CN1948212A - Inner wall surface decoration material and its preparation method - Google Patents
Inner wall surface decoration material and its preparation method Download PDFInfo
- Publication number
- CN1948212A CN1948212A CN 200610137828 CN200610137828A CN1948212A CN 1948212 A CN1948212 A CN 1948212A CN 200610137828 CN200610137828 CN 200610137828 CN 200610137828 A CN200610137828 A CN 200610137828A CN 1948212 A CN1948212 A CN 1948212A
- Authority
- CN
- China
- Prior art keywords
- parts
- wall surface
- mixed
- surface decoration
- decoration material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of interior wall finishing material. Its raw material composition includes (by weight portion) 100 portions of inorganic granulated aggregate, 60-140 portions of powder body, 3.2-48 portions of synthetic resin adhesive, 12.8-96 portions of inorganic porous powder body and 0.08-12 portions of compounding agent. The granule diameter of the described inorganic granulated aggregate is 0.15-6 mm, the granule diameter of the described powder body is 0.01-200 micrometers, and the granule diameter of the described inorganic porous powder body is 1-300 micrometers.
Description
Technical field
The present invention relates to a kind of finishing material and preparation method thereof, especially relate to a kind of inner wall surface decoration material and preparation method thereof.
Background technology
Finishing material is meant to lay or be coated with and is contained in building surface, comprises that inside and outside surface plays the material of decorative effect.Finishing material is logging material, technology, shape-designing, color, aesthstic material.The wide range that it relates to, not only relate to traditional material of construction,, also relate to various New Building Materials such as chemical building material, materials for construction, weaving building materials, metallurgical building materials as stone material, timber, pottery etc., kind has reached several ten thousand kinds more than, and is therefore also a lot of to its method of classifying.If the chemical property by finishing material can be divided into it organic finishing material (as wallpaper, floor, tackiness agent and the organic polymer coating etc. of building plastic class) and inorganic decorating material two big classes.Wherein the inorganic decorating material is divided into metal decorative material (as aluminium alloy, stainless steel, copper etc.) and nonmetallic decorative material (as ornamental stone, pottery, glass etc.) again.
Decorative material for internal wall generally comprises: 1, wallcovering class: wall paint, organic coating, inorganic paint, organic-inorganic coating etc.; 2, wallpaper class: paper paper substrate wallpaper, yarn fabric wallpaper, natural materials wallpaper, plastic wallpaper etc.; 3, decorative sheet class: wooden decorative wood-based plate, Tetefol high pressure laminated decorative board, formica, metal lagging, mineral decoration board, ceramic decoration mural painting, perforation decoration acoustic panel, flocking decoration acoustic panel etc.; 4, wall paper class: glass fibre WALL CLOTH, numb fine nonwoven wall paper, chemical fibre wall paper etc.; Inner wall decoration is the part of upholstery, and it takes into account and decorate the interior space, satisfies multiple functions such as service requirements and protection structure.But decorative material for internal wall has following defective more at present: 1) the general decorative cover that forms of existing finishing material all is slick plane, and the change of style only is the change of the collocation style of plane color and pattern, does not have stereoeffect; 2) atmospheric pollution to finishing and indoor other facility generation does not have effective protective effect; 3) crackle appears in decorative cover easily.
Summary of the invention
The technical problem to be solved in the present invention provides a kind of inner wall surface decoration material.Use the decorative cover of this material that Z-Correct bump mapping Z-correct is arranged, thereby give match volume; And this finishing material can adsorb and reduce the pollution that causes in the fitment process, also can effectively adsorb the reduction atmospheric pollution, to reduce the obnoxious flavour content in the room air; And this finishing material is not prone to crackle; Simultaneously, also finishing material has been increased a kind of new selection to people.
Another technical problem that the present invention will solve provides a kind of preparation method of inner wall surface decoration material.
