CN1593934A - Method for avoiding image background color infiltration between colored drawing and applique of cadmium red vitreous enamel - Google Patents
Method for avoiding image background color infiltration between colored drawing and applique of cadmium red vitreous enamel Download PDFInfo
- Publication number
- CN1593934A CN1593934A CN 200410023309 CN200410023309A CN1593934A CN 1593934 A CN1593934 A CN 1593934A CN 200410023309 CN200410023309 CN 200410023309 CN 200410023309 A CN200410023309 A CN 200410023309A CN 1593934 A CN1593934 A CN 1593934A
- Authority
- CN
- China
- Prior art keywords
- porcelain
- colored drawing
- white
- look
- marble paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a kind of method that solve the bottom-appearing problem of colored drawing of the cadmium red vitreous enamel and of applique picture. Adopt the white porcelain using marble paper whose white porcelain using pigment is 0.01-0.6mm in thickness, cut out it according to the colored drawing of the cadmium red vitreous enamel or the picture figure stick colored marble paper, then stick it to the location of the porcelain that needs colored drawing or sticking colored marble paper, and roast it in the range between 900-700 DEG C to turn the location needing colored drawing or sticking colored marble paper into white with even and unanimous thickness which will cover the bright red bottom, do the colored drawing and stick colored marble paper on the white location, then roast it in the range between 900-700 DEG C to make it into the colored drawing of the cadmium red vitreous enamel or applique porcelain with lifelike color. The products of colored drawing of the cadmium red vitreous enamel and the applique picture produced in this invention is lifelike in color, strong in level sense, clear and vivid in the outline.
Description
Technical field
The invention belongs to the ceramic technology field, be specifically related to a kind of reveal the exact details method of look of cadmium red glaze porcelain colored drawing and applique picture that solves.
Background technology
Cadmium red glaze porcelain is bright-coloured large red because of its surface color, carries out colored drawing or post the look marble paper on this kind porcelain, and its bright-coloured large red can influence colored drawing or post the color of look marble paper picture, causes the picture color distortion.Past, solution to this problem is to want the picture position of colored drawing to be coated with the last layer glass white earlier at porcelain, about 800 ℃, bake then and burn, after the cooling, scribbling the position colored drawing or the decal paper of glass white, again with its roasting burning about 800 ℃, because it is thicker that glass white is coated with, and became uneven is even, causes picture lines metamorphopsic distortion, influences image quality.
Summary of the invention
Technical problem to be solved by this invention is to carry out colored drawing or post the look marble paper at bright-coloured bright red cadmium red glaze porcelain in the prior art, its bright-coloured large red influences colored drawing or posts the color of look marble paper picture, cause the distortion of picture lines, picture color distortion, influence the defective of image quality, a kind of reveal the exact details method of look of cadmium red glaze porcelain colored drawing and applique picture that solves is provided.
Solving technical scheme that the technology of the present invention problem adopted and be the reveal the exact details method of look of this solutions cadmium red glaze porcelain colored drawing and applique picture is to adopt white porcelain marble paper, its white porcelain is as the criterion bright red background color can be hidden with the thickness of pigment, it is big or small on demand, after the shape cutting, be attached to the position that this porcelain needs colored drawing or posts the look marble paper, in the roasting burning of 900-750 ℃ of scope, the position that is about to need colored drawing or post the look marble paper becomes the white of thickness uniformity, thereby bright-coloured bright red background color is hidden, carry out colored drawing or post the look marble paper at this white position again, 900-750 ℃ of roasting the burning, make color cadmium red glaze colored drawing true to nature or applique porcelain then.The porcelain that adopts white is 0.01-0.6mm with its white porcelain of marble paper with the thickness of pigment.
The colored drawing and the applique picture product color of the cadmium red glaze porcelain of producing with the present invention are true to nature, and stereovision is strong, clear-cut, lively.
The specific embodiment
The present invention solves the reveal the exact details method of look of cadmium red glaze porcelain colored drawing and applique picture, adopt the porcelain marble paper of white, its white porcelain is as the criterion bright red background color can be hidden with the thickness of pigment, and its white porcelain is generally 0.01-0.6mm with the thickness of pigment, adopts white porcelain commonly used to use.It is big or small on demand, after the shape cutting, be attached to the position that this porcelain needs colored drawing or posts the look marble paper, the porcelain that posts white is that the roasting porcelain that burns or post white is to bake burning in muffle kiln with roasting burning of the porcelain of marble paper in electrical kiln with roasting burning of the porcelain of marble paper, in the roasting burning of 900-750 ℃ of scope, the position that is about to need colored drawing or post the look marble paper becomes the white of thickness uniformity, thereby bright-coloured bright red background color is hidden, carry out colored drawing or post the look marble paper at this white position again, the porcelain that has carried out colored drawing at white position or posted the look marble paper is roasting in electrical kiln to be burnt or posts porcelain in muffle kiln roasting burn of the porcelain of white with marble paper, 900-750 ℃ of roasting the burning, make color cadmium red glaze colored drawing true to nature or applique porcelain.
The invention will be further described below in conjunction with embodiment, and embodiment 1 and embodiment 2 manufacture for adopting art methods, and embodiment 3 and embodiment 4 manufacture for adopting the inventive method:
Example 1: get a cadmium red glaze porcelain vase, peony and peony leaves picture that will colored drawing be delineated out outline line with pencil on vase, then deployed peach ceramic paint is depicted in the outline line inside-paint peony of peony with writing brush, be depicted in the ceramic paint of deployed green in the outline line of peony leaves with writing brush, draw peony leaves, after picture is all finished, put into electric furnace and be warming up to 800 ℃, be incubated 10 minutes, after the cooling, from stove, take out, should be peach peony, become peony, and green peony leaves has become yellow green, picture does not have deep or light variation, no stereovision.
