CN110498637A - A kind of anion flexible sheet material and its manufacturing method - Google Patents
A kind of anion flexible sheet material and its manufacturing method Download PDFInfo
- Publication number
- CN110498637A CN110498637A CN201910914760.6A CN201910914760A CN110498637A CN 110498637 A CN110498637 A CN 110498637A CN 201910914760 A CN201910914760 A CN 201910914760A CN 110498637 A CN110498637 A CN 110498637A
- Authority
- CN
- China
- Prior art keywords
- anion
- sheet material
- flexible sheet
- layer
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to decorative materials technologies, disclose a kind of anion flexible sheet material, and anion layer by flexible sheet material body layer and thereon is constituted.Flexible sheet material body layer includes the following components of mass percent: acrylic emulsion 7-30%；Inorganic powder 20-60%；Quartz sand 20-70%；Pigment 0-3%；Water-retaining agent 0-2%；Water 0-20%.Anion layer includes the following components of mass percent: negative ion powder 3-15%；Acrylic emulsion 7-30%；Inorganic powder 20-60%；Quartz sand 20-70%；Pigment 0-3%；Water-retaining agent 0-2%；Water 0-20%.Flexible sheet material of the invention can not only promote the concentration of room air anion, avoid generating ozone, cation or electrostatic, more safety and environmental protection；And it can continue largely to generate negative aeroion for a long time, and anion attenuation rate is low, effectively in conjunction with the smog, dust and impurity that float in air, makes its sedimentation, the radiation for neutralizing the generations such as electrostatic, electric wave, computer, TV achievees the effect that fresh air, reduces radiation.
Description
Technical field
The present invention relates to decorative materials technology, specifically a kind of anion flexible sheet material and its manufacturing method.
Background technique
Currently, interior, which is easy to produce, generates the harmful substances such as ozone, cation, electrostatic, dust and radiation, to the body of people
Body health has certain harm.
Flexible sheet material combines the advantages of coating and stone material, has slackened the disadvantage of construction, while because of its distinctive flexibility,
Embody the protrusion bright spot " with object figuration ", extreme enrichment material selection and decorated style.Although existing flexible sheet material has
The characteristics of safety and environmental protection, but do not have the function of harmful substance in active decontamination chamber.Therefore, it is necessary to develop a kind of anion
Flexible sheet material.
Summary of the invention
In view of the above technical problems, the present invention discloses a kind of anion flexible sheet material and its manufacturing method.
The present invention to achieve the above object, takes following technical scheme to be achieved:
A kind of anion flexible sheet material, anion layer by flexible sheet material body layer and thereon are constituted；
The flexible sheet material body layer includes the following components of mass percent:
Acrylic emulsion 7-30%；
Inorganic powder 20-60%；
Quartz sand 20-70%；
Pigment 0-3%；
Water-retaining agent 0-2%；
Water 0-20%；
The anion layer includes the following components of mass percent:
Negative ion powder 3-15%；
Acrylic emulsion 7-30%；
Inorganic powder 20-60%；
Quartz sand 20-70%；
Pigment 0-3%；
Water-retaining agent 0-2%；
Water 0-20%.
Preferably, the negative ion powder is the mixture of tourmaline powder and rare earth.
Preferably, the inorganic powder is one of marble powder, wollastonite powder, flyash, ground granulated blast furnace slag or combination.
Another object of the present invention is to disclose a kind of preparation method of above-mentioned anion flexible sheet material, including following step
It is rapid:
(1) by anion layer be formulated in each component be uniformly mixed, formed anion layer slurry；Anion layer slurry is sprayed
On silica gel mould surface, coating thickness 0.5-5mm；
(2) by spray anion layer slurry silica gel mould at 80-170 DEG C heat drying, formed anion layer；
(3) each component in flexible sheet material ontology layer formula is uniformly mixed, forms bulk slurry；Anion after the drying
Bulk slurry, coating thickness 1-8mm are coated on layer；
(4) the silica gel mould heat drying solidification demoulding at 80-170 DEG C that will coat bulk slurry, forms flexible sheet material
Body layer.
Preferably, several layers net is placed between the anion layer and body layer of the flexible sheet material or centre of body layer
Ge Bu.
Compared with prior art, beneficial effects of the present invention are as follows:
Anion flexible sheet material of the invention can not only promote the concentration of room air anion, avoid generate ozone,
Cation or electrostatic, more safety and environmental protection；And can continue largely to generate negative aeroion for a long time, and anion attenuation rate is low,
Effectively in conjunction with the smog, dust and impurity that float in air, increase its specific gravity, make its sedimentation, neutralize electrostatic, electric wave, computer,
The radiation of the generations such as TV achievees the effect that fresh air, reduces radiation.
