CN1600578A - Artificial ornamental article made from jadestone or miniature landscape - Google Patents

Artificial ornamental article made from jadestone or miniature landscape Download PDF

Info

Publication number
CN1600578A
CN1600578A CN 200410070702 CN200410070702A CN1600578A CN 1600578 A CN1600578 A CN 1600578A CN 200410070702 CN200410070702 CN 200410070702 CN 200410070702 A CN200410070702 A CN 200410070702A CN 1600578 A CN1600578 A CN 1600578A
Authority
CN
China
Prior art keywords
mold
model
cured
glass fibre
shade
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200410070702
Other languages
Chinese (zh)
Inventor
李翠华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200410070702 priority Critical patent/CN1600578A/en
Publication of CN1600578A publication Critical patent/CN1600578A/en
Pending legal-status Critical Current

Abstract

A method for preparing synthetic jade decorations and potted flowers forms cubic red flower and green leaf by pouring and moulding synthetic jade materials prepared in advance and the method is not limited by space, specifications, colour, material, shape, etc.

Description

Artificial ornamental article made from jadestone or potted landscape
Technical field
The present invention relates to the making construction method of artificial ornamental article made from jadestone or potted landscape, belong to engraving, imitative emerald material, water the goods field of moulding.
Existing emerald goods are ring, Xu vessel used to hold grain at the imperial sacrifice, hand another name for Sichuan Province etc., and goods are frangible, can't change color, material, kind, traditional handicraft; Make big, superhuge stereo product, so goods are on sense organ, work with great care not as Counterfeit Item, color is soft and moist, imitated vestige.
The purpose of this invention is to provide the process for making of artificial ornamental article made from jadestone or potted landscape material and goods, goods obviously are better than existing goods, and the Counterfeit Item duration is short, and cost is low; Not being subjected to the restriction in space, kind, specification, color, classification, traditional handicraft, material, environmental protection, market, is to have material and the handicraft of viewing and admiring, collect, develop value.
1) simulation:
(1) system wooden mold: timber is sawed, cuts, carves, bondd, the model that joggle becomes to adhere to specification;
(2) system plaster cast: gypsum is added 801 glue, mix well, water and be filled in, after solidifying it is engraved as the model that adheres to specification than in big 0.5～10 centimeter sylphon of model by the mixing of 100: 40～70 ratio;
(3) system mud model: the model that foundry loam or rubber cement kneading model are become to adhere to specification;
(4) engraving: work with great care according to layout;
(5) polishing: use sand papering, from thick number to thin number, to the light cleaning;
(6) bonding: add talcum powder with 502 and add saw wood ash=100: 10～30: 10～30;
(7) play putty: add diluent with transparent resin and add curing agent and add required color=100: 10～30: 10～30: 10～30;
(8) polishing: with the sand polishing, from thick number to thin number, to the light cleaning;
(9) go up cured: the floor is cured or mould is cured or spray the table leather board sprays cured brush or be sprayed on the model, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
2) the three-dimensional soft or hard mould of system:
(1) fixed model: the position that model is narrow down, wide position stands on the tabula rasa up, adds talcum powder with 502 glue, by 100: 10～20 fixed ratio;
(3) system soft mode: add with silicon rubber and to solidify Ji, mix well, water and be filled on the model, up catch up with the mixing silicon rubber that grey cutter will down drop down from the model, till solidifying by 100: 5～20 ratio mixing;
(4) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(5) system gypsum mold: add curing agent with 801 glue, mix by 100: 40～70 ratio and mix well, be put on half of soft mold, extremely above till half 0,5～10 centimeters of soft mold;
(6) drying: dried in the shade 5～10 minutes;
(7) remove mould: the plaster mold over half 0,5～10 centimeters above soft mold removed;
(8) system hard mold 1: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on second half of the gypsum mold of having made, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
(9) drying: dried in the shade 10～30 minutes;
(10) remove mould: the gypsum mold that will make is all removed, and cleans up;
(11) go up cured: will plate cured or mould is cured or the table leather board sprays cured brush or be sprayed on half the soft mold of removing gypsum mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
(12) system hard mold 2: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on the soft mold of half of removing gypsum mold, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
(13) drying: dried in the shade 10～30 minutes;
(14) die sinking: the soft or hard mould is opened, taken out soft mold, soft mold is cut a mouth, take out the model of the inside;
(15) cut edge: the burr around the hard mold are cut off,
(16) polishing: corase grind machine, correct grinding are by hand, and be extremely smooth straight and even;
(17) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inwall of soft or hard mould, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
3) system plane soft or hard gypsum mold:
(1) system sylphon: vary in size according to model, make the sylphon of different size;
(2) system soft mold 1: silicon rubber is added curing agent, mix by 100: 5～20 ratio and mix well, water in the sylphon, to flooding soft mold till half;
(3) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(4) system hard mold 1: resin is added diluent add curing agent, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on half of soft mold, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed at fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
(5) drying: dried in the shade 10～30 minutes;
(6) system plaster mold 1: 801 glue are added land plaster, mix well, water and be filled on the thick glass fibre cloth, till flooding 0,5～10 centimeters of thick glass fibre cloth by the mixing of 100: 40～70 ratio;
(7) drying: dried in the shade 5～10 minutes;
(8) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on second half of soft or hard gypsum mold that brush makes; Dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
(9) system soft mold 2: silicon rubber is added curing agent, and by 100 ratios: 5～20 ratio is mixed and is mixed well, and waters in the sylphon, till flooding soft mold;
(10) drying: dried in the shade slow curing 2～24 hours 1～2 hour
(11) system hard mold 2: resin is added diluent add curing agent, ratio in 100: 10～30: 10～30: 10～30 is mixed and is mixed well, brush is on second half of the gypsum mold of having made, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
(13) drying: dried in the shade 10～30 minutes;
(14) system gypsum hard mold 2: 801 glue are added curing agent, mix well by 100: 40～70 ratio mixing, water and be filled in thick glass fibre cloth, till flooding 0,5～10 centimeters of thick glass fibre cloth;
(15) die sinking tool: the soft or hard gypsum mold is opened respectively, taken out the model of the inside;
(16) go up cured: it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor except that the position of mould, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
4) system plane soft mold:
(1) system box: according to the large and small difference of model, the ratio model of making different size is big 0.5 centimeter～10 centimeters sylphon;
(2) fixed model: model is placed on the tabula rasa, model bottom packing paper plate or fiberboard or plank or laminate, thickness determines what according to goods, goods fill up slab more, and goods fill up rich plate less, after fixing with 502 glue, again the sylphon of making is enclosed within on the model, fixes with 502 glue;
(3) system soft mold: silicon rubber is added curing agent, mix by 100: 5～20 ratio and mix well, water sylphon, till flooding 0.5～10 centimeter on model;
(4) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(5) die sinking tool: open box, remove tabula rasa, take out the model of the inside;
(6) go up cured: it is cured or mould is cured or it is cured to spray the spray of table leather board to brush the floor at the soft mold inwall, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly.