Example 2: get a cadmium red glaze porcelain vase, peony and peony leaves picture that will colored drawing be delineated out outline line with pencil on vase, then, deployed glass white is applied in the outline line with writing brush, for fear of the look of revealing the exact details, the thickness that glass white is coated with is greater than 0.4mm, dries up with hair dryer, put into electric furnace, be warming up to 800 ℃, be incubated 10 minutes, after the cooling, be depicted in deployed pink ceramic paint on the glass white of peony with writing brush, deployed green ceramic pigment is depicted in writing brush on the glass white of peony leaves, then, puts into electric furnace, be warming up to 800 ℃, be incubated 10 minutes, after the cooling, from electric furnace, take out, peach peony, green peony leaves, color is true to nature, and deep or light variation is arranged, but the distortion of the profile of peony and peony leaves, whole stereovision is not strong.
Example 3: get a cadmium red glaze porcelain vase, the peony that will colored drawing and the profile of peony leaves are with pencil drawing (the ceramic Chinese white thickness of this white marble paper is 0.1mm) on the marble paper of white, cut peony and peony leaves white marble paper with scissors along outline line, it is attached to the position that the cadmium red glaze porcelain vase needs colored drawing, put into the electric furnace kiln, be warming up to 800 ℃, be incubated 10 minutes, after the cooling, respectively deployed pink and green ceramic pigment be depicted on peony and the peony leaves, put into the electric furnace kiln, be warming up to 800 ℃, be incubated 10 minutes, after the cooling, from the electric furnace kiln, take out, the peony that goes out of colored drawing is pink like this, and peony leaves be a green, and color is true to nature, stereovision is strong, clear-cut, vividly.
Example 4: get a cadmium red glaze porcelain vase, the picture profile that will paste pink peony and green peony leaves marble paper is with pencil drawing (the ceramic Chinese white thickness of this white marble paper is 0.1mm) on the marble paper of white, cut peony and peony leaves white marble paper with scissors along outline line, it is attached to the position that the cadmium red glaze porcelain vase needs colored drawing, put into the electric furnace kiln, be warming up to 800 ℃, be incubated 10 minutes, after the cooling, the marble paper picture that will be printed on pink peony and green peony leaves respectively is attached on the corresponding white peony and peony leaves, put into the electric furnace kiln, be warming up to 800 ℃, be incubated 10 minutes, after the cooling, from the electric furnace kiln, take out, post the peony that the look marble paper makes like this and be pink, peony leaves be a green, and color is true to nature, stereovision is strong, clear-cut, vividly.
Claims (8)
1, a kind of reveal the exact details method of look of cadmium red glaze porcelain colored drawing and applique picture that solves, it is characterized in that adopting the porcelain marble paper of white, its white porcelain is as the criterion bright red background color can be hidden with the thickness of pigment, after its cutting on demand, be attached to the position that this porcelain needs colored drawing or posts the look marble paper, in the roasting burning of 900-750 ℃ of scope, the position that is about to need colored drawing or post the look marble paper becomes the white of thickness uniformity, thereby bright-coloured bright red background color is hidden, carry out colored drawing or post the look marble paper at this white position again, 900-750 ℃ of roasting the burning, make color cadmium red glaze colored drawing true to nature or applique porcelain then.
2, a kind of reveal the exact details method of look according to claim 1 of cadmium red glaze porcelain colored drawing and applique picture that solves is characterized in that the white porcelain that adopts is 0.01-0.6mm with its white porcelain of marble paper with the thickness of pigment.
3, a kind of reveal the exact details method of look according to claim 1 and 2 of cadmium red glaze porcelain colored drawing and applique picture that solves, the porcelain that it is characterized in that posting white is a roasting burning in electrical kiln with roasting burning of the porcelain of marble paper.
4, a kind of reveal the exact details method of look according to claim 3 of cadmium red glaze porcelain colored drawing and applique picture that solves is characterized in that roasting burning of porcelain of having carried out colored drawing at white position or having posted the look marble paper is roasting burning the in electrical kiln.
5, a kind of reveal the exact details method of look according to claim 4 of cadmium red glaze porcelain colored drawing and applique picture that solves is characterized in that porcelain roasting temperature of burning in electrical kiln of having carried out colored drawing at white position or having posted the look marble paper is 800 ℃.
6, a kind of reveal the exact details method of look according to claim 1 and 2 of cadmium red glaze porcelain colored drawing and applique picture that solves, the porcelain that it is characterized in that posting white is a roasting burning in muffle kiln with roasting burning of the porcelain of marble paper.
7, a kind of reveal the exact details method of look according to claim 6 of cadmium red glaze porcelain colored drawing and applique picture that solves is characterized in that roasting burning of the porcelain that has carried out colored drawing at white position or posted the look marble paper is to burn in that muffle kiln is roasting.
8, a kind of reveal the exact details method of look according to claim 4 of cadmium red glaze porcelain colored drawing and applique picture that solves is characterized in that porcelain roasting temperature of burning in muffle kiln of having carried out colored drawing at white position or having posted the look marble paper is 800 ℃.