CN1854195A - 增强尼龙和abs合金材料 - Google Patents
增强尼龙和abs合金材料 Download PDFInfo
- Publication number
- CN1854195A CN1854195A CN 200510025572 CN200510025572A CN1854195A CN 1854195 A CN1854195 A CN 1854195A CN 200510025572 CN200510025572 CN 200510025572 CN 200510025572 A CN200510025572 A CN 200510025572A CN 1854195 A CN1854195 A CN 1854195A
- Authority
- CN
- China
- Prior art keywords
- abs
- alloy material
- reinforced nylon
- abs alloy
- nylon according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种增强尼龙和ABS合金材料,它有一混合物组成,其重量配比组成为:尼龙6切片30-70%,ABS 10-50%,SAN 5-30%,玻璃纤维10-40%,相容剂1-10%,抗氧剂0.1-1%,润滑剂0.1-0.5%。本发明具有尺寸稳定,高强度,外观好,高流动性,耐药品性等特点,可用于注塑成型汽车轮罩、仪表盘圆架、保险杆、体育器械及其他电机产品。
Description
技术领域
本发明涉及一种增强尼龙和ABS合金材料,尤其涉及一种注塑成型汽车轮罩、仪表盘圆架、保险杆、体育器械及其他电机产品的一种增强尼龙和ABS合金材料。
技术背景
尼龙/ABS合金最早由美国的Borg Warner Chemicals公司和Monsanto公司推出,具有热变形温度比PA高,以及维卡软化温度较高的特点,因而成为制造汽车车身壳板等汽车部件的理想材料。
PA6具有耐磨、耐溶剂、耐油、使用温度广等优点,但也存在吸水性大、尺寸稳定性差、低温和干态冲击强度低等不足,大大限制了它的使用。将PA6与ABS共混,可制得既有ABS的韧性、又有PA的耐热性和耐油性的合金。该种合金被广泛应用于汽车、电子电器、家庭用器等。但是由于PA6是一种结晶性、强极性、熔体粘度很低的聚合物,而ABS是一种非结晶性、弱极性的聚合物,二者的溶解度参数相差较大,属热力学不相容,简单的工混导致两相界面张力很大,从而造成力学性能较差,因而要获得有实用价值的尼龙/ABS合金材料,必须进行形态控制和界面改性。
发明内容
本发明的目的在于提供一种具有尺寸稳定、高强度、外观好、高流动、,耐药品性的增强尼龙和ABS合金材料。
为实现以上目的,本发明的技术方案是提供一种高强度尼龙和ABS合金材料,它有一混合物组成,其重量配比组成为:
尼龙6切片 30-70%
ABS 10-50%
SAN 5-30%
玻璃纤维 10-40%
相容剂 1-10%
抗氧剂 0.1-1%
润滑剂 0.1-0.5%
其中尼龙6切片的相对粘度为2.4-3.8Pa·S;ABS为丙烯腈、丁二烯与苯乙烯三元共聚物,其橡胶含量为35%-70%;SAN为苯乙烯和丙烯腈的共聚物,其熔融指数为15-40g/10min;玻璃纤维为无碱玻璃纤维,其表面经硅烷偶联剂处理;相容剂为聚合物A接枝马来酸酐,可以为SMA、ABS-g-MAH;聚合物A可以是PS、AS、ABS;抗氧剂包括一种受阻酚类抗氧剂,可以是1076,和一种受阻酚类抗氧剂与亚磷酸酯类抗氧剂的复配体系,可以是1010/168(1∶1);润滑剂为超高分子量聚硅氧烷。
本发明的制备工艺为:除玻璃纤维外,先将其他组分按比例放入高混机种混合2-5分钟,然后与玻璃纤维一起用螺杆挤出机挤出造粒,加工温度在180-260℃,螺杆转数在180-600转/分。
PA6具有耐磨、耐溶剂、耐油、使用温度广等优点,是目前产量最大的工程塑料。
