KR101707621B1 - Preparation of concrete sculptures that high completeness cost savings - Google Patents
Preparation of concrete sculptures that high completeness cost savings Download PDFInfo
- Publication number
- KR101707621B1 KR101707621B1 KR1020140164451A KR20140164451A KR101707621B1 KR 101707621 B1 KR101707621 B1 KR 101707621B1 KR 1020140164451 A KR1020140164451 A KR 1020140164451A KR 20140164451 A KR20140164451 A KR 20140164451A KR 101707621 B1 KR101707621 B1 KR 101707621B1
- Authority
- KR
- South Korea
- Prior art keywords
- mold
- concrete
- molding
- primary
- sculpture
- Prior art date
Abstract
본 발명은
a) 점토나 유토, 나무,스티로폼 중의 어느 하나로 조소를 하여 조형물의 원형을 만드는 단계;
b) 상기 조형물의 원형에 합성수지를 입혀 1차 몰드를 만드는 단계;
c) 상기 1차 몰드를 샌딩이나 그라인딩으로 수정하는 단계;
d) 상기 1차 몰드를 조각으로 분리하는 단계;
e) 상기 조각으로 분리된 1차 몰드의 형틀을 만드는 단계;
f) 상기 조각으로 분리된 1차 몰드의 형틀을 볼트를 이용해서 조립하는 단계;
g) 상기 조립된 형틀의 높은 위치부분 및 모서리부는 1~3㎝로 구멍을 뚫는 단계;
h) 상기 조립된 조형물의 형틀 안에 철근을 엮어 보강하는 단계;
i) 상기 조형물의 형틀 안에 콘크리트를 타설하는 단계;
j) 상기 조형물의 형틀 내부에 바이브레이터를 사용하여 g)단계에서 생성한 구멍까지 콘크리트를 밀어 올리는 단계;
k) 상기 콘크리트가 굳은 후 조형물의 형틀을 떼어내는 단계;
l) 상기 형틀에서 떼어낸 조형물의 형틀조립부에 생긴 콘크리트 상의 연결부를 연삭으로 수정하는 단계;
m)상기 콘크리트 상에 묽게 한 도색액을 붓으로 바르는 1차 도색단계;
n)상기 1차 도색한 콘크리트 상의 겉면을 스프레이건으로 2차 도색단계; 를 포함하여 완성된 조형물은, 평평하고 넓은 부분 및 단순한 부분은 천연소재에 비하여 저렴하고 가볍고 외관이 미려하며 시공이 간편하며 내구성이 뛰어나고 방습, 내식성 등의 특징이 있는 유리섬유강화플라스틱(FRP)를 사용하여 직접 형틀을 만들고, 각진 부분 및 복잡한 부분은 실리콘으로 먼저 형틀을 만들고 실리콘 형틀 부분을 다시 유리섬유강화플라스틱(FRP)형틀로 이중으로 적충하여 만들어 조형물 완성시까지 시간이 절약되고 제조공정이 단순화해 비용 절감 효과가 있으며 생산성이 향상되고 작업효율성이 뛰어나며, 조립된 조형물의 형틀의 높은 위치 부분 및 모서리부는 1~3㎝로 구멍을 뚫어 미세한 부분까지 콘크리트를 밀어올려 단단하면서 견고한 조형물이 만들어지고 두 번 도색을 함으로써 색채감 및 시각적 효과를 극대화시킨다.The present invention
a) making a prototype of a sculpture by scouring with clay, oil, wood or styrofoam;
b) forming a primary mold by applying a synthetic resin to the mold of the molding;
c) modifying the primary mold by sanding or grinding;
d) separating said primary mold into pieces;
e) forming a mold of the primary mold separated by the piece;
f) assembling a mold of the primary mold separated by the piece using a bolt;
g) piercing the high position portion and the corner portion of the assembled mold 1 to 3 cm;
h) reinforcing the reinforcing bars in the mold of the assembled sculpture;
i) casting concrete into a mold of the molding;
j) using a vibrator inside the mold of the molding to push the concrete up to the hole created in step g);
k) removing the mold of the molding after the concrete is hardened;
l) modifying the connection portion on the concrete formed in the mold assembly part of the molding removed from the mold by grinding;
m) a primary painting step of applying a thinned paint on the concrete with a brush;
n) painting the surface of the primary colored concrete with a spray gun; (FRP), which is cheap, light, beautiful in appearance, simple in construction, durable, and resistant to moisture and corrosion, compared with natural materials, It is used to make a mold directly, angled parts and complex parts are made into a mold first with silicone, and silicon mold parts are re-doubled with a glass fiber reinforced plastic (FRP) mold to save time until the completion of molding and the manufacturing process is simplified It is cost effective, productivity is improved, work efficiency is excellent, and the high position part and corner part of the assembled sculpture are pierced with 1 ~ 3 ㎝ and the concrete is pushed up to the fine part to make hard and strong sculpture. The coloring and the visual effect are maximized by performing the coloring.
