CN1766251A - 轻质复合外墙板及其制造方法 - Google Patents

轻质复合外墙板及其制造方法 Download PDF

Info

Publication number
CN1766251A
CN1766251A CN 200510100655 CN200510100655A CN1766251A CN 1766251 A CN1766251 A CN 1766251A CN 200510100655 CN200510100655 CN 200510100655 CN 200510100655 A CN200510100655 A CN 200510100655A CN 1766251 A CN1766251 A CN 1766251A
Authority
CN
China
Prior art keywords
external wall
wall panel
light
composite external
light composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510100655
Other languages
English (en)
Inventor
沈宪光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGZHOU BISHEN NOVEL BUILDING MATERIALS CO Ltd
Original Assignee
GUANGZHOU BISHEN NOVEL BUILDING MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGZHOU BISHEN NOVEL BUILDING MATERIALS CO Ltd filed Critical GUANGZHOU BISHEN NOVEL BUILDING MATERIALS CO Ltd
Priority to CN 200510100655 priority Critical patent/CN1766251A/zh
Priority claimed from CNB2006100546389A external-priority patent/CN100385083C/zh
Publication of CN1766251A publication Critical patent/CN1766251A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种轻质复合外墙板及其制造方法。提供的轻质复合外墙板由纤维增强水泥平板和承载层复合而成,承载层是钢筋网加强轻集料混凝土层,其两侧复合有纤维增强水泥平板,其内部留有四周被轻集料混凝土包围的空腔,空腔内填充满保温材料。提供的轻质复合外墙板的制造方法依次进行如下过程:A.在模具内两侧放置纤维增强水泥平板;B.在两块纤维增强水泥平板之间放置中间夹有保温材料的钢筋网;C.在两块水泥平板和保温材料之间灌注轻集料混凝土;D.静置养护硬结后脱模即得轻质复合外墙板。本发明制造方法简单实用,效率高,产品具有轻质、高强、承载力大、保温隔热性好、抗震、防渗等优点。