丙烯腈/丁二烯/苯乙烯三元共聚物集合了苯乙烯具有的光泽性和成型性,丙烯腈具有的刚性和耐药品性以及优异的机械性能,丁二烯具有的耐冲击性,与尼龙共混可以改善尼龙的尺寸稳定性、冲击强度、耐化学性以及加工性能。
SAN具有极好的流动性能和抗药品性能以及刚性。在体系中与尼龙部分相容,可以提高合金材料的刚性和流动性能。
由于尼龙和ABS属热力学不相容材料,相容剂的加入可极大地提高两者的相容性,解决热力学不相容的问题,改善合金的综合力学性能。
抗氧剂包括一种受阻酚类抗氧剂,可以是1076,主要用于防止ABS/SAN的氧化,和一种受阻酚类抗氧剂与亚磷酸酯类抗氧剂的复配体系,可以是1010/168(1∶1),主要防止PA6的氧化。
超高分子量聚硅氧烷作为润滑剂,提高材料加工流动性,降低摩擦系数,提高滑爽性,改善表面光泽。
本发明采用尼龙6和ABS树脂,制得一种高强度尼龙/ABS合金材料,很好地解决了尼龙材料的尺寸不稳定、易翘曲的缺点,以及尼龙6和ABS材料的热力学不相容的特点,制备了一种具有尺寸稳定、强度高、外观好、高流动性、耐药品性的尼龙/ABS合金材料。
本发明的优点是兼具了尼龙6和ABS两者的特性,材料尺寸稳定,强度高,外观好,高流动性,耐药品性。
具体实施方案
下面结合实施例,对本发明作进一步详细说明:
实施例1和2:
以SMA、ABS-g-MAH为相容剂,1098/168(1∶1)和1076为抗氧剂,高分子量聚硅氧烷为润滑剂。
配比1-2
原料名称 | 配比1(wt%) | 配比2(wt%) |
PA6切片 | 30 | 40 |
ABS | 34 | 24 |
SAN | 10 | 8 |
玻璃纤维 | 20 | 20 |
SMA | 5 | -- |
ABS-g-MAH | -- | 7 |
1098/168(1∶1) | 0.4 | 0.4 |
1076 | 0.3 | 0.3 |
高分子量聚硅氧烷 | 0.3 | 0.3 |
除玻璃纤维外,先将其他组分按比例放入高混机种混合4分钟,然后与玻璃纤维一起用螺杆挤出机挤出造粒,加工温度在230℃,螺杆转数在500转/分。
根据实施例1、实施例2制得的样品1、样品2与BASF公司TRIAX系列的产品性能对比
测试性能对比(表2)
项目 | 样品1 | 样品2 | TRIAX |
拉伸强度Mpa | 107.6 | 110.3 | 98.0 |
弯曲强度Mpa | 145.2 | 146.0 | 138.0 |
抗弯模量Mpa | 5700 | 5756 | 5204 |
冲击强度J/M | 16.0 | 14.3 | 14.5 |
收缩率% | 0.2-0.5 | 0.2-0.4 | 0.2.0.5 |
Claims (9)
1.一种增强尼龙和ABS合金材料,它有一混合物组成,其重量配比组成为:
尼龙6切片 30-70%
ABS 10-50%
SAN 5-30%
玻璃纤维 10-40%
相容剂 1-10%
抗氧剂 0.1-1%
润滑剂 0.1-0.5%
2.根据权利要求1所述的增强尼龙和ABS合金材料,其中尼龙6切片的相对粘度为2.4-3.8Pa·S。
3.根据权利要求1所述的增强尼龙和ABS合金材料,其中ABS为丙烯腈、丁二烯与苯乙烯三元共聚物,其橡胶含量为35%-70%。
4.根据权利要求1所述的增强尼龙和ABS合金材料,其中SAN为苯乙烯和丙烯腈的共聚物,其熔融指数为15-40g/10min。
5.根据权利要求1所述的增强尼龙和ABS合金材料,其中玻璃纤维为无碱玻璃纤维,其表面经硅烷偶联剂处理。
6.根据权利要求1所述的增强尼龙和ABS合金材料,其中相容剂为聚合物A接枝马来酸酐,可以为SMA、ABS-g-MAH。
7.根据权利要求6所述的增强尼龙和ABS合金材料,其中聚合物A可以是PS、AS、ABS。
8.根据权利要求1所述的增强尼龙和ABS合金材料,其中抗氧剂包括一种受阻酚类抗氧剂,可以是1076,和一种受阻酚类抗氧剂与亚磷酸酯类抗氧剂的复配体系,可以是1010/168(1∶1)。
9.根据权利要求1所述的增强尼龙和ABS合金材料,其中润滑剂为超高分子量聚硅氧烷。