For solving above-mentioned first technical problem, a kind of inner wall surface decoration material of the present invention, it comprises following materials based on weight:
100 parts of inorganic granular aggregates; 60～140 parts of powders;
3.2～48 parts of synthetic resin binders; 12.8～96 parts of inorganic porous powders;
0.08～12 part of Synergist S-421 95;
The particle diameter of described inorganic granular aggregate is between 0.15～6 millimeter; Described powder granule diameter is between 0.01～200 micron; 1～300 micron of described inorganic porous powder granule diameter;
Described inorganic granular aggregate is the mixture a kind of or that two or more arbitrary proportion is mixed between them among quartz sand, color sand, the Mirabilitum crystallina;
Described powder is the mixture a kind of or that two or more arbitrary proportion is mixed between them among lime carbonate, titanium dioxide, kaolin, the talcum powder.
Described synthetic resin binder is the mixture a kind of or that two or more arbitrary proportion is mixed between them among solid, powdery synthetic resin binder, the emulsion-like synthetic resin tackiness agent.
Described solid, powdery synthetic resin binder is the mixture a kind of or that two or more arbitrary proportion is mixed between them among vinyl acetate between to for plastic powdex, vinyl acetate-ethylene powdex, acrylic clear powder resin, the organosilicon powder resin; The solid content of described solid, powdery synthetic resin binder is 80～100%.
Described emulsion-like synthetic resin tackiness agent is the mixture a kind of or that two or more arbitrary proportion is mixed between them among polyvinyl acetate resin emulsion, ester-polyurethane resin emulsion, Emulsion acrylic resin, silicone resin emulsion, the vinyl chloride resin emulsion, and the solid content of described emulsion-like synthetic resin tackiness agent is 30～65%.
Described inorganic porous powder is the mixture a kind of or that two or more arbitrary proportion is mixed between them among sepiolite, diatomite, zeolite, the attapulgite.
Described Synergist S-421 95 is the mixture a kind of or that two or more arbitrary proportion is mixed between them among methylcellulose gum, carboxymethyl cellulose, carboxylic propyl methocel, the polyvinyl alcohol.
Be above-mentioned first technical problem of better solution, a kind of inner wall surface decoration material of the present invention, it also comprises following materials based on weight:
0.32～14.4 part of fiber;
Described fiber is the mixture a kind of or that two or more arbitrary proportion is mixed between them among synthon, the mineral fibre.
Described synthon are the mixtures a kind of or that two or more arbitrary proportion is mixed between them among trevira, tynex, polyacrylonitrile fibre, polyvinyl alcohol fiber, thermovyl, polypropylene fibre, the polyurethane fibre.
Described mineral fibre is the mixture a kind of or that two or more arbitrary proportion is mixed between them among sepiolite fibre, carbon fibre, the rock wool fibers.
For solving above-mentioned second technical problem, the preparation method of a kind of inner wall surface decoration material of the present invention is as follows:
1, select following materials based on weight:
100 parts of inorganic granular aggregates; 60～140 parts of powders;
3.2～48 parts of synthetic resin binders; 12.8～96 parts of inorganic porous powders;
0.08～12 part of Synergist S-421 95; 0.32～14.4 part of fiber;
The particle diameter of described inorganic granular aggregate is between 0.15～6 millimeter; Described powder granule diameter is between 0.01～200 micron; 1～300 micron of described inorganic porous powder granule diameter;
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
When using this product, adopt ordinary method, mix with a certain amount of water and this product, to suiting to smear interior metope, then the inner wall surface decoration material that dilutes is applied to metope and gets final product.
The present invention has following advantage:
1, uses the decorative cover of this material that Z-Correct bump mapping Z-correct is arranged, thereby give stereoscopic sensation.
2, this finishing material can adsorb the pollution that causes in the reduction fitment process, also can effectively adsorb the reduction atmospheric pollution, to reduce the obnoxious flavour content in the room air.
3, this finishing material is not prone to crackle;
4, to people finishing material has been increased a kind of new selection.