Description

轻质复合外墙板及其制造方法
技术领域
本发明涉及建筑材料领域,尤其涉及一种轻质复合外墙板及其制造方法。
背景技术
传统的墙体材料是粘土砖,生产粘土砖既破坏农田,又需采用煤等燃料,增加能源消耗。为了节约土地资源,降低能耗,保护生态环境,国家一直积极推行墙体材料改革和建筑节能政策。国家建设部在《建设部建筑节能“十五”计划纲要》中提到,“目前,我国实心粘土砖的年产量还有5400多亿块,绝大部分由工艺技术落后、浪费能源和污染环境的小型企业生产,每年因此毁坏和占用耕地达95万亩”,并强调指出要“大力加强新型建筑墙体材料的推广应用”。
在国家政策的推动下,当前在建筑物内墙材料方面,已取得了较大的进展,出现了品种众多的内墙板材,但在外墙方面,因其有更高的功能要求,如:防渗漏、保温隔热、安装吊挂重物和防盗需要的足够强度以及消除由于室内外温差大造成的影响等,现有的外墙板种类不多,不能满足市场需求。
本公司较早前申请的专利号为200420072584.5的专利提出了一种“轻质复合外墙板”,在钢丝网混凝土层内夹有保温隔热层,钢丝网混凝土层的内墙侧复合有装饰内墙板,钢丝网混凝土层的外墙侧为防水水泥砂浆层,该专利为轻质外墙板提供了一种可行的技术方案。
本公司继续开发研究更多形式的轻质复合外墙板,向更轻、更强、更优的方向发展,以满足不同场合的需要。
发明内容
本发明的目的是提供一种轻质复合外墙板,这种外墙板不但具有高的抗冲击强度、抗弯强度和吊挂重物所需强度,而且还有优良的耐久性和轻质、保温、防渗漏性能,其能适合于框架结构、钢结构等各种建筑物的非承重外墙使用。
本发明的另一个目的是提出一种轻质复合外墙板的制造方法,这种方法具有生产效率高的特点。
本发明通过如下途径来实现:一种轻质复合外墙板,由纤维增强水泥平板和承载层复合而成,其特征在于:所述的承载层是钢筋网加强轻集料混凝土层,承载层的两侧复合有纤维增强水泥平板。
作为优化,为了进一步减轻重量和增强保温隔热效果,承载层内留有四周被轻集料混凝土包围的空腔,所述的空腔内填充满保温材料,所述保温材料是聚苯泡沫塑料板、矿棉板或岩棉板等轻质材料。
作为优化,所述的钢筋网为用钢筋支撑的双层钢筋网结构。
作为优化,制作承载层的混凝土是由水泥、砂和轻集料等混合构成的轻质高强混凝土。
作为优化,混凝土中所用的轻集料是如下轻集料的单一种或混合:陶粒、膨胀珍珠岩或聚苯颗粒。
作为优化,混凝土中所用的水泥为硫铝酸盐水泥或普通硅酸盐水泥。
一种轻质复合外墙板的制造方法,依次进行如下过程:A.在模具内两侧放置纤维增强水泥平板;B.在两块纤维增强水泥平板之间放置钢筋网;C.在两块水泥平板之间灌注轻集料混凝土,将钢筋网填埋;D.静置养护硬结后脱模即得轻质复合外墙板。
作为优化,过程B所述的钢筋网为用钢筋支撑的双层钢筋网结构。
进一步的优化是在过程B的钢筋网中间预夹置有保温材料。
与现有技术对比,本发明有如下实质性特点和显著的进步:1.本发明的轻质复合外墙板结构合理承载层为钢筋网增强混凝土层,可以根据使用要求采用陶粒、膨胀珍珠岩等无机轻集料或聚苯颗粒集料混凝土,也可以采用有机、无机轻集料混合混凝土,这些混凝土能确保外墙板的耐久性、荷载强度和防渗漏等性能;本发明的外侧采用维增强水泥平板,其与承载层都是以水泥为主要材料,相互结合好,不会产生开裂脱离等现象;墙板表面平整,安装后的墙体面无需批荡,可直接在墙板表面进行装饰。
保温隔热材料置于墙板的中部,并被承载层所包围,既大大减轻了墙板的重量,又增强了墙板的保温隔热效果。
2.本发明的轻质复合外墙板的制造方法实用,工效高由于最外层的是预制好的维增强水泥平板,内部的保温材料又是在制作双层钢筋网时夹好在中间了的,钢筋网又起到支撑水泥平板和定位保温材料的作用,使得灌注轻集料混凝土更加容易;由于外侧采用维增强水泥平板,使得拆模可以提早和容易;拆模后无需对墙板表面进行任何处理。
可以采用墙板成型机,多块墙板同时成型,机械化生产。
附图说明
图1是本发明之实例一(有保温材料)的外形示意图。
图2是本发明之实例一(有保温材料)的内部结构示意图。
图3是本发明之实例二(无保温材料)的外形示意图。
图4是本发明之实例二(无保温材料)的内部结构示意图。
具体实施方式
实施例一如图1和图2所示,本发明提供的一种轻质复合外墙板,其由纤维增强水泥平板2和承载层1复合而成,承载层1是由钢筋网3加强的轻集料混凝土层,承载层1的两侧面复合有纤维增强水泥平板2,承载层1内留有四周被轻集料混凝土包围的空腔,该空腔内填充满保温材料4,这种复合外墙板的中部为五层结构:纤维增强水泥平板2+承载层1(内置有钢筋网3)+保温材料4+承载层1(内置有钢筋网3)+纤维增强水泥平板2,而其两端部分则为三层结构:增强水泥平板2+承载层1(内置有钢筋网3)+纤维增强水泥平板2,承载层1的两端面设置成凸榫和凹榫,便于组装。
所述保温材料4优选为聚苯泡沫塑料板,也可以使用矿棉板或岩棉板等轻质填料,制作承载层1的混凝土是由水泥、砂和轻集料等混合构成的轻质高强混凝土,混凝土中所用的轻集料是陶粒或膨胀珍珠岩等无机轻集料。所用的水泥优选为硫铝酸盐水泥,也可使用普通硅酸盐水泥,所用的钢筋网3为用钢筋支撑的双层钢筋网,保温材料4夹在2层钢筋网3之间。
实施例二如图3和图4所示,本发明提供的一种轻质复合外墙板,其由纤维增强水泥平板2和承载层1复合而成,承载层1是由钢筋网3加强的轻集料混凝土层,承载层1的两侧面复合有纤维增强水泥平板2,承载层1的两端面设置成凸榫和凹榫,便于组装。
制作承载层1的混凝土是由水泥、砂和轻集料等混合构成的轻质高强混凝土,混凝土中所用的轻集料是聚苯颗粒轻集料,所用的水泥优选为硫铝酸盐水泥,也可使用普通硅酸盐水泥,所用的钢筋网3为用钢筋支撑的双层钢筋网。
实施例三一种如实施例一的轻质复合外墙板的制造方法,包括如下制作过程:A.将预制的纤维增强水泥平板2平行放置于墙板成型机的每个模腔内两侧;B.在两块水泥平板2之间放置入预制好的用钢筋支撑的双层钢筋网3,在双层钢筋网3之间预夹有保温材料4;
C.在两块水泥平板2之间及水泥平板2和保温材料4之间灌注轻集料混凝土将钢筋网3填埋,同时适当振动使轻集料混凝土填充满模腔内空隙;D.静置养护一定时间,待轻集料混凝土硬结后脱模、堆放。
实施例四一种如实施例二的轻质复合外墙板的制造方法,包括如下制作过程:A.将预制的纤维增强水泥平板2平行放置于墙板成型机的每个模腔内两侧;B.在两块水泥平板2之间放置入预制好的用钢筋支撑的双层钢筋网3;C.在两块水泥平板2之间灌注轻集料混凝土将钢筋网3填埋,同时适当振动使轻集料混凝土充满模腔内空隙;D.静置养护一定时间,待轻集料混凝土硬结后脱模、堆放。
本发明提出的轻质复合外墙板的制造方法,工艺简单,因采用预制的水泥平板作为复合墙板的边板,拆模方便,可以缩短成型周期,提高模具利用率,可以同时成型多块墙板。

