CN1709817A - Artificial granite, marble mechanical fitting and its preparing method - Google Patents

Artificial granite, marble mechanical fitting and its preparing method Download PDF

Info

Publication number
CN1709817A
CN1709817A CNA200510043683XA CN200510043683A CN1709817A CN 1709817 A CN1709817 A CN 1709817A CN A200510043683X A CNA200510043683X A CN A200510043683XA CN 200510043683 A CN200510043683 A CN 200510043683A CN 1709817 A CN1709817 A CN 1709817A
Authority
CN
China
Prior art keywords
marble
mechanical fitting
granularity
aggregate
mould
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA200510043683XA
Other languages
Chinese (zh)
Other versions
CN1280223C (en
Inventor
周卫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=35706113&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CN1709817(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Individual filed Critical Individual
Priority to CNB200510043683XA priority Critical patent/CN1280223C/en
Priority to JP2008513892A priority patent/JP2008542172A/en
Priority to KR1020077029020A priority patent/KR20080016848A/en
Priority to PCT/CN2005/001306 priority patent/WO2006128330A1/en
Publication of CN1709817A publication Critical patent/CN1709817A/en
Application granted granted Critical
Publication of CN1280223C publication Critical patent/CN1280223C/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses one kind of man-made granite, the marble's mechanical fitting and its preparation method, which belonged to the mechanical fitting processing domain. The man-made granite, the marble's mechanical fitting, which is made from the sizing material with percent by weight is 80% - 93% aggregate and 20% - 7%, after the ingredient, the pattern making, dense and so on the craft. Among them, the aggregate is the granularity- 0.01-25mm natural granite pellet or the marble pellet. Compares with the existing technology, this invention man-made granite, the marble mechanical fitting has stronger vibration hinder and lower cost, which widely applies to the engine bed equipment, the check-out facility, measure instrument fitting.