5) system gypsum mold:
(1) system sylphon: vary in size according to model, make big 0.5～20 centimeter sylphon of ratio model of a different size:
(2) fixed model; Model is placed on the tabula rasa, after fixing with 502 glue, again the sylphon of making is put on the model, fix with 502 glue again;
(3) system gypsum mold 1: add talcum powder with 801 glue, mix well, water in the sylphon, till flooding over half 0.5～10 centimeter of model by the mixing of 100: 40～70 ratio;
(4) drying: dried in the shade 5～10 minutes;
(5) remove mould: the gypsum mold that will make gypsum mold over half 0.5～10 centimeter is removed, and cleans up;
(6) go up cured: it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor except that the position of mould, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
(7) system gypsum mold 2: adding talcum powder with 801 glue, mix well in 100: 40～70 ratio mixing, water on second half model that is filled in the gypsum mold of having made, is last to flooding 0.5～10 centimeter on model;
(8) drying: dried in the shade 5～10 minutes;
(9) die sinking: gypsum mold is opened respectively, taken out the model of the inside;
(10) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inwall of gypsum mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times.
6) system gypsum hard mold:
(1) system sylphon: vary in size according to goods, make big 0.5～10 centimeter sylphon of ratio model of different size, fix with 502 glue;
(2) fixed model: model is placed on the tabula rasa, fixes, again sylphon is enclosed within on the model, fix with 502 glue with 502 glue;
(3) system gypsum mold: add land plaster with 801 glue, mix well, water sylphon, till flooding over half 0.5～10 centimeter of model by the mixing of 100: 40～70 ratio;
(4) drying: dried in the shade 5～10 minutes;
(5) remove mould: the gypsum mold that will make 0.5～10 centimeter gypsum mold over half has been carved, and cleans up;
(6) go up cured: will be except that the position of mould, it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor, dries in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
(7) system gypsum hard mold 1: resin is added the ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is being made on second half the model of gypsum mold, spread on two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth, again above-mentioned hybrid resin is brushed on thick glass fibre cloth, dried in the shade 10～30 minutes, again 801 glue are added land plaster, mix well in 100: 40～70 ratio mixing, sylphon is advanced in pouring, till flooding 0,5～10 centimeters on model;
(8) remove mould: the gypsum mold of second half of the hard mold that will make is all removed, and cleans up;
(9) go up cured: it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor except that the position of mould, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
(10) system hard mold 2: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on the model of removing gypsum mold, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth, again above-mentioned hybrid resin is brushed on thick glass fibre cloth, dried in the shade 10～30 minutes, again 801 glue are added land plaster, mix in 100: 40～70 ratio and mix well, water and be filled on the thick glass fibre cloth, till flooding 0,5～10 centimeters on model;
(11) die sinking tool: the gypsum hard mold is opened respectively, taken out the model of the inside;
(12) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inwall of gypsum hard mold.
