CN1586922A - Process for making artificial natural landscape stalactite karst cave - Google Patents
Process for making artificial natural landscape stalactite karst cave Download PDFInfo
- Publication number
- CN1586922A CN1586922A CN 200410070432 CN200410070432A CN1586922A CN 1586922 A CN1586922 A CN 1586922A CN 200410070432 CN200410070432 CN 200410070432 CN 200410070432 A CN200410070432 A CN 200410070432A CN 1586922 A CN1586922 A CN 1586922A
- Authority
- CN
- China
- Prior art keywords
- model
- add
- cured
- stalactite
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the technological process of making artificial natural landscape stalactite karst cave, and features that after the mold and material for stalactite karst cave is prepared, the stalactite karst cave is made through injection molding. The technological process is short, low in cost and environment friendly, and the product is high in artistic value.
Description
Technical field
The present invention relates to the making construction method of artificial landscape stalactite solution cavity, belong to watering and mould, carve, imitate the material product field.
Existing stalactite can only can't apply in the gardening view of gardens at the solution cavity that there was dampness in the air, so land waste is not so good as Counterfeit Item and works with great care on sense organ, moulding and different, imitated vestige numerous in variety.
The purpose of this invention is to provide the process for making of artificial stalactite solution cavity material and goods, goods obviously are better than existing goods, and the Counterfeit Item duration is short, and cost is low; Not being subjected to the restriction in environment, space, kind, specification, color, classification, traditional handicraft, material, environmental protection, market, is to have material and the goods of viewing and admiring, collect, develop value.
1) simulation:
(1) system wooden mold: timber is sawed, cuts, carves, bondd, the model that joggle becomes to adhere to specification;
(2) system plaster cast: gypsum is added 801 glue, mix well, water and be filled in, after solidifying it is engraved as the model that adheres to specification than in big 0.5～10 centimeter sylphon of model by the mixing of 100: 40～70 ratio;
(3) system mud model: the model that foundry loam or rubber cement kneading model are become to adhere to specification;
(4) engraving: work with great care according to layout;
(5) polishing: the corase grind machine, finish grind by hand, to the light cleaning;
(6) bonding: add talcum powder with 502 glue and add saw wood ash=100: 10～30: 10～30;
(7) play putty: add diluent with transparent resin and add curing agent=100: 10～30: 10～30;
(8) polishing: with the sand polishing, from thick number to thin number, to the light cleaning;
(9) go up cured: the floor is cured or mould is cured or the spray of table leather board is cured, brush or be sprayed on the model, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
2) system plane soft or hard mould:
(1) system sylphon: vary in size according to model, make the sylphon of different size;
(2) system soft mold: silicon rubber is added curing agent, mix well in 100: 5～20 ratio mixing, brush was being gone up on that cured half model;
(3) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(4) system hard mold: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush do not water gypsum mold half soft mold on, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed at fine glass fibre cloth, layer overlay thick glass fibre cloth waters above-mentioned hybrid resin and is filled on the thick glass fibre cloth till flood over half 0,5～10 centimeters of thick glass fibre cloth;
(5) drying: dried in the shade 10～30 minutes;
(6) die sinking tool: open box, remove tabula rasa, take out the model of the inside;
(7) upward cured; The floor is cured or mould is cured or table leather board spray is cured, brush or be sprayed on the soft or hard mould inner wall, to dry in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
3) system plane soft mold:
(1) system box: vary in size according to model, make different size, than model big 0.5 centimeter～10 centimeters sylphon;
(2) fixed model: model is placed on the tabula rasa, model bottom packing paper plate or fiberboard or plank or laminate, thickness determines what according to goods, goods fill up slab more, and goods fill up rich plate less, after fixing with 502 glue, again the sylphon of making is enclosed within on the model, fixes with 502 glue;
(3) system soft mold: silicon rubber is added curing agent, mix by 100: 5～20 ratio and mix well, water sylphon, till flooding 0.5～10 centimeter on model;
(4) in hot-tempered: dried in the shade slow curing 2～24 hours 1～2 hour;
(5) die sinking tool: open box, remove tabula rasa, take out the model of the inside;
(6) go up cured: the floor is cured or mould is cured or it is cured to spray the spray of table leather board, brush or be sprayed on the soft mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
4) the imitative stalactite material of system: transparent resin is added diluent add curing agent and add talcum powder and add required color=100: 10～30: 10～30: 10～30: 10～30.
