CN101993681A - Water-proof heat-insulating composite material - Google Patents

Water-proof heat-insulating composite material Download PDF

Info

Publication number
CN101993681A
CN101993681A CN2009100132635A CN200910013263A CN101993681A CN 101993681 A CN101993681 A CN 101993681A CN 2009100132635 A CN2009100132635 A CN 2009100132635A CN 200910013263 A CN200910013263 A CN 200910013263A CN 101993681 A CN101993681 A CN 101993681A
Authority
CN
China
Prior art keywords
percent
agent
water
heat
composite material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009100132635A
Other languages
Chinese (zh)
Inventor
王猛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009100132635A priority Critical patent/CN101993681A/en
Publication of CN101993681A publication Critical patent/CN101993681A/en
Pending legal-status Critical Current

Abstract

The invention discloses a water-proof heat-insulating composite material, which is particularly suitable for the industrial fields such as petrifaction, electric power, metallurgy, building materials and the like, and provides the water-proof heat-insulating composite material which can effectively save energy and preserve the heat and has the effect of water proofing. The material is prepared from the following raw materials: 10 to 50 percent of perlite, 0.1 to 0.3 percent of high-temperature glue, 1 to 10 percent of diatomite, 1 to 3 percent of adhesive, 1 to 6 percent of composite rare earth additive, 1 to 5 percent of mineral wool, 2 to 10 percent of gypsum powder, 2 to 5 percent of aluminum silicate fiber, 0.8 to 1.3 percent of succinic acid, 15 to 22 percent of calcium hydroxide, 15 to 22 percent of kaoline, 0.1 to 0.2 percent of foaming agent and 0.1 to 0.4 percent of air entraining agent.

Description

A kind of waterproof, heat-preserving complex material
Technical field:
The present invention relates to a kind of waterproof, heat-preserving complex material, is specially adapted to industrial circles such as petrochemical industry, electric power, metallurgy, building materials.
Background technology:
Raising along with Economic development and technology, people improve gradually to the requirement of building, require material of construction to play multiple functions, but also pay attention to more, and whether the resident also pays much attention to health is harmful indoor heat insulation effect and material for heat insulation effect.China requires also very high to the energy-conserving action of material of construction, wall heat transfer causes power loss, and the insulation effect of existing lagging material is good inadequately, especially a year material of construction of a specified duration crackle can occur and easily seeps water, and also there are some toxic substances in the lagging material that has, have radioactivity or carcinogenic, the utmost point influences HUMAN HEALTH.And the complex process that has, the packed and transported difficulty is difficult for preserving.
Summary of the invention:
The present invention is exactly at the problems referred to above, and a kind of waterproof, heat-preserving complex material are provided, can be effectively energy-conservation, insulation, and play waterproof action.
Preparation of raw material of the present invention is:
Perlite 10～50%, high-temp glue 0.1～0.3%, diatomite 1～10%, tackiness agent 1～3%, compound rare-earth additive 1～6%, mineral cotton 1～5%, terra alba 2～10%, aluminum silicate fiber 2～5%, succsinic acid 0.8～1.3%, calcium hydroxide 15～22%, kaolin 15～22%, whipping agent 0.1～0.2%, air entrapment agent 0.1～0.4%.
Beneficial effect of the present invention:
Environmental nonpollution of the present invention, free from extraneous odour, corrosion-resistant, easy construction, high-low temperature resistant, waterproof have good heat retaining property, convenient storage, bonding firmly, need not use the advantage of other waterproof measures, saving of work and time, effective.A certain proportion of perlite and aluminum silicate fiber is compound, and the composite product good heat insulating has higher intensity and elasticity, and manufacturing process is simple, easy construction, and production cost reduces greatly, and remarkable in economical benefits is so have promotional value.
Embodiment:
Embodiment 1, adopts the following manner preparation:
Perlite 15%, high-temp glue 0.15%, diatomite 2%, tackiness agent 1.5%, compound rare-earth additive 2%, mineral cotton 2%, terra alba 3%, aluminum silicate fiber 3%, succsinic acid 0.9%, calcium hydroxide 17%, kaolin 17%, whipping agent 0.1%, air entrapment agent 0.2%.
Embodiment 2, adopt the following manner preparation:
Perlite 30%, high-temp glue 0.2%, diatomite 5%, tackiness agent 2%, compound rare-earth additive 5%, mineral cotton 2%, terra alba 5%, aluminum silicate fiber 4%, succsinic acid 1.0%, calcium hydroxide 17%, kaolin 17%, whipping agent 0.15%, air entrapment agent 0.3%.

Claims (3)

1. a waterproof, heat-preserving complex material is characterized in that preparation of raw material of the present invention is: perlite 10～50%, high-temp glue 0.1～0.3%, diatomite 1～10%, tackiness agent 1～3%, compound rare-earth additive 1～6%, mineral cotton 1～5%, terra alba 2～10%, aluminum silicate fiber 2～5%, succsinic acid 0.8～1.3%, calcium hydroxide 15～22%, kaolin 15～22%, whipping agent 0.1～0.2%, air entrapment agent 0.1～0.4%.
2. a kind of waterproof according to claim 1, heat-preserving complex material,, it is characterized in that perlite 15%, high-temp glue 0.15%, diatomite 2%, tackiness agent 1.5%, compound rare-earth additive 2%, mineral cotton 2%, terra alba 3%, aluminum silicate fiber 3%, succsinic acid 0.9%, calcium hydroxide 17%, kaolin 17%, whipping agent 0.1%, air entrapment agent 0.2%.
3. a kind of waterproof according to claim 1, heat-preserving complex material,, it is characterized in that perlite 30%, high-temp glue 0.2%, diatomite 5%, tackiness agent 2%, compound rare-earth additive 5%, mineral cotton 2%, terra alba 5%, aluminum silicate fiber 4%, succsinic acid 1.0%, calcium hydroxide 17%, kaolin 17%, whipping agent 0.15%, air entrapment agent 0.3%.
CN2009100132635A 2009-08-20 2009-08-20 Water-proof heat-insulating composite material Pending CN101993681A (en)