CN1837306A - 塑料装饰涂料与配套稀释剂 - Google Patents
塑料装饰涂料与配套稀释剂 Download PDFInfo
- Publication number
- CN1837306A CN1837306A CN 200510055664 CN200510055664A CN1837306A CN 1837306 A CN1837306 A CN 1837306A CN 200510055664 CN200510055664 CN 200510055664 CN 200510055664 A CN200510055664 A CN 200510055664A CN 1837306 A CN1837306 A CN 1837306A
- Authority
- CN
- China
- Prior art keywords
- plastic coating
- decorative plastic
- coating according
- agent
- thinner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种塑料装饰涂料，该涂料包括有以下组分：丙烯酸树脂、颜料或染料、溶剂、添加剂、辅料；以及与此涂料配套的稀释剂。本发明使用丙烯酸树脂、颜料、溶剂、添加剂等材料制造塑料装饰涂料，无论春夏秋冬都能在无表面处理的条件下一次性喷涂装饰聚丙烯(PP)、聚苯乙烯、ABS、聚碳酸酯(PC)、尼龙等塑料工件；适用于电子琴、音响、汽车装饰材料等大规模工业喷涂，可大幅度减少次品，节省劳力和物力；自然干燥，漆膜坚硬，附着力强，颜色丰富，美观亮丽。可根据客户要求加工生产不同光泽、不同性能、不同色彩的产品。
Description
技术领域
本发明涉及一种塑料装饰涂料及与其配套的稀释剂。
背景技术
作为塑料装饰涂料的涂装，除清洗工序外，根据塑料性质，一般均需采取表面前处理方法后再进行涂装，如：火焰处理、UV照射处理、化学试剂处理。也有使用特殊专用底漆作多层次涂装的，如PP专用底漆。迄今的方法工效低、次品多，难以适用大工业生产的需要。一次性涂装方法工艺简单，但往往由于技术上的原因出现吸漆、发花、剥落的现象，从而影响装饰效果及漆膜的物理性能。
发明内容
本发明所要解决的技术问题在于避免上述现有技术中的不足，而提出一种只需一次性涂装、施工简便、物理性能牢靠的塑料装饰涂料，以及与此涂料配套的稀释剂。
本发明所提供的技术方案是：一种塑料装饰涂料，该涂料包括有以下组分：丙烯酸树脂23～80％、颜料或染料2～37％、溶剂10～50％、添加剂0.1～1％、辅料0～10％。
进一步地，所述的涂料还包括有铝银浆或珠光粉。
进一步地，所述的丙烯酸树脂为甲基丙烯酸甲酯、丙烯酸丁酯和丙烯酸乙酯的聚合物。
进一步地，所述的溶剂为甲苯、二甲苯、醋酸丁酯、乙二醇丁醚、环己烷、二丙酮醇、正丁醇、异丙醇、甲醇、丙酮。
进一步地，所述的添加剂是指涂料用分散剂、润湿剂、流平剂、消泡剂、螯合剂、偶联剂、渗透剂。
进一步地，所述的辅料是指二氧化硅消光粉、聚乙烯蜡、醋酸丁酸纤维素。
进一步地，所述的颜料染料是指油漆制作所常用的有机颜料、无机颜料、金属络合染料。
一种与上述塑料装饰涂料配套使用的稀释剂，该稀释剂包括有以下组分：氯化聚烯烃10～25％、二甲苯10～25％、甲苯30～55％、乙二醇丁醚10～20％。
另一种与上述塑料装饰涂料配套使用的稀释剂，该稀释剂包括有以下组分：二丙酮醇2～15％、醋酸乙酯10～15％、乙二醇丁醚10～25％、正丁醇0～15％、丙酮3～8％、甲醇6～20％、异丙醇10～30％。
本发明有如下优点：使用丙烯酸树脂、颜料、溶剂、添加剂等材料制造塑料装饰涂料，无论春夏秋冬都能在无表面处理的条件下一次性喷涂装饰聚丙烯(PP)、聚苯乙烯、ABS、聚碳酸酯(PC)、尼龙等塑料工件；适用于电子琴、音响、汽车装饰材料等大规模工业喷涂，可大幅度减少次品，节省劳力和物力；自然干燥，漆膜坚硬，附着力强，颜色丰富，美观亮丽。可根据客户要求加工生产不同光泽、不同性能、不同色彩的产品。
