CN1986479A - Water-base epoxy color sand mortar and its preparing process and construction process - Google Patents
Water-base epoxy color sand mortar and its preparing process and construction process Download PDFInfo
- Publication number
- CN1986479A CN1986479A CN 200510120760 CN200510120760A CN1986479A CN 1986479 A CN1986479 A CN 1986479A CN 200510120760 CN200510120760 CN 200510120760 CN 200510120760 A CN200510120760 A CN 200510120760A CN 1986479 A CN1986479 A CN 1986479A
- Authority
- CN
- China
- Prior art keywords
- water
- color sand
- base epoxy
- component
- epoxy color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The water-base epoxy color sand mortar consists of two components, including component A of KNP WEM601A in 16.5-17.5 weight portions; and component B comprising KNP WEM601B in 10.0-10.6 weight portions, quartz sand in 62.0-64.0 weight portions, water-base epoxy color sand in 2.0-3.0 weight portions and water in 5.0-5.5 weight portions. The water-base epoxy color sand mortar as one kind of environment friendly decoration product has specific decoration effect and is water resistant, chemical corrosion resistant, oil contamination resistant, wear resistant, high in strength and high in adhesion strength.
Description
[technical field]
The present invention relates to paint field, particularly be a kind of water-base epoxy color sand mortar and preparation method thereof and constructional method.
[background technology]
Along with the increasing of national environmental protection dynamics, people have promoted to be the development of the low-contamination type coating of representative with the water-borne coatings to the enhancing of environmental consciousness and to the raising of ornamental requirement, and aqueous epoxy coating is adapting to development of times with the harmless characteristics of low toxicity.
Needs in conjunction with the house fitting-up development; in traditional-family's finishing, adopt ceramic tile, timber floor etc. mostly; make the decorative effect of terrace have stationarity; water-base epoxy color sand mortar is except playing a very good protection to the floor, and needs that can also satisfying personalized decoration: Decoration Design changes flexibly and the effect personalized design that realizes attractive in appearance.
What at present the industry ground slab usage quantity was more is the solvent-borne type epoxide terrace, contains in the SOLVENT BASED EPOXY FLOOR COATINGS in a large number the poisonous and hazardous organic solvent of human body, in use environment is caused serious pollution.Nontoxic, the not pollution of water-base epoxy color sand mortar series can provide the physical and chemical performance suitable with solvent-borne type, and replacing solvent-borne type epoxide terrace industrial paint is the certainty that adapts to era development.
With ground that the earth directly contacts on construct, for non-solvent epoxy, solvent-borne type epoxy, the general moisture that comes up can't be discharged timely from ground, and phenomenon such as coating can occur bubbling, comes off, hollowing has a strong impact on the sticking power on non-solvent epoxy or solvent-borne type epoxy and ground.And water-base epoxy color sand mortar has particular performances, it is permeable watertight, can be effectively the moisture on ground be discharged by the kapillary of way layer, like this coating with regard to can not occur bubbling, come off, the phenomenon of hollowing, the sticking power on coating and ground can be not influenced yet.
In the daily clean and maintenance process of terrace, what be difficult to clean most is exactly ceramic tile seam, timber floor seam, and contamination resistance is poor.After the water-base epoxy color sand mortar terrace is made, integral seamless, smoothly beautifully reach mirror effect, easy to cleanly be convenient to safeguard, dustproof, waterproof, anti-electrostatic or the like.
In the solvent-borne type epoxy construction process, there is the release of a large amount of obnoxious flavoures construction aspect at the scene, and construction workman's health is caused certain injury, and influences surrounding environment; And the water-base epoxy color sand mortar floor construction is simple, quick and easy, the release of no obnoxious flavour in the construction process, and safety and environmental protection, after the construction, service tool directly water cleans; The working procedure of ceramic tile, timber floor is complicated, long construction period.
[summary of the invention]
The purpose of this invention is to provide a kind of water-base epoxy color sand mortar and preparation method thereof and constructional method.This water-base epoxy color sand mortar has nontoxic, non-stimulated smell, does not contain toxic organic solvent (as: benzene class, ketone, ester etc.), do not contain any harmful heavy metal material (as: lead, mercury etc.), belong to environmental protection safety type product, it is good to have water-fast, alkaline-resisting, anti-solvent, oil resistant dirt, wear resistance, resistance to compression, bending resistance and tensile strength advantages of higher.Preparation technology is simple, requires low to production unit.
A kind of water-base epoxy color sand mortar consists of by weight:
The A component, KNP WEM601A, 16.5～17.5 parts;
The B component, 10.0～10.6 parts of KNP WEM601B;
No. 6 quartz sands, 62.0～64.0 parts;
Water-base epoxy color sand, 2.0～3.0 parts;
Water, 5.0～5.5 parts.
The preparation method of above-mentioned water-base epoxy color sand mortar may further comprise the steps:
A, take by weighing water-base epoxy color sand mortar A component, water-base epoxy color sand mortar B component, quartz sand, color sand, water by weight;
B, pour water-base epoxy color sand mortar A component and B component into agitator and stir 10min, make its thorough mixing even with 1000r/min;
C, quartz sand, color sand, water are poured in the compound of A component and B component, in agitator, mixed, obtain water-base epoxy color sand mortar.
The constructional method of above-mentioned water-base epoxy color sand mortar may further comprise the steps:
A, the surface of constructing is cleaned, and absorbed the dust and the sand grains on construction surface with suction cleaner;
B, employing seal coat carry out back cover to the surface of constructing;
The construction that coating method carries out color sand mortar is scraped in C, employing, is limited to 2 hours during construction, coating thickness≤2mm, and 10～45 ℃ of construction temperatures, humidity is less than 80%;
D, construction back maintenance seven days can be gone up the people after three days, normally came into operation after seven days.
