CN1693194A - 用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺 - Google Patents

用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺 Download PDF

Info

Publication number
CN1693194A
CN1693194A CNA2005102003240A CN200510200324A CN1693194A CN 1693194 A CN1693194 A CN 1693194A CN A2005102003240 A CNA2005102003240 A CN A2005102003240A CN 200510200324 A CN200510200324 A CN 200510200324A CN 1693194 A CN1693194 A CN 1693194A
Authority
CN
China
Prior art keywords
sodium
sulfite
carbon black
white carbon
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2005102003240A
Other languages
English (en)
Other versions
CN100545085C (zh
Inventor
卢元健
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Nanping Sanyuan Circulation Technology Co ltd
Win Jiaxen White Carbon Black Nanping Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2005102003240A priority Critical patent/CN100545085C/zh
Publication of CN1693194A publication Critical patent/CN1693194A/zh
Priority to EP06742113A priority patent/EP1888461A1/en
Priority to JP2008515032A priority patent/JP2008542186A/ja
Priority to BRPI0611942-5A priority patent/BRPI0611942B1/pt
Priority to KR1020077028663A priority patent/KR20080016836A/ko
Priority to US11/916,663 priority patent/US20080199384A1/en
Priority to RU2008100098/15A priority patent/RU2008100098A/ru
Priority to PCT/CN2006/001227 priority patent/WO2006131065A1/en
Priority to IL186762A priority patent/IL186762A0/en
Application granted granted Critical
Publication of CN100545085C publication Critical patent/CN100545085C/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺，其特征在于将石英沙、硫酸钠和炭置于窑炉内反应，生成的固体和二氧化硫分别经下列步骤处理生成白炭黑、亚硫酸钠和亚硫酸氢钠：(1)生成白炭黑：将生成的固体溶解、沉淀过滤后加入硫酸，经洗涤、打浆、干燥得白炭黑；(2)生产亚硫酸钠：纯碱加入亚硫酸氢钠溶液中生成亚硫酸钠溶液，一部分浓缩干燥得亚硫酸钠；一部分与生成的二氧化硫反应后，生成亚硫酸氢钠溶液，回用生产亚硫酸钠；(3)生产亚硫酸氢钠：纯碱加入亚硫酸氢钠溶液中生成亚硫酸钠溶液，与生成的二氧化硫反应后，经结晶、干燥得亚硫酸氢钠。本发明的工艺流程简单、联产多种产品，生产成本低，具有较大的应用推广价值。