Description
본 발명은 인공조형물 제작시 조형물의 단순한 부분과 넓은 부분은 FRP로 직접 형틀을 제작해 제조 공정을 줄이고 조립된 형틀의 높은 부분 및 모서리 부위에 구멍을 뚫어 콘크리트를 채워 견고하고 단단하면서 완성도가 높은 콘크리트 조형물을 제조하는 제조방법에 관한 것이다.
In the present invention, when manufacturing an artificial sculpture, a simple part and a wide part of a sculpture are made of a FRP to reduce a manufacturing process, and a hole is formed in a high part and a corner of an assembled mold to fill a concrete, And a manufacturing method of manufacturing a sculpture.
일반적으로 건물 실내외를 장식하기 위하여 설치하는 건축물에는 인조바위, 동물모양조형물, 인조나무 등등 여러 가지 형태의 조형물이 설치되고 있으며, 이러한 조형물의 소재로, 석재, 목재와 같은 천연소재와 유리섬유강화플라스틱(FRP), 스티로폼, 폴리우레탄, 실리콘몰드 등과 같은 소재가 사용되고 있다.Generally, various types of building materials such as artificial rocks, animal-shaped buildings, artificial trees, etc. are installed in the buildings to be used for decorating indoor and outdoor buildings. Natural materials such as stone and wood, glass fiber reinforced plastic (FRP), styrofoam, polyurethane, silicone mold and the like are used.
이중 유리섬유강화플라스틱(FRP)는 천연소재에 비하여 저렴하고 가볍고 외관이 미려하며 성형형성이 우수하고 시공이 간편하며 디테일은 떨어지나 내구성이 뛰어나고 방습, 내식성 등의 특성이 있어 널리 사용되고 있다.Double glass-fiber reinforced plastic (FRP) is inexpensive, lightweight, beautiful in appearance, has excellent molding formability, is easy to construct, has low durability, and is widely used because of its durability and corrosion resistance.
실리콘몰드는 디테일이 요구되는 작업일 경우에 사용이 용이하고, 석고는 표면질감이 우수하고 채색성이 좋아 단품으로 간단한 작업시, 또는 원형을 빨리 작업할 경우에 이용되지만, 쉽게 파손되는 단점이 있다.Silicone mold is easy to use in case of work requiring detail, and gypsum is excellent in surface texture and coloring property and is used for simple work or simple work of circular work, but it is easily broken .
건축 및 조경 기술의 발달과 관심이 고조됨에 따라 다양한 조형물에 대한 소비가 늘어나고 있다.As the development and interest in architecture and landscaping technology grows, so does the consumption of various sculptures.
이러한 조형물은 합성수지 등의 수지로 만들어지거나 또는 대리석 등을 조각하여 제작된다.Such a molding is made of a resin such as a synthetic resin or is made by carving marble or the like.
이러한 조형물들 중 합성수지를 이용하여 만들어진 조형물의 경우 시간이 경과되면 자외선에 의해 변성되어 쉽게 부서지는 단점이 있고, 대리석으로 만들어진 조형물의 경우 고가의 대리석을 사용하면 재료비 상승의 요인이 된다.Among these sculptures, the sculptures made of synthetic resin have a disadvantage that they are easily broken by ultraviolet rays after a lapse of time, and in the case of sculptures made of marble, expensive marbles cause a rise in material cost.
이러한 단점을 줄이기 위해 일반 FRP로 성형한 몰드를 이용한 조형물 제작 방법은 주 몰드와 보조 몰드로 구성된 몰드로 만들어지고, 주 몰드의 경우 내면에 조형물의 형상이 형성되어 조형 재료가 채워져 조형물을 성형하는 역할을 하고, 보조 몰드는 부 몰드의 강도를 보강하기 위한 수단으로 사용되나, 특히 조형물이 보여지는 면에서 역 경사가 질 경우 즉, 깊이 파인 부분에 설치되어 주 몰드를 지지하는 역할을 한다.In order to reduce such disadvantages, a molding method using a mold molded by a general FRP is made of a mold composed of a main mold and an auxiliary mold, and in the case of a main mold, a shape of a molding is formed on the inner surface to form a molding The auxiliary mold is used as a means for reinforcing the strength of the secondary mold. In particular, when the backside slope is observed on the surface where the molding is seen, the secondary mold is installed at the depth-pitched portion and supports the main mold.
또한 조형물 제작시 실리콘으로 형틀을 만든 다음 다시 FRP를 입히는 과정을 거치기 때문에 비용과 시간이 많이 소요되고 있다.In addition, it takes a lot of time and cost because molds are made from silicone when they are manufactured, and then they are coated with FRP again.
