10%, bright red toner 8%, palm fibre chrome yellow powder 12%, carbon black 2.5%, thioxanthone photoinitiator 3%, acetophenones light trigger 3%, tertiary amine 0.5%, BYK 055 0.2%, Disperbyk 163 0.3%.
The percentage by weight of ultraviolet light polymerization finish paint consists of: epoxy acrylate 10%, fluorochemical urethane acrylate 50%, polyester acrylate 10%, PETA 10%, and PO-NPGDA 15%, acetophenones light trigger 4%, BYK 052 0.2%, Disperbyk 103 0.8%.

Claims (8)

1. ultraviolet curing chromatic PVC decorative board, it is characterized in that: the external coating at the PVC decorative board matrix has ultraviolet cured colored paint, at the external coating of ultraviolet cured colored paint coating the ultraviolet light polymerization finish paint is arranged.
2. ultraviolet curing chromatic PVC decorative board according to claim 1 is characterized in that: polypropylene or polyethylene protective film are posted in the surface of described ultraviolet light polymerization topcoat.
3. ultraviolet curing chromatic PVC decorative board according to claim 1 and 2 is characterized in that: the thickness of described ultraviolet light polymerization topcoat is 10~150um, and the gloss of coating is that 10~100 degree are adjustable.
4. ultraviolet curing chromatic PVC decorative board according to claim 1 is characterized in that: described ultraviolet cured colored paint coating is the compound enamelled coating of 2 layers of ultraviolet cured colored paint coating.
5. ultraviolet curing chromatic PVC decorative board according to claim 1 is characterized in that: the thickness of described ultraviolet cured colored paint coating is 1~50um.
6. ultraviolet curing chromatic PVC decorative board according to claim 4 is characterized in that: the gross thickness of described compound enamelled coating is 1~50um.
7. according to claim 1,4 or 5 described ultraviolet curing chromatic PVC decorative boards, it is characterized in that: described ultraviolet cured colored paint is ultraviolet light polymerization solid-shade paint or ultraviolet light polymerization metal flash paint.
8. ultraviolet curing chromatic PVC decorative board according to claim 1 is characterized in that: described PVC decorative board matrix is colored PVC plate, white PVC plate or colourless PVC plate.
CN2009202777211U 2009-12-08 2009-12-08 UV curing colored PVC decorative sheet Expired - Lifetime CN201566396U (en)