CN1896329A - 一种铝电解用纯氟体系电解质 - Google Patents
一种铝电解用纯氟体系电解质 Download PDFInfo
- Publication number
- CN1896329A CN1896329A CN 200610051113 CN200610051113A CN1896329A CN 1896329 A CN1896329 A CN 1896329A CN 200610051113 CN200610051113 CN 200610051113 CN 200610051113 A CN200610051113 A CN 200610051113A CN 1896329 A CN1896329 A CN 1896329A
- Authority
- CN
- China
- Prior art keywords
- electrolyte
- alf
- electrolysis
- pure
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝电解用纯氟体系电解质,它由AlF3、LiF、CaF2、MgF2、KF、Al2O3、Na3AlF6配制而成。按重量百分比计,各组分所占比例为:AlF35%~30%,LiF2%~40%,CaF22~6%,MgF22~8%,KF2~10%,Al2O32~2.5%,余量为Na3AlF6,按常规方法配制成电解槽所用电解质;本发明具有能减少氟化物挥发损失和改善铝电解厂房周边环境、降低槽电压和能耗及生产成本、延长铝电解槽寿命等优点。
Description
技术领域:
本发明涉及一种铝电解生产中电解槽所用的纯氟体系电解质。
技术背景:
自霍尔-埃鲁法诞生以来,它就成为了铝工业生产金属铝的首选工艺方法。100多年来,其工艺技术和装备都有了巨大的改进和提高,但其基本原理仍为钠冰晶石-氧化铝熔盐电解。长期的生产实践证实,该法尚有电解温度高(940~960℃)、导电率低(约2S/cm2)、能耗高和污染大的缺点。
霍尔-埃鲁法工艺是自电解质体系来建立的,电解质体系的组成,决定了电解质体系的物性。要想改变电解质体系的物性,就必须变化电解质体系的组成,这里添加剂的研究是必不可少的。在铝工业界,对电解质添加剂的研究很多,但大多是研究某一种添加剂的影响,而未从整个电解质成分体系来考虑如何使其更适用于铝电解工艺。
发明内容:
本发明的目的在于:提供一种纯氟体系电解质,它可降低铝电解质初晶温度,减少能耗和氟化物损失,提高铝电解质电导率,使铝电解生产的节能降耗增产得到较大的改善。
本发明是这样实现的:
所述的铝电解电解质,它由AlF3、LiF、CaF2、MgF2、KF、Al2O3、Na3AlF6配制而成。按重量百分比计,各组分所占比例为:AlF35%~30%,LiF2%~40%,CaF22~6%,MgF22~8%,KF2~10%,Al2O32~2.5%,余量为Na3AlF6;按常规方法配制而成。
该铝电解用电解质的初晶温度在800-850℃,比重为1.9~2.1g/cm3,导电率为3~4Ω-1.cm-1。
本发明与现有铝电解技术相比,由于作业温度的降低和电解质导电率的提高,能减少氟化物挥发损失和改善铝电解厂房周边环境、降低槽电压和能耗及生产成本、延长铝电解槽寿命;而且本电解质体系是纯氟化物构成,现有铝电解工业不需做大的变动即可使用。
具体实施方式:
本发明的实施例:
取AlF330%,LiF10%,CaF22.5%,MgF22.5%,KF2.5%,Al2O32.5%,Na3AlF650%,按重量百分比称量好,均匀混合后放入铝电解槽中供生产所用。在此组分下,电解质初晶温度为839℃,比重为2.1g/cm3,导电率为3.3Ω-1.cm-1。
Claims (2)
1、一种铝电解用纯氟体系电解质,它由AlF3、LiF、CaF2、MgF2、KF、Al2O3、Na3AlF6配制而成,其特征在于:按重量百分比计,各组分所占比例为:AlF35%~30%,LiF2%~40%,CaF22~6%,MgF22~8%,KF2~10%,Al2O32~2.5%,余量为Na3AlF6;按常规方法配制而成。
2、根据权利要求1所述的电解铝用纯氟化物电解质,其特征在于:所述的电解质的初晶温度在800-850℃,比重为1.9~2.1g/cm3,导电率为3~4Ω-1.cm-1。