일반적으로 콘크리트 조형물의 경우 실리콘 조각 몰드를 쓰지 않고 석고 조각 몰드를 사용하기 때문에 바이브레이타 등을 강하게 사용할 경우, 석고 몰드가 깨짐으로 콘크리트가 몰드의 구석진 부분까지 채워지지 못하는 문제가 있고, 몰드의 연결부분으로 콘크리트 물이 누출되어 완성된 조형물의 모양이 일정하지 않거나 표면이 세밀하지 않을 뿐만 아니라 강도 또한 현저히 떨어지는 단점이 있었으며, 몰드의 내부에 콘크리트를 타설할 때 조형물의 돌출된 부분 중 위로 향한 부분에는 콘크리트가 완전히 충진되지 않는 문제가 있다.
Generally, in the case of a concrete molding, since a plaster mold is used without using a silicon piece mold, there is a problem that when the vibrator is strongly used, the concrete is not filled up to the corner portion of the mold due to the breakage of the plaster mold, There is a disadvantage in that the shape of the finished sculpture is not constant or the surface is not fine and the strength is also remarkably low. When concrete is poured into the mold, the upward part of the protruding part of the sculpture There is a problem that the concrete is not completely filled.
상기와 같은 문제점을 해결하기 위해 본 발명은 평평하고 넓은 부분 및 단순부는 직접 유리섬유강화플라스틱(FRP)로 직접 형틀을 만들기 때문에 시간 및 비용을 절감하는 콘크리트 조형물을 제공하는 것을 목적으로 한다.
In order to solve the above-mentioned problems, it is an object of the present invention to provide a concrete molding which saves time and costs because flat, wide and simple parts make direct molds with direct glass fiber reinforced plastic (FRP).
또한 바이브레이터를 사용해도 공기가 차 있어서 채워지지 못한 부분인 조립된 조형물 형틀의 높은 위치부분 및 모서리부는 1~3㎝로 구멍을 뚫어 공기를 밀어내면서 콘크리트가 채워져 완성도가 높고 깨끗한 콘크리트 조형물을 제공하는 것을 목적으로 한다.
In addition, the high position portion and the corner portion of the assembled sculptural form frame, which is a portion where air is not filled even when a vibrator is used, is pierced with a hole of 1 to 3 cm to push the air to provide concrete, thereby providing a high-quality and clean concrete sculpture The purpose.
상기 목적을 해결하기 위해서,In order to solve the above object,
a) 점토나 유토, 나무 스티로폼 중의 어느 하나로 조소를 하여 조형물의 원형을 만드는 단계;a) making a prototype of a sculpture by scooping it with clay, oat or wood styrofoam;
b) 상기 조형물의 원형에 합성수지를 입혀 1차 몰드를 만드는 단계;b) forming a primary mold by applying a synthetic resin to the mold of the molding;
c) 상기 1차 몰드를 샌딩이나 그라인딩으로 수정하는 단계;c) modifying the primary mold by sanding or grinding;
d) 상기 1차 몰드를 조각으로 하여 분리하는 단계;d) separating the primary mold into pieces;
e) 상기 조각으로 분리된 1차 몰드의 형틀을 만드는 단계;e) forming a mold of the primary mold separated by the piece;
f) 상기 조각으로 분리된 1차 몰드의 형틀을 볼트를 이용해서 조립하는 단계;f) assembling a mold of the primary mold separated by the piece using a bolt;
g) 상기 조립된 형틀의 높은 위치부분 및 모서리부는 1~3㎝로 구멍을 뚫는 단계;g) piercing the high position portion and the corner portion of the assembled mold 1 to 3 cm;
h) 상기 조립된 조형물의 형틀 안에 철근을 엮어 보강하는 단계;h) reinforcing the reinforcing bars in the mold of the assembled sculpture;
i) 상기 조형물의 형틀 안에 콘크리트를 타설하는 단계;i) casting concrete into a mold of the molding;
j) 상기 조형물의 형틀 내부에 바이브레이터를 사용하여 g)단계에서 생성한 구멍까지 콘크리트를 밀어 올리는 단계;j) using a vibrator inside the mold of the molding to push the concrete up to the hole created in step g);
k) 상기 콘크리트가 굳은 후 조형물의 형틀을 떼어내는 단계;k) removing the mold of the molding after the concrete is hardened;
l) 상기 형틀에서 떼어낸 조형물의 형틀조립부에 생긴 콘크리트 상의 연결부를 연삭으로 수정하는 단계;l) modifying the connection portion on the concrete formed in the mold assembly part of the molding removed from the mold by grinding;
m)상기 콘크리트 상에 묽게 한 도색액을 붓으로 바르는 1차 도색단계;m) a primary painting step of applying a thinned paint on the concrete with a brush;
n)상기 1차 도색한 콘크리트 상의 겉면을 스프레이건으로 2차 도색단계; 를 거쳐 완성도가 높은 콘크리트 조형물을 제조하여 본 발명을 완성하였다.
n) painting the surface of the primary colored concrete with a spray gun; To thereby complete the present invention.
