CN100532477C - Tempering ceramic glaze paint - Google Patents

Tempering ceramic glaze paint Download PDF

Info

Publication number
CN100532477C
CN100532477C CNB2006100437521A CN200610043752A CN100532477C CN 100532477 C CN100532477 C CN 100532477C CN B2006100437521 A CNB2006100437521 A CN B2006100437521A CN 200610043752 A CN200610043752 A CN 200610043752A CN 100532477 C CN100532477 C CN 100532477C
Authority
CN
China
Prior art keywords
agent
glaze paint
defoamer
ceramic glaze
tempering
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006100437521A
Other languages
Chinese (zh)
Other versions
CN101063020A (en
Inventor
王健
Original Assignee
王健
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 王健 filed Critical 王健
Priority to CNB2006100437521A priority Critical patent/CN100532477C/en
Publication of CN101063020A publication Critical patent/CN101063020A/en
Application granted granted Critical
Publication of CN100532477C publication Critical patent/CN100532477C/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a tempering ceramic glaze paint, which comprises the following steps: allocating 40-45 wt hydroxy acrylic resin, 10-20 wt inorganic ceramic colors, 2-5 wt leveling agent, 0. 5-5 wt anti-settling agent, 5-10 wt adhesive force promotion agent, 5-10 wt disperser and 5-15 wt filler; getting the product. This invention possesses slide, firm, corrosion resistant and so on property of enamel glaze, which durability can reach above ten years.