Advantage of the present invention: preparation technology is simple, and equipment requirements is low, and routine maintenance is easy; Water-fast, the dirt of chemicals-resistant burn into oil resistant; Wear resistance is good, resistance to compression, bending resistance, cohesive strength height; Generic environmental protection safety type product, water be as thinner, extremely low or VOC free discharging, pollution-free and burning, explosion hazard; After adding color sand in the water-base epoxy mortar, has special individual decoration effect.
[embodiment]
In the present invention, the component of water-base epoxy color sand mortar is: A component, B component, quartz sand, color sand, water.Water-base epoxy color sand mortar A component is meant the KNP WEM601A that extra large river chemical company produces, and its consumption is 16.5～17.5 parts (weight, as follows); Water-base epoxy color sand mortar B component is meant the KNP WEM601B that extra large river chemical company produces, and its consumption is 10.0～10.6 parts; Quartz sand is No. 6 general quartz sands, and its consumption is 62.0～64.0 parts; Color sand is meant the water-base epoxy color sand that extra large river chemical company produces, and its consumption is 2.0～3.0 parts; Water plays diluting effect, regulates viscosity, is convenient to construction, and its consumption is 5.0～5.5 parts.
The preparation method of water-base epoxy color sand mortar may further comprise the steps:
A, take by weighing water-base epoxy color sand mortar A component, water-base epoxy color sand mortar B component, quartz sand, color sand, water by weight;
B, pour water-base epoxy color sand mortar A component and B component into agitator and stir 10min, make its thorough mixing even with 1000r/min;
C, quartz sand, color sand, water are poured in the compound of A component and B component, in agitator, mixed, obtain water-base epoxy color sand mortar.
The constructional method of water-base epoxy color sand mortar may further comprise the steps:
A, the surface of constructing is cleaned, and absorbed the dust and the sand grains on construction surface with suction cleaner;
B, employing seal coat carry out back cover to the surface of constructing;
The construction that coating method carries out color sand mortar is scraped in C, employing, is limited to 2 hours during construction, coating thickness≤2mm, and 10～45 ℃ of construction temperatures, humidity is less than 80%;
D, construction back maintenance seven days can be gone up the people after three days, normally came into operation after seven days.
Embodiment 1:
Take by weighing the A component, KNP WEM601A, 16.5kg; The B component, KNP WEM601B, 10.6kg; No. 6 quartz sands, 64.0kg; Water-base epoxy color sand, 2.5kg; Water, 5.0kg.Pour water-base epoxy color sand mortar A component and B component into agitator and stir 10min, make its thorough mixing even with 1000r/min.Quartz sand, color sand, water are poured in the compound of A component and B component, in agitator, mixed, obtain water-base epoxy color sand mortar.The surface of constructing is cleaned, and absorbed the dust and the sand grains on construction surface with suction cleaner; Adopt seal coat that back cover is carried out on the surface of constructing; The construction that coating method carries out color sand mortar is scraped in employing, is limited to 2 hours during construction, coating thickness≤2mm, and 10～45 ℃ of construction temperatures, humidity is less than 80%; Adopt transparent varnish that color sand mortar is carried out Lacquer finish.Construction back maintenance seven days can be gone up the people after three days, normally came into operation after seven days.
Embodiment 2:
Take by weighing the A component, KNP WEM601A, 17.5kg; The B component, KNP WEM601B, 10.3kg; No. 6 quartz sands, 63.0kg; Water-base epoxy color sand, 3.0kg; Water, 5.5kg.Preparation process and constructional method are with embodiment 1.
Embodiment 3:
Take by weighing the A component, KNP WEM601A, 17.0kg; The B component, KNP WEM601B, 10.0kg; No. 6 quartz sands, 62.0kg; Water-base epoxy color sand, 2.0kg; Water, 5.3kg.Preparation process and constructional method are with embodiment 1.
Contain red quartz sand in the color sand mortar terrace, added aesthetic to screed.Have good physicals and chemical resistance.Have integral seamless, smooth beautiful mirror effect, easy to clean being convenient to safeguarded.
Claims (3)
1, a kind of water-base epoxy color sand mortar consists of by weight:
The A component, KNP WEM601A, 16.5～17.5 parts;
The B component, 10.0～10.6 parts of KNP WEM601B;
No. 6 quartz sands, 62.0～64.0 parts;
Water-base epoxy color sand, 2.0～3.0 parts;
Water, 5.0～5.5 parts.
2, prepare the method for the described water-base epoxy color sand mortar of claim 1, may further comprise the steps:
A, take by weighing water-base epoxy color sand mortar A component, water-base epoxy color sand mortar B component, quartz sand, color sand, water by weight;
B, pour water-base epoxy color sand mortar A component and B component into agitator and stir 10min, make its thorough mixing even with 1000r/min;
C, quartz sand, color sand, water are poured in the compound of A component and B component, in agitator, mixed, obtain water-base epoxy color sand mortar.
3, the constructional method of the described water-base epoxy color sand mortar of claim 1 may further comprise the steps:
A, the surface of constructing is cleaned, and absorbed the dust and the sand grains on construction surface with suction cleaner;
B, employing seal coat carry out back cover to the surface of constructing;
The construction that coating method carries out color sand mortar is scraped in C, employing, is limited to 2 hours during construction, coating thickness≤2mm, and 10～45 ℃ of construction temperatures, humidity is less than 80%;
D, construction back maintenance seven days can be gone up the people after three days, normally came into operation after seven days.