Description

Stonite, marble mechanical fitting and preparation method thereof
Technical field
The present invention relates to a kind of nonmetal mechanical fitting, specifically a kind of stonite, marble mechanical fitting and preparation method thereof.
Background technology
In the prior art, various machining tools, test set form with metal material processing such as cast iron, steel mostly.Along with the raising to the spare parts processing machinery accuracy requirement, the running speed of processing machine tool also greatly improves, and like this, will produce violent vibrations in the course of processing.But, metallic substance is but because self cuts down the indifferent of vibrations, can't sponge the vibrations that produce in the machine tool operation process effectively, the thermal expansivity that adds metallic substance is big, make the Installation and Debugging process of equipment become very complicated, and therefore the working accuracy of accessory also is subjected to very big restriction.In addition, also there are deficiencies such as energy-output ratio is big, contaminate environment in the course of processing of metal mechanical fitting.
At present, though there are many kinds of technology can produce stonite or artificial marble material,, and can only serve as finishing material because of physical indexs such as intensity, hardness can't reach the performance requriements of mechanical fitting.
Summary of the invention
Technical assignment of the present invention is at above-mentioned the deficiencies in the prior art, a kind of stonite, marble mechanical fitting are provided, this mechanical fitting is that non-metallic composite material is made, when satisfying the every performance index of metal insert, increased the vibration damping and the thermotolerance of accessory, and production cost is lower greatly.
Another technical assignment of the present invention provides the preparation method of this stonite, marble mechanism accessory.
Technical assignment of the present invention is realized in the following manner: stonite, marble mechanical fitting, make by following raw materials by weight percent:
Aggregate 80-93% sizing material 20%-7%;
Described aggregate is that granularity is natural granite particle or the marble particle of 0.01-25mm.
The preferred size scope of described aggregate and the endocorpuscular weight percent of each size range consist of:
Granularity is the particle of 8-25mm: 55%-60%;
Granularity is the particle of 1-8mm: 20%-25%;
Granularity is the stone flour of 0.01-0.5mm: 15%-25%.
Described sizing material can be selected Resins, epoxy or acrylic resin for use.
The preparation method of preferred stonite of the present invention, marble mechanical fitting may further comprise the steps:
A, according to formula rate metering aggregate, sizing material, both are mixed and adorn mould;
B, the mould that will adorn behind the mould are placed on the shaking table vibratory compaction 30-60 minute;
C, 20-40 ℃ following maintenance 48-60 hour, the demoulding promptly gets the waste material of mechanical fitting.
In addition, for improving the performance of mechanical fitting, also comprise the promotor of 1%-5% sizing material amount in its raw material, described promotor is that granularity is talcum powder, natural granite powder or the natural marble powder of 0.01-0.5mm.
Its preparation method may further comprise the steps:
A, according to formula rate metering aggregate, sizing material and promotor, the three is mixed back dress mould.
B, the mould that will adorn behind the mould are placed on the shaking table vibratory compaction 30-60 minute;
C, 20-40 ℃ following maintenance 48-60 hour, the demoulding promptly gets the waste material of mechanical fitting.
Mechanical fitting of the present invention is to be the nonmetal synthetic mechanical fitting that aggregate is made with granite or marble, compares with the metal mechanical fitting of prior art to have following outstanding beneficial effect:
(1) vibration damping is stronger
The step and the time of rigging up and debugging have been reduced;
When utilizing the optical sensor equipment to detect, can must obtain the ideal image sooner;
For fast browsing provides fabulous stability;
Reduce the vibrations that produce in the High-speed machining process, thereby improved the working accuracy of workpiece.
(2) cost is low
Can save precision work for the second time and machining cost;
Can the corresponding consumption that reduces expensive structured material.
(3) good heat resistance
The coefficient of expansion is little than metal insert;
Heat-resisting gradient is little.
Description of drawings
Accompanying drawing 1: the crust strength test figure of stonite's mechanical fitting of the embodiment of the invention one preparation;
Accompanying drawing 2: the crust strength test figure of steel;
Accompanying drawing 3: the crust strength test figure of cast iron;
Accompanying drawing 4: the crust strength test figure of aluminum oxide.
Embodiment
Reach the physicals experimental data by the following examples and further set forth the beneficial effect of mechanical fitting of the present invention.
Embodiment one:
Aggregate: natural granite particle 90kg
Wherein, granularity is that the particle of 8-10mm accounts for 58%, is 52.2kg;
Granularity is that the particle of 1-2mm accounts for 22%, is 19.8kg;
Granularity is that the powder of 0.01-0.5mm accounts for 20%, is 18kg
Sizing material: Resins, epoxy 10kg
Promotor: the talcum powder of 3% sizing material amount is 10 * 3%=0.3kg, granularity 0.01-0.5mm
Preparation process:
A, screen the aggregate of corresponding granularity, and it is mixed standby according to formula rate;
B, to take by weighing the talcum powder of Resins, epoxy and formula ratio according to formula rate standby;
Behind c, the aggregate with obtaining among step a, the b, sizing material and the talcum powder thorough mixing, the dress mould placed on the shaking table vibratory compaction 35 minutes, and is last, can the demoulding get the waste material of mechanical fitting in 48 hours 20-30 ℃ of following maintenance.
Product physical property index is as follows:
Density 2.32g/cm 2
Ultimate compression strength 110-117MPa
Tensile strength 15.2MPa
Bending strength 17.2MPa
Young elasticity 35.982MPa
Poisson's ratio 0.23
Thermal expansivity 16.9 * 10 -6Mm/mm ℃
Thermal conductivity 0.24Wcm/ ℃
Specific heat 0.23-0.26cal/g ℃
With regard to the casting material sample of 1.5in. * 1.5in. * 9in. crust pressure, under 70 Fahrenheit temperature conditions, its vibration damping ability is tested, and contrast with the test result of steel, cast iron, aluminum oxide respectively, the result is shown in accompanying drawing 1-accompanying drawing 4.Fast 45 times of the ability ratio aluminum oxide of foundry goods reduction vibrations of the present invention as can be seen; Than fast 10 times of cast iron and steel.
Embodiment two:
Aggregate: natural marble particle 85kg
Wherein, granularity is that the particle of 10-14mm accounts for 56%, is 47.6kg;
Granularity is that the particle of 2-3.5mm accounts for 24%, is 20.4kg;
Granularity is that the powder of 0.01-0.5mm accounts for 20%, is 17kg
Sizing material: Resins, epoxy 15kg
Promotor: the natural marble powder of 4.5% sizing material amount is 15 * 4.5%=0.675kg, granularity 0.01-0.5mm
Preparation process:
A, screen the aggregate of corresponding granularity, and it is mixed standby according to formula rate;
B, to take by weighing the natural marble powder of Resins, epoxy and formula ratio according to formula rate standby;
Behind c, the aggregate with obtaining among step a, the b, sizing material and the natural marble powder thorough mixing as promotor, the dress mould placed on the shaking table vibratory compaction 45 minutes, and is last, and 25-35 ℃ of following maintenance can the demoulding get the waste material of mechanical fitting in 60 hours.
Embodiment three:
Aggregate: natural granite particle 82kg
Wherein, granularity is that the particle of 14-24mm accounts for 59%, is 48.38kg;
Granularity is that the particle of 4.5-8mm accounts for 23%, is 18.86kg;
Granularity is that the powder of 0.01-0.5mm accounts for 18%, is 14.76kg
Sizing material: acrylic resin 18kg
Promotor: the natural granite powder of 1.5% sizing material amount is 18 * 1.5%=0.27kg, granularity 0.01-0.5mm
Preparation process:
A, screen the aggregate of corresponding granularity, and it is mixed standby according to formula rate;
B, to take by weighing the natural granite powder of acrylic resin and formula ratio according to formula rate standby;
Behind c, the aggregate with obtaining among step a, the b, sizing material and the natural granite powder thorough mixing as promotor, the dress mould placed on the shaking table vibratory compaction 50 minutes, and is last, and 30-40 ℃ of following maintenance can the demoulding get the waste material of mechanical fitting in 60 hours.