Embodiment
Embodiment 1
A kind of inner wall surface decoration material, it comprises following materials based on weight:
100 parts of quartz sands; 60 parts in lime carbonate;
3.2 parts of vinyl acetate between to for plastic powdexes; 12.8 parts of sepiolites;
0.08 part of methylcellulose gum;
The particle diameter of described quartz sand is 0.15 millimeter; Described calcium carbonate granule diameter is 0.01 micron; 1 micron of described sepiolite particle diameter; The solid content 80% of described vinyl acetate between to for plastic powdex.
A kind of preparation method of inner wall surface decoration material is as follows:
1, select following materials based on weight::
100 parts of quartz sands; 60 parts in lime carbonate;
3.2 parts of vinyl acetate between to for plastic powdexes; 12.8 parts of sepiolites;
0.08 part of methylcellulose gum;
The particle diameter of described quartz sand is 0.15 millimeter; Described calcium carbonate granule diameter is 0.01 micron; 1 micron of described sepiolite particle diameter;
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
Embodiment 2
A kind of inner wall surface decoration material, it comprises following materials based on weight:
100 parts in color sand; 140 parts of titanium dioxides;
48 parts of vinyl acetate-ethylene powdexes; 96 parts in diatomite;
12 parts of carboxymethyl celluloses;
The particle diameter of described color sand is 6 millimeters; Described titanium dioxide particle diameter is 200 microns; Described diatomite particle diameter is 20 microns; The solid content 100% of described vinyl acetate-ethylene powdex.
A kind of preparation method of inner wall surface decoration material is as follows:
1, select following materials based on weight::
100 parts in color sand; 140 parts of titanium dioxides;
48 parts of vinyl acetate-ethylene powdexes; 96 parts in diatomite;
12 parts of carboxymethyl celluloses;
The particle diameter of described color sand is 6 millimeters; Described titanium dioxide particle diameter is 200 microns; Described diatomite particle diameter is 20 microns; The solid content 100% of described vinyl acetate-ethylene powdex;
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
Embodiment 3
A kind of inner wall surface decoration material, it comprises following materials based on weight:
100 parts of Mirabilitum crystallinas; 70 parts of kaolin;
10 parts of acrylic clear powder resins; 15 parts in zeolite;
1 part of carboxylic propyl methocel;
The particle diameter of described Mirabilitum crystallina is 1 millimeter; Described kaolin particle diameter is 15 microns; 50 microns of described zeolite granular diameters; The solid content 85% of described acrylic clear powder resin.
A kind of preparation method of inner wall surface decoration material is as follows:
1, select following materials based on weight:
100 parts of Mirabilitum crystallinas; 70 parts of kaolin;
10 parts of acrylic clear powder resins; 15 parts in zeolite;
1 part of carboxylic propyl methocel;
The particle diameter of described Mirabilitum crystallina is 1 millimeter; Described kaolin particle diameter is 15 microns; 50 microns of described zeolite granular diameters; The solid content 85% of described acrylic clear powder resin;
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
Embodiment 4
A kind of inner wall surface decoration material, it comprises following materials based on weight:
100 parts of quartz sands; 80 parts of talcum powder;
15 parts of organosilicon powder resins; 20 parts of attapulgites;
2 parts of polyvinyl alcohol;
The particle diameter of described quartz sand is 2 millimeters; Described talcum powder particle diameter is 20 microns; 100 microns of described attapulgite particle diameters; The solid content 90% of described polyvinyl alcohol.