7) system hollow mould:
(1) system box: vary in size according to external model, make big 0.5～10 centimeter sylphon of ratio model of different size;
(2) fixing external model: model is placed on the tabula rasa, model bottom packing paper plate or fiberboard or plank or laminate, what determine that goods fill up slab more to thickness according to goods, goods fill up rich plate less, after fixing with 502 glue, sylphon are enclosed within on the model;
(3) system gypsum mold: 801 glue are added land plaster, mix by 100: 40～70 ratio and mix well, water sylphon, till flooding over half 0.5～10 centimeter of model;
(5) drying: dried in the shade 5～10 minutes;
(6) remove mould: the gypsum mold over half 0,5～10 centimeters above gypsum mold removed, cleaned up;
(7) go up cured: cured or table leather board sprays cured brush or is sprayed on position except that mould with the cured mould in floor, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
(8) system outer mold 1: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on second half model of the gypsum mold of having made, spread two layers of fine glass fibre cloth, again with above-mentioned hybrid resin, brush is on fine glass fibre cloth, layer overlay thick glass fibre cloth, again with above-mentioned hybrid resin, water and be filled on the thick glass fibre cloth, till flooding 0.5～10 centimeter of thick glass fibre cloth;
(9) drying: dried in the shade 10～30 minutes;
(10) remove mould: the gypsum mold of second half of the outer mold 1 that will make is all removed, and cleans up;
(11) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on that half model of removing gypsum mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
(12) system outer mold 2: resin is added ketone slurry add and buy liquid and add talcum powder, mixing is mixed well, brush has been removed on half the model of gypsum mold, spread on two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth waters above-mentioned hybrid resin and is filled on the thick glass fibre cloth, till flooding 0.5～10 centimeter of thick glass fibre cloth;
(15) drying: dried in the shade 10～30 minutes;
(16) die sinking tool: hard mold is opened respectively, taken out the model of the inside;
(17) cut edge: the burr around the hard mold are cut off;
(18) polishing: with the machine polishing, to smooth straight and even;
(19) system box:, make big 0.5～10 centimeter sylphon of ratio inner model of different size according to inner model size shape difference;
(20) fixing inner mold: inner mold is placed on the tabula rasa, fixes, again sylphon is enclosed within on the inner model, fix with 502 glue with 502 glue;
(21) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inner model;
(22) system inner mold: resin is added ketone slurry add and buy liquid and add talcum powder, the ratio by 100: 10～30: 10～30: 10～30 is mixed and is mixed well, and waters sylphon, till flooding inner model;
(22) drying: dried in the shade 10～30 minutes;
(22) engraving: unnecessary hybrid resin has been carved, cleaned up;
(23) die sinking tool: open box, take out inner model;
(24) polishing: the corase grind machine, finish grind by hand, till the light cleaning;
(25) go up cured: with the mould brush or the floor is cured or the table leather board sprays cured brush or be sprayed on the inner mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
8) the imitative emerald material of system: transparent resin is added diluent add curing agent and add required color=100: 10～30: 10～30: 10～30.
9) imitative emerald material of system and goods:
(1) mould: soft mold is put in the hard mold;
(2) goods: transparent resin is added diluent add curing agent and add required color, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, with syringe or other vessel, inject or water and be filled in soft mold or soft or hard mould or hard mold or the gypsum mold, buckle the pressing mold tool, with the limit that a plurality of clips are clamped mould, above-mentioned hybrid resin can't be leached;
(3) drying: dry in the shade to just solidifying;
(4) die sinking tool: open mould, take out early-products;
(5) engraving: early-products is engraved as the goods that adhere to specification;
(6) cool off: goods are placed in the cold water soaked 30 minutes～1 hour;
(7) polishing: the corase grind machine, finish grind by hand, to the light cleaning;
(8) go up coloring agent: transparent resin is added diluent add curing agent and add required color, mix to mix well system is described, to meeting the color of transferring meter to require;
(9) drying: cloudy in 10～30 minutes;
(10) japanning: with blowing varnish goods are sprayed repeatedly, dried in the shade 15～20 minutes, this step needs 2～3 times repeatedly.
Combination shaping 1:
(1) main body is shaped: by perforating bonding, joggle, grafting method, on main body, allow body reach layout required article combination;
(2) bonding: flower 302 glue, the branch bar adds talcum powder with 502 glue and adds saw wood ash=100: 10～30: 10～30
(2) engraving: adhesive has been carved, cleaned up;
(3) polishing: carry out with fine sandpaper, from thick number to thin number, to the light cleaning;
(4) go up coloring agent: add diluent with the agent of resin gel coat reinforcingization and add required color mixture and mix well, goods are described, to the color that adheres to specification;
(5) drying: dried in the shade 10～30 minutes;
(6) drying: with being sprayed on the duplicate from spraying paint, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
With Jade Accessories or artificial potted landscape that above-mentioned process for making is finished, workmanship is exquisite, lines are graceful, happy, is that the utmost point has material and the goods of viewing and admiring, collect, develop value.
The specific embodiment:
Introduce the step of making emerald material and goods of process provided by the present invention below.
Ornaments or artificial potted landscape---camellia profile: long * wide * high=0.98 meter * 0.68 meter * 0.78 meter
Basic pattern is the imitative emerald camellia that red blossoms and green leaves is had in a strain, and root is tied in the base of basin.
1) simulation:
(1) system wooden mold: timber is sawed, cuts, carves, bondd, the model that joggle becomes to adhere to specification;
(2) system plaster cast; Gypsum is added 801 glue, mix in 100: 40～70 ratio and mix well, water and be filled in, after solidifying it is engraved as the model that adheres to specification than in big 0.5～10 centimeter sylphon of model;
(3) system mud model: the model that foundry loam or rubber cement kneading model are become to adhere to specification;
(4) engraving: work with great care according to layout;
(5) polishing: use sand papering, from thick number to thin number, to the light cleaning;
(6) bonding: add talcum powder with 502 and add saw wood ash=100: 10～30: 10～30;
(7) play putty: add diluent with transparent resin and add curing agent and add required color=100: 10～30: 10～30: 10～30;
(8) polishing: with the sand polishing, from thick number to thin number, to the light cleaning;
(9) go up cured: it is cured or mould is cured or it is cured to spray the spray of table leather board to brush the floor on model, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly.