평평하고 넓은 부분 및 단순한 부분은 천연소재에 비하여 저렴하고 가볍고 외관이 미려하며 시공이 간편하며 내구성이 뛰어나고 방습, 내식성 등의 특징이 있는 유리섬유강화플라스틱(FRP)를 사용하여 직접 형틀을 만들고, 각진 부분 및 복잡한 부분은 실리콘으로 먼저 형틀을 만들고 실리콘 형틀 부분을 다시 유리섬유강화플라스틱(FRP)형틀로 이중으로 적층하여 만들어 조형물 완성시까지 시간이 절약되고 제조공정이 단순화해 비용 절감 효과가 있으며 생산성이 향상되고 작업효율성이 뛰어나며, 조립된 형틀의 높은 위치 부분 및 모서리부는 1~3㎝로 구멍을 뚫어 미세한 부분까지 콘크리트를 밀어올려 단단하면서 견고한 조형물이 만들어지고 두 번 도색을 함으로써 색채감 및 시각적 효과를 극대화시킨다.
Flat, wide and simple parts are made of glass fiber reinforced plastic (FRP) which is cheap, light, beautiful in appearance, easy to install, durable and resistant to moisture and corrosion compared with natural materials, Partial and complex parts are made of silicone first and the silicon mold part is double laminated with glass fiber reinforced plastic (FRP) mold to save time until completion of molding and simplify the manufacturing process. It is improved and the work efficiency is excellent. The high position part and the corner part of the assembled mold are pierced with holes of 1 ~ 3 cm, pushing the concrete up to the minute part, and the hard and strong molding is made. .
도 1은 본 발명품을 완성하기 위한 제조 공정을 나타낸 블럭도이다.1 is a block diagram showing a manufacturing process for completing the present invention.
a) 점토나 유토, 나무,스티로폼 중의 어느 하나로 조소를 하여 조형물의 원형을 만든다.a) Make a prototype of a sculpture by scouring with clay, oil, wood, or styrofoam.
상기 조형물의 원형은 점토나 유토, 나무, 스티로폼 중의 어느 하나로 조소를 한 것을 의미하는데 점성이 있는 점토나 기름에 섞인 흙인 유토, 나무, 또는 합성수지를 이용하여 만들어진다.The circular shape of the molding is made of clay, yuo, wood or styrofoam, and is made of viscous clay or earthy oil mixed with oil, wood, or synthetic resin.
그러나 합성수지를 이용하여 만들어진 조형물의 경우 시간이 지나면 자외선에 의해 변성되어 쉽게 부서지는 단점이 있고, 대리석으로 만들어진 조형물은 재료비 상승의 원인이 된다.However, in the case of a molding made using synthetic resin, it is easily deformed by ultraviolet rays over time and easily broken, and a molding made of marble causes a rise in material cost.
본 발명에서 조형물의 원형은 기름에 진흙을 섞은 유토를 사용한다.In the present invention, the prototype circular shape uses a mixture of oil and mud.
b) 상기 조형물의 원형에 합성수지를 입혀 1차 몰드를 만든다.b) A primary mold is made by applying a synthetic resin to the prototype prototype.
상기 1차 몰드는 조형물의 원형에 합성수지를 입혀 만든 것을 의미한다.The above-mentioned primary mold means that a circular shape of a molding is formed by applying synthetic resin.
c) 상기 1차 몰드를 샌딩이나 그라인딩으로 수정한다.c) Modify the primary mold by sanding or grinding.
1차 몰드에 보다 세밀한 조형물 제작을 위해 샌딩이나 그라인딩으로 수정하는 즉 연마하는 과정에 의해 조형물의 특징을 부각할 수 있고 ,세밀한 조형물의 제작을 위해 다듬는 과정이다.It is a process of refining for the production of fine sculpture, which can highlight the characteristics of the sculpture by the process of modifying or polishing the first mold by sanding or grinding to produce a more detailed sculpture.
d) 상기 1차 몰드를 조각으로 하여 분리한다. d) Separate the primary mold as a piece.
상기 단계에서는 쪽을 나누는 분할을 하고, 다수로 분리된 각 조각을 조형물의 원형으로부터 분리한다.In this step, the dividing division is performed, and each of the plurality of separated pieces is separated from the original shape of the molding.
1차 몰드를 조각으로 분리하는 과정에서 조형물의 원형의 재료로 사용한 점토나 유토, 나무 등을 제거된다.In the process of separating the primary mold into pieces, the clay, the soil, and the wood used as the circular material of the molding are removed.
1차 몰드를 조각으로 분리하여 구성함으로써 아주 세밀한 부분까지 조형물을 제작할 수 있고 외부로부터 충격이 가해져도 미세한 부분이 부러지는 것을 방지할 수 있다.By constructing the primary mold by separating it into pieces, it is possible to manufacture the molding to a very fine portion, and it is possible to prevent the minute portion from being broken even if an impact is applied from the outside.
e) 상기 조각으로 분리된 1차 몰드의 형틀을 만든다.e) A mold of the primary mold separated by the piece is made.
