CN102898085A - Heat insulation mortar and preparation method of heat insulation mortar - Google Patents
Heat insulation mortar and preparation method of heat insulation mortar Download PDFInfo
- Publication number
- CN102898085A CN102898085A CN2012104245013A CN201210424501A CN102898085A CN 102898085 A CN102898085 A CN 102898085A CN 2012104245013 A CN2012104245013 A CN 2012104245013A CN 201210424501 A CN201210424501 A CN 201210424501A CN 102898085 A CN102898085 A CN 102898085A
- Authority
- CN
- China
- Prior art keywords
- insulation mortar
- percent
- heat insulation
- water
- thermal insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses heat insulation mortar, which consists of the following ingredients in percentage by weight: 25 to 50 percent of cement, 10 to 20 percent of carclazyte, 10 to 15 percent of gypsum, 5 to 10 percent of binding agents, 2 to 3 percent of waterproof agents, 1 to 2 percent of brightening agents, 4 to 10 percent of calcium powder, 2 to 3 percent of polyvinyl alcohol, 2 to 5 percent of polystyrene foam particles and the balance water. The heat insulation mortar has the advantages that the heat insulation mortar is nontoxic, tasteless and non-radioactive, no harm is caused on human bodies, the environment is not polluted, the advantages of energy saving and environment protection are realized, and the production cost is low.
Description
Technical field
The present invention relates to a kind of thermal insulation mortar and preparation method thereof.
Background technology
Thermal insulation mortar is a kind of exterior wall surface that is coated in, and is used for the material that external body of wall is incubated.The quality of thermal insulation mortar quality directly affects the heat-insulating property of exterior wall.Its heat insulation effect of existing thermal insulation mortar is bad, can not adapt to the changeable climate environment, and easily cracking glides, and can not satisfy user demand.Therefore, should provide a kind of new technical scheme to address the above problem.
Summary of the invention
The objective of the invention is: for above-mentioned deficiency, provide a kind of heat insulation effect, work-ing life of a specified duration, thermal insulation mortar not easy to crack and preparation method thereof.
For achieving the above object, the technical solution used in the present invention is:
A kind of thermal insulation mortar is made of the component of following weight percentage:
Cement 25-50%;
Carclazyte 10-20%;
Gypsum 10-15%;
Binding agent 5-10%;
Water-resisting agent 2-3%;
Brightening agent 1-2%;
Calcium powder 4-10%;
Polyvinyl alcohol 2-3%;
Polystyrene foam particles 2-5%;
Water surplus.
A kind of preparation method of thermal insulation mortar comprises the steps:
Polystyrene foam is ground into size up to specification;
The dilute with water high polymer binder with each above-mentioned component, mixes and adds suitable quantity of water by its proportioning and be modulated into paste;
After the above-mentioned mortar that is modulated into paste left standstill 10-12h, can use.
The particle diameter of described polystyrene foam particles is the 10-50 order.
Advantage of the present invention is: this thermal insulation mortar is nontoxic, tasteless, "dead", and is harmless, free from environmental pollution, has advantages of energy-conserving and environment-protective, and production cost is low.
Embodiment
Embodiment 1
A kind of thermal insulation mortar is made of the component of following weight percentage: cement 25%,
Carclazyte 10%, gypsum 10%, binding agent 5%, water-resisting agent 2%, brightening agent 1%, calcium powder 4%, polyvinyl alcohol 2%, polystyrene foam particles 2%, surplus is water.
A kind of preparation method of thermal insulation mortar comprises the steps:
Polystyrene foam is ground into size up to specification;
The dilute with water high polymer binder with above-mentioned each component, mixes and adds suitable quantity of water by its proportioning and be modulated into paste;
After the above-mentioned mortar that is modulated into paste left standstill 10h, can use.
The particle diameter of described polystyrene foam particles is 10 orders.
Embodiment 2
A kind of thermal insulation mortar is made of the component of following weight percentage: cement 30%,
Carclazyte 10%, gypsum 10%, binding agent 5 %, water-resisting agent 3%, brightening agent 1%, calcium powder 6%, polyvinyl alcohol 2%, polystyrene foam particles 2%, surplus is water.
A kind of preparation method of thermal insulation mortar comprises the steps:
Polystyrene foam is ground into size up to specification;
The dilute with water high polymer binder with above-mentioned each component, mixes and adds suitable quantity of water by its proportioning and be modulated into paste;
After the above-mentioned mortar that is modulated into paste left standstill 11h, can use.
The particle diameter of described polystyrene foam particles is 30 orders.
Embodiment 3
A kind of thermal insulation mortar is made of the component of following weight percentage: cement 30%,
Carclazyte 15%, gypsum 13%, binding agent 8%, water-resisting agent 3%, brightening agent 2%, calcium powder 10%, polyvinyl alcohol 3%, polystyrene foam particles 2%, surplus is water.
A kind of preparation method of thermal insulation mortar comprises the steps:
Polystyrene foam is ground into size up to specification;
The dilute with water high polymer binder with above-mentioned each component, mixes and adds suitable quantity of water by its proportioning and be modulated into paste;
After the above-mentioned mortar that is modulated into paste left standstill 12h, can use.
The particle diameter of described polystyrene foam particles is 50 orders.
Claims (3)
1. thermal insulation mortar, it is characterized in that: the component by following weight percentage consists of:
Cement 25-50%;
Carclazyte 10-20%;
Gypsum 10-15%;
Binding agent 5-10%;
Water-resisting agent 2-3%;
Brightening agent 1-2%;
Calcium powder 4-10%;
Polyvinyl alcohol 2-3%;
Polystyrene foam particles 2-5%;
Water surplus.
2. the preparation method of a thermal insulation mortar is characterized in that, comprises the steps:
Polystyrene foam is ground into size up to specification;
The dilute with water high polymer binder with each component claimed in claim 1, mixes and adds suitable quantity of water by its proportioning and be modulated into paste;
After the above-mentioned mortar that is modulated into paste left standstill 10-12h, can use.
3. a kind of thermal insulation mortar according to claim 1, it is characterized in that: the particle diameter of polystyrene foam particles is the 10-50 order.