2) the three-dimensional soft or hard mould of system:
(1) fixed model: the position that model is narrow down, wide position stands on the tabula rasa up, with 502 glue add a small amount of talcum powder fixing after,
(3) system soft mode: add with silicon rubber and to solidify Ji, mix well, water and be filled on the model, up catch up with the mixing silicon rubber that grey cutter will down drop down from the model, till solidifying by 100: 5～20 ratio mixing;
(4) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(5) system gypsum mold: add curing agent with 801 glue, mix by 100: 40～70 ratio and mix well, be put on half of soft mold, extremely above till half 0,5～10 centimeters of soft mold;
(6) drying: dried in the shade 5～10 minutes;
(7) remove mould: the plaster mold over half 0,5～10 centimeters above soft mold removed;
(8) system hard mold 1: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on second half of the gypsum mold of having made, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
(9) drying: dried in the shade 10～30 minutes;
(10) remove mould: the gypsum mold that will make is all removed, and cleans up;
(11) go up cured: will plate cured or mould is cured or the table leather board sprays cured brush or be sprayed on half the soft mold of removing gypsum mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
(12) system hard mold 2: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on the soft mold of half of removing gypsum mold, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
(13) drying: dried in the shade 10～30 minutes;
(14) die sinking: the soft or hard mould is opened, taken out soft mold, soft mold is cut a mouth, take out the model of the inside;
(15) cut edge: the burr around the hard mold are cut off,
(16) polishing: corase grind machine, correct grinding are by hand, and be extremely smooth straight and even;
(17) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inwall of soft or hard mould, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
3) system plane soft or hard gypsum mold:
(1) system sylphon: vary in size according to model, make the sylphon of different size;
(2) system soft mold 1: silicon rubber is added curing agent, mix by 100: 5～20 ratio and mix well, water in the sylphon, to flooding soft mold till half;
(3) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(4) system hard mold 1: resin is added diluent add curing agent, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on half of soft mold, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed at fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
(5) drying: dried in the shade 10～30 minutes;
(6) system plaster mold 1: 801 glue are added land plaster, mix well, water and be filled on the thick glass fibre cloth, till flooding 0,5～10 centimeters of thick glass fibre cloth by the mixing of 100: 40～70 ratio;
(7) drying: dried in the shade 5～10 minutes;
(8) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on second half of soft or hard gypsum mold that brush makes; Dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
(9) system soft mold 2: silicon rubber is added curing agent, and by 100 ratios: 5～20 ratio is mixed and is mixed well, and waters in the sylphon, till flooding soft mold;
(10) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(11) system hard mold 2: resin is added diluent add curing agent, ratio in 100: 10～30: 10～30: 10～30 is mixed and is mixed well, brush is on second half of the gypsum mold of having made, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
(13) drying: dried in the shade 10～30 minutes;
(14) system gypsum hard mold 2: 801 glue are added curing agent, mix well by 100: 40～70 ratio mixing, water and be filled in thick glass fibre cloth, till flooding 0,5～10 centimeters of thick glass fibre cloth;
(15) die sinking tool: the soft or hard gypsum mold is opened respectively, taken out the model of the inside;
(16) go up cured: it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor except that the position of mould, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly.
4) system plane soft mold:
(13) system box: according to the large and small difference of model, the ratio model of making different size is big 0.5 centimeter～10 centimeters sylphon;
(14) fixed model: model is placed on the tabula rasa, model bottom packing paper plate or fiberboard or plank or laminate, thickness determines what according to goods, goods fill up slab more, and goods fill up rich plate less, after fixing with 502 glue, again the sylphon of making is enclosed within on the model, fixes with 502 glue;
(15) system soft mold: silicon rubber is added curing agent, mix by 100: 5～20 ratio and mix well, water sylphon, till flooding 0.5～10 centimeter on model;
(16) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(17) die sinking tool: open box, remove tabula rasa, take out the model of the inside;
(18) go up cured: it is cured or mould is cured or it is cured to spray the spray of table leather board to brush the floor at the soft mold inwall, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly.
5) system gypsum mold:
(11) system sylphon: vary in size according to model, make big 0.5～20 centimeter sylphon of ratio model of a different size:
(12) fixed model: model is placed on the tabula rasa, after fixing with 502 glue, again the sylphon of making is put on the model, fix with 502 glue again;
(13) system gypsum mold 1: add talcum powder with 801 glue, mix well, water in the sylphon, till flooding over half 0.5～10 centimeter of model by the mixing of 100: 40～70 ratio;
(14) drying: dried in the shade 5～10 minutes;
(15) remove mould: the gypsum mold that will make gypsum mold over half 0.5～10 centimeter is removed, and cleans up;
(16) go up cured: it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor except that the position of mould, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
(17) system gypsum mold 2: adding talcum powder with 801 glue, mix well in 100: 40～70 ratio mixing, water on second half model that is filled in the gypsum mold of having made, is last to flooding 0.5～10 centimeter on model;
(18) drying: dried in the shade 5～10 minutes;
(19) die sinking: gypsum mold is opened respectively, taken out the model of the inside;
(20) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inwall of gypsum mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times;
6) system gypsum hard mold:
(2) system sylphon: vary in size according to goods, make big 0.5～10 centimeter sky of ratio model of different size
Box is fixed with 502 glue;
(2) fixed model: model is placed on the tabula rasa, fixes, again sylphon is enclosed within on the model, fix with 502 glue with 502 glue;
(3) system gypsum mold: add land plaster with 801 glue, mix well, water sylphon, till flooding over half 0.5～10 centimeter of model by the mixing of 100: 40～70 ratio;
(4) drying: dried in the shade 5～10 minutes;
(5) remove mould: the gypsum mold that will make 0.5～10 centimeter gypsum mold over half has been carved, and cleans up;
(6) go up cured: will be except that the position of mould, it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor, dries in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
(19) system gypsum hard mold 1: resin is added the ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is being made on second half the model of gypsum mold, spread on two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth, again above-mentioned hybrid resin is brushed on thick glass fibre cloth, dried in the shade 10～30 minutes, again 801 glue are added land plaster, mix well in 100: 40～70 ratio mixing, sylphon is advanced in pouring, till flooding 0,5～10 centimeters on model;
(20) remove mould: the gypsum mold of second half of the hard mold that will make is all removed, and cleans up;
(21) go up cured: it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor except that the position of mould, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
(22) system hard mold 2: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on the model of removing gypsum mold, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth, again above-mentioned hybrid resin is brushed on thick glass fibre cloth, dried in the shade 10～30 minutes, again 801 glue are added land plaster, mix in 100: 40～70 ratio and mix well, water and be filled on the thick glass fibre cloth, till flooding 0,5～10 centimeters on model;
(23) die sinking tool: the gypsum hard mold is opened respectively, taken out the model of the inside;
(24) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inwall of gypsum hard mold.
