CN1597816A - 纳米复合材料墙面漆 - Google Patents
纳米复合材料墙面漆 Download PDFInfo
- Publication number
- CN1597816A CN1597816A CN 200410040262 CN200410040262A CN1597816A CN 1597816 A CN1597816 A CN 1597816A CN 200410040262 CN200410040262 CN 200410040262 CN 200410040262 A CN200410040262 A CN 200410040262A CN 1597816 A CN1597816 A CN 1597816A
- Authority
- CN
- China
- Prior art keywords
- agent
- granularity
- less
- kilogram
- nanometer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种纳米复合材料墙面漆,它是在现有技术上加入了纳米级特种功能助剂、纳米级硅丙乳液和高性能荷叶疏水乳液,并对颜填料等进行了复合改性,从而具有耐久、高抗沾污、自洁性强的特点,灰尘、赃物不易吸附,轻轻用水擦洗即能清除污渍,荷叶般的疏水性能,能长久保持墙面爽洁。
Description
(一)技术领域
本发明涉及一种墙体表面处理材料—墙面漆,属建材领域。
(二)背景技术
目前的墙面漆,一般是由水、颜料、填料、成膜助剂、润湿剂、分散剂、消泡剂、增稠剂、防冻剂等配制而成的组合物,具有墙体表面装饰效果,但其抗污性、耐磨耐擦性较差、硬度低、涂膜易老化、易失光、退色、变色、粉化,严重影响装饰效果和使用价值。
(三)发明内容
本发明所要解决的技术问题在于提供一种高耐候、抗污性强、耐磨耐擦洗、耐碱耐水、易清洗、硬度高、附着力强、色彩亮丽的墙面漆。
解决本发明技术问题的方案在于:按重量百分比包括下列组分:
水 10-30% 分散剂 0.2-0.8%
润湿剂 0.1-0.5% 消泡剂 0.1-0.5%
防腐剂 0.05-0.5% 防冻剂 0.5-3%
粒度小于50nm耐擦洗剂 0.5-2% 粒度小于50nm的SiO2 1-2%
粒度小于50nm的疏水剂 2-6% 香精 0.01-0.2%
PH调节剂 0.1-0.3% 钛白粉 5-25%
成膜助剂 0.5-3% 增稠流平剂 0.3-1%
粒度小于50nm的硅丙乳液或/和苯丙乳液 5-60%
其中:分散剂、湿润剂对颜填料进行调湿分散,使离子表面带电荷,防止各原料分散后从新凝聚,防腐剂的作用是防止产品在储藏过程中腐败变质,香精增加产品香气,消泡剂防止颜填料在高速分散过程中产生大量泡沫,防冻剂防止产品在低温保存时冻结,钛白粉为颜料,起遮盖作用,硅丙乳液、苯丙乳液为成膜物质,粘结颜填料,成膜助剂降低乳液的成膜温度,PH调节剂调节产品的酸碱度,利于和墙壁粘合,增稠流平剂增加产品的粘度,防止在存储过程中结块沉淀,SiO2提高硬度,增加抗紫外线、抗沾污能力,纳米耐擦洗剂,提高涂膜的硬度和韧性,增加耐擦洗性能,纳米疏水剂提高涂膜的憎水性,使其不粘水。
本发明还有下列组分:
粒度小于50nm的纳米抗沾污剂 0-1% 立德粉 0-15%
煅烧高岭土 0-5% 滑石粉 0-10%
轻钙 0-15%
立德粉为颜料,起遮盖作用,滑石粉、煅烧高龄土、轻钙为填料,增加颜料的遮盖力和产生一定厚度,纳米抗沾污剂,降低涂膜的表面能,提高涂膜的抗沾污能力。
本发明产品是这样来制备的:
(1)、在分散容器内加入配方水,然后依次加入分散剂、润湿剂、部分消泡剂、防腐剂、防冻剂、耐擦洗剂、SiO2混合均匀;
(2)、在高速(1000转/分)搅拌下,加入钛白粉,分散30-40分钟;
(3)、将前道工序制成的料浆在胶体磨内或砂磨机内研磨至细度30μm左右的料浆;
(4)、将硅丙乳液或/和苯丙乳液、PH调节剂、成膜助剂在低速(300转/分)搅拌下混合均匀;
(5)、将前述(3)磨好的料浆加入到步骤(4)制成的乳液中,在低速(300转/分)搅拌下依加入疏水剂、剩余的消泡剂、香精、增稠流平剂、,再低速(300转/分)分散30分钟;