5) imitative stalactite material of system and goods:
(1) mould: soft mold is put in the hard mold;
(2) goods: transparent resin is added diluent add curing agent and add talcum powder and add required color, ratio mixing in 100: 10～30: 10～30: 10～30: 10～30 is mixed well, water with vessel and to be filled in soft mold or soft or hard mould or hard mold or the gypsum mold, buckle the pressing mold tool, with the limit that a plurality of clips are clamped mould, above-mentioned hybrid resin can't be leached;
(3) drying: dry in the shade to just solidifying;
(4) die sinking tool: open mould, take out early-products;
(5) engraving: early-products is engraved as the goods that adhere to specification;
(6) cool off: goods are placed in the cold water soaked 30 minutes～1 hour;
(7) polishing: the corase grind machine, finish grind by hand, to the light cleaning;
(8) gluing: with above-mentioned mixed transparent resin goods are described repeatedly, till satisfied;
(9) drying: dried in the shade 10～30 minutes;
(10) japanning: with blowing varnish goods are sprayed repeatedly, dried in the shade 15～20 minutes, this step needs 2～3 times repeatedly.
Combination shaping:
(1) main body is shaped: the goods of making by above-mentioned same process method all are combined on the main body with methods such as perforating, bonding, vertebra connect, allow body reach design standard;
(2) engraving: adhesive has been carved, cleaned up;
(3) polishing: carry out with fine sandpaper, from thick number to thin number, to the light cleaning;
(4) gluing: with above-mentioned transparent mixing tree is cured goods are described, to the standard that adheres to specification;
(5) drying: dried in the shade 30 minutes～1 hour;
(6) drying: with being sprayed on the goods from spraying paint, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
With the artificial landscape stalactite solution cavity that above-mentioned process for making is finished, it is exquisite, elegant in appearance to do manual work, and is that the utmost point has material and the goods of viewing and admiring, develop value.
The specific embodiment:
Introduce the step of making artificial landscape stalactite solution cavity material and goods of process provided by the present invention below.
Artificial landscape stalactite solution cavity profile: long * wide * high=198 meters * 168 meters * 178 meters
Basic pattern is a stalactitic solution cavity that overworks different shape.
1) simulation:
(1) system wooden mold: timber is sawed, cuts, carves, bondd, the model that joggle becomes to adhere to specification;
(2) system plaster cast: gypsum is added 801 glue, mix well, water and be filled in, after solidifying it is engraved as the model that adheres to specification than in big 0.5～10 centimeter sylphon of model by the mixing of 100: 40～70 ratio;
(3) system mud model: the model that foundry loam or rubber cement kneading model are become to adhere to specification;
(4) engraving: work with great care according to layout;
(5) polishing: the corase grind machine, finish grind by hand, to the light cleaning;
(6) bonding: add talcum powder with 502 glue and add saw wood ash=100: 10～30: 10～30;
(7) play putty: add diluent with transparent resin and add curing agent=100: 10～30: 10～30;
(8) polishing: with the sand polishing, from thick number to thin number, to the light cleaning;
(9) go up cured: the floor is cured or mould is cured or the spray of table leather board is cured, brush or be sprayed on the model, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
2) system plane soft or hard mould:
(1) system sylphon: vary in size according to model, make the sylphon of different size;
(2) system soft mold: silicon rubber is added curing agent, mix well in 100: 5～20 ratio mixing, brush was being gone up on that cured half model;
(3) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(4) system hard mold: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush do not water gypsum mold half soft mold on, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed at fine glass fibre cloth, layer overlay thick glass fibre cloth waters above-mentioned hybrid resin and is filled on the thick glass fibre cloth till flood over half 0,5～10 centimeters of thick glass fibre cloth;
(5) drying: dried in the shade 10～30 minutes;
(6) go up cured: analyse ground cured or mould is cured or the spray of table leather board is cured, brush or be sprayed on the soft or hard mould inner wall, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
3) system plane soft mold:
(1) system box: vary in size according to model, make different size, than model big 0.5 centimeter～10 centimeters sylphon;
(2) fixed model: model is placed on the tabula rasa, model bottom packing paper plate or fiberboard or plank or laminate, thickness determines what according to goods, goods fill up slab more, and goods fill up rich plate less, after fixing with 502 glue, again the sylphon of making is enclosed within on the model, fixes with 502 glue;
(3) system soft mold: silicon rubber is added curing agent, mix by 100: 5～20 ratio and mix well, water sylphon, till flooding 0.5～10 centimeter on model;
(4) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(5) die sinking tool: open box, remove tabula rasa, take out the model of the inside;
(6) go up cured: the floor is cured or mould is cured or it is cured to spray the spray of table leather board, brush or be sprayed on the soft mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
4) the imitative stalactite material of system: transparent resin is added diluent add curing agent and add talcum powder and add required color=100: 10～30: 10～30; 10～30: 10～30.