조각으로 분리된 1차 몰드에서 평평하고 넓은 부분 및 단순부는 FRP로 직접 형틀을 만드는 데, 상기 FRP는 유리강화플라스틱(Glass fiber reinforced plastic)으로, 유리섬유, 탄성섬유, 콘크리트 등의 방향족 나이론섬유와 불포화 폴리에스터, 에폭시수지 등의 열경화성수지를 결합한 물질이며, 콘크리트의 상부에 도포 되어 외부충격과 장력 강도를 증가시키는 것을 특징으로 한다.The FRP is a glass fiber reinforced plastic, which is made of glass fiber, elastic fiber, concrete, and other aromatic nylon fibers, and the like. An unsaturated polyester, or an epoxy resin, and is applied to the top of the concrete to increase external impact and tensile strength.
또한 각진 부분, 굽어진 부분,뽀족한 부분 미세한 부분 및 복잡한 부분은 실리콘으로 직접 형틀을 만들고 그 위에 FRP로 중첩하여 형틀을 만든다.In addition, the angled part, the curved part, the fine part and the complicated part are formed by directly making a mold with silicon and superimposing it with FRP on the mold.
기존의 기술은 모양이나 크기 복잡하거나 미세한 부분에 상관없이 모두를 실리콘으로 직접 형틀을 만든 다음 그 위에 중첩하여 FRP를 발라서 형틀을 완성하였다.Conventional technology forms a mold directly to silicon with all shapes and sizes, regardless of complexity or fineness, and then superimposed on it to complete FRP.
그러나 본 발명에서는 조형물의 모양이나 구조에 따라 나누어 분리하여 형틀을 만드는데,복잡하거나 미세한 부분은 실리콘으로 조형물의 형틀을 만들고, 평평하거나 면이 넓은 곳은 직접 FRP로 형틀을 만들어 조형물 제작 시간을 단축하고 비용절감의 효과를 동시에 얻을 수 있다.However, according to the present invention, the mold is separated by dividing it according to the shape and the structure of the molding, and the complicated or fine part is made of silicone and the mold is made into the mold. The effect of cost reduction can be obtained at the same time.
각진 부분 및 복잡한 부분의 내층은 실리콘으로 제작함으로써 실리콘이 조형물 모형의 미세한 부분까지 덮혀 보다 미세한 형틀을 제작할 수 있는데, 실리콘 형틀만으로는 콘크리트를 지지할 수 없기 때문에 이를 지지하기 위하여 실리콘 형틀 외면에 FRP형틀을 중첩하여 도포한다. Since the inner layer of the angled part and the complicated part is made of silicon, silicon can be covered to the fine part of the molding model to make a finer mold. Since the silicon mold can not support the concrete, Overlapping.
각진부분 및 복잡한 부분의 형틀의 내층은 상온에서 경화되는 액상 RTV(Room Temperature Vulcanizing) 실리콘으로 구성되고, 외층은 액상유리섬유강화플라스틱(FRP ;Fiberglass Reinforced Plastics)으로 만들어진다.The inner layer of the molded part of the angled part and the complex part is made of liquid RTV (Room Temperature Vulcanizing) silicone which is cured at room temperature, and the outer layer is made of FRP (Fiberglass Reinforced Plastics).
각진 부분 및 복잡한 부분을 실리콘으로 형성하는 이유는 형틀의 내면이 탄성을 갖음으로써 형틀을 조형물의 원형으로부터 분리할 때 작은 유격이 생겨 용이하게 분리할 수 있고, 조형물을 제작할 때 조형물 재료가 소성된 상태에서 형틀을 분리할 때에도 실리콘의 탄성에 의한 작은 유격에 의해 조형물로부터 용이하게 분리할 수 있게 하기 위한 것이다.The reason for forming the angled portion and the complicated portion with silicon is that the inner surface of the mold is elastic so that a small clearance is generated when the mold is separated from the mold of the mold, so that the mold can be easily separated, So that the mold can be easily separated from the molding by a small clearance due to the elasticity of silicon.
각진 부분 및 복잡한 부분을 실리콘형틀에 FRP형틀을 중첩시키면 실리콘 형틀에 콘크리트를 타설할 때 실리콘형틀의 형상이 변하는 것을 방지하고 견고한 형틀을 제조할 수 있다.When the FRP frame is superimposed on the silicon frame with the angled portion and the complicated portion, the shape of the silicon frame can be prevented from changing when the concrete is poured into the silicon frame, and a rigid frame can be manufactured.
콘크리트가 양생하면 형틀을 콘크리트에서 용이하게 분리하기 위해서 콘크리트와 형틀분리가 용이하게 하기 위해서 이형제인 식용유나 오일을 바른다.When the concrete is cured, mold oil or oil is applied to easily separate the concrete from the concrete in order to facilitate separation of the concrete from the concrete.
f) 상기 조각으로 분리된 1차 몰드의 형틀을 볼트를 이용해서 조립한다.f) Assemble the mold of the primary mold separated by the piece with a bolt.
