CN1594176A - 一种原模具石膏粉组合料 - Google Patents

一种原模具石膏粉组合料 Download PDF

Info

Publication number
CN1594176A
CN1594176A CN 200410023377 CN200410023377A CN1594176A CN 1594176 A CN1594176 A CN 1594176A CN 200410023377 CN200410023377 CN 200410023377 CN 200410023377 A CN200410023377 A CN 200410023377A CN 1594176 A CN1594176 A CN 1594176A
Authority
CN
China
Prior art keywords
mould
terra alba
gypsum powder
weight part
weight parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200410023377
Other languages
English (en)
Other versions
CN1257125C (zh
Inventor
易湘如
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200410023377 priority Critical patent/CN1257125C/zh
Publication of CN1594176A publication Critical patent/CN1594176A/zh
Application granted granted Critical
Publication of CN1257125C publication Critical patent/CN1257125C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种原模具石膏粉配方,由α石膏粉、磺化三聚氰胺甲醛树脂、桃胶和白水泥组成,其特征在于:它按每100重量份α石膏粉中,掺0.4-0.65重量份磺化三聚氰胺甲醛树脂,0.07-0.12重量份的桃胶,5-10重量份的白水泥的配比量组成。在实际使用中,按石膏粉∶水=1∶0.4使用时,其搅拌时间为8-12分钟,可流动时间为8-12分钟,初凝时间为22-25分钟,终凝时间为40-45分钟;在干抗折强度和干抗压强度方面均有较大提高。用于陶瓷原模具制作时,既具有足够修模时间,而且也有良好强度。

Description

一种原模具石膏粉组合料
技术领域
本发明涉及一种原模具石膏粉组合料,属陶瓷生产用石膏模具的制作材料类。
背景技术
陶瓷石膏模具是陶瓷生产企业在生产过程中必须大量使用的原模具,目前大多数厂家均直接使用高强石膏(α石膏)制作。用这种α石膏原料制作模具时,由于产品标稠高,石膏粉与水之比通常在1∶0.5-0.55之间,有效搅拌时间只有3分钟,流动时间在3-4分钟;初凝时间为8-11分钟;终凝时间30分钟。同时,用上述α石膏制作的模具,由于材料上的固有原因,使产品膨胀系数大,为0.5%左右;其干抗折强度为7Mpa左右,干抗压强度为22Mpa左右。由于材料初凝时间过短、过快,搅拌时间和流动时间短,既不利于操作,也不利于对模具的修整;此外,由于强度不高,对模具的使用寿命带来不利影响。
因此,寻求一种合理、科学的原模具石膏粉配方,通过延长石膏粉初凝、流动时间,既使制作者有比较理想的模具整修时间,并较大地提高模具的使用性能,已经成为产品生产厂家和模具使用者的一种期望。
技术内容
本发明的目的:旨在提供一种科学、合理的原模具制作用石膏粉组合配方,希望用这种石膏粉在制作陶瓷制品原模具时,既要有较长的搅拌时间和流动时间,也有适当的初凝时间和终凝时间,最终希望在模具的综合强度方面也有较大的提高,为产品使用厂家带来积极的使用效果。
这种原模具石膏粉组合料,由α石膏粉、磺化三聚氰胺甲醛树脂、桃胶和白水泥组成,其特征在于:它按每100重量份α石膏粉中,掺0.4-0.65重量份磺化三聚氰胺甲醛树脂,0.07-0.12份的桃胶,5-10份的白水泥的配比量组成。
根据以上技术方案提出的这种原模具石膏粉组合料,与目前普遍使用的α石膏粉料相比,除继续保持无毒、无害的本质外,无论在搅拌时间、可流动时间、初凝时间、终凝时间,还是在干抗折强度或干抗压强度,都有十分明显的改善。使用该配料生产的原模具与祖模具的接触表面极其平整光滑,干燥后既达到不变形,而且结构坚实,强度也普遍提高35%;从而也提高了模具使用寿命。
具体实施方式
以下给出原模具石膏粉组合料的实施例:
实施例1
α石膏粉                100重量份
磺化三聚氰胺甲醛树脂    0.4重量份
桃胶                    0.07重量份
白水泥                  5.0重量份
实施例2
α石膏粉                100重量份
磺化三聚氰胺甲醛树脂    0.525重量份
桃胶                    0.095重量份
白水泥                  7.5重量份
实施例3
α石膏粉                100重量份
磺化三聚氰胺甲醛树脂    0.65重量份
桃胶                    0.12重量份
白水泥                  10重量份
如上述配比的可用于制作陶瓷原模具的石膏粉组合料标稠低,其实际使用中按石膏粉∶水=1∶0.4,搅拌时间为8-10分钟,比α法生产的石膏粉增长一倍左右;流动性好,可流动时间为8-12分钟,比α法生产的石膏粉提高一倍左右,便于浇制模具;初凝时间适当,为22-25分钟,比α法生产的石膏粉增长近二倍左右(且初凝时间可按用户要求配制);终凝时间为40-45分钟,比α法生产的石膏粉增长约30%,有足够时间修整模具,模具结构坚实,强度高。干抗折强度为10-11Mpa,比α法生产的石膏粉提高40%左右;干抗压强度为30-35Mpa,比α法生产的石膏粉提高35左右,(强度受初、终凝时间和环境温度的影响);膨胀系数小,只有0.008-0.1%左右,仅相当α法生产的石膏粉的膨胀系数的五分之一;且生产工艺简单,成本低,应用广泛。
上述这种原模具石膏粉组合料的使用方法如下:
将组合粉料以1∶0.4的比例投入水中,经浸泡1分钟以后,进行真空搅拌8-10分钟,即可用于浇模。待其初凝以后就可对模具进行修整,待模具完全干燥后便可作原模具使用。
原模具石膏粉新型配方配制的产品,完全可以达到目前国内陶瓷工艺品企业对原模具要求的各项技术参数,取代进口的和其它原模具原料;该产品用途广泛,还可用于类似陶瓷工艺品的产品模具的制作;全部原材料国内均有供应,而且产品生产成本低,工艺简单,市场需求量大,是社会效益和经济效益都很好的实用新型产品。
在上述组成原材料中,除a石膏粉是主要材料外,白水泥主要起增强剂作用,磺化三聚氰胺甲醛树脂是该混合粉料中的减水剂,也有增强剂或胶粘剂作用;而本发明案中所用的桃胶,既起到一定的胶粘剂作用,也起到一定的缓凝作用,是石膏制品成型中常用的一种添加剂。

Claims (1)

1、一种原模具石膏粉配方,由α石膏粉、磺化三聚氰胺甲醛树脂、桃胶和白水泥组成,其特征在于:它按每100重量份α石膏粉中,掺0.4-0.65重量份磺化三聚氰胺甲醛树脂,0.07-0.12重量份的桃胶,5-10重量份的白水泥的配比量组成。
CN 200410023377 2004-07-01 2004-07-01 一种原模具石膏粉组合料 Expired - Fee Related CN1257125C (zh)