Description

Tempering ceramic glaze paint
Technical field
The invention belongs to paint field, particularly a kind of tempering ceramic glaze paint.
Background technology
Ceramic tile is mainly used in the decoration and the protection of buildings interior and exterior wall, ceramic tile glaze smooth surface, and beautiful in colour, corrosion resistance is strong.But As time goes on, being exposed to the sun and the pollution of atmospheric environment of the sun, the ceramic tile be full of cracks that wears loses original color and gloss, and spot is innumerable especially particularly to be subjected to the exterior wall of acid rain and sea wind etch, has a strong impact on attractive in appearance and city look and feel.But ceramic tile and buildings are combined as a whole, can't fire again.Because the ceramic tile appearance is very smooth, general coating and paint etc. are difficult to for a long time attached to its surface, so adopt the mode of swabbing not deal with problems.Paste if old ceramic tile is pounded again dress again, both needed a lot of man power and materials, lose time again and money, and cause very big inconvenience for the environment and the traffic of periphery.
Summary of the invention
Technical problem to be solved by this invention provides a kind of tempering ceramic glaze paint, can be painted on ceramic tile surface, reaches the effect of ceramic tile glaze.
Tempering ceramic glaze paint of the present invention, it is characterized in that consisting of by weight percentage: hydroxy acryl acid resin 40~45, inorganic ceramic pigment 10~20, flow agent 2~5, defoamer 0.5~5, anti-settling agent 0.5~5, sticking power promotor 5~10, dispersion agent 5~10 and filler 5~15.
Described flow agent can be selected acrylate type flow agent (is the product of MFAOH, MFPX50 as the trade mark), wax powder or special modified-reaction type polysiloxane (is the product of DE2890, DE8380 as the trade mark).
Described defoamer can be selected brokenly bubble polysiloxane solution such as the trade mark 861,891, non-silicon degassing defoamer (consisting of high molecular weight ethylene ether/ester copolymer) CFC-2000 or calcium stearate.
Described anti-settling agent can select HFGEL series organobentonite to become auxiliary agent 140 types or 160 types, polymeric amide sag prevention (as the product of the trade mark into CIMA240-20 or 290-20).
Described sticking power promotor can be selected silane (is KEPER 993 as the trade mark) for use.
Described dispersion agent can be selected Zinic stearas, aluminum stearate or barium stearate.
Described filler can be selected titanium dioxide, lime carbonate, aluminum oxide powder or Tianna solution.
Inorganic ceramic pigment can be commercially available known various beramic color products, and color difference is as requested selected suitable pigment, as gold palm fibre, chrome green etc.
The present invention is when making, solid ingredient should be more than 800 orders, and beramic color is more than 600 orders, and concrete making method is: according to each proportioning raw materials, in stainless steel or enamel stirrer, put into hydroxy acryl acid resin, inorganic ceramic pigment earlier, mix, add other component then, stirred at a slow speed 6~8 hours, reinstalling stainless steel or enamel reactor rises and falls and oozes 4~6 hours mutually, join at last in the stainless-steel grinding machine and ground blowing, the pail pack of packing into 4~6 hours.
The constructional method of product of the present invention needs normal temperature to brush or spraying is solidified as common coating, can reach the performance such as mellow and full, smooth, firm, corrosion-resistant of enamel matter.
Advantage of the present invention:
Construction is simple, can brush or the spraying of common spraying equipment with brush, has performances such as enamel matter is mellow and full, smooth, firm, corrosion-resistant.Resistance to soiling is strong, and easy cleaning has solved traditional emulsion paint bad contamination-proof capability, not the disadvantage of easy cleaning.Through test of many times, no abnormal variation in low temperature resistant-40 ℃~high temperature resistant 160 ℃ of scopes; Water tolerance 268 hours is no abnormal; Alkali resistance 168 hours is no abnormal; Abrasion resistance 〉=2000 time; Artificial weathering ageing resistance 1000 hours is non-foaming, do not peel off, flawless; It is accessible that two roads are brushed in construction; 5 circulations of coating temperature-change resistance are no abnormal.This product price is low, and the life-span can reach more than 10 years.
Product of the present invention also has very strong anticorrosion, waterproof ability, can be widely used in the pot-type equipment and the pipeline of industries such as viaduct, steel construction, petrochemical industry, electric power, is used for the decoration and the protection of new building.
Below be the survey report of coating pigment product quality test center, Shandong Province to this product sample:
Embodiment
Following examples are in parts by weight, and the present invention is not limited to following examples.
Embodiment 1:
Hydroxy acryl acid resin (trade mark AH2870) 43
Inorganic ceramic pigment 15
Acrylate type flow agent (MFAOH) 4
Defoamer: broken bubble polysiloxane solution 861 2
Anti-settling agent: HFGEL series organobentonite becomes auxiliary agent 140 types 3
Sticking power promotor: silane (KEPER993) 7
Dispersion agent: Zinic stearas 8
Filler: titanium dioxide 10
Embodiment 2:
Hydroxy acryl acid resin (trade mark AH2870) 40
Inorganic ceramic pigment 10
Flow agent: wax powder (DE8418) 3
Defoamer: CFC-2000 0.5
Anti-settling agent: HFGEL series organobentonite becomes auxiliary agent 160 types 1
Sticking power promotor: silane (KEPER993) 5
Dispersion agent: aluminum stearate 5
Filler: lime carbonate 5
Embodiment 3:
Hydroxy acryl acid resin (trade mark AH2870) 45
Inorganic ceramic pigment 20
Flow agent: special modified-reaction type polysiloxane (DE2890) 5
Defoamer: calcium stearate 5
Anti-settling agent: polymeric amide sag prevention (CIMA240-20) 5
Sticking power promotor: silane (KEPER993) 10
Dispersion agent: barium stearate 9
Filler: aluminum oxide powder 12
Embodiment 4:
Hydroxy acryl acid resin (trade mark AH2870) 42
Inorganic ceramic pigment 16
Flow agent: special modified-reaction type polysiloxane (DE8380) 2
Defoamer: calcium stearate 3
Anti-settling agent: polymeric amide sag prevention (CIMA290-20) 0.5
Sticking power promotor: silane (KEPER993) 5
Dispersion agent: Zinic stearas 7
Filler: Tianna solution 8

Claims (3)

1, a kind of tempering ceramic glaze paint, it is characterized in that by weight percentage, consist of: hydroxy acryl acid resin 40~45, inorganic ceramic pigment 10~20, flow agent 2~5, defoamer 0.5~5, anti-settling agent 0.5~5, sticking power promotor 5~10, dispersion agent 5~10 and filler 5~15, described flow agent is acrylate type flow agent or wax powder, defoamer is broken bubble polysiloxane solution 861, broken bubble polysiloxane solution 891, non-silicon degassing defoamer CFC-2000 or calcium stearate, anti-settling agent is that HFGEL series organobentonite becomes auxiliary agent 140 types or 160 types, polymeric amide sag prevention CIMA240-20 or 290-20, sticking power promotor are KEPER 993 silane.
2, tempering ceramic glaze paint according to claim 1 is characterized in that described dispersion agent is Zinic stearas, aluminum stearate or barium stearate.
3, tempering ceramic glaze paint according to claim 1 is characterized in that described filler is titanium dioxide, lime carbonate, aluminum oxide powder or Tianna solution.
CNB2006100437521A 2006-04-28 2006-04-28 Tempering ceramic glaze paint Expired - Fee Related CN100532477C (en)