CN108863234A - A kind of negative ion far-infrared inorganic artificial stone slab and preparation method thereof - Google Patents

A kind of negative ion far-infrared inorganic artificial stone slab and preparation method thereof Download PDF

Info

Publication number
CN108863234A
CN108863234A CN201810844876.2A CN201810844876A CN108863234A CN 108863234 A CN108863234 A CN 108863234A CN 201810844876 A CN201810844876 A CN 201810844876A CN 108863234 A CN108863234 A CN 108863234A
Authority
CN
China
Prior art keywords
parts
stone slab
negative ion
artificial stone
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810844876.2A
Other languages
Chinese (zh)
Inventor
谭淑仪
郭栋
郗毅
戎延团
吴勇杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Global Classical New Material Co Ltd In Dongguan
Original Assignee
Global Classical New Material Co Ltd In Dongguan
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Global Classical New Material Co Ltd In Dongguan filed Critical Global Classical New Material Co Ltd In Dongguan
Priority to CN201810844876.2A priority Critical patent/CN108863234A/en
Publication of CN108863234A publication Critical patent/CN108863234A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of negative ion far-infrared inorganic artificial stone slab and preparation method thereof, the stone slab is made of following component in parts by weight：14-25 parts of cement, 1-7 parts of calcined kaolin, 50-70 parts of sand material, 1-5 parts of mountain flour, 6-15 parts of water, 2-6 parts of water-reducing agent, 1-2 parts of anion mineral powder, 0.1-6 parts of magnesia pigment.The present invention can discharge anion, purify air, remove odors, and eliminate formaldehyde, reduce radiation, enrich the function of slabstone.

