CN1944311A - 四氟浸涂复膜玻璃纤维及其制造方法 - Google Patents
四氟浸涂复膜玻璃纤维及其制造方法 Download PDFInfo
- Publication number
- CN1944311A CN1944311A CN 200610047779 CN200610047779A CN1944311A CN 1944311 A CN1944311 A CN 1944311A CN 200610047779 CN200610047779 CN 200610047779 CN 200610047779 A CN200610047779 A CN 200610047779A CN 1944311 A CN1944311 A CN 1944311A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- make
- ptfe
- coated glass
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
四氟浸涂复膜玻璃纤维及其制造方法，属四氟浸涂复膜玻璃纤维的研制开发领域。产品用于制造工业烟气过滤制品。现有方法生产的玻璃纤维属脆性材料，不耐折，不耐复合酸气腐蚀。制出的产品使用寿命短，使用范围窄。本发明包括复膜剂的配制和浸涂复膜。复膜剂配方成份有聚四氟乙烯分散液、水溶性环氧树脂、偶联剂、甲基丙烯酰氧基丙基3甲氧基硅烷及水等。配制方法是将水及其他成分物质在调配槽内混配均匀即可。涂复是将复膜剂盛于拉丝装置上的拉丝油容器内，纤维从拉丝头出来后，通过拉丝油喷嘴，使复膜剂均匀地复在玻纤表面。用本方法生产的玻纤制成的过滤用品具有耐高温，抗折，耐复合酸气的特点。产品使用寿命长，使用范围广。其方法简单，易于操作。
Description
技术领域
本发明属四氟浸涂复膜玻璃纤维的研制开发领域。
背景技术
目前，用于工业烟气过滤材料主要有两大类，一类是无机纤维，以玻璃纤维为主。另一类是有机纤维。玻璃纤维具有强力大，耐高温，耐单一种分酸气的特点，一直是作为生产工业烟气过滤制品的主要原料。但它不耐折，属脆性材料，不耐复合酸气。因此在使用中，便显现出使用寿命短的缺点。随着工业的发展，对烟气过滤材料的要求不断提高。为提高烟气过滤用品的使用寿命，研制出耐折、抗老化、耐复合酸气的玻纤材料是一个重大课题。到目前为止，还没有与本发明相同方法生产的玻纤材料在生产实际中应用。
发明内容
本发明的目的是提供一种生产耐折、抗老化、耐复合酸气的玻璃纤维的方法，用该方法生产的玻纤材料制造的工业烟气过滤用品，可有效地提高使用寿命，扩大使用范围，以解决现有传统方法生产的玻纤材料制作过滤用品存在的使用寿命短的问题。
本发明是通过如下技术方案得以实现的；其核心内容是生产出的玻璃纤维的表面上带有一层四氟浸涂复膜。其生产方法分为两个步骤，一是复膜剂的配制，二是在生产中将复膜剂浸涂在产品表面上。
1、复膜剂配制
1～1技术配方
成份 重量比
60％聚四氟乙烯分散液 0.5～2.0Kg
55％681水溶性环氧树脂乳液 1～10Kg
SR1-1偶联剂 0.5～5Kg
95％甲基丙烯酰氧基丙基3甲氧基硅烷 0.1～1Kg
100％乙醇 0.1～1Kg
平平加 0.1～1Kg
二辛酯 0.1～1Kg
水 70～100Kg
1～2配制方法
