CN102766312B - Crack resistant base cloth - Google Patents
Crack resistant base cloth Download PDFInfo
- Publication number
- CN102766312B CN102766312B CN2011101149378A CN201110114937A CN102766312B CN 102766312 B CN102766312 B CN 102766312B CN 2011101149378 A CN2011101149378 A CN 2011101149378A CN 201110114937 A CN201110114937 A CN 201110114937A CN 102766312 B CN102766312 B CN 102766312B
- Authority
- CN
- China
- Prior art keywords
- base cloth
- kilograms
- crack resistant
- calcium carbonate
- sterilant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a base cloth for filling an indoor wire duct, especially to a crack resistant base cloth. The crack resistant base cloth comprises water, CMC cellulose, an acrylic acid emulsion, calcium carbonate, powdered steatile 16.7, a dispersant 0.16, a bactericide 0.12 and mekralon. In a present method, a quick drying powder is used for fixing, sand ash is then used for surface rolling, and gesso or cement is added into the sand ash for mixing. In comparison with the present method, the crack resistant base cloth has an excellent crack resistant effect, is healthy and environmentally friendly, can be used to effectively prevent the problem that the wire duct is easy to crack during filling process due to deep depth of the wire duct, and obviously raises aesthetic property of interior walls. In addition, the crack resistant base cloth is simple to construct, is sturdy and durable, has long service life, and can be used to reduce usage and maintenance costs of buildings in the future.
Description
Technical field
The present invention relates to a kind of indoor wire casing place and fill up base cloth, particularly a kind of cracking resistance base cloth.
Background technology
Along with social progress, expanding economy, the progress of science and technology, people are to the indoor wall decorative effect
Requirement also more and more higher, therefore all kinds of indoor wall cracking resistance products flood the market.Filling up of indoor wire casing place in the market is mainly to adopt fast dry powder to fix,, terra alba floating with the sand ash or cement add sand mixing etc. again, although to a certain extent filling up of wire casing place played to certain decorative effect, but this kind of traditional processing of filling up to the wire casing place easily causes the metope cracking, construction is complicated, so research and develop a kind of easy construction, the good cracking resistance base cloth of effect of prestressed has great economic benefit.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, and a kind of easy construction is provided, effect of prestressed is good, sturdy and durable, health environment-friendly and can alleviate the cracking resistance base cloth of the cost of working service in the future of buildings.
The objective of the invention is to be achieved through the following technical solutions: the cracking resistance base cloth, by the quality percentage composition, it mainly comprises:
Water 10.1 ~ 14%, CMC Mierocrystalline cellulose 0.9 ~ 1.1%, ACRYLIC EMULSION 35 ~ 37%, calcium carbonate 29 ~ 34%, talcum powder 15 ~ 17.3%, dispersion agent 0.15 ~ 0.2%, anticorrosive mildewproof sterilant 0.1 ~ 0.15%, polypropylene fibre 1.2-1.5%.
As of the present invention, one improve again, described cracking resistance base cloth, by the quality percentage composition, it mainly comprises:
Water 10.1%, CMC Mierocrystalline cellulose 0.9%, ACRYLIC EMULSION 37%, calcium carbonate 34%, talcum powder 15.3%, dispersion agent 0.2%, anticorrosive mildewproof sterilant 0.1%, polypropylene fibre 1.2%.
As of the present invention, one improve again, described cracking resistance base cloth, by the quality percentage composition, it mainly comprises:
Water 12%, CMC Mierocrystalline cellulose 1.1%, ACRYLIC EMULSION 36%, calcium carbonate 33%, talcum powder 16%, dispersion agent 0.15%, anticorrosive mildewproof sterilant 0.15%, polypropylene fibre 1.3%.
As of the present invention, one improve again, described cracking resistance base cloth, by the quality percentage composition, it mainly comprises:
Water 14%, CMC Mierocrystalline cellulose 1%, ACRYLIC EMULSION 36.5%, calcium carbonate 29%, talcum powder 17.3%, dispersion agent 0.18%, anticorrosive mildewproof sterilant 0.14%, polypropylene fibre 1.5%.
