CN106077424A - A kind of new instrument casting resin sand - Google Patents
A kind of new instrument casting resin sand Download PDFInfo
- Publication number
- CN106077424A CN106077424A CN201610608898.XA CN201610608898A CN106077424A CN 106077424 A CN106077424 A CN 106077424A CN 201610608898 A CN201610608898 A CN 201610608898A CN 106077424 A CN106077424 A CN 106077424A
- Authority
- CN
- China
- Prior art keywords
- parts
- sand
- phenolic resin
- content
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of new instrument casting resin sand, it includes the raw material of following parts by weight: 100 parts of reclaimed sand material, thermoplastic phenolic resin 1 ~ 3 part, 0.2 ~ 1 part of firming agent, coupling agent 0.1 ~ 0.3 part, alkali-free glass fibre 1 ~ 3 part, modified add auxiliary agent 10 ~ 20 parts;The dissociate content of aldehyde of described thermoplastic phenolic resin is 0.1%, and the content of free phenol is 0.2%;The described modified auxiliary agent that adds is one or more in Gypsum Fibrosum powder, Kaolin, meerschaum, pitchstone, hydroxylapatite powder.A kind of new instrument casting resin sand sand mold intensity that the present invention prepares is high, dimensional discrepancy is little, collapsibility good, energy resource consumption is few, and the feature of environmental protection is excellent simultaneously, can be used for the production casting of various molding sand instrument foundry goods, and the surface quality of foundry goods and dimensional accuracy are high.
Description
Technical field
The present invention relates to a kind of moulding sand for casting technical field, be specifically related to the new instrument casting that a kind of casting character is excellent
Molding resins sand material.
Background technology
Molding sand effect in Foundry Production is particularly important, and the casting wasted product caused because of the poor quality of molding sand accounts for casting
The 30~50% of the total rejection number of part.Foundry Production generally requirement to molding sand is: have higher intensity and heat stability, to hold
Acted on by various external force and high temperature;Good mobility, i.e. molding sand are mutually moved between sand grains under external force or action of gravity own
Dynamic ability;Certain plasticity, i.e. molding sand deform under external force, the shape that can keep being given after external force is removed
Ability;Preferably breathability, i.e. molding sand hole are through the ability of gas;High knockability, also known as collapsibility, i.e. at casting solidification
Whether rear molding sand is easily destroyed, if the performance easily removed from foundry goods.
Casting sand used is required higher by instrument and equipment, existing molding sand casting apparatus warp in foundry production
Various different casting flaw often can occur, such as crackle, pore, sand holes, shrinkage cavity etc., have impact on the usability of molding sand casting apparatus
Can, and the generation of these defects and the caking property between foundry goods and casting sand, detachment are relevant, existing casting sand uses
Poor-performing, easily produces bonding with foundry goods, causes foundry goods to be not easily stripped, and cast breathability, plasticity and mobility not
Good, thus cause cast(ing) surface coarse so that Mechanical processing of casting percent defective is higher.
Summary of the invention
Not enough for prior art, the invention provides the new instrument casting resin sand material that a kind of casting character is excellent
Material.
The present invention solves the technical scheme that above-mentioned technical problem uses: a kind of new instrument casting resin sand, including with
The raw material of lower parts by weight: 100 parts of reclaimed sand material, thermoplastic phenolic resin 1 ~ 3 part, 0.2 ~ 1 part of firming agent, coupling agent 0.1 ~
0.3 part, alkali-free glass fibre 1 ~ 3 part, modified add auxiliary agent 10 ~ 20 parts;
The dissociate content of aldehyde of described thermoplastic phenolic resin is 0.1%, and the content of free phenol is 0.2%;
The described modified auxiliary agent that adds is the one in Gypsum Fibrosum powder, Kaolin, meerschaum, pitchstone, hydroxylapatite powder or several
Kind.
Further, described a kind of new instrument casting resin sand, including the raw material of following parts by weight: reclaimed sand material
100 parts, thermoplastic phenolic resin 2 parts, 0.5 part of firming agent, coupling agent 0.2 part, alkali-free glass fibre 2 parts, modified add auxiliary agent
15 parts;The dissociate content of aldehyde of described thermoplastic phenolic resin is 0.1%, and the content of free phenol is 0.2%;Described modified interpolation
Auxiliary agent is Gypsum Fibrosum powder, Kaolin pitchstone and hydroxylapatite powder.
Further, described a kind of new instrument casting resin sand, including the raw material of following parts by weight: reclaimed sand material
100 parts, thermoplastic phenolic resin 1 part, 0.2 part of firming agent, coupling agent 0.1 part, alkali-free glass fibre 1 part, modified add auxiliary agent
10 parts;The dissociate content of aldehyde of described thermoplastic phenolic resin is 0.1%, and the content of free phenol is 0.2%;Described modified interpolation
Auxiliary agent is Gypsum Fibrosum powder and pitchstone.
Further, described a kind of new instrument casting resin sand, including the raw material of following parts by weight: reclaimed sand material
100 parts, thermoplastic phenolic resin 3 parts, 1 part of firming agent, coupling agent 0.3 part, alkali-free glass fibre 3 parts, modified add auxiliary agent 20
Part;The dissociate content of aldehyde of described thermoplastic phenolic resin is 0.1%, and the content of free phenol is 0.2%;Described modified interpolation helps
Agent is Gypsum Fibrosum powder, Kaolin, meerschaum, pitchstone and hydroxylapatite powder.