(6)、将搅拌均匀的料浆用80目左右的筛网过滤即成。
本发明产品还可以这样来制备:在上述方法的第(1)步中,加入耐擦洗剂后,加入抗沾污剂,在第(2)步中,加入钛白粉后,再依次加入立德粉、煅烧高岭土、滑石粉、轻钙,其他步骤和方法与其相同。
本发明由于在现有技术上加入了纳米级特种功能助剂、纳米级硅丙乳液或/和高性能荷叶疏水性能的苯丙乳液,并对颜填料等进行了复合改性,从而使其耐磨性耐擦性较现有产品提高10倍、耐水性、耐碱性、耐人工老化性提高3-5倍,具有良好的疏水性、自洁性、硬度高等优点,灰尘、赃物不易吸附,轻轻用水擦洗即能清除污渍,荷叶般的疏水性能,能长久保持墙面爽洁。
(四)实施方式
下面结合实施例作进一步说明,但不仅限于此。
实施例1
按100千克原料配制:取
水 15千克
分散剂 台湾德谦化学品公司生产的DP-518(聚丙烯酸氨盐) 0.6千克
润湿剂 台湾德谦化学品公司生产的DP-18(直链非离子界面活性剂) 0.2千克
消泡剂 台湾德谦化学品公司生产的082(非硅酮含疏水粒子矿物油混合物) 0.4千克
防腐剂 台湾德谦化学品公司生产的MB-11(5-氯-2-甲基-4-异噻唑啉-3-
酮/2-甲基-4-异噻唑啉-酮=3/1) 0.1千克
纳米抗沾污剂 北京首创纳米有限公司生产的NZX-1 0.5千克
纳米耐洗剂 北京首创纳米有限公司生产的NCX-1 1.5千克
北京首创纳米有限公司生产的纳米SiO2 1千克
防冻剂 丙二醇 1.5千克
纳米疏水剂 北京首创纳米有限公司生产的SS-1 2.5千克
PH调节剂 台湾德谦化学品公司生产的DMAE(二甲基乙醇胺) 0.2千克
钛白粉 18千克
立德粉 10千克
煅烧高龄土 3千克
滑石粉 8千克
硅丙乳液 江苏国联化工生产的GHSN 5千克
苯丙乳液 北京首创纳米有限公司生产的SKSH-1 30千克
成膜助剂 醇脂-12 1.7千克
香精 0.1千克
增稠流平剂 台湾德谦化学品公司生产的WT-105A 0.7千克。
生产工艺步骤如下:
(1)、在分散容器内加入配方水,然后依次加入分散剂、润湿剂、部分消泡剂、防腐剂、丙二醇、耐擦洗剂、SiO2、,混合均匀;
(2)、在高速(1000转/分)搅拌下,加入钛白粉、立德粉、煅烧高龄土、滑石粉,分散30分钟;
(3)、将前道工序制成的料浆在砂磨机内研磨至25-30μm;
(4)、将硅丙乳液、苯丙乳液、PH调节剂、成膜助剂在低速(300转/分)搅拌下混合均匀;
(5)、将前述(3)的料浆加入到步骤(4)制成的乳液中,在低速(300转/分)搅拌下依次加入疏水剂、剩余的消泡剂、香精、增稠流平剂,再低速分散30分钟;
(6)、将搅拌均匀的料浆用80目左右的筛网过滤即成。
通过上述方法,得成品99.86千克,产品技术指标如下:
耐擦洗次数 12700次(GB/T9755-2001规定标准2000次,实验方法按此标准。以下引用相同)
耐水性 240小时无变化(96小时) 耐碱性100小时无变化(48小时)
耐人工老化性1100小时(250小时) 抗污染性无污染(无规定)
疏水性落水滚下,不留水迹(无规定)。
实施例2
按100千克原料配制:取
水 11千克
分散剂 美国Rohm&hass生产的Tamol731(二聚异丁烯顺丁烯二酸钠) 0.4千克
润湿剂 美国UCAR生产的CF-10(烷基芳基聚醚) 0.2千克
消泡剂 德国Henkel生产的SN-369(含有破泡成分的液体) 0.4千克
防腐剂 美国Rohm&hass公司生产的LXE(异噻唑啉酮) 0.05千克
纳米抗擦洗剂 北京首创纳米有限公司生产的NCX-1 0.8千克
纳米抗沾污 北京首创纳米有限公司生产的NZX-1 0.5千克
纳米SiO2 1千克
防冻剂 丙二醇 1.5千克
纳米疏水剂 北京首创纳米有限公司生产的SS-1 3.5千克
钛白粉 22千克
硅丙乳液 江苏国联化工生产的GHSN 55千克
成膜助剂 美国EASTMAN生产的TEXAND酯醇(2,2,4-三甲基-1,3-戊二醇
单异丁酸脂) 2.5千克
PH调节剂 美国ANGUS生产的AMP-95(2-氯基-2-甲基-1-丙醇) 0.1千克
香精 0.15千克
增稠剂 美国Rohm&hass生产的RM-8(增水改性聚氨脂) 0.3千克