5) imitative stalactite material of system and goods:
(1) mould: soft mold is put in the hard mold;
(2) goods: transparent resin is added diluent add curing agent and add talcum powder and add required color, ratio mixing in 100: 10～30: 10～30: 10～30: 10～30 is mixed well, water with vessel and to be filled in soft mold or soft or hard mould or hard mold or the stone agate cream mould, buckle the pressing mold tool, with the limit that a plurality of clips are clamped mould, above-mentioned hybrid resin can't be leached;
(3) drying: dry in the shade to just solidifying;
(4) die sinking tool: open mould, take out early-products;
(5) engraving: early-products is engraved as the goods that adhere to specification;
(6) cool off: goods are placed in the cold water soaked 30 minutes～1 hour;
(7) polishing: the corase grind machine, finish grind by hand, to the light cleaning;
(8) gluing: with above-mentioned mixed transparent resin goods are described repeatedly, till the standard that adheres to specification;
(9) drying: dried in the shade 10～30 minutes;
(11) japanning: with blowing varnish goods are sprayed repeatedly, dried in the shade 15～20 minutes, this step needs 2～3 times repeatedly.
Combination shaping 1:
(1) main body is shaped: by perforating bonding, joggle, grafting method, on main body, allow body reach design standard required article combination;
(2) engraving: adhesive has been carved, cleaned up;
(3) gluing, with above-mentioned mixed transparent resin to describing repeatedly on the goods, to the standard that adheres to specification;
(4) polishing: carry out with fine sandpaper, from thick number to thin number, to the light cleaning;
(5) drying: dried in the shade 30 minutes～1 hour;
(6) drying: with being sprayed on the duplicate from spraying paint, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
Claims (9)
1, the process for making of artificial landscape stalactite solution cavity, its particular-trade are to carry out according to the following steps:
1) simulation:
(1) system wooden mold: timber is sawed, cuts, carves, bondd, the model that joggle becomes to adhere to specification;
(2) system plaster cast: gypsum is added 801 glue, mix well, water and be filled in, after solidifying it is engraved as the model that adheres to specification than in big 0.5～10 centimeter sylphon of model by the mixing of 100: 40～70 ratio;
(3) system mud model: the model that foundry loam or rubber cement kneading model are become to adhere to specification;
(4) engraving: work with great care according to layout;
(5) polishing: the corase grind machine, finish grind by hand, to the light cleaning;
(6) bonding: add talcum powder with 502 glue and add saw wood ash=100: 10～30: 10～30;
(7) play putty: add diluent with transparent resin and add curing agent=100: 10～30: 10～30;
(8) polishing: with the sand polishing, from thick number to thin number, to the light cleaning;
(9) go up cured: the floor is cured or mould is cured or the spray of table leather board is cured, brush or be sprayed on the model, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
2) system plane soft or hard mould:
(1) system sylphon: vary in size according to model, make the sylphon of different size;
(2) system soft mold: silicon rubber is added curing agent, mix well in 100: 5～20 ratio mixing, brush was being gone up on that cured half model;
(3) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(4) system hard mold: resin is added ketone slurry add and buy liquid and add talcum powder, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, brush do not water gypsum mold half soft mold on, spread two layers of fine glass fibre cloth, again above-mentioned hybrid resin is brushed at fine glass fibre cloth, layer overlay thick glass fibre cloth waters above-mentioned hybrid resin and is filled on the thick glass fibre cloth till flood over half 0,5～10 centimeters of thick glass fibre cloth;
(5) drying: dried in the shade 10～30 minutes;
(6) go up cured: analyse ground cured or mould is cured or the spray of table leather board is cured, brush or be sprayed on the soft or hard mould inner wall, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
3) system plane soft mold:
(1) system box: vary in size according to model, make different size, than model big 0.5 centimeter～10 centimeters sylphon;
(2) fixed model: model is placed on the tabula rasa, model bottom packing paper plate or fiberboard or plank or laminate, thickness determines what according to goods, goods fill up slab more, and goods fill up rich plate less, after fixing with 502 glue, again the sylphon of making is enclosed within on the model, fixes with 502 glue;
(3) system soft mold: silicon rubber is added curing agent, mix by 100: 5～20 ratio and mix well, water sylphon, till flooding 0.5～10 centimeter on model;
(4) drying: dried in the shade slow curing 2～24 hours 1～2 hour;
(5) die sinking tool: open box, remove tabula rasa, take out the model of the inside;
(6) go up cured: the floor is cured or mould is cured or it is cured to spray the spray of table leather board, brush or be sprayed on the soft mold, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly.