A kind of preparation method of inner wall surface decoration material is as follows:
1, select following materials based on weight::
100 parts of quartz sands; 80 parts of talcum powder;
15 parts of organosilicon powder resins; 25 parts of attapulgites;
2.5 parts of polyvinyl alcohol;
The particle diameter of described quartz sand is 2 millimeters; Described talcum powder particle diameter is 20 microns; 100 microns of described attapulgite particle diameters; The solid content 90% of described polyvinyl alcohol;
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
Embodiment 5
A kind of inner wall surface decoration material, it comprises following materials based on weight:
100 parts of quartz sands; 90 parts in lime carbonate;
20 parts of polyvinyl acetate resin emulsions; 30 parts of sepiolites;
4 parts of methylcellulose gum;
The particle diameter of described quartz sand is 3 millimeters; Described calcium carbonate granule diameter is 40 microns; 150 microns of described sepiolite particle diameters; The solid content 30% of described polyvinyl acetate resin emulsion.
A kind of preparation method of inner wall surface decoration material is as follows:
1, select following materials based on weight::
100 parts of quartz sands; 90 parts in lime carbonate;
20 parts of polyvinyl acetate resin emulsions; 30 parts of sepiolites;
4 parts of methylcellulose gum;
The particle diameter of described quartz sand is 3 millimeters; Described calcium carbonate granule diameter is 40 microns; 150 microns of described sepiolite particle diameters; The solid content 30% of described polyvinyl acetate resin emulsion;
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
Embodiment 6
A kind of inner wall surface decoration material, it comprises following materials based on weight:
100 parts in color sand; 100 parts of titanium dioxides;
25 parts of ester-polyurethane resin emulsions; 35 parts in diatomite;
5 parts of carboxymethyl celluloses;
The particle diameter of described color sand is 3.8 millimeters; Described titanium dioxide particle diameter is 60 microns; Described diatomite particle diameter is 200 microns; The solid content 65% of described ester-polyurethane resin emulsion.
A kind of preparation method of inner wall surface decoration material is as follows:
1, select following materials based on weight::
100 parts in color sand; 100 parts of titanium dioxides;
25 parts of ester-polyurethane resin emulsions; 35 parts in diatomite;
5 parts of carboxymethyl celluloses;
The particle diameter of described color sand is 3.8 millimeters; Described titanium dioxide particle diameter is 60 microns; Described diatomite particle diameter is 200 microns; The solid content 65% of described ester-polyurethane resin emulsion;
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
Embodiment 7
A kind of inner wall surface decoration material, it comprises following materials based on weight:
100 parts of Mirabilitum crystallinas; 120 parts of kaolin;
30 parts of Emulsion acrylic resins; 40 parts in zeolite;
6 parts of carboxylic propyl methocels;
The particle diameter of described Mirabilitum crystallina is 4.5 millimeters; Described kaolin particle diameter is 80 microns; Described zeolite granular diameter is 250 microns; The solid content 45% of described emulsion-like synthetic resin tackiness agent.
A kind of preparation method of inner wall surface decoration material is as follows:
1, select following materials based on weight::
100 parts of Mirabilitum crystallinas; 120 parts of kaolin;
30 parts of Emulsion acrylic resins; 40 parts in zeolite;
6 parts of carboxylic propyl methocels;
The particle diameter of described Mirabilitum crystallina is 4.5 millimeters; Described kaolin particle diameter is 80 microns; Described zeolite granular diameter is 250 microns; The solid content 45% of described emulsion-like synthetic resin tackiness agent.
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
Embodiment 8
A kind of inner wall surface decoration material, it comprises following materials based on weight:
100 parts of quartz sands; 130 parts of talcum powder;
35 parts of silicone resin emulsions; 45 parts of attapulgites;
7 parts of methylcellulose gum; 0.32 part of carboxylic propyl methocel;
The particle diameter of described quartz sand is 5 millimeters; Described talcum powder particle diameter is 140 microns; Described attapulgite particle diameter is 300 microns; The solid content 50% of described silicone resin emulsion.