Specific embodiment
The present invention will be further described with reference to the examples below, but it should be recognized that embodiment is not to this hair
Bright claimed range is construed as limiting.
Embodiment 1
A kind of anion flexible sheet material, anion layer by flexible sheet material body layer and thereon are constituted.
Wherein, flexible sheet material body layer includes the following components of mass percent: acrylic emulsion 7-30%；Inorganic powder
20-60%；Quartz sand 20-70%；Pigment 0-3%；Water-retaining agent 0-2%；Water 0-20%.
Anion layer includes the following components of mass percent: negative ion powder 3-15%；Acrylic emulsion 7-30%；It is inorganic
Powder 20-60%；Quartz sand 20-70%；Pigment 0-3%；Water-retaining agent 0-2%；Water 0-20%.
Wherein, negative ion powder is the mixture of tourmaline powder and rare earth.Inorganic powder be marble powder, wollastonite powder, flyash,
One of ground granulated blast furnace slag or combination.
The preparation method of above-mentioned anion flexible sheet material, comprising the following steps:
(1) by anion layer be formulated in each component be uniformly mixed, formed anion layer slurry；Anion layer slurry is sprayed
On silica gel mould surface, coating thickness 0.5-5mm；
(2) by spray anion layer slurry silica gel mould at 80-170 DEG C heat drying, formed anion layer；
(3) each component in flexible sheet material ontology layer formula is uniformly mixed, forms bulk slurry；Anion after the drying
Bulk slurry, coating thickness 1-8mm are coated on layer；
(4) the silica gel mould heat drying solidification demoulding at 80-170 DEG C that will coat bulk slurry, forms flexible sheet material
Body layer.
Between the anion layer and body layer of flexible sheet material or the intermediate of body layer places several layers grid cloth.
Embodiment 2
A kind of anion flexible sheet material, anion layer by flexible sheet material body layer and thereon are constituted.
Wherein, flexible sheet material body layer includes the following components of mass percent: acrylic emulsion 12%；Flyash
26%；Quartz sand 50%；Iron oxide red 0.3%；Hydroxymethyl cellulose 0.1%；Water 11.6%.
Anion layer includes the following components of mass percent: the ceramics of the prosperous certain herbaceous plants with big flowers macromolecule new material Co., Ltd in Kunshan are used
Negative ion powder 3%；Acrylic emulsion 12%；Flyash 26%；Quartz sand 50%；Iron oxide red 0.3%；Hydroxymethyl cellulose
0.1%；Water 8.6%.
The preparation method of above-mentioned anion Flexible decorative sheet, comprising the following steps:
(1) by anion layer be formulated in each component be uniformly mixed, formed anion slurry；Anion slurry is sprayed on silicon
Sealing rubber die surface, coating thickness 1.5mm；
(2) by spray anion slurry silica gel mould at 80-170 DEG C heat drying, formed anion layer；
(3) each component in flexible sheet material ontology layer formula is uniformly mixed, forms bulk slurry；Anion after the drying
Bulk slurry, coating thickness 2mm are coated on layer；
(4) the silica gel mould heat drying solidification demoulding at 80-170 DEG C that will coat bulk slurry, forms anion
Flexible sheet material.
Embodiment 3
A kind of anion flexible sheet material, anion layer by flexible sheet material body layer and thereon are constituted.
Wherein, flexible sheet material body layer includes the following components of mass percent: acrylic emulsion 18%；Marble powder
30%；Quartz sand 42%；Iron oxide yellow 0.2%；Hydroxymethyl cellulose 0.1%；Water 9.7%.
Anion layer includes the following components of mass percent: the anion agent of Dongguan City Chun Liang process materials Co., Ltd
8%；Acrylic emulsion 18%；Marble powder 26%；Quartz sand 42%；Iron oxide yellow 0.2%；Hydroxymethyl cellulose 0.1%；Water
5.7%.
The preparation method of the Flexible decorative sheet of above-mentioned anion, comprising the following steps:
(1) by anion layer be formulated in each component be uniformly mixed, formed anion slurry；Anion slurry is sprayed on silicon
Sealing rubber die surface, coating thickness 1mm；
(2) by spray anion slurry silica gel mould at 80-170 DEG C heat drying, formed anion layer；
(3) glass fiber reticular cloth is placed after anion layer
(4) each component in flexible sheet material ontology layer formula is uniformly mixed, forms bulk slurry；This is perfused in grid cloth
Somaplasm material, grid cloth and slurry overall thickness are 2mm；
(5) the silica gel mould heat drying solidification demoulding at 80-170 DEG C again that will coat upper body slurry, forms soft
Property sheet body layer.