流平剂 美国Rohm&hass生产的RM-1020PR(聚氨脂) 0.6千克。
生产工艺步骤如下;
(1)、在分散容器内加入配方水,然后依次加入分散剂、润湿剂、部分消泡剂、防腐剂、丙二醇、抗擦洗剂、纳米抗沾污剂、SiO2、混合均匀;
(2)、在高速搅拌下(1000转份),加入钛白粉、分散30分钟;
(3)、将前道工序制成的料浆在胶体磨内研磨至25-30μm;
(4)、将硅丙乳液、PH调节剂、成膜助剂在低速(300转/分)搅拌下混合均匀;
(5)、将前述(3)的料浆加入到步骤(4)制成的乳液中,在低速(300转/分)搅拌下依加入疏水剂、剩余的消泡剂、香精、增稠剂、流平剂、,再低速分散30分钟;
(6)、将搅拌均匀的料浆用80目左右的筛网过滤即成。
通过上述方法,得成品99.85千克,产品技术指标如下:
耐擦洗次数 16000次(GB/T9755-2001规定标准1000次,实验方法按此标准。以下引用相同)
耐水性 225小时无变化(96小时) 耐碱性110小时无变化(48小时)
耐人工老化性1140小时(250小时) 涂层耐温变性47次循环无变化(10次)
抗污染性 无污染(无规定) 疏水性落水滚下,不留水迹(无规定)。
实施例3
按100千克原料配制:取
水 20千克
分散剂 新光化工公司生产的XG-505(聚丙烯酸铵盐) 0.5千克
润湿剂 新光化工公司生产的XG-301(含羟基的共聚物) 0.3千克
消泡剂 新光化工公司生产的XG-039(矿物油,改性疏水硅) 0.4千克
防腐剂 新光化工公司生产的XG-3(有机杂环化合物) 0.2千克
纳米耐擦洗剂 北京首创纳米有限公司生产的NCX-1 1.5千克
纳米抗沾污剂 北京首创纳米有限公司生产的NZX-1 0.8千克
北京首创纳米有限公司生产的纳米SiO2 1.5千克
防冻剂 丙二醇 1.6千克
纳米疏水剂 北京首创纳米有限公司生产的SS-II 2千克
钛白粉 10千克
立德粉 15千克
滑石粉 6千克
轻钙 10千克
苯丙乳液 北京首创纳米有限公司生产的SKSH-1 28千克
成膜助剂 醇酯-12 1.1千克
PH调节剂新光化工公司生产的XG 95 0.2千克
香精 0.1千克
增稠流平剂 新光化工公司生产的XG-202(疏水改性聚氨脂) 0.8千克。
生产工艺步骤如下:
(1)、在分散容器内加入配方水,然后依次加入分散剂、润湿剂、部分消泡剂、防腐剂、纳米抗沾污剂、SiO2、丙二醇,混合均匀;
(2)、在高速搅拌下(1000转/分),加入钛白粉、立德粉、滑石粉、轻钙,分散30分钟;
(3)、将前道工序制成的料浆在胶体磨内研磨至25-30μm;
(4)、将苯丙乳液、PH调节剂、成膜助剂在低速(300转/分)搅拌下混合均匀:
(5)、将前述(3)的料浆加入到步骤(4)制成的乳液中,在低速(300转/分)搅拌下依加入疏水剂、剩余的消泡剂、香精、增稠流平剂、,再低速分散30分钟;
(6)、将搅拌均匀的料浆用80目左右的筛网过滤即成。
通过上述方法,得成品99.89千克,产品技术指标如下;
耐擦洗次数 16700次(GB/T9755-2001规定标准1000次,实验方法按此标准。以下引用相同)
耐水性 240小时无变化(96小时) 耐碱性100小时无变化(48小时)
耐人工老化性1100小时(250小时) 涂层耐温变性42次循环无变化(10次)
抗污染性 无污染(无规定) 疏水性落水滚下,不留水迹(无规定)
Claims (2)
1、一种纳米复合材料墙面漆,其特征在于:按重量百分比包括下列组分:
水 10-30% 分散剂 0.2-0.8%
润湿剂 0.1-0.5% 消泡剂 0.1-0.5%
防腐剂 0.05-0.5% 防冻剂 0.5-3%
粒度小于50nm耐擦洗剂 0.5-2% 粒度小于50nm的SiO2 1-2%
粒度小于50nm的疏水剂 2-6% 香精 0.01-0.2%
PH调节剂 0.1-0.3% 钛白粉 5-25%
成膜助剂 0.5-3% 增稠流平剂 0.3-1%
粒度小于50nm的硅丙乳液或/和苯丙乳液 5-60%
2、根据权利要求1所述的纳米复合材料墙面漆,其特征在于:它还有
粒度小于50nm的纳米抗沾污剂 0-1% 立德粉 0-15%
煅烧高岭土 0-5% 滑石粉 0-10%
轻钙 0-15%