CN109181187A - A kind of high-performance wall facing layer material and preparation method thereof - Google Patents
A kind of high-performance wall facing layer material and preparation method thereof Download PDFInfo
- Publication number
- CN109181187A CN109181187A CN201810938761.XA CN201810938761A CN109181187A CN 109181187 A CN109181187 A CN 109181187A CN 201810938761 A CN201810938761 A CN 201810938761A CN 109181187 A CN109181187 A CN 109181187A
- Authority
- CN
- China
- Prior art keywords
- wall facing
- facing layer
- preparation
- layer material
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-performance wall facing layer materials and preparation method thereof, are made of the raw material of following mass fraction: 30~50 parts of marble powder, 20~40 parts of calcium silicates, 40~60 parts of acrylic resin, 5~8 parts of technical grade sodium alginate, 4~10 parts of algae clay, 5~10 parts of fire retardant, 3~6 parts of ultraviolet absorbing agent, 2~5 parts of stabilizer, 1~3 part of stearic acid；The preparation method of the high-performance wall facing plate by raw material weighing, be stirred, smash and grind, be pressed and molded, cool down, six part of overlay film forms.Wall facing layer material prepared by the present invention not only has the advantages that water proof fire retardant, but also preparation method is simple, can be mass produced, and the technical grade sodium alginate and algae clay of addition make wall facing layer material be not easy to be infected with dust, safety and environmental protection.
Description
Technical field
The present invention relates to wall body building material field, especially a kind of high-performance wall facing layer material and its preparation side
Method.
Background technique
In building materials and ornaments field, for the beauty of wall, Decorative wall plate usually is pasted in exterior surface of wall,
In, can be used as Decorative wall plate material be brick perhaps ceramic tile and the material of face brick or metal material on the market is close
Degree is big, transport is inconvenient, and manufacturing cost is high, is not suitable for the decoration for carrying out large area, and the mounting condition of these materials is high, to day
It is stringent that gas bar part and installer are put into requirement.In recent years, with the continuous development and innovation of shingle nail material and manufacture craft,
At present using it is most common be complex shingle panel, not only simple structure, construction are convenient but also can mass production system for complex shingle panel
It makes.The outermost layer of building is arranged in wall facing layer material, is exposed in sunlight and air for a long time, and it is different to become easily infected by dust
Object, and the phenomenon that material aging can be generated after the irradiation of prolonged sunlight.
Summary of the invention
In order to solve the above problem existing for the art, the dust protection adherency and ageing resistance of wall facing layer are improved
Can, the invention proposes a kind of high-performance wall facing layer materials and preparation method thereof.
The technical solution adopted by the present invention to solve the technical problems is: a kind of high-performance wall facing layer material and its system
Preparation Method is made of the raw material of following mass fraction:
Above-mentioned a kind of high-performance wall facing layer material and preparation method thereof, the fire retardant are TCPP, DMMP, poly- phosphorus
One of sour ammonium.
Above-mentioned a kind of high-performance wall facing layer material and preparation method thereof, the ultraviolet absorbing agent are UV-531.
Above-mentioned a kind of high-performance wall facing layer material and preparation method thereof, the stabilizer be lead sulfate tribasic,
One of dibasic lead phosphite, zinc stearate.
Above-mentioned a kind of high-performance wall facing layer material and preparation method thereof, the lubricant are stearic acid, stearic acid
The mixture of one or both of butyl ester.
Above-mentioned a kind of high-performance wall facing layer material and preparation method thereof, the work of the technical grade sodium alginate preparation
Skill process is as follows: dry or wet sea grass or seaweed pulverized, the extraction of washed with impurities, highly basic water, clarify thick alginate is molten
Liquid obtains colored calcium alginate through calcium chloride precipitation, with acid processing after being decolourized, being deodorized, removes soluble impurity and obtains alginic acid
Precipitating, alginic acid precipitating sodium alginate is reacted to obtain with sodium carbonate, then through drying, crushing, be sieved to obtain sodium alginate powder.
Above-mentioned a kind of high-performance wall facing layer material and preparation method thereof, the granularity of the marble powder are 1400
~1500 mesh, the granularity of sodium alginate powder are 1400~1600 mesh.
Above-mentioned a kind of high-performance wall facing layer material and preparation method thereof, preparation method is as follows:
(1) weighing of material raw material weighing: is carried out according to the mass fraction composition of the high-performance wall facing layer material；
(2) it is stirred: the raw material that step (1) claims being added in batch mixer and is stirred mixing；
(3) it smashes and grinds: the raw material being uniformly mixed in step (2) being added in grinder and is ground, powder is obtained
Material；
(4) it is pressed and molded: the powder in step (3) being heated at high temperature to 225~240 DEG C, by high temperature powder carry to mould
Has extrusion forming, molding keeps 30~40min；
(5) cooling: panel after molding is cooled to room temperature；
(6) overlay film: panel after cooling is sent to the coating processing of progress upper epidermis on laminating machine.
Compared with original technology, the present invention has the advantages that property and helpfulness effect following prominent:
The invention has the advantages that proposed in a kind of high-performance wall facing layer material of the present invention and preparation method thereof
Wall facing layer material not only has the advantages that water proof fire retardant, but also preparation method is simple, can be mass produced, be added
The technical grade sodium alginate and algae clay entered makes wall facing layer material be not easy to be infected with dust, safety and environmental protection.
Specific embodiment
Technical solution in order to enable those skilled in the art to better understand the present invention, With reference to embodiment to this
Invention elaborates.