상기 단계에서 분리한 1차 몰드의 형틀조각이 서로 다른 조각과 연결할 때 연결부재인 볼트를 이용해 고정한다.When the mold pieces of the primary mold separated in the above step are connected to different pieces, they are fixed by using a bolt which is a connecting member.
다수의 조각으로 분리된 형틀 조각은 볼트를 이용하여 연결하여 하나의 조형물의 형틀을 만든다.The plural pieces of the mold piece are connected by using the bolts to make a mold of one molding.
다수개의 형틀 조각을 조립하여도 무방하고, 일반적으로 작은 조형물은 일체로 성형된 형틀을 사용하여도 무방하다.A plurality of mold pieces may be assembled. In general, a mold may be formed by integrally molding a small mold.
g) 조립된 조형물 형틀의 높은 위치부분 및 모서리부는 1~3㎝로 구멍을 뚫는 단계;g) piercing the assembled sculptor with a high position portion and a corner portion of 1 to 3 cm;
상기 단계를 거치면서 시멘트를 타설하는 과정에서 바이브레이터 등과 같은 진동 발생수단을 이용하여 진동이 가해져도 공기가 들어있는 부분인 콘크리트가 채워질 수 없는 부분까지 콘크리트가 채워질 수 있게 콘크리트를 밀어 올린다.In the process of placing the cement through the above steps, the vibration generating means such as a vibrator is used to push the concrete so that the concrete can be filled up to the portion where the air can not be filled even if the vibration is applied.
또한 손가락 발가락 등과 같은 미세하고 세밀한 부분까지 시멘트가 채워져 외부로부터 충격이 가해져도 미세한 부분이 부러지는 것을 방지할 수 있다.In addition, fine and fine parts such as a finger toe are filled up with cement, so that it is possible to prevent a minute portion from being broken even when an impact is applied from the outside.
굴곡이 심한 조형물을 용이하게 제작할 수 있을 뿐만 아니라 제작이 용이하다.It is not only easy to produce a molding with severe bending but also easy to manufacture.
타설되는 콘크리트가 상방으로 돌출된 부분, 미세한 부분까지 채워져 완성도가 높은 조형물이 제작된다.The concrete part to be poured upwards is filled up to the minute part, and the highly finished sculpture is manufactured.
조립된 조형물 형틀의 상단 모서리 부분에 구멍을 형성하여 내부에 있는 공기가 배출될 수 있게 함으로써 내부에 채워지는 콘크리트가 높은 부분 및 돌출된 부분까지 채워질 수 있게 한다.By forming a hole in the upper corner portion of the assembled sculpture mold, air inside can be discharged, so that the filled concrete can be filled up to the high portion and the protruding portion.
h) 조립된 조형물의 형틀 안에 철근을 엮어 보강한다.h) Reinforcing reinforcing bars in the frame of the assembled sculpture.
조형물이 안정적으로 지지되게 하기 위해 기초가 되는 철근을 엮어 보강한다.Reinforcing bases are reinforced by reinforcing the foundation so that the building can be stably supported.
i) 철근을 엮어 보강한 조립된 조형물의 형틀안에 콘크리트를 타설한다.i) Concrete is placed in a mold of assembled sculpture reinforced by weaving reinforcing bars.
상기 과정을 거침으로써 조형 재료를 타설하여 굳혀서 조형물을 제작함으로써 보다 견고하고 정밀한 조형물을 제작할 수 있다.By performing the above process, the molding material is poured and hardened to produce the molding, thereby making it possible to manufacture a more rigid and precise molding.
j) 바이브레이터를 사용하여 g)단계에서 생성한 구멍까지 콘크리트를 밀어 올린다.j) Using a vibrator, push the concrete up to the hole created in step g).
조형물 형틀 안에 콘크리트를 타설하는 데 타설하는 과정에서 바이브레이터 등과 같은 진동 발생수단을 이용하여 콘크리트에 진동이 가해지게 함으로써 콘크리트가 골고루 채워지게 하고 콘크리트 중에 포함된 기포가 배출될 수 있다.In the process of pouring concrete into the molding form frame, vibration is applied to the concrete by using a vibration generating means such as a vibrator, so that the concrete can be evenly filled and the bubbles contained in the concrete can be discharged.
바이브레이터를 사용하여 진동을 시키면 형틀 내부의 각진 부분이나 미세한 부분가지 콘크리트가 채워질 수 있다.When using a vibrator to vibrate, the angles inside the mold can be filled with minute portions of concrete.
j) 콘크리트가 굳은 후 조립된 조형물의 형틀을 떼어낸다.j) After the concrete has set, remove the mold of the assembled sculpture.
콘크리트가 충분히 굳으면 조립된 조형물의 형틀을 조형물로부터 분리한다.When the concrete is sufficiently hardened, the mold of the assembled molding is separated from the molding.