7) system hollow mould:
(1) system box: vary in size according to external model, make big 0.5～10 centimeter sylphon of ratio model of different size;
(2) fixing external model: model is placed on the tabula rasa, model bottom packing paper plate or fiberboard or plank or laminate, what determine that goods fill up slab more to thickness according to goods, goods fill up rich plate less, after fixing with 502 glue, sylphon are enclosed within on the model;
(3) system gypsum mold: 801 glue are added land plaster, mix by 100: 40～70 ratio and mix well, water sylphon, till flooding over half 0.5～10 centimeter of model;
(5) drying: dried in the shade 5～10 minutes;
(6) remove mould: the gypsum mold over half 0,5～10 centimeters above gypsum mold removed, cleaned up;
(7) go up cured: cured or table leather board sprays cured brush or is sprayed on position except that mould with the cured mould in floor, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
(8) system outer mold 1: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on second half model of the gypsum mold of having made, spread two layers of fine glass fibre cloth, again with above-mentioned hybrid resin, brush is on fine glass fibre cloth, layer overlay thick glass fibre cloth, again with above-mentioned hybrid resin, water and be filled on the thick glass fibre cloth, till flooding 0.5～10 centimeter of thick glass fibre cloth;
(9) drying: dried in the shade 10～30 minutes;
(10) remove mould: the gypsum mold of second half of the outer mold 1 that will make is all removed, and cleans up;
(11) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on that half model of removing gypsum mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
(12) system outer mold 2: resin is added ketone slurry add and buy liquid and add talcum powder, mixing is mixed well, brush has been removed on half the model of gypsum mold, spread on two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth waters above-mentioned hybrid resin and is filled on the thick glass fibre cloth, till flooding 0.5～10 centimeter of thick glass fibre cloth;
(15) drying: dried in the shade 10～30 minutes;
(16) die sinking tool: hard mold is opened respectively, taken out the model of the inside;
(17) cut edge: the burr around the hard mold are cut off;
(18) polishing: with the machine polishing, to smooth straight and even;
(19) system box:, make big 0.5～10 centimeter sylphon of ratio inner model of different size according to inner model size shape difference;
(20) fixing inner mold: inner mold is placed on the tabula rasa, fixes, again sylphon is enclosed within on the inner model, fix with 502 glue with 502 glue;
(21) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inner model;
(22) system inner mold: resin is added ketone slurry add and buy liquid and add talcum powder, the ratio by 100: 10～30: 10～30: 10～30 is mixed and is mixed well, and waters sylphon, till flooding inner model;
(22) drying: dried in the shade 10～30 minutes;
(22) engraving: unnecessary hybrid resin has been carved, cleaned up;
(23) die sinking tool: open box, take out inner model;
(24) polishing: the corase grind machine, finish grind by hand, till the light cleaning;
(25) go up cured: with the mould brush or the floor is cured or the table leather board sprays cured brush or be sprayed on the inner mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
8) the imitative emerald material of system: transparent resin is added diluent add curing agent and add required color=100: 10～30: 10～30: 10～30.
9) imitative emerald material of system and goods;
(11) mould: soft mold is put in the hard mold;
(12) goods: transparent resin is added diluent add curing agent and add required color, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, with syringe or other vessel, inject or water and be filled in soft mold or soft or hard mould or hard mold or the gypsum mold, buckle the pressing mold tool, with the limit that a plurality of clips are clamped mould, above-mentioned hybrid resin can't be leached;
(13) drying: dry in the shade to just solidifying;
(14) die sinking tool: open mould, take out early-products;
(15) engraving: early-products is engraved as the goods that adhere to specification;
(16) cool off: goods are placed in the cold water soaked 30 minutes～1 hour;
(17) polishing: the corase grind machine, finish grind by hand, to the light cleaning;
(18) go up coloring agent: transparent resin is added diluent add curing agent and add required color, mix to mix well system is described, to meeting the color of transferring meter to require;
(19) drying: dried in the shade 10～30 minutes;
(20) japanning: with blowing varnish goods are sprayed repeatedly, dried in the shade 15～20 minutes, this step needs 2～3 times repeatedly.
Combination shaping 1:
(3) main body is shaped: by perforating bonding, joggle, grafting method, on main body, allow body reach layout required article combination;
(4) bonding: flower 302 glue, the branch bar adds talcum powder with 502 glue and adds saw wood ash=100: 10～30: 10～30
(2) engraving: adhesive has been carved, cleaned up;
(3) polishing: carry out with fine sandpaper, from thick number to thin number, to the light cleaning;
(4) go up coloring agent: add diluent with the agent of resin gel coat reinforcingization and add required color mixture and mix well, goods are described, to the color that adheres to specification;
(5) drying: dried in the shade 10～30 minutes;
(6) drying: with being sprayed on the duplicate from spraying paint, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
Accompanying drawing is flourishing camellia floral diagram.