4) the imitative stalactite material of system: transparent resin is added diluent add curing agent and add required color=100: 10～30:: 10～30: 10～30.
5) imitative stalactite material of system and goods:
(1) mould: soft mold is put in the hard mold;
(2) goods: transparent resin is added diluent add curing agent and add required color, ratio mixing in 100: 10～30: 10～30: 10～30 is mixed well, water with vessel and to be filled in soft mold or soft or hard mould or hard mold or the gypsum mold, buckle the pressing mold tool, with the limit that a plurality of clips are clamped mould, above-mentioned hybrid resin can't be leached;
(3) drying: dry in the shade to just solidifying;
(4) die sinking tool: open mould, take out early-products;
(5) engraving: early-products is engraved as the goods that adhere to specification;
(6) cool off: goods are placed in the cold water soaked 30 minutes～1 hour;
(7) polishing: the corase grind machine, finish grind by hand, to the light cleaning;
(8) gluing: with above-mentioned mixed transparent resin goods are described repeatedly, till satisfied;
(9) drying: dried in the shade 10～30 minutes;
(1) japanning: with blowing varnish goods are sprayed repeatedly, dried in the shade 15～20 minutes, this step needs 2～3 times repeatedly.
Combination shaping 1:
(1) main body is shaped: by perforating bonding, joggle, grafting method, on the steel construction main body, allow body reach design standard required article combination;
(2) engraving: adhesive has been carved, cleaned up;
(3) gluing adds diluent with transparent resin and adds curing agent and mix and to mix well, and describes repeatedly on goods, to the effect that adheres to specification;
(4) polishing: carry out with fine sandpaper, from thick number to thin number, to the light cleaning;
(5) drying: dried in the shade 30 minutes～1 hour;
(6) drying: with being sprayed on the duplicate from spraying paint, dried in the shade 15～20 minutes, this step need be carried out 2～3 times repeatedly;
2, model: the preparation method of artificial landscape stalactite solution cavity according to claim 1 is characterized in that described cast material is that wood, 801 glue add the shape that land plaster=100: 40～70 or foundry loam, rubber sculpture become designing requirement.
3, main body bonding: the preparation method of artificial landscape stalactite solution cavity according to claim 1 is characterized in that described binding material is that 302 glue or 502 glue add talcum powder and add saw wood ash=100: 10～30: 10～30.
4, moulding: the method for manufacturing technology of artificial landscape clock breast solution cavity according to claim 1 is characterized in that described Modeling Material is reinforcing bar or steel pipe or iron wire or iron pipe or iron nail or fastener or copper wire or copper pipe.
5, putty: artificial landscape stalactite solution cavity according to claim 1 process for making, it is characterized in that described putty material is that transparent resin adds diluent and adds curing agent and add talcum powder and add required color=100: 10～30: 10～30: 10～30: 10～30 or atom ash and add curing agent and add required color=100: 10～30: 10～30.
6, soft mold: the process for making of artificial landscape stalactite solution cavity according to claim 1 is characterized in that described soft model material is that silicon rubber adds curing agent=100: 5～20.
7, hard mold and hollow mould: the process for making of artificial landscape clock breast jade solution cavity according to claim 1, it is characterized in that described hard mold and hollow mould material are that resin adds ketone slurry and adds and buy liquid and add talcum powder=100: 10～30: 10～30: 10～30 and add two layers of fine glass fibre cloth, one deck thick glass fibre cloth.
8, imitative stalactite: the process for making of artificial landscape stalactite solution cavity according to claim 1 is characterized in that described stalactite material is that transparent resin adds diluent and adds curing agent and add required color=100: 1030: 10～30: 10～30.
9, go up coloring agent: the process for making of ornaments according to claim 1 or artificial stalactite solution cavity is characterized in that described coloring agent material is that transparent resin adds diluent and adds curing agent.