본 발명에서는 콘크리트와 형틀분리가 용이하게 하기 위해서 이형제인 오일 이나 식용유를 사용하는데, 미끄럽기 때문에 분리가 용이하고, 흑연을 이용하기도 하는 데 흑연은 층상을 이루고 있어 윤활제, 감마제, 활마제로도 사용된다.In the present invention, oil or edible oil, which is a mold release agent, is used in order to facilitate separation of concrete and a mold. Since it is slippery, separation is easy and graphite is used. Graphite is used as a lubricant, .
k) 상기 형틀에서 떼어낸 조형물의 형틀조립부에서 생긴 콘크리트상의 연결부를 연삭으로 수정한다.k) Modify the connection part of the concrete formed in the mold part of the moldings removed from the mold by grinding.
상기와 같은 과정을 거친 조형물의 덧칠해진 홈부분의 콘크리트를 제거하고 보다 세밀한 조형물의 제작을 위해 콘크리트상의 연결부를 연삭으로 수정하여 보다 표면이 고르고 매끈하게 조형물을 완성할 수 있다.In order to remove the concrete of the overlaid groove portion of the molding after the above-described process and to modify the connection portion of the concrete on the concrete in order to manufacture a finer molding, the surface of the molding can be completed smoothly and smoothly.
조립된 조형물의 형틀조각의 연결부분으로 콘크리트가 누출되어 완성된 조형물의 모양이 일정하지 않거나 표면이 세밀하지 않을 경우에는 도색을 두 번 하여도 질감도 저하되고 완성도가 감소하기 때문에 상기 과정을 거친다.If the shape of the completed molding is not uniform or the surface is not fine, the concrete is leaked due to the connection part of the mold piece of the assembled molding, and the texture is lowered and the completeness is decreased even if the painting is repeated twice.
완성된 조형물의 표면에 남아있는 가루나 원하지 않는 요철이 형성될 수 있기 때문에 요철 등을 그라인더 등을 이용하여 연마한다.Residual irregularities may be formed on the surface of the completed molding, so the irregularities are polished using a grinder or the like.
l) 콘크리트상에 묽게 한 도색액을 붓으로 바르는 1차 도색한다.l) Paint the diluted paint on the concrete with a brush.
상기 단계에서는 붓으로 바르는 1차 도색단계를 거치는 이유는 붓에 의해서 칠이 꼼꼼히 하여 내부까지 깊숙이 스며드는 효과가 있다.In the above step, the primary coloring step of applying with the brush is effected by the paint brushing to penetrate deeply into the inside.
m) 1차 도색한 겉면을 스프레이건으로 도색하여 칠이 안벗겨지게 하고, 2차 도색하여 완성도가 높은 콘크리트 조형물이 제조된다.m) The primary painted surface is painted with a spray gun so that the surface is not peeled off, and the secondary paint is applied to produce a high quality concrete concrete.
1차 도색단계를 거친 조형물에 다시 스프레이건으로 2차 도색을 하여 백화현상을 방지하며, 표면 갈라짐이 방지되어 경량화된, 완성도가 높은 조형물을 제작할 수 있으며 겉면에 착색효과가 있어 칠이 청동색으로 안벗겨지고 오래간다.It can prevent whitening due to secondary painting with a spray gun on the primer after the first painting step, prevent the surface from cracking, and can make lightweight, high-quality sculpture, and has a coloring effect on the surface. Peel off and last.
2차 도색을 함으로써 조형물의 표면이 매끄럽고 질감이 살아있는 조형물이 제작되고, 실제와 유사한 이미지를 만들어 준다.Secondary painting makes the sculpture's surface smooth and textured, and makes a realistic image.
본 발명은 평평하고 넓은 부분 및 단순부는 FRP로 직접 조형물의 형틀을 만들고 각진부분, 돌출부분 및 복잡한 부분은 형틀이 되는 내층을 실리콘으로 제작하고, 외층은 FRP로 보강하여 형틀을 이중으로 적충하여 보다 견고한 형틀을 제공할 수 있을 뿐만 아니라 세밀한 부분까지 콘크리트가 채워져 견고하고 단단한 조형물을 제작할 수 있다.In the present invention, a flat, wide part and a simple part are made of FRP directly and a molding part of an angular part, a protruding part and a complicated part are made of silicone, and the outer layer is reinforced with FRP to double- In addition to providing a robust formwork, concrete can be filled up to a fine detail to create a solid and rigid sculpture.
본 발명에 따른 콘크리트는 시멘트와 모래 및 물이 혼합된 것으로써 통상의 콘크리트보다 시멘트를 많이 혼합하였으며, 점도를 높이기 위해 물의 양을 줄였다.The concrete according to the present invention is a mixture of cement, sand, and water, which contains much cement than ordinary concrete and reduces the amount of water to increase the viscosity.