先将水加入于调配槽中，然后加入681水溶性环氧树脂，再加入SR1-1偶联剂。加入后搅拌均匀。然后将甲基丙烯酰氧基丙基3甲氧基硅烷和乙醇调配后加入调配槽中。再将平平加和二辛酯分别加热溶化后将二者调配均匀，再加入到调配槽中，充分搅拌，使各配料混合均匀。然后将聚四氟乙烯分散流加入到调配槽。再进行充分搅拌，达到均匀混配。制成复膜剂。呈乳液状。
2、浸涂复膜
将制得的玻纤复膜剂，盛于拉丝装置的拉丝油容器内。在初生纤维从拉丝头出来后，纤维通过拉丝油喷咀，使复膜剂均匀地涂复在初生纤维表面。随着纤维的冷却，复膜剂在纤维表面固化成型。制得四氟浸涂复膜玻璃纤维。根据所生产过滤用品的不同要求，其复膜的厚度亦不一样。采用调节复膜剂浓度的方法来解决。复膜浓度则由加水的量来调节。复膜剂浓度大，则复膜厚，反之则复膜厚度薄。本发明方法简单，易于操作。采用本发明方法制成的玻璃纤维，不仅保持自身的强力大，耐高温的特点。由于带有一层四氟复膜，提高了它的耐折性，而老化和耐复合酸气能力也得到改善。制成的工业烟气过滤制品的使用寿命也得到极大的提高，是一种理想的工业烟气过滤用品制造材料。
本发明无附图
具体实施方式
1、复膜剂配制
1～1技术配方
成份 重量比
60％聚四氟乙烯分散液 1.5Kg
55％681水溶性环氧树脂乳液 8Kg
SR1-1偶联剂 4Kg
95％甲基丙烯酰氧基丙基3甲氧基硅烷 0.7Kg
100％乙醇 0.7Kg
平平加 0.7Kg
二辛酯 0.7Kg
水 100Kg
1～2配制方法
先将水加入于调配槽中，然后加入681水溶性环氧树脂，再加入SR1-1偶联剂。加入后搅拌均匀。然后将甲基丙烯酰氧基丙基3甲氧基硅烷和乙醇调配后加入调配槽中。再将平平加和二辛酯分别加热溶化后将二者调配均匀，再加入到调配槽中，充分搅拌，使各配料混合均匀。然后将聚四氟乙烯分散流加入到调配槽。再进行充分搅拌，达到均匀混配。制成复膜剂。呈乳液状。
2、浸涂复膜
将制得的玻纤复膜剂，盛于拉丝装置的拉丝油容器内。在初生纤维从拉丝头出来后，纤维通过拉丝油喷咀，使复膜剂均匀地涂复在初生纤维表面。随着纤维的冷却，复膜剂在纤维表面固化成型。制得四氟浸涂复膜玻璃纤维。根据所生产过滤用品对复膜厚度要求的不同。则采用调节复膜剂浓度即调节加水量的方法来解决。但水的用量在70～100公斤范围内。复膜剂浓度大，则复膜厚，反之则复膜厚度薄。
Claims (2)
1、四氟浸涂复膜玻璃纤维，其特征在于表面上带有一层四氟浸涂复膜。
2、四氟浸涂复膜玻璃纤维的制造方法，其特征是：
复膜剂配制
技术配方
成份 重量比
60％聚四氟乙烯分散液 0.5～2.0Kg
55％681水溶性环氧树脂乳液 1～10Kg
SR1-1偶联剂 0.5～5Kg
95％甲基丙烯酰氧基丙基3甲氧基硅烷 0.1～1Kg
100％乙醇 0.1～1Kg
平平加 0.1～1Kg
二辛酯 0.1～1Kg
水 70～100Kg
配制方法
先将水加入于调配槽中，然后加入681水溶性环氧树脂，再加入SR1-1偶联剂，加入后搅拌均匀，然后将甲基丙烯酰氧基丙基3甲氧基硅烷和乙醇调配后加入调配槽中，再将平平加和二辛酯分别加热溶化后将二者调配均匀，再加入到调配槽中，充分搅拌，使各配料混合均匀，然后将聚四氟乙烯分散流加入到调配槽，再进行充分搅拌，达到均匀混配，
浸涂复膜
将制得的玻纤复膜剂，盛于拉丝装置的拉丝油容器内，在初生纤维从拉丝头出来后，纤维通过拉丝油喷咀，使复膜剂均匀地涂复在初生纤维表面，随着纤维的冷却，复膜剂在纤维表面固化成型。