As of the present invention, one improve again, described cracking resistance base cloth, by the quality percentage composition, it mainly comprises: water 13%, CMC Mierocrystalline cellulose 1.05%, ACRYLIC EMULSION 35%, calcium carbonate 32%, talcum powder 17%, dispersion agent 0.19%, anticorrosive mildewproof sterilant 0.13%, polypropylene fibre 1.4%.
As of the present invention, one improve again, described cracking resistance base cloth, by the quality percentage composition, it mainly comprises: water 12.8%, CMC Mierocrystalline cellulose 1.08%, ACRYLIC EMULSION 35.9%, calcium carbonate 32.5%, talcum powder 15.9%, dispersion agent 0.16%, anticorrosive mildewproof sterilant 0.12%, polypropylene fibre 1.42%.
Beneficial effect of the present invention: cracking resistance base cloth of the present invention contains water, the CMC Mierocrystalline cellulose, ACRYLIC EMULSION, calcium carbonate, talcum powder 16.7, dispersion agent 0.16, anticorrosive mildewproof sterilant 0.12 and polypropylene fibre, with the fast dry powder of existing employing, fix, use again the sand ash floating, terra alba or cement add the method for sand mixing and compare, cracking resistance base cloth effect of prestressed of the present invention is good, health environment-friendly, be highly resistant to when the wire casing place is filled up because the degree of depth is dark the problem of cracking that easily produces, obviously improve the aesthetics of indoor wall, and, its easy construction, sturdy and durable, life-span is long, alleviated the cost of working service in the future of buildings.
Embodiment
Embodiment 1
Fetch water 101 kilograms, 9 kilograms of CMC Mierocrystalline celluloses, 370 kilograms of ACRYLIC EMULSION, 340 kilograms, calcium carbonate, 153 kilograms of talcum powder, 2 kilograms of dispersion agents, 1 kilogram, anticorrosive mildewproof sterilant, 12 kilograms of polypropylene fibres.
Water is dropped into and stirs in filling, slowly run, slowly drop into the CMC Mierocrystalline cellulose, be stirred to without evengranular thick, then drop into dispersion agent, anticorrosive mildewproof sterilant, polypropylene fibre, ACRYLIC EMULSION, stirring at low speed 15 minutes, drop into again calcium carbonate, talcum powder, high-speed stirring 20 minutes, feeding, make novel anti-crack base cloth of the present invention.
Embodiment 2
Water intaking 120 kg, 11 kilograms of CMC Mierocrystalline celluloses, 360 kilograms of ACRYLIC EMULSION, 330 kilograms, calcium carbonate, 160 kilograms of talcum powder, 1.5 kilograms of dispersion agents, 1.5 kilograms, anticorrosive mildewproof sterilant, 13 kilograms of polypropylene fibres.
Water is dropped into and stirs in filling, slowly run, slowly drop into the CMC Mierocrystalline cellulose, be stirred to without evengranular thick, then drop into dispersion agent, anticorrosive mildewproof sterilant, polypropylene fibre, ACRYLIC EMULSION, stirring at low speed 15 minutes, drop into again calcium carbonate, talcum powder, high-speed stirring 20 minutes, feeding, make novel anti-crack base cloth of the present invention.
Embodiment 3
Fetch water 140 kilograms, 10 kilograms of CMC Mierocrystalline celluloses, 365 kilograms of ACRYLIC EMULSION, 290 kilograms, calcium carbonate, 173 kilograms of talcum powder, 1.8 kilograms of dispersion agents, 1.4 kilograms, anticorrosive mildewproof sterilant, 15 kilograms of polypropylene fibres.
Water is dropped into and stirs in filling, slowly run, slowly drop into the CMC Mierocrystalline cellulose, be stirred to without evengranular thick, then drop into dispersion agent, anticorrosive mildewproof sterilant, polypropylene fibre, ACRYLIC EMULSION, stirring at low speed 15 minutes, drop into again calcium carbonate, talcum powder, high-speed stirring 20 minutes, feeding, make novel anti-crack base cloth of the present invention.