Claims (6)

1, stonite, marble mechanical fitting is characterized in that it is made by following raw materials by weight percent:
Aggregate 80-93% sizing material 20%-7%;
Described aggregate is that granularity is natural granite particle or the marble particle of 0.01-25mm.
2, stonite according to claim 1, marble mechanical fitting is characterized in that natural granite or the marble granulometric composition of described aggregate by following size range:
Granularity is the particle of 8-25mm: 55%-60%;
Granularity is the particle of 1-8mm: 20%-25%;
Granularity is the stone flour of 0.01-0.5mm: 15%-25%.
3, stonite according to claim 1, marble mechanism accessory is characterized in that described sizing material is Resins, epoxy or acrylic resin.
4, a kind of method for preparing the mechanical fitting of claim 1 is characterized in that may further comprise the steps:
A, according to formula rate metering aggregate, sizing material, both are mixed and adorn mould;
B, the mould that will adorn behind the mould are placed on the shaking table vibratory compaction 30-60 minute;
C, 20-40 ℃ following maintenance 48-60 hour, the demoulding promptly gets the waste material of mechanical fitting.
5, according to the described stonite of claim 1, marble mechanical fitting, it is characterized in that, the promotor that also comprises 1%-5% sizing material amount in its raw material, described promotor are that granularity is talcum powder, natural granite powder or the natural marble powder of 0.01-0.5mm.
6, the method for the mechanical fitting of preparation claim 5 is characterized in that it may further comprise the steps:
A, according to formula rate metering aggregate, sizing material and promotor, the three is mixed back dress mould.
B, the mould that will adorn behind the mould are placed on the shaking table vibratory compaction 30-60 minute;
C, 20-40 ℃ following maintenance 48-60 hour, the demoulding promptly gets the waste material of mechanical fitting.
CNB200510043683XA 2005-05-31 2005-05-31 Artificial granite, marble mechanical fitting and its preparing method Active CN1280223C (en)