본 발명의 조형물을 제조하기 위해서는 시멘트와 모래의 비율 중 시멘트의 비율은 높이고, 물의 함량을 낮게 함으로서 소성 후 조형물이 변형되는 것을 방지하였다.
In order to produce the sculpture of the present invention, the proportion of cement in the ratio of cement to sand is increased and water content is lowered, thereby preventing the molding from being deformed after firing.
본 발명품인 콘크리트 조형물 제작방법은 평평하고 넓은 부분 및 단순부는 FRP로 직접 형틀 제작을 하여 제조공정을 줄이고 조립된 형틀의 높은 위치부분 및 모서리부는 1~3㎝로 구멍을 뚫어 상기 부위까지 콘크리트가 타설되어 견고한 조형물이 제작되어 비용절감 효과가 있어서 산업상 이용가능성이 크다.
The manufacturing method of the concrete molding of the present invention is flat, and the wide part and the simple part are made of FRP and the manufacturing process is reduced. The high position part and the corner part of the assembled mold are pierced by 1 ~ 3 cm, This makes it possible to manufacture the robust sculpture, which is cost effective, and thus is highly industrially applicable.
Claims (3)
b) 상기 조형물의 원형에 합성수지를 입혀 1차 몰드를 만드는 단계;
c) 상기 1차 몰드를 샌딩이나 그라인딩으로 수정하는 단계;
d) 상기 1차 몰드를 조각으로 하여 분리하는 단계;
e) 상기 조각으로 분리된 1차 몰드의 형틀을 만드는 단계;
f) 상기 조각으로 분리된 1차 몰드의 형틀을 볼트를 이용해서 조립하는 단계;
g) 상기 조립된 조형물 형틀의 상단 및 모서리부는 1~3㎝로 구멍을 뚫는 단계;
h) 상기 조립된 조형물의 형틀 안에 철근을 엮어 보강하는 단계;
i) 상기 조형물의 형틀 안에 콘크리트를 타설하는 단계;
j) 상기 조형물의 형틀 내부에 바이브레이터를 사용하여 g)단계에서 생성한 구멍까지 콘크리트를 밀어 올리는 단계;
k) 상기 콘크리트가 굳은 후 조형물의 형틀을 떼어내는 단계;
l) 상기 형틀에서 떼어낸 조형물의 형틀조립부에 생긴 콘크리트 상의 연결부를 연삭으로 수정하는 단계;
m)상기 콘크리트 상에 묽게 한 도색액을 붓으로 바르는 1차 도색단계;
n)상기 1차 도색한 콘크리트 상의 겉면을 스프레이건으로 2차 도색단계;를 포함하고,
e)단계의 1차 몰드의 형틀 제조시 평평하고 넓은부분 및 단순부는 직접 FRP로 형틀을 만들고 각진 부분, 굽어진 부분, 뾰족한 부분 및 복잡한 부분 및 미세한 부분은 실리콘으로 내층의 형틀을 만들어 실리콘이 조형물 모형의 미세한 부분까지 덮여 보다 미세한 형틀을 제작하고 외층은 FRP로 적층하여 조각으로 분리된 1차 몰드의 형틀을 만드는 단계를 포함하고,
k) 단계에서는 분리가 용이하게 하기 위하여 이형제인 식용유 또는 오일을 바르는 단계;를 포함하고,
상기 실리콘은 상온에서 경화되는 액상 RTV(Room Temperature Vulcanizing) 실리콘인 것을 특징으로 하는 완성도가 높은 콘크리트 조형물의 제조방법.a) making a prototype of a sculpture by scouring with clay, oil, wood or styrofoam;
b) forming a primary mold by applying a synthetic resin to the mold of the molding;
c) modifying the primary mold by sanding or grinding;
d) separating the primary mold into pieces;
e) forming a mold of the primary mold separated by the piece;
f) assembling a mold of the primary mold separated by the piece using a bolt;
g) piercing the upper and the lower edge of the assembled sculptor with 1 ~ 3 cm;
h) reinforcing the reinforcing bars in the mold of the assembled sculpture;
i) casting concrete into a mold of the molding;
j) using a vibrator inside the mold of the molding to push the concrete up to the hole created in step g);
k) removing the mold of the molding after the concrete is hardened;
l) modifying the connection portion on the concrete formed in the mold assembly part of the molding removed from the mold by grinding;
m) a primary painting step of applying a thinned paint on the concrete with a brush;
n) painting the surface of the primary colored concrete with a spray gun,
In the production of the molds of the primary mold of step e), the flat, wide and simple parts make the mold with direct FRP, and the angled part, curved part, sharp part and complicated part and fine part form the inner layer mold with silicone, Forming a finer mold to cover the fine portion of the mold, and laminating the outer layer with FRP to form a mold of a primary mold separated into pieces,
(k) step of applying edible oil or oil, which is a mold release agent, in order to facilitate separation,
Wherein the silicon is liquid RTV (Room Temperature Vulcanizing) silicone which is cured at room temperature.