CN203093595U - Grisaille painting decorative porcelain product - Google Patents
Grisaille painting decorative porcelain product Download PDFInfo
- Publication number
- CN203093595U CN203093595U CN 201320134053 CN201320134053U CN203093595U CN 203093595 U CN203093595 U CN 203093595U CN 201320134053 CN201320134053 CN 201320134053 CN 201320134053 U CN201320134053 U CN 201320134053U CN 203093595 U CN203093595 U CN 203093595U
- Authority
- CN
- China
- Prior art keywords
- glaze
- grisaille painting
- grisaille
- millimeter
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to a grisaille painting decorative porcelain product which is produced by arranging a grisaille painting decorative pattern layer (3) inside a glaze layer (2) and by sintering a blank (1) and the glaze layer (2). The product is smooth and bright in surface, is completely integrated, is novel, natural and high in three-dimension feeling in pattern, rich in decorative effect and accurate in meaning expression, and a novel technique is provided for porcelain pattern decoration, so that the product has wide market prospects.
Description
Technical field
The utility model belongs to ceramic product and decorates the field, more specifically relates to a kind of grisaille painting decorating ceramic products.
Background technology
The grisaille painting wound was burnt in the clear Yongzheng's reign, originally was a kind of of porcelain overglaze color, and based on gorgeous black, the coloured silk material that is equipped with other is described pattern on the white glaze face, makes after low temperature (700-800 ℃) baking.
Grisaille painting develops into the modern times, art present and technology aspect bigger change has all been arranged.Aspect technology, developed into decoration under the glaze from the glaze decoration, firing temperature increases substantially.Color is that dominant hue develops into multiple color tones from gorgeous black also, and in general, the ceramic decoration effect of the artistic effect as modern, picture is elegant, color the is pleasant ink and wash suitable color all calls and is grisaille painting.
No matter being high temperature grisaille painting under low temperature grisaille painting (700-800 ℃) or the glaze, all is the comparatively complicated decorative technique of a kind of technology with grisaille painting is decorated and glazing is carried out step by step.As high temperature grisaille painting under the glaze, generally adopting elder generation on biscuit, to create on the creation, execute the bluish white glaze of high temperature again, at high temperature at last (＞1300 ℃) once are fired into porcelain, product has unique artistic effect, and bold and vigorous down color decoration of the ceramic glaze of Chu Xianing is exactly a kind of form of expression that the high temperature grisaille painting is decorated in recent years.
Yet because current ceramic grisaille painting decorative technique process implementing process is comparatively loaded down with trivial details, and then restricted the application of grisaille painting decorative technique in the ceramic decoration industry.
Summary of the invention
The technical problems to be solved in the utility model provides a kind of decorative pattern to be had nature, harmony, is rich in the grisaille painting decorating ceramic products of texture at random.
The technical solution of the utility model is: a kind of grisaille painting decorating ceramic products comprises that base substrate and glaze layer through the product that sintering obtains, is characterized in that: be provided with grisaille painting decorative pattern layer in the glaze layer.
Described glaze layer thickness is 0.18～1. 5 millimeter.
Described product is tabular when pottery, and the glaze layer thickness is preferably 0.8～1.2 millimeter.
When described product was the ampuliform pottery, the glaze layer thickness was preferably 0.3～0.5 millimeter.
When described product was special-shaped ceramics, the glaze layer thickness was preferably 1～1.5 millimeter.
The position of above-mentioned decorative pattern layer can be provided with according to the decorative effect needs.
The thickness of described decorative pattern layer is 0.05～0.5 millimeter.
The thickness of described decorative pattern layer center is 0.3～0.5 millimeter, and the thickness of both sides is 0.05～0.1 millimeter.
It is application background that the utility model is decorated with the ceramic high temperature grisaille painting, on a large amount of experimental basis, to high-temperature glaze, high temperature decorating colour, multiple additives is carried out rational allocation, the technology barriers of glazing after the first illuminated during grisaille painting is decorated under the breakthrough high-temperature glaze, illuminated and glaze decoration are combined together, reach illuminated glazing simultaneously, glazing is the technological effect of illuminated simultaneously, abbreviate, represent artistic style very, product burns till smoothly light of rear surface, decorative pattern unique style, style is changeable at random, smooth nature, be rich in texture and anima, decorative effect is abundant, passes expectation and reaches accurately.
Description of drawings
Fig. 1 is a kind of grisaille painting decorating ceramic products of the utility model section structure schematic diagram.
1, base substrate, 2, the glaze layer, 3, the decorative pattern layer.
The specific embodiment
Below in conjunction with the accompanying drawing 1 and the specific embodiment the utility model is described in further detail.