Embodiment 4
A kind of anion flexible sheet material, anion layer by flexible sheet material body layer and thereon are constituted.
Wherein, flexible sheet material body layer includes the following components of mass percent: acrylic emulsion 8%；Ground granulated blast furnace slag
30%；Quartz sand 42%；Iron oxide yellow 0.2%；Hydroxymethyl cellulose 0.1%；Water 9.7%.
Anion layer includes the following components of mass percent: Dongguan City Chun Liang process materials Co., Ltd negative ion powder
10%；Acrylic emulsion 8%；Ground granulated blast furnace slag 25%；Quartz sand 42%；Iron oxide yellow 0.2%；Hydroxymethyl cellulose 0.1%；
Water 16.7%.
The preparation method of the Flexible decorative sheet of above-mentioned anion, comprising the following steps:
(1) by anion layer be formulated in each component be uniformly mixed, formed anion slurry；Anion slurry is sprayed on silicon
Sealing rubber die surface, coating thickness 1.5mm；
(2) by spray anion slurry silica gel mould at 80-170 DEG C heat drying, formed anion layer；
(3) each component in flexible sheet material ontology layer formula is uniformly mixed, forms bulk slurry；It is applied after anion layer
Bulk slurry, with a thickness of 2mm；
(4) grid cloth is placed on bulk slurry；
(5) slurry is struck off, grid cloth intermediate gaps is made to fill up slurry
(6) the heat drying solidification demoulding at 80-170 DEG C again, forms the flexible sheet material of anion.
The detection of anion flexible sheet material made from embodiment 2-4 is as shown in the table:
As can be seen from the above table, anion flexible sheet material of the invention can not only promote the dense of room air anion
Degree avoids generating ozone, cation or electrostatic, more safety and environmental protection；And can continue largely to generate negative aeroion for a long time, and
Anion attenuation rate is low, effectively in conjunction with the smog, dust and impurity that float in air, increases its specific gravity, makes its sedimentation, neutralizes
The radiation of the generations such as electrostatic, electric wave, computer, TV achievees the effect that fresh air, reduces radiation.
It is provided for the embodiments of the invention technical solution above to be described in detail, specific case used herein
The principle and embodiment of the embodiment of the present invention are expounded, the explanation of above embodiments is only applicable to help to understand this
The principle of inventive embodiments；At the same time, for those skilled in the art, according to an embodiment of the present invention, in specific embodiment party
There will be changes in formula and application range, in conclusion the contents of this specification are not to be construed as limiting the invention.
Claims (5)
1. a kind of anion flexible sheet material, which is characterized in that anion layer by flexible sheet material body layer and thereon is constituted；
The flexible sheet material body layer includes the following components of mass percent:
Acrylic emulsion 7-30%；
Inorganic powder 20-60%；
Quartz sand 20-70%；
Pigment 0-3%；
Water-retaining agent 0-2%；
Water 0-20%；
The anion layer includes the following components of mass percent:
Negative ion powder 3-15%；
Acrylic emulsion 7-30%；
Inorganic powder 20-60%；
Quartz sand 20-70%；
Pigment 0-3%；
Water-retaining agent 0-2%；
Water 0-20%.
2. a kind of anion flexible sheet material according to claim 1, which is characterized in that the negative ion powder is tourmaline powder
With the mixture of rare earth.
3. a kind of anion flexible sheet material according to claim 1, which is characterized in that the inorganic powder be marble powder,
One of wollastonite powder, flyash, ground granulated blast furnace slag or combination.
4. the preparation method of anion flexible sheet material as described in claim any one of 1-3, which is characterized in that including following step
It is rapid:
(1) by anion layer be formulated in each component be uniformly mixed, formed anion layer slurry；Anion layer slurry is sprayed on silicon
Sealing rubber die surface, coating thickness 0.5-5mm；
(2) by spray anion layer slurry silica gel mould at 80-170 DEG C heat drying, formed anion layer；
(3) each component in flexible sheet material ontology layer formula is uniformly mixed, forms bulk slurry；On anion layer after the drying
Coat bulk slurry, coating thickness 1-8mm；
(4) the silica gel mould heat drying solidification demoulding at 80-170 DEG C that will coat bulk slurry, forms flexible sheet material ontology
Layer.
5. the preparation method of anion flexible sheet material according to claim 4, which is characterized in that the flexible sheet material bear from
Between sublayer and body layer or the intermediate of body layer places several layers grid cloth.