Claims (10)

1.一种轻质复合外墙板,由纤维增强水泥平板和承载层复合而成,其特征在于:所述的承载层是钢筋网加强轻集料混凝土层,承载层两侧复合有纤维增强水泥平板。
2.根据权利要求1所述的轻质复合外墙板,其特征在于:承载层内留有四周被轻集料混凝土包围的空腔,所述的空腔内填充满保温材料。
3.根据权利要求1或2所述的轻质复合外墙板,其特征在于:所述的钢筋网为用钢筋支撑的双层钢筋网。
4.根据权利要求1或2所述的轻质复合外墙板,其特征在于:制作承载层的轻集料混凝土层是由水泥、砂和轻集料等混合构成的轻质高强混凝土。
5.根据权利要求4所述的轻质复合外墙板,其特征在于:所述的轻集料是如下轻集料的单一种或混合:陶粒、膨胀珍珠岩或聚苯颗粒。
6.根据权利要求4所述的轻质复合外墙板,其特征在于:所用的水泥为硫铝酸盐水泥或普通硅酸盐水泥。
7.根据权利要求2所述的轻质复合外墙板,其特征在于:所述保温材料是聚苯泡沫塑料板、矿棉板或岩棉板。
8.一种轻质复合外墙板的制造方法,其特征在于依次进行如下过程:A.在模具内两侧放置纤维增强水泥平板;B.在两块纤维增强水泥平板之间放置钢筋网;C.在两块纤维增强水泥平板之间灌注轻集料混凝土,将钢筋网填埋;D.静置养护硬结后脱模即得到如权利要求1或2所述的轻质复合外墙板。
9.根据权利要求8所述的轻质复合外墙板的制造方法,其特征在于:过程B所述的钢筋网为用钢筋支撑的双层钢筋网。
10.根据权利要求8或9所述的轻质复合外墙板的制造方法,其特征在于:在钢筋网内预先夹置保温材料。
CN 200510100655 2005-10-28 2005-10-28 轻质复合外墙板及其制造方法 Pending CN1766251A (zh)