The first step: select surface tension≤340mNm for use
-1, melt temperature is that 1250 ℃ high temperature glaze slip is standby;
Second step: add 1wt% dextrin and 0.1wt%CMC in the glaze slip that the first step is chosen after, to expect: ball: water=1:1.8:0.65 carries out ball milling, crosses 325 mesh sieves behind the ball milling and obtains the modification glaze slip;
The 3rd step: in the refractory ceramics colorant, add 0.4wt% oleic acid, put into ball mill and mix the back oven dry, cross 250 mesh sieves and obtain modification refractory ceramics colorant;
The 4th step: the 3rd modification refractory ceramics colorant that make of step is spilled in the modification glaze slip that second step made, makes high temperature grisaille painting glaze,
The 5th step: adopt the pattern that applies glazing, dip in high temperature grisaille painting glaze with writing brush, on the tabular ceramic body 1 after the biscuiting, apply thickness and be 1 millimeter glaze layer 2, utilizing the shape and the thickness of writing brush control decorative pattern layer 3 simultaneously is 0.07～0.3 millimeter, treat to burn till in 1280 ℃ of high temperature after glaze layer 2 drying, obtain the grisaille painting decorating ceramic products.
The first step: select surface tension≤340mNm for use
-1, melt temperature is that 1280 ℃ high temperature glaze slip is standby;
Second step: add 1wt% dextrin and 0.1wt%CMC in the glaze slip that the first step is chosen after, to expect: ball: water=1:1.8:0.65 carries out ball milling, crosses 325 mesh sieves behind the ball milling and obtains the modification glaze slip;
The 3rd step: in the refractory ceramics colorant, add 0.4wt% oleic acid, put into ball mill and mix the back oven dry, cross 250 mesh sieves and obtain modification refractory ceramics colorant;
The 4th step: the 3rd modification refractory ceramics colorant that make of step is spilled in the modification glaze slip that second step made, makes high temperature grisaille painting glaze,
The 5th step: adopt the pattern that applies glazing, dip in high temperature grisaille painting glaze with writing brush, on the ampuliform ceramic body 1 after the biscuiting, apply thickness and be 0.4 millimeter glaze layer 2, utilizing the shape and the thickness of writing brush control decorative pattern layer 3 simultaneously is 0.08～0.4 millimeter, treat to burn till in 1300 ℃ of high temperature after glaze layer 2 drying, obtain the grisaille painting decorating ceramic products.
The first step: select surface tension≤340mNm for use
-1, melt temperature is that 1300 ℃ high temperature glaze slip is standby;
Second step: add 1wt% dextrin and 0.1wt%CMC in the glaze slip that the first step is chosen after, to expect: ball: water=1:1.8:0.65 carries out ball milling, crosses 325 mesh sieves behind the ball milling and obtains the modification glaze slip;
The 3rd step: in the refractory ceramics colorant, add 0.4wt% oleic acid, put into ball mill and mix the back oven dry, cross 250 mesh sieves and obtain modification refractory ceramics colorant;
The 4th step: the 3rd modification refractory ceramics colorant that make of step is spilled in the modification glaze slip that second step made, makes high temperature grisaille painting glaze,
The 5th step: adopt the pattern that applies glazing, dip in high temperature grisaille painting glaze with writing brush, on the non-conventional type ceramic base substrate 1 after the biscuiting, apply thickness and be 1.3 millimeters glaze layer 2, utilizing the shape and the thickness of writing brush control decorative pattern layer 3 simultaneously is 0.09～0.5 millimeter, treat to burn till in 1320 ℃ of high temperature after glaze layer 2 drying, obtain the grisaille painting decorating ceramic products.
The glaze that this grisaille painting decorating ceramic products adopted can be all kinds of refractory ceramics glaze such as clear frit, opaque glaze, crystalline glaze; selected colorant can be the refractory ceramics colorant of any color; so the grisaille painting decorating ceramic products that the utility model is protected is various in style; the above; it only is the preferable specific embodiment of the utility model; but the utility model protection domain is not limited thereto; be equal to replacement or change according to the technical solution of the utility model and inventive concept thereof, all should be encompassed within the protection domain of the present utility model.
Claims (8)
1. a grisaille painting decorating ceramic products comprises that base substrate (1) and glaze layer (2) through the product that sintering obtains, is characterized in that: be provided with grisaille painting decorative pattern layer (3) in glaze layer (2).
2. according to right 1 described a kind of grisaille painting decorating ceramic products, it is characterized in that: described glaze layer (2) thickness is 0.18～1. 5 millimeter.
3. a kind of grisaille painting decorating ceramic products according to claim 2 is characterized in that: described product is tabular when pottery, and glaze layer (2) thickness is preferably 0.8～1.2 millimeter.
4. a kind of grisaille painting decorating ceramic products according to claim 2 is characterized in that: when described product was the ampuliform pottery, glaze layer (2) thickness was preferably 0.3～0.5 millimeter.
5. a kind of grisaille painting decorating ceramic products according to claim 2 is characterized in that: when described product was special-shaped ceramics, glaze layer (2) thickness was preferably 1～1.5 millimeter.
6. according to the arbitrary described a kind of grisaille painting decorating ceramic products of claim 1-5, it is characterized in that: the position of described decorative pattern layer (3) can be provided with according to the decorative effect needs.
7. a kind of grisaille painting decorating ceramic products according to claim 6 is characterized in that: the thickness of described decorative pattern layer (3) is 0.05～0.5 millimeter.
8. a kind of grisaille painting decorating ceramic products according to claim 7 is characterized in that: the thickness of described decorative pattern layer (3) center is 0.3～0.5 millimeter, and the thickness of both sides is 0.05～0.1 millimeter.