Claims (10)

  1. The process for making of 1 artificial ornamental article made from jadestone or potted landscape, its particular-trade are to carry out according to the following steps:
    1) simulation:
    (1) system wooden mold: timber is sawed, cuts, carves, bondd, the model that joggle becomes to adhere to specification;
    (2) system plaster cast: gypsum is added 801 glue, mix well, water and be filled in, after solidifying it is engraved as the model that adheres to specification than in big 0.5～10 centimeter sylphon of model by the mixing of 100: 40～70 ratio;
    (3) system mud model: the model that foundry loam or rubber cement kneading model are become to adhere to specification;
    (4) engraving: work with great care according to layout;
    (5) polishing: use sand papering, from thick number to thin number, to the light cleaning;
    (6) bonding: add talcum powder with 502 and add saw wood ash=100: 10～30: 10～30;
    (7) play putty: add diluent with transparent resin and add curing agent and add required color=100: 10～30: 10～30: 1～30;
    (8) polishing: with the sand polishing, from thick number to thin number, to the light cleaning;
    (9) go up cured: it is cured or mould is cured or it is cured to spray the spray of table leather board to brush the floor on model, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly.
    2) the three-dimensional soft or hard mould of system:
    (1) fixed model: the position that model is narrow down, wide position stands on the tabula rasa up, adds talcum powder by 100: 10～30 fixed ratio with 502 glue;
    (3) system soft mode: add with silicon rubber and to solidify Ji, mix well, water and be filled on the model, up catch up with the mixing silicon rubber that grey cutter will down drop down from the model, till solidifying by 100: 5～20 ratio mixing;
    (4) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
    (5) system gypsum mold: add curing agent with 801 glue, mix by 100: 40～70 ratio and mix well, be put on half of soft mold, extremely above till half 0,5～10 centimeters of soft mold;
    (6) drying: dried in the shade 5～10 minutes;
    (7) remove mould: the plaster mold over half 0,5～10 centimeters above soft mold removed;
    (8) system hard mold 1: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on second half of the gypsum mold of having made, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
    (9) drying: dried in the shade 10～30 minutes;
    (10) remove mould: the gypsum mold that will make is all removed, and cleans up;
    (11) go up cured: will plate cured or mould is cured or the table leather board sprays cured brush or be sprayed on half the soft mold of removing gypsum mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
    (12) system hard mold 2: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on the soft mold of half of removing gypsum mold, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
    (13) drying: dried in the shade 10～30 minutes;
    (14) die sinking: the soft or hard mould is opened, taken out soft mold, soft mold is cut a mouth, take out the model of the inside;
    (15) cut edge: the burr around the hard mold are cut off,
    (16) polishing: corase grind machine, correct grinding are by hand, and be extremely smooth straight and even;
    (17) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or is sprayed on the inwall of soft or hard mould the moon
    3) system plane soft or hard gypsum mold:
    (1) system sylphon: vary in size according to model, make the sylphon of different size;
    (2) system soft mold 1: silicon rubber is added curing agent, mix by 100: 5～20 ratio and mix well, water in the sylphon, to flooding soft mold till half;
    (3) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
    (4) system hard mold 1: resin is added diluent add curing agent, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on half of soft mold, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed at fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
    (5) drying: dried in the shade 10～30 minutes;
    (6) system plaster mold 1: 801 glue are added land plaster, mix well, water and be filled on the thick glass fibre cloth, till flooding 0,5～10 centimeters of thick glass fibre cloth by the mixing of 100: 40～70 ratio;
    (7) drying: dried in the shade 5～10 minutes;
    (8) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on second half of soft or hard gypsum mold that brush makes; Dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
    (9) system soft mold 2: silicon rubber is added curing agent, and by 100 ratios: 5～20 ratio is mixed and is mixed well, and waters in the sylphon, till flooding soft mold;
    (10) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
    (11) system hard mold 2: resin is added diluent add curing agent, ratio in 100: 10～30: 10～30: 10～30 is mixed and is mixed well, brush is on second half of the gypsum mold of having made, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth is brushed above-mentioned hybrid resin on thick glass fibre cloth again;
    (13) drying: dried in the shade 10～30 minutes;
    (14) system gypsum hard mold 2: 801 glue are added curing agent, mix well by 100: 40～70 ratio mixing, water and be filled in thick glass fibre cloth, till flooding 0,5～10 centimeters of thick glass fibre cloth;
    (15) die sinking tool: the soft or hard gypsum mold is opened respectively, taken out the model of the inside;
    (16) go up cured: it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor except that the position of mould, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly.
    4) system plane soft mold:
    (1) system box: according to the large and small difference of model, the ratio model of making different size is big 0.5 centimeter～10 centimeters sylphon;
    (2) fixed model: model is placed on the tabula rasa, model bottom packing paper plate or fiberboard or plank or laminate, thickness determines what according to goods, goods fill up slab more, and goods fill up rich plate less, after fixing with 502 glue, again the sylphon of making is enclosed within on the model, fixes with 502 glue;
    (3) system soft mold: silicon rubber is added curing agent, mix by 100: 5～20 ratio and mix well, water sylphon, till flooding 0.5～10 centimeter on model;
    (4) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
    (5) die sinking tool: open box, remove tabula rasa, take out the model of the inside;
    (6) go up cured: it is cured or mould is cured or it is cured to spray the spray of table leather board to brush the floor at the soft mold inwall, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly.
