CN1635005A - 氯乙烯和醋酸乙烯共聚树脂的合成方法 - Google Patents
氯乙烯和醋酸乙烯共聚树脂的合成方法 Download PDFInfo
- Publication number
- CN1635005A CN1635005A CN 200310122147 CN200310122147A CN1635005A CN 1635005 A CN1635005 A CN 1635005A CN 200310122147 CN200310122147 CN 200310122147 CN 200310122147 A CN200310122147 A CN 200310122147A CN 1635005 A CN1635005 A CN 1635005A
- Authority
- CN
- China
- Prior art keywords
- vinyl acetate
- resin
- copolymer resins
- charging
- vinylchlorid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明氯乙烯和醋酸乙烯共聚树脂的合成方法，提供一种改善氯乙烯和醋酸乙烯共聚树脂的质量的合成方法。是通过在氯乙烯单体聚合反应过程中加入一定量的醋酸乙烯单体，加入一定量的pH值调节剂，即可得到一种比较理想的共聚树脂，本发明氯乙烯和醋酸乙烯共聚树脂的合成方法是这样实现的，首先，在聚合反应器中加入总重量为60～70％的无离子水，依次加入3～5％的醋酸乙烯单体，以及0.15～0.3％的pH调节剂。然后按聚合反应时间和树脂的颗粒形态依次加入一定量的引发剂和分散剂。其次，压入30～35％的氯乙烯单体，然后搅拌十分钟，升温至所需聚合温度，进行聚合反应控制，即可得到所需树脂。
Description
所属技术领域
本发明氯乙烯和醋酸乙烯共聚树脂的合成方法，涉及氯乙烯与另一种单体的二元共聚合反应，尤其涉及的是氯乙烯和醋酸乙烯两种单体的共聚合方法。
背景技术
聚氯乙烯材料是我国及世界最大宗塑料之一，由于它有很多优良的力学性能和化学性能。但是，在实际加工应用中也存在着一些显著的缺点。它在制作IC卡片和地板砖时，由于制品硬而脆，指使所做制品不够美观耐用。近年来，人们为了弥补聚氯乙烯这方面的不足，开始研究聚氯乙烯的共聚物，以达到对聚氯乙烯进行改性的目的，氯乙烯和醋酸乙烯共聚树脂在国内外都有企业生产过，但由于醋酸乙烯在共聚树脂的分布不够均匀，直接导致氯乙烯和醋酸乙烯共聚树脂的质量不是很稳定，影响了其的加工使用。
发明内容
本发明氯乙烯和醋酸乙烯共聚树脂的合成方法，提供一种改善氯乙烯和醋酸乙烯共聚树脂的质量的合成方法。是通过在氯乙烯单体聚合反应过程中加入一定量的醋酸乙烯单体，加入一定量的PH值调节剂，即可得到一种比较理想的共聚树脂，在一定程度上改善了共聚树脂的质量，使树脂的溶解性能和塑性得到改善，使其加工应用起来更方便。本发明氯乙烯和醋酸乙烯共聚树脂的合成方法是这样实现的，首先，在聚合反应器中加入总重量为60～70％的无离子水，依次加入3～5％的醋酸乙烯单体，以及0.15～0.3％的PH调节剂。然后按聚合反应时间和树脂的颗粒形态依次加入一定量的引发剂和分散剂。其次，压入30～35％的氯乙烯单体，然后搅拌十分钟，升温至所需聚合温度，进行聚合反应控制，即可得到所需树脂。
具体实施方式
本发明氯乙烯和醋酸乙烯共聚树脂的合成方法，提供一种改善氯乙烯和醋酸乙烯共聚树脂的质量的合成方法。是在氯乙烯单体聚合反应过程中加入一定量的醋酸乙烯单体，通过对PH值的控制，得到的一种比较理想的共聚树脂，改善了氯乙烯和醋酸乙烯共聚树脂的质量，克服了醋酸乙烯分子在共聚合大分子中的分布不均匀的情况，使树脂的溶解性能和塑性得到改善。其具体实施方式为：
实施例1：
在30立升的聚合釜中加入无离子水16升，氯乙烯和醋酸乙烯按4~6∶1的比例加入，0.15~0.3％的PH值调节剂，复合分散剂12克，复合引发剂9毫升，按规定的聚合温度升温控制，即可生产出所需的共聚树脂。按上述的配方生产的共聚树脂，吸油率在5~10％，表观密度在0.45~0.60g/ml颗粒在主要集中在80目至120目之间。醋酸乙烯的含量在9~11％之间。
实施例2：
在5立方米的聚合釜中加入无离子水2.8立方米，氯乙烯和醋酸乙烯按4~6∶1的比例加入，0.15~0.3％的PH值调节剂，复合引发剂0.95升，复合分散剂1.6千克，按规定的聚合温度升温控制，即可生产出所需要的共聚树脂。按上述的配方生产的共聚树脂，表观密度为0.47~0.53，吸油率为5~10％，醋酸乙烯的含量为9.49~10.86％。
实施例3：
在13.5立方米的聚合釜中加入无离子水7.1立方米，氯乙烯和醋酸乙烯4~6∶1加入，0.15~0.3％的PH值调节剂，复合引发剂2.55升，复合分散剂4千克，按规定的聚合温度升温，进行聚合控制，即可得到该树脂。所生产的树脂的表观密度为0.50~0.57，醋酸乙烯的含量在9~11％之间，白度85~95％之间。
Claims (2)
1、一种氯乙烯和醋酸乙烯共聚树脂的合成方法，其特征在于：在聚合反应器内加入总重量60～70％的无离子水，依次加入3～5％醋酸乙烯单体，以及0.15～0.3％的PH值调节剂。然后按所需的反应时间和树脂的颗粒形态加入一定比例的引发剂和分散剂。
2、根据权利要求1所述氯乙烯和醋酸乙烯共聚树脂的合成方法，其特征在于：在加入无离子水、醋酸乙烯单体、PH调节剂、引发剂和分散剂的聚合反应器中压入30～35％的氯乙烯单体，然后搅拌，升温至所需聚合温度，进行聚合反应控制。