Description

A kind of negative ion far-infrared inorganic artificial stone slab and preparation method thereof
Technical field
The invention belongs to plate field, specifically a kind of negative ion far-infrared inorganic artificial stone slab and its preparation side Method.
Background technique
Due to the attention that environment increasingly deteriorates and Environmental is protected, especially increased in recent years to atmosphere pollution The discharge of organic volatile has been included into priority control range during management, artificial wood-based board and Furniture manufacturing.
The surface decoration material of furniture and decoration face artificial board have melamine-impregnated bond paper, PVC, fire-proof plate, Water paint and solvent based coating (being commonly called as painting), wherein with solvent based coating and melamine-impregnated bond paper use scope It is most wide.Solvent based coating is because of the spies such as coating is full, color is abundant, adhesive force is good, and high and low temperature resistance is strong, surface hardness is moderate Point is widely used in Furniture manufacture in the past 50 years and the main of Decorating Project uses material -- in artificial board facing.But people Make in plate and paint containing a large amount of effumability and the longer toxic noxious species of retention time, as formaldehyde, benzene, toluene, Dimethylbenzene, VOCs etc..High risks are caused to the health of constructor and user, at present in Decorating Project and Furniture manufacturing Field is forbidden to use solvent based coating.
For the whole industry all in the finishing material for developing alternative paint, water paint (aqua type cold coating) enters house in recent years Has production field, but because at high cost, the problems such as equipment investment is big, difficulty of construction is high, surface decoration effect is undesirable causes to promote It is obstructed.Therefore, a kind of itself not discharge unwanted volatile and have good facing function, wood-based plate and furniture be discharged Unwanted volatile in and/or by chemical reaction be allowed to discharge beneficial health elements, can inherently change furniture and artificial Plate pollutes the defect finishing material of environment, becomes the long-term pursuit of numerous practitioners.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of negative ion far-infrared inorganic artificial stone slab and its preparation sides Method can discharge anion, purify air, remove odors, and eliminate formaldehyde, reduce radiation, enrich the function of slabstone.
In order to solve the above-mentioned technical problem, the present invention takes following technical scheme：
A kind of negative ion far-infrared inorganic artificial stone slab, the stone slab are made of following component in parts by weight： 14-25 parts of cement, 1-7 parts of calcined kaolin, 50-70 parts of sand material, 1-5 parts of mountain flour, 6-15 parts of water, 2-6 parts of water-reducing agent, anion 1-2 parts of mineral powder, 0.1-6 parts of magnesia pigment.
The sand material is quartz sand or calcium carbonate sand.
The water-reducing agent is polycarboxylate water-reducer.
The cement is portland cement or composite Portland cement.
A kind of preparation method of negative ion far-infrared inorganic artificial stone slab, includes the following steps：
First by calcined kaolin, cement, mountain flour, sand material, anion mineral powder, magnesia pigment, which are placed in agitator tank, carries out first Secondary stirring, stirring is stirred 2-5 minutes for the first time with the speed of 100-1000 turns/min for this, is stirred evenly；
Stir for the second time after water and water-reducing agent is added in agitator tank again, is somebody's turn to do second of stirring with 500-2000 turns/min's Speed stirs 3-8 minutes, the mixture stirred evenly；
Mixture is placed in mold, press, compression moulding are used；
Shaped article is conserved 6-8 days；
Last sanding and polishing, obtains finished product.
The mixing speed of the first time stirring is less than the mixing speed of second of stirring.
The present invention can be used for indoor or outdoor Floor Covering can discharge anion, have during usage Restraining and sterilizing bacteria, dedusting deodorization, the function improve body immunity, improve cardiac function, neutralizing positive charge：Can with floated in air Smog, dust and impurity combine, increase its specific gravity, make its sedimentation, neutralize the spoke of the generations such as electrostatic, electric wave, computer, TV It penetrates, achievees the effect that fresh air, reduces radiation.
Detailed description of the invention
Attached drawing 1 is the sectional view of plate prepared by the present invention.
Specific embodiment
To further understand the features of the present invention, technological means and specific purposes achieved, function, below with reference to Present invention is further described in detail for specific embodiment.
Embodiment one
A kind of negative ion far-infrared inorganic artificial stone slab, is made of the component of following parts by weight：It 14 parts of portland cement, forges 7 parts of kaolin of burning, 70 parts of calcium carbonate sand, 5 parts of mountain flour, 15 parts of water, 6 parts of water-reducing agent, 2 parts of anion mineral powder, magnesia pigment 6 Part.
When specific preparation, first by calcined kaolin, portland cement, mountain flour, calcium carbonate sand, anion mineral powder, oxidation Magnesium pigment, which is placed in agitator tank, carries out first time stirring, and stirring is stirred 5 minutes for the first time with the speed of 300 turns/min for this, stirring Uniformly.
Second of stirring is carried out after water and water-reducing agent is added in agitator tank again, is somebody's turn to do second of stirring with 1000 turns/min's Speed stirs 7 minutes, the mixture stirred evenly
Mixture is placed in mold, using press, compression moulding molds corresponding stone slab, as needed, it is plastic go out Different shapes.
Shaped article is conserved 8 days；
Last sanding and polishing, obtains finished product.
Embodiment two
A kind of negative ion far-infrared inorganic artificial stone slab, the stone slab are made of following component in parts by weight： 20 parts of portland cement, 5 parts of calcined kaolin, 60 parts of quartz sand, 3 parts of mountain flour, 10 parts of water, 4 parts of water-reducing agent, anion mineral powder 1 part, 3 parts of magnesia pigment.
When specific preparation, first by calcined kaolin, portland cement, mountain flour, quartz sand, anion mineral powder, magnesia Pigment, which is placed in agitator tank, carries out first time stirring, and stirring is stirred 4 minutes for the first time with the speed of 500 turns/min for this, and stirring is equal It is even.
Second of stirring is carried out after water and water-reducing agent is added in agitator tank again, is somebody's turn to do second of stirring with 1500 turns/min's Speed stirs 5 minutes, the mixture stirred evenly
Mixture is placed in mold, using press, compression moulding molds corresponding stone slab, as needed, it is plastic go out Different shapes.
Shaped article is conserved 7 days；
Last sanding and polishing, obtains finished product.
Embodiment three
A kind of negative ion far-infrared inorganic artificial stone slab, the stone slab are made of following component in parts by weight： 25 parts of composite Portland cement, 1 part of calcined kaolin, 50 parts of quartz sand, 1 part of mountain flour, 6 parts of water, 2 parts of water-reducing agent, anion mine 2 parts of object powder, 0.1 part of magnesia pigment.
When specific preparation, first by calcined kaolin, composite Portland cement, mountain flour, quartz sand, anion mineral powder, oxygen Change magnesium pigment and be placed in progress first time stirring in agitator tank, stirring is stirred 2 minutes for the first time with the speed of 1000 turns/min for this, is stirred It mixes uniformly.
Second of stirring is carried out after water and water-reducing agent is added in agitator tank again, is somebody's turn to do second of stirring with 2000 turns/min's Speed stirs 3 minutes, the mixture stirred evenly.
Mixture is placed in mold, press, compression moulding are used.
Shaped article is conserved 6 days；
Last sanding and polishing, obtains finished product.
In the present invention, by being added into anion complex mineral in artificial stone material, anion is contained to be formed The material of complex mineral material obtains slabstone using compression moulding.Anion complex mineral therein can discharge anion, When slabstone is more, it will be able to a large amount of anion is generated, which can effectively decompose the various harmful substances in air, Have the function of restraining and sterilizing bacteria, dedusting deodorization, improves body immunity, improve cardiac function, neutralize positive charge：Can in air Smog, dust and the impurity of floating combine, and increase its specific gravity, make its sedimentation, neutralize the generations such as electrostatic, electric wave, computer, TV Radiation achievees the effect that fresh air, reduces radiation.
It should be noted that these are only the preferred embodiment of the present invention, it is not intended to restrict the invention, although ginseng According to embodiment, invention is explained in detail, for those skilled in the art, still can be to aforementioned reality Technical solution documented by example is applied to modify or equivalent replacement of some of the technical features, but it is all in this hair Within bright spirit and principle, any modification, equivalent replacement, improvement and so on should be included in protection scope of the present invention Within.