具体实施方式
下面结合说明本发明的具体实施方式。
实施例1： 制备色浆(有机黄色浆例)：
有机黄颜料 8
AR-013丙烯酸树脂 65
正丁醇 5
乙二醇丁醚 3
醋酸丁酯 7
甲苯 11.7
YK164分散剂 0.3
100
将AR-013树脂30KG、正丁醇3KG、乙二醇丁醚2KG、醋酸丁酯3KG、甲苯10KG投入调漆缸，搅拌中缓慢加入有机黄颜料8KG，搅拌均匀后打入有碾磨介质的分散机，循环碾磨3小时，测细度达10微米以下时，打入成品调漆缸内，剩余料用于清洗分散机后合并打入成品调漆缸，经搅拌过滤检测包装待用。
实施例2： 制备色浆(白色浆例)：
钛白粉颜料 32
AR-013丙烯酸树脂 55
正丁醇 2
乙二醇丁醚 3
醋酸丁酯 2
甲苯 5.7
BYK110分散剂 0.3
100
将AR-013树脂10KG、正丁醇1KG、乙二醇丁醚2KG、醋酸丁酯1KG、甲苯2KG投入调漆缸，搅拌中缓慢加入钛白粉颜料32KG，搅拌均匀后打入有碾磨介质的分散机，循环碾磨3小时，测细度达10微米以下时，打入成品调漆缸内，剩余料用于清洗分散机后合并打入成品调漆缸，经搅拌过滤检测包装待用。
实施例3： 制备色浆(蓝色浆例)：
酞青蓝颜料 7
AR-013丙烯酸树脂 68
正丁醇 5
乙二醇丁醚 6
醋酸丁酯 5
甲苯 8.5
超分散剂 0.5
100
将AR-013树脂30KG、正丁醇3KG、乙二醇丁醚3KG、醋酸丁酯2KG、甲苯3KG投入调漆缸，搅拌中缓慢加入酞青蓝颜料7KG，搅拌均匀后打入有碾磨介质的分散机，循环碾磨3小时，测细度达10微米以下时，打入成品调漆缸内，剩余料用于清洗分散机后合并打入成品调漆缸，经搅拌过滤检测包装待用。
塑料装饰涂料能否适用各种塑料工件的涂装，能否全天候地适应大规模工业喷涂，除涂料本身的适应性外，配套稀释剂的使用是至关重要的。本发明配套稀释剂的有效成分如乙二醇丁醚与本发明塑料装饰涂料的有效成分如流平剂、润湿剂等配套使用，可显著降低涂料的表面张力，提高漆膜对塑料基材的附着力，形成平整光滑的漆膜外观。
实施例4：PP专用稀释剂
PP由于其结晶度高，表面极性和表面能低，涂膜难以附着。一般采用表面前处理，对表面进行改性，然后再配以底漆和面漆。也有配套PP专用底漆后再上以面漆的方法。传统工艺的复杂造成工作效率低、次品率高的现象，难以适应经济高速发展的需要。
本发明塑料装饰涂料PP专用稀释剂，对PP材料可以全天候一次性进行涂装。漆膜附着力强，外观平整光洁，不易出现次品。
①PP稀释剂的制备方法为：
氯化聚烯烃 10～20％
二甲苯 10～25％
甲苯 30～45％
乙二醇丁醚 10～20％
②使用方法为：
AC-130色漆 50(重量份)
PP专用稀释剂 50(重量份)
100
按配比搅拌均匀后，直接涂装。漆膜自干，8小时/20℃以后，铅笔硬度为H，附着力100/100。
实施例5：尼龙专用稀释剂
尼龙内聚能大，表面结晶度高，漆膜很难附着，一般需要进行表面化学改性或等离子表面处理。
本发明塑料装饰涂料尼龙专用稀释剂能够全天候一次性对尼龙工件进行大规模工业喷涂。漆膜附着力强，外观平整光洁，不易出现次品。
①尼龙专用稀释剂的制备方法为：
改性氯化聚烯烃 15～25％
二甲苯 10～20％
甲苯 30～55％
乙二醇丁醚 10～20％
②使用方法为：
PU-600色漆 50(重量份)
尼龙专用稀释剂 50(重量份)
100
按配比搅拌均匀后，直接涂装。漆膜自干，8小时/20℃以后，铅笔硬度为H，附着力100/100。本涂料不仅对尼龙有良好附着力，而且对铝合金等有色金属具有优异的附着力，目前已用于尼龙铝合金组合件的喷涂，经济效益显著。
实施例6：PS、PC专用稀释剂
聚苯乙烯(PS)为非结晶，无色透明塑料，耐溶剂性差，热变形温度低，涂装后只能采用60℃以下强制干燥，或自然干燥。因此除选用相应的涂料品种外，应配套专用稀释剂。