A kind of preparation method of inner wall surface decoration material is as follows:
1, select following materials based on weight::
100 parts of quartz sands; 130 parts of talcum powder;
35 parts of silicone resin emulsions; 45 parts of attapulgites;
7 parts of methylcellulose gum; 2 parts of carboxylic propyl methocels;
The particle diameter of described quartz sand is 5 millimeters; Described talcum powder particle diameter is 140 microns; Described attapulgite particle diameter is 300 microns; The solid content 50% of described silicone resin emulsion;
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
Embodiment 9
A kind of inner wall surface decoration material, it comprises following materials based on weight:
50 parts of quartz sands; 50 parts of Mirabilitum crystallinas; 30 parts in lime carbonate; 50 parts of titanium dioxides; 10 parts of kaolin; 4 parts of vinyl acetate between to for plastic powdexes; 5 parts of vinyl acetate-ethylene powdexes; 6 parts of organosilicon powder resins; 7 parts of vinyl chloride resin emulsions; 6 parts of sepiolites, 16 parts in diatomite, 13 parts in zeolite, 14 parts of attapulgites; 1 part of methylcellulose gum; 2 parts of carboxymethyl celluloses; 3 parts of polyvinyl alcohol;
The particle diameter of described quartz sand, Mirabilitum crystallina is 2 millimeters; Described lime carbonate, titanium dioxide, kaolinic particle diameter are 20 microns; Described sepiolite, diatomite, zeolite, attapulgite particle diameter are 160 microns; The solid content 85% of described vinyl acetate between to for plastic powdex, vinyl acetate-ethylene powdex, organosilicon powder resin, the solid content 50% of described vinyl chloride resin emulsion.
A kind of preparation method of inner wall surface decoration material is as follows:
1, select following materials based on weight:
50 parts of quartz sands; 50 parts of Mirabilitum crystallinas; 30 parts in lime carbonate; 50 parts of titanium dioxides; 10 parts of kaolin; 4 parts of vinyl acetate between to for plastic powdexes; 5 parts of vinyl acetate-ethylene powdexes; 6 parts of organosilicon powder resins; 7 parts of vinyl chloride resin emulsions; 6 parts of sepiolites, 16 parts in diatomite, 13 parts in zeolite, 14 parts of attapulgites; 1 part of methylcellulose gum; 2 parts of carboxymethyl celluloses; 3 parts of polyvinyl alcohol;
The particle diameter of described quartz sand, Mirabilitum crystallina is 2 millimeters; Described lime carbonate, titanium dioxide, kaolinic particle diameter are 20 microns; Described sepiolite, diatomite, zeolite, attapulgite particle diameter are 160 microns; The solid content 85% of described vinyl acetate between to for plastic powdex, vinyl acetate-ethylene powdex, organosilicon powder resin, the solid content 50% of described vinyl chloride resin emulsion.
2, mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.
Embodiment 10
Repeat embodiment 1, its difference is: a kind of inner wall surface decoration material, it also comprises following materials based on weight: 0.32 part on trevira.
Embodiment 11
Repeat embodiment 2, its difference is: a kind of inner wall surface decoration material, it also comprises following materials based on weight: 14.4 parts of tynexs.
Embodiment 12
Repeat embodiment 3, its difference is: a kind of inner wall surface decoration material, it also comprises following materials based on weight: 2 parts of polyacrylonitrile fibres.
Embodiment 13
Repeat embodiment 4, its difference is: a kind of inner wall surface decoration material, it also comprises following materials based on weight: 4 parts of polyvinyl alcohol fibers.
Embodiment 14
Repeat embodiment 5, its difference is: a kind of inner wall surface decoration material, and it also comprises following materials based on weight: 6 parts of thermovyls;
Embodiment 15
Repeat embodiment 6, its difference is: a kind of inner wall surface decoration material, it also comprises following materials based on weight: 8 parts of thermovyls.
Embodiment 16
Repeat embodiment 7, its difference is: a kind of inner wall surface decoration material, it also comprises following materials based on weight: 10 parts of polypropylene fibres.
Embodiment 17
Repeat embodiment 8, its difference is: a kind of inner wall surface decoration material, it also comprises following materials based on weight: 12 parts of polyurethane fibres.