[embodiment 1]
A kind of high-performance wall facing layer material and preparation method thereof, is made of the raw material of following mass fraction:
Specifically, the fire retardant is ammonium polyphosphate, the ultraviolet absorbing agent is UV-531, and the stabilizer is three salt
Base lead sulfate, the lubricant are stearic acid, and the algae clay is the algae clay powder after drying, the technical grade sodium alginate
Granularity for dry sodium alginate powder and sodium alginate powder is 1400 mesh, and the granularity of the marble powder is 1400
Mesh.
The high-performance wall facing layer material the preparation method is as follows:
(1) weighing of material raw material weighing: is carried out according to the mass fraction composition of the high-performance wall facing layer material；
(2) it is stirred: the raw material that step (1) claims being added in batch mixer and is stirred mixing；
(3) it smashes and grinds: the raw material being uniformly mixed in step (2) being added in grinder and is ground, powder is obtained
Material；
(4) it is pressed and molded: the powder in step (3) is heated at high temperature to 225 DEG C, high temperature powder carry to mold is squeezed
Molding, molding keep 40min；
(5) cooling: panel after molding is cooled to room temperature；
(6) overlay film: panel after cooling is sent to the coating processing of progress upper epidermis on laminating machine.
[embodiment 2]
A kind of high-performance wall facing layer material and preparation method thereof, is made of the raw material of following mass fraction:
Specifically, the fire retardant is TCPP, the ultraviolet absorbing agent is UV-531, and the stabilizer is that dibasic is sub-
Lead phosphate；The lubricant is the mixture of stearic acid and butyl stearate, wherein the matter of the stearic acid and butyl stearate
Amount is than being 1:1；The algae clay be it is dry after algae clay powder and the granularity of sodium alginate powder be 1600 mesh, the Dali
The granularity of mountain flour body is 1500 mesh.
The high-performance wall facing layer material the preparation method is as follows:
(1) weighing of material raw material weighing: is carried out according to the mass fraction composition of the high-performance wall facing layer material；
(2) it is stirred: the raw material that step (1) claims being added in batch mixer and is stirred mixing；
(3) it smashes and grinds: the raw material being uniformly mixed in step (2) being added in grinder and is ground, powder is obtained
Material；
(4) it is pressed and molded: the powder in step (3) is heated at high temperature to 230 DEG C, high temperature powder carry to mold is squeezed
Molding, molding keep 35min；
(5) cooling: panel after molding is cooled to room temperature；
(6) overlay film: panel after cooling is sent to the coating processing of progress upper epidermis on laminating machine.
[embodiment 3]
A kind of high-performance wall facing layer material and preparation method thereof, is made of the raw material of following mass fraction:
Specifically, the fire retardant is DMMP, the ultraviolet absorbing agent is UV-531, and the stabilizer is stearic acid
Zinc, the lubricant are butyl stearate；The algae clay be it is dry after algae clay powder, and the granularity of sodium alginate powder
For 1500 mesh, the granularity of the marble powder is 1500 mesh.
The high-performance wall facing layer material the preparation method is as follows:
(1) weighing of material raw material weighing: is carried out according to the mass fraction composition of the high-performance wall facing layer material；
(2) it is stirred: the raw material that step (1) claims being added in batch mixer and is stirred mixing；
(3) it smashes and grinds: the raw material being uniformly mixed in step (2) being added in grinder and is ground, powder is obtained
Material；
(4) it is pressed and molded: the powder in step (3) is heated at high temperature to 240 DEG C, high temperature powder carry to mold is squeezed
Molding, molding keep 30min；
(5) cooling: panel after molding is cooled to room temperature；
(6) overlay film: panel after cooling is sent to the coating processing of progress upper epidermis on laminating machine.
Above embodiments are only exemplary embodiment of the present invention, are not used in the limitation present invention, protection scope of the present invention
It is defined by the claims.Those skilled in the art can within the spirit and scope of the present invention make respectively the present invention
Kind modification or equivalent replacement, this modification or equivalent replacement also should be regarded as being within the scope of the present invention.
Claims (6)
1. a kind of high-performance wall facing layer material and preparation method thereof, which is characterized in that by the raw material group of following mass fraction
At:
2. a kind of high-performance wall facing layer material according to claim 1 and preparation method thereof, which is characterized in that described
Fire retardant is one of TCPP, DMMP, ammonium polyphosphate.
3. a kind of high-performance wall facing layer material according to claim 1 and preparation method thereof, which is characterized in that described
Ultraviolet absorbing agent is UV-531.
4. a kind of high-performance wall facing layer material according to claim 1 and preparation method thereof, which is characterized in that described
Stabilizer is one of lead sulfate tribasic, dibasic lead phosphite, zinc stearate.
5. a kind of high-performance wall facing layer material according to claim 1 and preparation method thereof, which is characterized in that described
Lubricant is the mixture of one or both of stearic acid, butyl stearate.
6. a kind of high-performance wall facing layer material according to claim 1 and preparation method thereof, which is characterized in that Gao Xing
Can wall facing layer material the preparation method is as follows:
(1) weighing of material raw material weighing: is carried out according to the mass fraction composition of the high-performance wall facing layer material；
(2) it is stirred: the raw material that step (1) claims being added in batch mixer and is stirred mixing；
(3) it smashes and grinds: the raw material being uniformly mixed in step (2) being added in grinder and is ground, powder is obtained；
(4) it is pressed and molded: the powder in step (3) being heated at high temperature to 225~240 DEG C, high temperature powder carry to mold is squeezed
Molded, molding keeps 30~40min；
(5) cooling: panel after molding is cooled to room temperature；
(6) overlay film: panel after cooling is sent to the coating processing of progress upper epidermis on laminating machine.