Compared with prior art, what the present invention possessed has the beneficial effect that
A kind of new instrument casting resin sand sand mold intensity that the present invention prepares is high, dimensional discrepancy is little, collapsibility good, energy resource consumption
Few, use the reclaimed sand material feature of environmental protection excellent, concurrently facilitate the cost reducing resin sand;The resin sand of the present invention can be used for various
The production casting of molding sand instrument foundry goods, the surface quality of foundry goods and dimensional accuracy are high.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described further.
Embodiment 1: a kind of new instrument casting resin sand, including the raw material of following parts by weight: 100 parts of reclaimed sand material,
Thermoplastic phenolic resin 2 parts, 0.5 part of firming agent, coupling agent 0.2 part, alkali-free glass fibre 2 parts, modified interpolation auxiliary agent 15 parts;Institute
The dissociate content of aldehyde of the thermoplastic phenolic resin stated is 0.1%, and the content of free phenol is 0.2%;The described modified auxiliary agent that adds is
Gypsum Fibrosum powder, Kaolin pitchstone and hydroxylapatite powder.
Embodiment 2: a kind of new instrument casting resin sand, including the raw material of following parts by weight: 100 parts of reclaimed sand material,
Thermoplastic phenolic resin 1 part, 0.2 part of firming agent, coupling agent 0.1 part, alkali-free glass fibre 1 part, modified interpolation auxiliary agent 10 parts;Institute
The dissociate content of aldehyde of the thermoplastic phenolic resin stated is 0.1%, and the content of free phenol is 0.2%;The described modified auxiliary agent that adds is
Gypsum Fibrosum powder and pitchstone.
Embodiment 3: a kind of new instrument casting resin sand, including the raw material of following parts by weight: 100 parts of reclaimed sand material,
Thermoplastic phenolic resin 3 parts, 1 part of firming agent, coupling agent 0.3 part, alkali-free glass fibre 3 parts, modified interpolation auxiliary agent 20 parts;Described
The dissociate content of aldehyde of thermoplastic phenolic resin be 0.1%, the content of free phenol is 0.2%;The described modified auxiliary agent that adds is stone
Cream powder, Kaolin, meerschaum, pitchstone and hydroxylapatite powder.
Concrete, in use, be on the waiting list raw material by described parts by weight, by described reclaimed sand material, modified add auxiliary agent,
Firming agent, coupling agent, alkali-free glass fibre, thermoplastic phenolic resin are blended in being sequentially added into continuous muller, i.e. get Ben Fa
Bright resin sand.
The above is only the preferred embodiment of the present invention, it is noted that for the common skill of the art
For art personnel, under the premise without departing from the principles of the invention, it is also possible to make some improvement and modification, these improve and modify
Also should be regarded as protection scope of the present invention.
Claims (4)
1. a new instrument casting resin sand, it is characterised in that include the raw material of following parts by weight: 100 parts of reclaimed sand material,
Thermoplastic phenolic resin 1 ~ 3 part, coupling agent 0.1 ~ 0.3 part, alkali-free glass fibre 1 ~ 3 part, 0.2 ~ 1 part of firming agent, modified interpolation
Auxiliary agent 10 ~ 20 parts;
The dissociate content of aldehyde of described thermoplastic phenolic resin is 0.1%, and the content of free phenol is 0.2%;
The described modified auxiliary agent that adds is the one in Gypsum Fibrosum powder, Kaolin, meerschaum, pitchstone, hydroxylapatite powder or several
Kind.
A kind of new instrument casting resin sand the most according to claim 1, it is characterised in that include following parts by weight
Raw material: 100 parts of reclaimed sand material, thermoplastic phenolic resin 2 parts, coupling agent 0.2 part, alkali-free glass fibre 2 parts, 0.5 part of firming agent,
Modified interpolation auxiliary agent 15 parts;The dissociate content of aldehyde of described thermoplastic phenolic resin is 0.1%, and the content of free phenol is 0.2%;Institute
The modified auxiliary agent that adds stated is Gypsum Fibrosum powder, Kaolin pitchstone and hydroxylapatite powder.
A kind of new instrument casting resin sand the most according to claim 1, it is characterised in that include following parts by weight
Raw material: 100 parts of reclaimed sand material, thermoplastic phenolic resin 1 part, coupling agent 0.1 part, alkali-free glass fibre 1 part, 0.2 part of firming agent,
Modified interpolation auxiliary agent 10 parts;The dissociate content of aldehyde of described thermoplastic phenolic resin is 0.1%, and the content of free phenol is 0.2%;Institute
The modified auxiliary agent that adds stated is Gypsum Fibrosum powder and pitchstone.
A kind of new instrument casting resin sand the most according to claim 1, it is characterised in that include following parts by weight
Raw material: 100 parts of reclaimed sand material, thermoplastic phenolic resin 3 parts, coupling agent 0.3 part, alkali-free glass fibre 3 parts, 1 part of firming agent, change
Property add auxiliary agent 20 parts;The dissociate content of aldehyde of described thermoplastic phenolic resin is 0.1%, and the content of free phenol is 0.2%;Described
The modified auxiliary agent that adds be Gypsum Fibrosum powder, Kaolin, meerschaum, pitchstone and hydroxylapatite powder.