根据不同季节和环境温度设计的本发明配套稀释剂挥发速度均衡，不侵蚀底材，使本发明涂料具备了流平性好，漆膜平整光滑，干燥性好的特点。稀释剂分以下几个型号：夏季型S-611、冬季型S-606、春秋季型S-607。天气异常时，可将以上型号自行复配微调，以达到更理想的效果。
稀释剂的制备方法：
二丙酮醇 2～15％
醋酸乙酯 10～15
乙二醇丁醚 10～25
正丁醇 0～15
丙酮 3～8
甲醇 6～20
异丙醇 10～30
根据溶解力参数沸点合理配比，拟定出春秋季型、夏季型、冬季型稀释剂配方，直接供用户使用。按配方将以上溶剂投入反应釜，搅拌均匀后过滤出料。
实施例7： 调色(金属闪光黄色涂料例)：
有机黄色浆 15
CAB浆液 20
铝银浆 10
溶剂 10
AR-013树脂 44.5
各种添加剂 0.5
100
按色样调制喷样检验合格后，灌装成品。
实验实施例：
本发明塑料装饰涂料的物理性能如表1所示：
| 项目 | 指标 | 检验方法 | 检测结果 |
| 涂膜颜色及外观 | 涂膜平整光滑颜色符合标准板 | GB1729 | 合格 |
| 粘度(涂4#杯) | 50～70 | GB/T1723 | 合格 |
| 固含量 | 35±5 | GB1725 | 合格 |
| 细度(微米) | ＜20 | GB1724 | ＜10 |
| 遮盖力 | 不低于标准板 | JISK5400 | 合格 |
| 附着力(划格法) | 100/100 | GB9286 | 合格 |
| 铅笔硬度 | F～H | GB6739 | H |
| 耐热性(60℃) | 120H，无变化 | 合格 | |
| 耐候性 | 300H，无变化 | GB/T1865 | 合格 |
| 光泽(％) | 符合标准板 | GB1743 | 合格 |
| 耐乙醇 | 不泛白，不变色 | 乙醇布檫拭，＞20次 | ＞50次 |
| 耐盐水 | 不泛白，不变色 | 3％Nacl，72h | 合格 |
| 耐碱性 | 无变化 | 0.1mol/L，NaOH 48h | 合格 |
| 耐酸性 | 无变化 | 0.05mol/L，H2SO4 48h | 合格 |
综上所述，本发明塑料装饰涂料与配套稀释剂施工简便、外观平整光洁、物理性能牢靠、能全天候、一次性进行大规模工业喷涂，可大幅度减少次品，节省劳力和物力，具有良好的工业价值。
Claims (9)
1、一种塑料装饰涂料，该涂料包括有以下组分：丙烯酸树脂23～80％、颜料或染料2～37％、溶剂10～50％、添加剂0.1～1％、辅料0～10％。
2、根据权利要求1所述的塑料装饰涂料，其特征在于：所述的涂料还包括有铝银浆或珠光粉。
3、根据权利要求1或2所述的塑料装饰涂料，其特征在于：所述的丙烯酸树脂为甲基丙烯酸甲酯、丙烯酸丁酯和丙烯酸乙酯的聚合物。
4、根据权利要求1或2所述的塑料装饰涂料，其特征在于：所述的溶剂为甲苯、二甲苯、醋酸丁酯、乙二醇丁醚、环己烷、二丙酮醇、正丁醇、异丙醇、甲醇、丙酮。
5、根据权利要求1或2所述的塑料装饰涂料，其特征在于：所述的添加剂是指涂料用分散剂、润湿剂、流平剂、消泡剂、螯合剂、偶联剂、渗透剂。
6、根据权利要求1或2所述的塑料装饰涂料，其特征在于：所述的辅料是指二氧化硅消光粉、聚乙烯蜡、醋酸丁酸纤维素。
7、根据权利要求1或2所述的塑料装饰涂料，其特征在于：所述的颜料染料是指油漆制作所常用的有机颜料、无机颜料、金属络合染料。
8、一种与上述权利要求1或2所述的塑料装饰涂料配套使用的稀释剂，该稀释剂包括有以下组分：氯化聚烯烃10～25％、二甲苯10～25％、甲苯30～55％、乙二醇丁醚10～20％。
9、一种与上述权利要求1或2所述的塑料装饰涂料配套使用的稀释剂，该稀释剂包括有以下组分：二丙酮醇2～15％、醋酸乙酯10～15％、乙二醇丁醚10～25％、正丁醇0～15％、丙酮3～8％、甲醇6～20％、异丙醇10～30％。