Embodiment 4
Fetch water 130 kilograms, 10.5 kilograms of CMC Mierocrystalline celluloses, 350 kilograms of ACRYLIC EMULSION, 320 kilograms, calcium carbonate, 170 kilograms of talcum powder, 1.9 kilograms of dispersion agents, 1.3 kilograms, anticorrosive mildewproof sterilant, 14 kilograms of polypropylene fibres.
Water is dropped into and stirs in filling, slowly run, slowly drop into the CMC Mierocrystalline cellulose, be stirred to without evengranular thick, then drop into dispersion agent, anticorrosive mildewproof sterilant, polypropylene fibre, ACRYLIC EMULSION, stirring at low speed 15 minutes, drop into again calcium carbonate, talcum powder, high-speed stirring 20 minutes, feeding, make novel anti-crack base cloth of the present invention.
Embodiment 5
Fetch water 128 kilograms, 10.8 kilograms of CMC Mierocrystalline celluloses, 359 kilograms of ACRYLIC EMULSION, 325 kilograms, calcium carbonate, 159 kilograms of talcum powder, 1.6 kilograms of dispersion agents, 1.2 kilograms, anticorrosive mildewproof sterilant, 14.2 kilograms of polypropylene fibres.
Water is dropped into and stirs in filling, slowly run, slowly drop into the CMC Mierocrystalline cellulose, be stirred to without evengranular thick, then drop into dispersion agent, anticorrosive mildewproof sterilant, polypropylene fibre, ACRYLIC EMULSION, stirring at low speed 15 minutes, drop into again calcium carbonate, talcum powder, high-speed stirring 20 minutes, feeding, make novel anti-crack base cloth of the present invention.
The above only As preferred embodiment of the present invention, and not only above restriction the present invention, all any modifications of doing within the spirit and principles in the present invention, be equal to and replace and improvement etc., all should be included in protection scope of the present invention.
Claims (6)
1. cracking resistance base cloth, it is characterized in that: by the quality percentage composition, it mainly comprises: water 10.1 ~ 14%, CMC Mierocrystalline cellulose 0.9 ~ 1.1%, ACRYLIC EMULSION 35 ~ 37%, calcium carbonate 29 ~ 34%, talcum powder 15 ~ 17.3%, dispersion agent 0.15 ~ 0.2%, sterilant 0.1 ~ 0.15%, polypropylene fibre 1.2-1.5%.
2. cracking resistance base cloth as claimed in claim 1, it is characterized in that: by the quality percentage composition, it mainly comprises: water 10.1%, CMC Mierocrystalline cellulose 0.9%, ACRYLIC EMULSION 37%, calcium carbonate 34%, talcum powder 15.3%, dispersion agent 0.2%, sterilant 0.1%, polypropylene fibre 1.2%.
3. cracking resistance base cloth as claimed in claim 1, it is characterized in that: by the quality percentage composition, it mainly comprises: water 12%, CMC Mierocrystalline cellulose 1.1%, ACRYLIC EMULSION 36%, calcium carbonate 33%, talcum powder 16%, dispersion agent 0.15%, sterilant 0.15%, polypropylene fibre 1.3%.
4. cracking resistance base cloth as claimed in claim 1, it is characterized in that: by the quality percentage composition, it mainly comprises: water 14%, CMC Mierocrystalline cellulose 1%, ACRYLIC EMULSION 36.5%, calcium carbonate 29%, talcum powder 17.3%, dispersion agent 0.18%, sterilant 0.14%, polypropylene fibre 1.5%.
5. cracking resistance base cloth as claimed in claim 1, it is characterized in that: by the quality percentage composition, it mainly comprises: water 13%, CMC Mierocrystalline cellulose 1.05%, ACRYLIC EMULSION 35%, calcium carbonate 32%, talcum powder 17%, dispersion agent 0.19%, sterilant 0.13%, polypropylene fibre 1.4%.
6. cracking resistance base cloth as claimed in claim 1, it is characterized in that: by the quality percentage composition, it mainly comprises: water 12.8%, CMC Mierocrystalline cellulose 1.08%, ACRYLIC EMULSION 35.9%, calcium carbonate 32.5%, talcum powder 15.9%, dispersion agent 0.16%, sterilant 0.12%, polypropylene fibre 1.42%.