CN102701690B - 一种高强度轮胎模铸造石膏粉及其制备工艺 - Google Patents
一种高强度轮胎模铸造石膏粉及其制备工艺 Download PDFInfo
- Publication number
- CN102701690B CN102701690B CN201210001880.5A CN201210001880A CN102701690B CN 102701690 B CN102701690 B CN 102701690B CN 201210001880 A CN201210001880 A CN 201210001880A CN 102701690 B CN102701690 B CN 102701690B
- Authority
- CN
- China
- Prior art keywords
- gypsum powder
- parts
- mould casting
- tire
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种高强度轮胎模铸造石膏粉及其制备工艺，该石膏粉由以下重量份数的原料制成：α-石膏粉100份，玻璃纤维15～30份，磺化三聚氰胺甲醛树脂0.3～0.5份，桃胶0.05～0.1份。本发明还包括所述高强度轮胎模铸造石膏粉的制备工艺。本发明高强度轮胎模铸造模石膏粉既有较长的有效搅拌时间和流动时间，又有适当的初凝时间和终凝时间，用其所制成产品强度高，可完全达到目前国内轮胎企业对轮胎铸造模具的各项技术参数要求，适应范围广，使用寿命长；其制备工艺简单，易于操作，有利于工业化生产。
Description
技术领域
本发明涉及一种轮胎模铸造石膏粉及其制备工艺，尤其是涉及一种高强度轮胎模铸造石膏粉及其制备工艺。
背景技术
目前，大多数轮胎铸造石膏模具生产厂家在制作轮胎铸造石膏模具时，都直接使用高强度石膏（α-石膏）粉为原材料，按质量比为1:0.5～0.55与水混合进行模具制作，由于所得石膏浆的稀稠程度较高，其有效搅拌时间只有3min，流动时间3～5min，初凝时间9min，终凝时间30min。此外，利用上述α-石膏粉所制得模具，膨胀系数大，约为0.5；干燥抗折强度低，为7MPa左右；干燥抗压强度也较低，22MPa左右。由于原材料初凝时间过短、有效搅拌时间和流动时间也较短，不仅给操作造成了一定的局限性，而且也不利于对所制得模具的修整，特别是由于强度不足，大大降低了模具的使用寿命。
发明内容
本发明的目的在于克服现有技术的不足，提供一种既有较长的有效搅拌时间和流动时间，又有适当的初凝时间和终凝时间，且用其所制得石膏模具强度得到较大改善的高强度轮胎模铸造石膏粉及其制备工艺。
本发明的目的是通过以下技术方案实现的：
本发明之高强度轮胎模铸造石膏粉，由以下重量份数的原料制成：α-石膏粉100份，玻璃纤维15～30份，磺化三聚氰胺甲醛树脂0.3～0.5份，桃胶0.05～0.1份。
进一步，所述高强度轮胎模铸造石膏粉的优选方案，由以下重量份数的原料制成：α-石膏粉100份，玻璃纤维25份，磺化三聚氰胺甲醛树脂0.4份，桃胶0.08份。
本发明之高强度轮胎模铸造石膏粉的制备工艺：首先按所述重量份数称取各组分原料，然后将各组分原料置于混料机中混合10～20min，即成。
所述原料中：α-石膏粉为主要材料；玻璃纤维为增强剂；磺化三聚氰胺甲醛树脂为减水剂，也起增强剂和胶黏剂作用；桃胶为添加剂，既有胶黏作用又有缓凝作用。
与现有α-石膏粉相比，本发明之高强度轮胎铸造模石膏粉，不仅在有效搅拌时间、流动时间、初凝时间和终凝时间方面有明显改善，而且所制得轮胎铸造模具的强度明显提高，可完全达到目前国内轮胎企业对轮胎铸造模具的各项技术参数要求，适应范围广，使用寿命长；其制备工艺简单，易于操作，有利于工业化生产。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例1
本实施例之高强度轮胎模铸造石膏粉，由以下重量份数的原料制成：α-石膏粉100份，玻璃纤维15份，磺化三聚氰胺甲醛树脂0.3份，桃胶0.05份。
制备：首先按所述重量份数称取各组分原料，然后将各组分原料置于混料机中混合15min，即成。
实施例2
本实施例之高强度轮胎模铸造石膏粉，由以下重量份数的原料制成：α-石膏粉100份，玻璃纤维25份，磺化三聚氰胺甲醛树脂0.4份，桃胶0.08份。
实施例3
本实施例之高强度轮胎模铸造石膏粉，由以下重量份数的原料制成：α-石膏粉100份，玻璃纤维30份，磺化三聚氰胺甲醛树脂0.5份，桃胶0.1份。
其制备工艺同实施例1。
所述实施例1-3的高强度轮胎模铸造石膏粉的使用方法：
将所述高强度轮胎模铸造石膏粉按质量比为1:0.4的比例投入水中，浸泡2min后，真空搅拌9min，即可用于浇模；初凝以后对模具进行修整，待模具完全干燥后，便可使用。
将实施例1-3所得高强度轮胎模铸造石膏粉和现有α-石膏粉分别按上述方法进行模具制作，对其有效搅拌时间、流动时间、初凝时间、终凝时间进行测试，并对其制成产品的干抗折强度、干抗压强度按QB/T 1640-1992分别进行测试，测试结果见表1。
表1
| 实施例1 | 实施例2 | 实施例3 | 现有α-石膏粉 | |
| 有效搅拌时间（min） | 6.2 | 7.1 | 6.8 | 3.5 |
| 流动时间（min） | 8.3 | 9.2 | 8.6 | 4.2 |
| 初凝时间（min） | 20.5 | 23.4 | 25.3 | 8.9 |
| 终凝时间（min） | 35.6 | 38.1 | 39.2 | 29.8 |
| 干燥抗折强度(MPa) | 9.2 | 12.0 | 10.6 | 7.3 |
| 干燥抗压强度(MPa) | 24.8 | 27.3 | 25.7 | 22.5 |
由上表实验结果可以看出，本发明之高强度轮胎模铸造石膏粉的有效搅拌时间可为6～7.1 min，比现有α-石膏粉的有效搅拌时间增长1倍多；流动性好，流动时间为8～10min，比现有α-石膏粉的流动时间增长1倍多，便于浇制模具；初凝时间为20～25min，比现有α-石膏粉的初凝时间增长近两倍；终凝时间为35～40min，比现有α-石膏粉的终凝时间也有所增长；用其所制成的轮胎模具的干燥抗折强度和干燥抗压强度，与用现有α-石膏粉所制成的轮胎模具相比，也有大大的提高，从而可提高使用寿命。
Claims (3)
1. 一种高强度轮胎模铸造石膏粉，其特征在于，由以下重量份数的原料制成：α-石膏粉100份，玻璃纤维15～30份，磺化三聚氰胺甲醛树脂0.3～0.5份，桃胶0.05～0.1份。
2.根据权利要求1所述的高强度轮胎模铸造石膏粉，其特征在于，由以下重量份数的原料制成：α-石膏粉100份，玻璃纤维25份，磺化三聚氰胺甲醛树脂0.4份，桃胶0.08份。
3.一种权利要求1所述的高强度轮胎模铸造石膏粉的制备工艺：首先按所述重量份数称取各组分原料，然后将各组分原料置于混料机中混合10～20min，即成。