CN100575296C - Light flame-retardant decorating material and preparation method thereof - Google Patents
Light flame-retardant decorating material and preparation method thereof Download PDFInfo
- Publication number
- CN100575296C CN100575296C CN 200710131519 CN200710131519A CN100575296C CN 100575296 C CN100575296 C CN 100575296C CN 200710131519 CN200710131519 CN 200710131519 CN 200710131519 A CN200710131519 A CN 200710131519A CN 100575296 C CN100575296 C CN 100575296C
- Authority
- CN
- China
- Prior art keywords
- colorant
- resin
- glass fibre
- talcum powder
- weight ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Light flame-retardant decorating material and preparation method thereof, its component are magnesium chloride, sal epsom, magnesium oxide, expanded polystyrene beads material, glass fibre, water, talcum powder, resin, colorant.Each compositions in weight percentage is: magnesium chloride: 26-30%, sal epsom: 10-18%, magnesium oxide: 16-20%, expanded polystyrene beads material: 8-15%, glass fibre: 4-16%, water: 5-10%, talcum powder: 6-10%, resin: 5-16%, colorant: 0.8-1.8%.Magnesium chloride, sal epsom, magnesium oxide are pressed above-mentioned weight ratio, use water dissolution, and stir, adding particle diameter by above-mentioned weight ratio again is the glass fibre that 1 millimeter expanded polystyrene beads material and length are 5 millimeters, adds talcum powder, resin, colorant by above-mentioned weight ratio.Fully stir, become sticky shape, reinject framed in, under the temperature of 60 degree Celsius, left standstill the demoulding, moulding 2 hours.Use light flame-retardant decorating material of the present invention, light weight, fire prevention, intensity height.
Description
Affiliated technical field
The present invention relates to finishing material for building and preparation method thereof.
Background technology
Existing finishing material for building, have as plank, can not prevent fires; Have as cement plate, too heavy; Have as plasterboard, intensity is not high.
Content of the present invention
The objective of the invention is provides a kind of light flame-retardant decorating material in order to overcome above-mentioned weak point, light weight, fire prevention, intensity height.
The technical solution adopted for the present invention to solve the technical problems is: the component of light flame-retardant decorating material is magnesium chloride, sal epsom, magnesium oxide, expanded polystyrene beads material, glass fibre, water, talcum powder, resin, colorant.Each compositions in weight percentage is:
Magnesium chloride 26-30%
Sal epsom 10-18%
Magnesium oxide 16-20%
Expanded polystyrene beads material 8-15%
Glass fibre 4-16%
Water 5-10%
Talcum powder 6-10%
Resin 5-16%
Colorant 0.8-1.8%
The preparation method of light flame-retardant decorating material for building of the present invention is: with magnesium chloride, sal epsom, magnesium oxide by above-mentioned weight ratio, use water dissolution, and stir, make concentration at 60-70%, adding particle diameter by above-mentioned weight ratio again is the glass fibre that 1 millimeter expanded polystyrene beads material and length are 5 millimeters, adds talcum powder, resin, colorant by above-mentioned weight ratio.Fully stir, become sticky shape.With sticky shape raw material inject framed in, under the temperature of 60 degree Celsius, left standstill the demoulding, moulding 2 hours.
Effective effect of the present invention is to use light flame-retardant decorating material of the present invention, light weight, fire prevention, intensity height.
Specific implementation method
Embodiment 1, and the component of light flame-retardant decorating material is magnesium chloride, sal epsom, magnesium oxide, expanded polystyrene beads material, glass fibre, water, talcum powder, resin, colorant.Each compositions in weight percentage is:
Magnesium chloride 28%
Sal epsom 12%
Magnesium oxide 16%
Expanded polystyrene beads material 10%
Glass fibre 7%
Water 8%
Talcum powder 8%
Resin 10%
Colorant 1%
Magnesium chloride, sal epsom, magnesium oxide are pressed above-mentioned weight ratio, use water dissolution, and stir, make concentration 65%, adding particle diameter by above-mentioned weight ratio again is the glass fibre that 1 millimeter expanded polystyrene beads material and length are 5 millimeters, adds talcum powder, resin, colorant by above-mentioned weight ratio.Fully stir, become sticky shape.With sticky shape raw material inject framed in, under the temperature of 60 degree Celsius, left standstill the demoulding, moulding 2 hours.
Embodiment 2, and the component of light flame-retardant decorating material is magnesium chloride, sal epsom, magnesium oxide, expanded polystyrene beads material, glass fibre, water, talcum powder, resin, colorant.Each compositions in weight percentage is:
Magnesium chloride 26%
Sal epsom 14%
Magnesium oxide 18%
Expanded polystyrene beads material 8%
Glass fibre 8%
Water 7%
Talcum powder 8%
Resin 9.5%
Colorant 1.5%
Magnesium chloride, sal epsom, magnesium oxide are pressed above-mentioned weight ratio, use water dissolution, and stir, make concentration 65%, adding particle diameter by above-mentioned weight ratio again is the glass fibre that 1 millimeter expanded polystyrene beads material and length are 5 millimeters, adds talcum powder, resin, colorant by above-mentioned weight ratio.Fully stir, become sticky shape.With sticky shape raw material inject framed in, under the temperature of 60 degree Celsius, left standstill the demoulding, moulding 2 hours.
Claims (2)
1, light flame-retardant decorating material, its feature are down: its component is that magnesium chloride, sal epsom, magnesium oxide, foaming are got vinylbenzene pellet, glass fibre, water, talcum powder, resin, colorant, each compositions in weight percentage and be:
Magnesium chloride 26-30%
Sal epsom 10-18%
Magnesium oxide 16-20%
Expanded polystyrene beads material 8-15%
Glass fibre 4-16%
Water 5-10%
Talcum powder 6-10%
Resin 5-16%
Colorant 0.8-1.8%
2, the preparation method of light flame-retardant decorating material according to claim 1, it is characterized in that: magnesium chloride, sal epsom, magnesium oxide are pressed above-mentioned weight ratio, use water dissolution, and stir, make concentration at 60-70%, adding particle diameter by above-mentioned weight ratio again is the glass fibre that 1 millimeter expanded polystyrene beads material and length are 5 millimeters, add talcum powder, resin, colorant by above-mentioned weight ratio, fully stir, become sticky shape, with sticky shape raw material inject framed in, under the temperature of 60 degree Celsius, left standstill demoulding, moulding 2 hours.