Description

用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺
技术领域
本发明涉及一种用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺。
技术背景
白炭黑又名轻质二氧化硅，是橡胶的良好补强剂；也用作润滑剂、绝缘材料及塑料制品、纸张、油漆、纺织品等的填充料或白色颜料。目前，国内外最常用的生产白炭黑的传统方法是沉淀法，该法需要消耗大量的纯碱和硫酸，成本较高。
发明内容
本发明的目的在于提供一种用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺，该工艺降低了生产白炭黑的成本。
本发明的用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺，其特征在于将石英沙、硫酸钠和炭混合后放入窑炉内进行反应，生成的硅酸钠固体和二氧化硫分别经下列步骤处理后生成白炭黑、亚硫酸钠和亚硫酸氢钠：(1)生成白炭黑：将生成的硅酸钠固体按100∶180～488的重量比加入水进行溶解，得到硅酸钠液体，经沉淀过滤后，硅酸钠液体与浓度为98％的硫酸按13～19∶1的体积比，于70～100℃下反应1～4h，反应后进行洗涤，将洗涤后的物料进行打浆，最后干燥出白炭黑；(2)生产亚硫酸钠：将纯碱按1∶1摩尔比加入到亚硫酸氢钠溶液中，生成亚硫酸钠溶液，一部分经浓缩干燥制出亚硫酸钠，一部分亚硫酸钠溶液与生成的二氧化硫按1∶1的摩尔比，于20～50℃下进行反应后，生成亚硫酸氢钠溶液，再与纯碱反应回用生产亚硫酸钠。(3)生产亚硫酸氢钠：将纯碱按1∶1摩尔比加入到亚硫酸氢钠溶液中，与生成的二氧化硫按1∶1的摩尔比，于20～50℃下进行反应后，生成过饱和亚硫酸氢钠溶液，经结晶、干燥制出亚硫酸氢钠产品。
本发明的理论基础是：
较之已有的技术，本发明的优点在于：一是在生产白炭黑同时，联产亚硫酸钠、亚硫酸氢钠等产品，在反应过程后硫酸钠可循环使用，这样就降低了生产成本回收；二是无废物排放；三利用全保温马蹄焰窑炉连续生产硫酸钠法水玻璃。
具体实施方式
本发明是这样实现的：将原料石英砂、硫酸钠和碳(已经粉碎)按照SiO2∶Na2SO4∶C＝100∶81.4∶6.5比例混合，连续投入马蹄形全保温窑炉，反应温度1420℃～1450℃，连续出料，物料经水淬、溶解得到3.5M、29Be′水玻璃液体。在5L的反应釜中加入底水2.5L，预加水玻璃0.075L，加温至86℃，在100分钟的时间内，同时均匀加入水玻璃溶液1.163L和硫酸0.072L，反应结束后，加入0.011L进行后酸后调整PH值到4.5。所得物料经洗涤干燥制得白炭黑348.1g(BET为185m2/g)，溶液通过浓缩干燥得到235.14g硫酸钠。
其中，在生成白炭黑的过程中，洗涤后的洗涤液经浓缩干燥制出可回收利用的硫酸钠。
生成亚硫酸钠：将纯碱按1∶1摩尔比加入到亚硫酸氢钠溶液中，生成亚硫酸钠溶液，一部分经浓缩干燥制出亚硫酸钠，一部分亚硫酸钠溶液与生成的二氧化硫按1∶1的摩尔比，于20～50℃下进行反应后，生成亚硫酸氢钠溶液，再与纯碱反应回用生产亚硫酸钠。
生产亚硫酸氢钠：将纯碱按1∶1摩尔比加入到亚硫酸氢钠溶液中，与生成的二氧化硫按1∶1的摩尔比，于20～50℃下进行反应后，生成过饱和亚硫酸氢钠溶液，经结晶、干燥制出亚硫酸氢钠产品。
本发明的工艺流程简单、生产成本低，具有较大的应用推广价值。

Claims (4)

1.一种用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺，其特征在于将石英沙、硫酸钠和炭混合后放入窑炉内进行反应，生成的硅酸钠固体和二氧化硫分别经下列步骤处理后生成白炭黑、亚硫酸钠和亚硫酸氢钠：
(1)生成白炭黑：将生成的硅酸钠固体按100∶180～488的重量比加入水进行溶解，得到硅酸钠液体，经沉淀过滤后，硅酸钠液体与浓度为98％的硫酸按13～19∶1的体积比，于70～100℃下反应1～4h，反应后进行洗涤，将洗涤后的物料进行打浆，最后干燥出白炭黑；
(2)生产亚硫酸钠：将纯碱按1∶1摩尔比加入到亚硫酸氢钠溶液中，生成亚硫酸钠溶液，一部分经浓缩干燥制出亚硫酸钠，一部分亚硫酸钠溶液与生成的二氧化硫按1∶1的摩尔比，于20～50℃下进行反应后，生成亚硫酸氢钠溶液，再与纯碱反应回用生产亚硫酸钠。
(3)生产亚硫酸氢钠：将纯碱按1∶1摩尔比加入到亚硫酸氢钠溶液中，与生成的二氧化硫按1∶1的摩尔比，于20～50℃下进行反应后，生成过饱和亚硫酸氢钠溶液，经结晶、干燥制出亚硫酸氢钠产品。
2.根据权利要求1所述的一种用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺，其特征在于所用的石英沙、硫酸钠和炭的重量配比为：118.3～147.9∶100∶4～12，所述的反应温度为1200℃～1500℃。
3.根据权利要求1所述的一种用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺，其特征在于所述的生成白炭黑的过程中，洗涤后的洗涤液经浓缩干燥制出可回收利用的硫酸钠。
4.根据权利要求1或2所述的一种用硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺，其特征在于所述的窑炉为全保温马蹄焰窑炉。
CNB2005102003240A 2005-06-10 2005-06-10 硫酸钠法生产白炭黑、亚硫酸钠和亚硫酸氢钠的工艺 Active CN100545085C (zh)