CN106517890A - Production method of mechanical fitting - Google Patents
Production method of mechanical fitting Download PDFInfo
- Publication number
- CN106517890A CN106517890A CN201611059235.3A CN201611059235A CN106517890A CN 106517890 A CN106517890 A CN 106517890A CN 201611059235 A CN201611059235 A CN 201611059235A CN 106517890 A CN106517890 A CN 106517890A
- Authority
- CN
- China
- Prior art keywords
- mechanical fitting
- die
- granularity
- aggregate
- sizing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to the technical field of mechanical fittings, and concretely relates to a production method of a mechanical fitting. The method comprises the following steps: 1, uniformly mixing aggregates, a rubber compound and a promoter according to a formula ratio, and filling a die with the above obtained mixture; and 2, placing the filled die on a vibration table, carrying out vibration compaction for 50-80 min, curing the compacted mixture at 50-70 DEG C for 50-70 h, and carrying out die stripping to obtain a mechanical fitting blank. The method is used for solving the problem of certain defects existing in most of present mechanical fittings made of iron and steel.
Description
Technical field
The invention belongs to mechanical fitting technical field, specifically, is a kind of mechanical fitting preparation method.
Background technology
In prior art, various machining tools, testing equipment are formed with metal material processings such as cast iron, steel mostly
's.With the raising to spare parts processing machinery required precision, the running speed for processing machine tool is also greatly improved, so, processed
Violent vibrations will be produced in journey.But, metal material is but because itself cuts down the indifferent of vibrations, it is impossible to effectively inhale
The vibrations produced in receiving machine tool operation process, the thermal coefficient of expansion for adding metal material are big so that the installation and debugging of equipment
Journey becomes sufficiently complex, and the machining accuracy of accessory also therefore suffers from greatly restriction.In addition, metal machinery accessory is processed
Also there is the deficiencies such as big, the pollution environment of energy-output ratio in journey.
At present, although have multiple technologies perhaps produce stonite or artificial marble materials, but because of intensity, hard
The physical indexs such as degree are unable to reach the performance requirement of mechanical fitting, and can only serve as ornament materials.
The content of the invention
The present invention seeks to a kind of mechanical fitting preparation method has been aimed to provide, for solving current most of mechanical fittings
Processed by iron, steel and there is certain defect.
To realize above-mentioned technical purpose, the technical solution used in the present invention is as follows：
A kind of mechanical fitting preparation method, comprises the following steps：Step one：According to formula rate by aggregate, sizing material, promotion
Agent is well mixed and die-filling；Step 2：Mould after will be die-filling is placed on a vibration table, vibratory compaction 50-80 minutes；50-70
50-70 hours are conserved at DEG C, the demoulding obtains final product mechanical fitting blank.
Further limit, the formula rate is made up of the raw material of following percentage by weight：Aggregate 60-70%, sizing material 8-
30%th, accelerator 1-6%.
Further limit, the aggregate is made up of the natural granite or marble particle of following particle size range：Granularity is
The particle of 30mm：65%；Particle of the granularity for 9mm：30%；Stone flour of the granularity for 0.6mm：30%.
Further limit, the sizing material is epoxy resin or acrylic resin.
Further limit, the accelerator is the talcum powder that granularity is 0.6mm, natural granite powder or natural marble
Powder.
Beneficial effects of the present invention are that vibration damping is stronger, the step of reduce rigging up and debugging and the time；Utilizing
Optical sensor equipment faster can must obtain preferable image when detecting；Fabulous stability is provided for fast browsing；Reduce
The vibrations produced during High-speed machining, so as to improve the machining accuracy of workpiece, low cost, can save second finishing and
Machining cost；The consumption of the structural material of costliness can accordingly be reduced.Heat-resist, the coefficient of expansion is little compared with metal fittings；It is heat-resisting
Gradient is little.