    5) system gypsum mold:
    (1) system sylphon: vary in size according to model, make big 0.5～20 centimeter sylphon of ratio model of a different size:
    (2) fixed model: model is placed on the tabula rasa, after fixing with 502 glue, again the sylphon of making is put on the model, fix with 502 glue again;
    (3) system gypsum mold 1: add talcum powder with 801 glue, mix well, water in the sylphon, till flooding over half 0.5～10 centimeter of model by the mixing of 100: 40～70 ratio;
    (4) drying: dried in the shade 5～10 minutes;
    (5) remove mould: the gypsum mold that will make gypsum mold over half 0.5～10 centimeter is removed, and cleans up;
    (6) go up cured: it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor except that the position of mould, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
    (7) system gypsum mold 2: adding talcum powder with 801 glue, mix well in 100: 40～70 ratio mixing, water on second half model that is filled in the gypsum mold of having made, is last to flooding 0.5～10 centimeter on model;
    (8) drying: dried in the shade 5～10 minutes;
    (9) die sinking: gypsum mold is opened respectively, taken out the model of the inside;
    (10) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inwall of gypsum mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times;
    6) system gypsum hard mold:
    (1) system sylphon: vary in size according to goods, make big 0.5～10 centimeter sylphon of ratio model of different size, fix with 502 glue;
    (2) fixed model: model is placed on the tabula rasa, fixes, again sylphon is enclosed within on the model, fix with 502 glue with 502 glue;
    (3) system gypsum mold: add land plaster with 801 glue, mix well, water sylphon, till flooding over half 0.5～10 centimeter of model by the mixing of 100: 40～70 ratio;
    (4) drying: dried in the shade 5～10 minutes;
    (5) remove mould: the gypsum mold that will make 0.5～10 centimeter gypsum mold over half has been carved, and cleans up;
    (6) go up cured: will be except that the position of mould, it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor, dries in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
    (7) system gypsum hard mold 1: resin is added the ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is being made on second half the model of gypsum mold, spread on two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth, again above-mentioned hybrid resin is brushed on thick glass fibre cloth, dried in the shade 10～30 minutes, again 801 glue are added land plaster, mix well in 100: 40～70 ratio mixing, sylphon is advanced in pouring, till flooding 0,5～10 centimeters on model;
    (8) remove mould: the gypsum mold of second half of the hard mold that will make is all removed, and cleans up;
    (9) go up cured: it is cured or mould is cured or spray the table leather board sprays curedly to brush the floor except that the position of mould, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
    (10) system hard mold 2: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on the model of removing gypsum mold, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth, again above-mentioned hybrid resin is brushed on thick glass fibre cloth, dried in the shade 10～30 minutes, again 801 glue are added land plaster, mix in 100: 40～70 ratio and mix well, water and be filled on the thick glass fibre cloth, till flooding 0,5～10 centimeters on model;
    (11) die sinking tool: the gypsum hard mold is opened respectively, taken out the model of the inside;
    (12) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inwall of gypsum hard mold.
    7) system hollow mould:
    (1) system box: vary in size according to external model, make big 0.5～10 centimeter sylphon of ratio model of different size;
    (2) fixing external model: model is placed on the tabula rasa, model bottom packing paper plate or fiberboard or plank or laminate, what determine that goods fill up slab more to thickness according to goods, goods fill up rich plate less, after fixing with 502 glue, sylphon are enclosed within on the model;
    (3) system gypsum mold: 801 glue are added land plaster, mix by 100: 40～70 ratio and mix well, water sylphon, till flooding over half 0.5～10 centimeter of model;
    (5) drying: dried in the shade 5～10 minutes;
    (6) remove mould: the gypsum mold over half 0,5～10 centimeters above gypsum mold removed, cleaned up;
    (7) go up cured: cured or table leather board sprays cured brush or is sprayed on position except that mould with the cured mould in floor, dries in the shade 15～20 minutes, and this step need be carried out 2～3 times repeatedly;
    (8) system outer mold 1: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush is on second half model of the gypsum mold of having made, spread two layers of fine glass fibre cloth, again with above-mentioned hybrid resin, brush is on fine glass fibre cloth, layer overlay thick glass fibre cloth, again with above-mentioned hybrid resin, water and be filled on the thick glass fibre cloth, till flooding 0.5～10 centimeter of thick glass fibre cloth;
    (9) drying: dried in the shade 10～30 minutes;
    (10) remove mould: the gypsum mold of second half of the outer mold 1 that will make is all removed, and cleans up;
    (11) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on that half model of removing gypsum mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
    (12) system outer mold 2: resin is added ketone slurry add and buy liquid and add talcum powder, mixing is mixed well, brush has been removed on half the model of gypsum mold, spread on two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed on fine glass fibre cloth, layer overlay thick glass fibre cloth waters above-mentioned hybrid resin and is filled on the thick glass fibre cloth, till flooding 0.5～10 centimeter of thick glass fibre cloth;
    (15) drying: dried in the shade 10～30 minutes;
    (16) die sinking tool: hard mold is opened respectively, taken out the model of the inside;
    (17) cut edge: the burr around the hard mold are cut off;
    (18) polishing: with the machine polishing, to smooth straight and even;
    (19) system box:, make big 0.5～10 centimeter sylphon of ratio inner model of different size according to inner model size shape difference;
    (20) fixing inner mold: inner mold is placed on the tabula rasa, fixes, again sylphon is enclosed within on the inner model, fix with 502 glue with 502 glue;
    (21) go up cured: the floor is cured or mould is cured or the table leather board sprays cured brush or be sprayed on the inner model;
    (22) system inner mold: resin is added ketone slurry add and buy liquid and add talcum powder, the ratio by 100: 10～30: 10～30: 10～30 is mixed and is mixed well, and waters sylphon, till flooding inner model;
    (22) drying: dried in the shade 10～30 minutes;
    (22) engraving: unnecessary hybrid resin has been carved, cleaned up;
    (23) die sinking tool: open box, take out inner model;
    (24) polishing: the corase grind machine, finish grind by hand, till the light cleaning;
    (25) go up cured: with the mould brush or the floor is cured or the table leather board sprays cured brush or be sprayed on the inner mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
    8) the imitative emerald material of system: transparent resin is added diluent add curing agent and add required color=100: 10～30: 10～30: 10～30.