Claims (6)

1. a kind of negative ion far-infrared inorganic artificial stone slab, which is characterized in that the stone slab by it is following according to parts by weight The component of meter is constituted：14-25 parts of cement, 1-7 parts of calcined kaolin, 50-70 parts of sand material, 1-5 parts of mountain flour, 6-15 parts of water, diminishing 2-6 parts of agent, 1-2 parts of anion mineral powder, 0.1-6 parts of magnesia pigment.
2. negative ion far-infrared inorganic artificial stone slab according to claim 1, which is characterized in that the sand material is quartz Sand or calcium carbonate sand.
3. negative ion far-infrared inorganic artificial stone slab according to claim 1, which is characterized in that the water-reducing agent is poly- Carboxylic acid water reducer.
4. negative ion far-infrared inorganic artificial stone slab according to claim 1, which is characterized in that the cement is silicic acid Salt cement or composite Portland cement.
5. a kind of preparation method of negative ion far-infrared inorganic artificial stone slab according to any one of claims 1-5, Include the following steps：
First by calcined kaolin, cement, mountain flour, sand material, anion mineral powder, magnesia pigment, which are placed in agitator tank, carries out first Secondary stirring, stirring is stirred 2-5 minutes for the first time with the speed of 100-1000 turns/min for this, is stirred evenly；
Stir for the second time after water and water-reducing agent is added in agitator tank again, is somebody's turn to do second of stirring with 500-2000 turns/min's Speed stirs 3-8 minutes, the mixture stirred evenly；
Mixture is placed in mold, press, compression moulding are used；
Shaped article is conserved 6-8 days；
Last sanding and polishing, obtains finished product.
6. the preparation method of negative ion far-infrared inorganic artificial stone slab according to claim 5, which is characterized in that described The mixing speed of stirring is less than the mixing speed of second of stirring for the first time.
CN201810844876.2A 2018-07-27 2018-07-27 A kind of negative ion far-infrared inorganic artificial stone slab and preparation method thereof Pending CN108863234A (en)