Embodiment 18
Repeat embodiment 9, its difference is: a kind of inner wall surface decoration material, it also comprises following materials based on weight: 2 parts of 2 parts of sepiolite fibres, 3 parts of carbon fibres and rock wool fibers.
Claims (8)
1, a kind of inner wall surface decoration material, it is characterized in that: it comprises following materials based on weight:
100 parts of inorganic granular aggregates; 60～140 parts of powders;
3.2～48 parts of synthetic resin binders; 12.8～96 parts of inorganic porous powders;
0.08～12 part of Synergist S-421 95;
Described inorganic granular aggregate is the mixture a kind of or that two or more arbitrary proportion is mixed between them among quartz sand, color sand, the Mirabilitum crystallina;
Described powder is the mixture a kind of or that two or more arbitrary proportion is mixed between them among lime carbonate, titanium dioxide, kaolin, the talcum powder;
The particle diameter of described inorganic granular aggregate is between 0.15～6 millimeter; Described powder granule diameter is between 0.01～200 micron; 1～300 micron of described inorganic porous powder granule diameter.
2, a kind of inner wall surface decoration material according to claim 1 is characterized in that: described synthetic resin binder is the mixture a kind of or that two or more arbitrary proportion is mixed between them among solid, powdery synthetic resin binder, the emulsion-like synthetic resin tackiness agent.
3, a kind of inner wall surface decoration material according to claim 2 is characterized in that: described solid, powdery synthetic resin binder is the mixture a kind of or that two or more arbitrary proportion is mixed between them among vinyl acetate between to for plastic powdex, vinyl acetate-ethylene powdex, acrylic clear powder resin, the organosilicon powder resin; The solid content of described solid, powdery synthetic resin binder is 80～100%.
4, a kind of inner wall surface decoration material according to claim 2, it is characterized in that: described emulsion-like synthetic resin tackiness agent is the mixture a kind of or that two or more arbitrary proportion is mixed between them among polyvinyl acetate resin emulsion, ester-polyurethane resin emulsion, Emulsion acrylic resin, silicone resin emulsion, the vinyl chloride resin emulsion, and the solid content of described emulsion-like synthetic resin tackiness agent is 30～65%.
5, a kind of inner wall surface decoration material according to claim 1 is characterized in that: described inorganic porous powder is the mixture a kind of or that two or more arbitrary proportion is mixed between them among sepiolite, diatomite, zeolite, the attapulgite.
6, a kind of inner wall surface decoration material according to claim 1 is characterized in that: described Synergist S-421 95 is the mixture a kind of or that two or more arbitrary proportion is mixed between them among methylcellulose gum, carboxymethyl cellulose, carboxylic propyl methocel, the polyvinyl alcohol.
7, a kind of inner wall surface decoration material according to claim 1, it is characterized in that: it also comprises following materials based on weight:
0.32～14.4 part of fiber;
Described fiber is the mixture a kind of or that two or more arbitrary proportion is mixed between them among synthon, the mineral fibre; Described synthon are the mixtures a kind of or that two or more arbitrary proportion is mixed between them among trevira, tynex, polyacrylonitrile fibre, polyvinyl alcohol fiber, thermovyl, polypropylene fibre, the polyurethane fibre; Described mineral fibre is the mixture a kind of or that two or more arbitrary proportion is mixed between them among sepiolite fibre, carbon fibre, the rock wool fibers.
8, a kind of preparation method of inner wall surface decoration material is characterized in that:
1) select following materials based on weight:
100 parts of inorganic granular aggregates; 60～140 parts of powders;
3.2～48 parts of synthetic resin binders; 12.8～96 parts of inorganic porous powders;
0.08～12 part of Synergist S-421 95; 0.32～14.4 part of fiber;
The particle diameter of described inorganic granular aggregate is between 0.15～6 millimeter; Described powder granule diameter is between 0.01～200 micron; 1～300 micron of described inorganic porous powder granule diameter;
2) mix: the raw material of above-mentioned parts by weight is mixed; Promptly get product.