    9) imitative emerald material of system and goods:
    (1) mould: soft mold is put in the hard mold;
    (2) goods: transparent resin is added diluent add curing agent and add required color, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, with syringe or other vessel, inject or water and be filled in soft mold or soft or hard mould or hard mold or the gypsum mold, buckle the pressing mold tool, with the limit that a plurality of clips are clamped mould, above-mentioned hybrid resin can't be leached;
    (3) drying: dry in the shade to just solidifying;
    10～30 ratio is mixed and is mixed well, and with syringe or other vessel, injects or waters and be filled in soft mold or soft or hard mould or hard mold or the gypsum mold, buckles the pressing mold tool, with the limit that a plurality of clips are clamped mould, above-mentioned hybrid resin can't be leached;
    (3) drying; Dry in the shade to just solidifying;
    (4) die sinking tool: open mould, take out early-products;
    (5) engraving: early-products is engraved as the goods that adhere to specification;
    (6) cool off: goods are placed in the cold water soaked 30 minutes～1 hour;
    (7) polishing: the corase grind machine, finish grind by hand, to the light cleaning;
    (8) go up coloring agent: transparent resin is added diluent add curing agent and add required color, mix to mix well system is described, to meeting the color of transferring meter to require;
    (9) drying: dried in the shade 10～30 minutes;
    (10) japanning: with blowing varnish goods are sprayed repeatedly, dried in the shade 15～20 minutes, this step needs 2～3 times repeatedly.
    Combination shaping 1:
    (1) main body is shaped: by perforating bonding, joggle, grafting method, on main body, allow body reach layout required article combination;
    (2) bonding: flower 302 glue, the branch bar adds talcum powder with 502 glue and adds saw wood ash=100: 10～30: 10～30
    (3) engraving: adhesive has been carved, cleaned up;
    (4) polishing: carry out with fine sandpaper, from thick number to thin number, to the light cleaning;
    (5) go up coloring agent: add diluent with the agent of resin gel coat reinforcingization and add required color mixture and mix well, goods are described, to the color that adheres to specification;
    (6) drying: dried in the shade 10～30 minutes;
    (7) drying: with being sprayed on the duplicate from spraying paint, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
  2. 2, model: the preparation method of artificial ornamental article made from jadestone according to claim 1 or potted landscape is characterized in that described cast material is that wood, 801 glue add the shape that land plaster=100: 40～70 or foundry loam, rubber engraving, kneading model become designing requirement.
  3. 3, main body bonding: the preparation method of artificial ornamental article made from jadestone according to claim 1 or potted landscape is characterized in that described binding material is that 302 glue or 502 glue add talcum powder=100: 10～30: 10～30.
  4. 4, moulding: the method for manufacturing technology of artificial ornamental article made from jadestone according to claim 1 or potted landscape is characterized in that described Modeling Material is reinforcing bar or steel pipe or iron wire or iron pipe or iron nail or fastener or copper wire or copper pipe.
  5. 5, putty: artificial ornamental article made from jadestone according to claim 1 or potted landscape process for making, it is characterized in that described putty material is that transparent resin adds diluent and adds talcum powder and add required color=100: 10～30: 10～30: 10～30 or atom ash and add curing agent and add required color=100: 10～30: 10～30.
  6. 6, soft mold: the process for making of artificial ornamental article made from jadestone according to claim 1 or potted landscape is characterized in that described soft model material is that silicon rubber adds curing agent=100: 5～20.
  7. 7, hard mold and hollow mould: the process for making of artificial ornamental article made from jadestone according to claim 1 or potted landscape, it is characterized in that described hard mold and hollow mould material are that resin adds ketone slurry and adds and buy liquid and add talcum powder=100: 10～30: 10～30: 10～30 and add two layers of fine glass fibre cloth, one deck thick glass fibre cloth.
  8. 8, imitative emerald: the process for making of artificial ornamental article made from jadestone according to claim 1 or potted landscape is characterized in that described emerald material is that transparent resin adds the diluent curing agent and adds required color=100: 10～30: 10～30: 10～30.
  9. 9, required color: the manufacture craft process of artificial ornamental article made from jadestone according to claim 1 or potted landscape is characterized in that described coloration material is food additives or color inks=10～30: 10～30.
  10. 10, goods: the process for making of artificial ornamental article made from jadestone according to claim 1 or potted landscape is characterized in that ornaments or artificial potted landscape that described emerald goods are various different colors, kind, specification, shape, class.
CN 200410070702 2004-07-21 2004-07-21 Artificial ornamental article made from jadestone or miniature landscape Pending CN1600578A (en)