Specific embodiment
In order that those skilled in the art may be better understood the present invention, with reference to embodiment to the technology of the present invention
Scheme is further illustrated.
A kind of mechanical fitting preparation method, comprises the following steps：Step one：According to formula rate by aggregate, sizing material, promotion
Agent is well mixed and die-filling；Step 2：Mould after will be die-filling is placed on a vibration table, vibratory compaction 50-80 minutes；50-70
50-70 hours are conserved at DEG C, the demoulding obtains final product mechanical fitting blank.
Optimization formula ratio is made up of the raw material of following percentage by weight：Aggregate 60-70%, sizing material 8-30%, accelerator
1-6%.In fact, other percentages can be selected as the case may be.
It is preferred that aggregate is made up of the natural granite or marble particle of following particle size range：Particle of the granularity for 30mm：
65%；Particle of the granularity for 9mm：30%；Stone flour of the granularity for 0.6mm：30%.In fact, can consider as the case may be.
It is preferred that sizing material is epoxy resin or acrylic resin.In fact, can select as the case may be.
Preferred accelerators are the talcum powder that granularity is 0.6mm, natural granite powder or natural marble powder.In fact, can
Select as the case may be.
Embodiment 1
A kind of mechanical fitting preparation method, comprises the following steps：Step one：According to formula rate by aggregate, sizing material, promotion
Agent is well mixed and die-filling；Step 2：Mould after will be die-filling is placed on a vibration table, vibratory compaction 50 minutes；Support at 50 DEG C
Shield 50 hours, the demoulding obtains final product mechanical fitting blank, wherein aggregate 60%, sizing material 8%, accelerator 1%.
Embodiment 2
A kind of mechanical fitting preparation method, comprises the following steps：Step one：According to formula rate by aggregate, sizing material, promotion
Agent is well mixed and die-filling；Step 2：Mould after will be die-filling is placed on a vibration table, vibratory compaction 80 minutes；Support at 70 DEG C
Shield 70 hours, the demoulding obtains final product mechanical fitting blank, wherein wherein aggregate 70%, sizing material 30%, accelerator 6%.
Interest-bearing accessory vibration damping in the present invention is stronger, and low cost is heat-resist, and the coefficient of expansion is little compared with metal fittings；
Heat-Resistant Gradient is little.
Above a kind of mechanical fitting preparation method that the present invention is provided is described in detail.The explanation of specific embodiment
It is only intended to help and understands the method for the present invention and its core concept.It should be pointed out that for the ordinary skill people of the art
Member for, under the premise without departing from the principles of the invention, some improvement and modification can also be carried out to the present invention, these improve and
Modification is also fallen in the protection domain of the claims in the present invention.
Claims (5)
1. a kind of mechanical fitting preparation method, it is characterised in that comprise the following steps：Step one：According to formula rate by aggregate,
Sizing material, accelerator are well mixed and die-filling；Step 2：Mould after will be die-filling is placed on a vibration table, vibratory compaction 50-80 point
Clock；50-70 hours are conserved at 50-70 DEG C, the demoulding obtains final product mechanical fitting blank.
2. a kind of mechanical fitting preparation method according to claim 1, it is characterised in that the formula rate is by following heavy
The raw material of amount percentage is made：Aggregate 60-70%, sizing material 8-30%, accelerator 1-6%.
3. a kind of mechanical fitting preparation method according to claim 2, it is characterised in that the aggregate is by following granularity model
The natural granite for enclosing or marble particle composition：Particle of the granularity for 30mm：65%；Particle of the granularity for 9mm：30%；Grain
Spend the stone flour for 0.6mm：30%.
4. a kind of mechanical fitting preparation method according to claim 3, it is characterised in that the sizing material be epoxy resin or
Acrylic resin.
5. a kind of mechanical fitting preparation method according to claim 4, it is characterised in that the accelerator for granularity is
The talcum powder of 0.6mm, natural granite powder or natural marble powder.