CN1570211A - 镀银纤维织物的制备方法 - Google Patents

镀银纤维织物的制备方法 Download PDF

Info

Publication number
CN1570211A
CN1570211A CN 200410024079 CN200410024079A CN1570211A CN 1570211 A CN1570211 A CN 1570211A CN 200410024079 CN200410024079 CN 200410024079 CN 200410024079 A CN200410024079 A CN 200410024079A CN 1570211 A CN1570211 A CN 1570211A
Authority
CN
China
Prior art keywords
silver
fabric
terylene
plating
plated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200410024079
Other languages
English (en)
Other versions
CN1276127C (zh
Inventor
夏芝林
夏龙泉
孙煊伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200410024079 priority Critical patent/CN1276127C/zh
Publication of CN1570211A publication Critical patent/CN1570211A/zh
Application granted granted Critical
Publication of CN1276127C publication Critical patent/CN1276127C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种镀银纤维织物的制备方法，属于真空镀和电镀技术领域。其制备步骤为：基体采用化纤织物或涤纶无纺布；基体在氮气或氩气的保护下，采用离子镀膜法镀银或不锈钢；采用传统的电镀塑料的技术工艺在基材表面再连续镀镍、铜或银；然后将上述材料，冲洗、烘干、切边、计量、切割、包装即完成工序。该方法可连续化生产，成品率高，质量好，成本低、镀层无杂质，其生产的镀银纤维织物屏蔽性能好。广泛用于高档手机、PDP－TV、LCD－TV和技术含量高的电子技术产品，以及军事保密系统的电子通信设备、仪器，在现代电子战争中可做为电子设备的屏蔽。

Description

镀银纤维织物的制备方法
技术领域
本发明涉及一种对绝缘、阻燃、软体材料(包括涤纶织物、涤纶无纺布)进行导电处理、制备软体电磁屏蔽织物的方法。属于真空镀和电镀技术领域。
背景技术
随着电子技术的发展，电子、电气设备、PDP-TV、LCD-TV及办公自动化系统获得了广泛的应用，由于这些设备的增加，电磁干扰也在增加，电磁环境越来越恶劣，对电子仪器造成的信号失真、失误屡见不鲜，其损失难以估量，同时电磁辐射，对人体健康的影响也越来越严重。当前市场上流行的镀铜镍的导电布，已不能满足电子设备、精密仪器快速发展的需要及人民健康生活的需要。日本、南韩、美国镀铜银导电布、纯镀银导电布、镀银涤纶纤维被广泛采用到PDP-TV、LCD-TV、军用电子产品和高端电子产品中。在这些领域将逐渐取代当前的镀镍导电布，在民用的屏蔽服用制品中，也被广泛采用镀银织物，镀(铜)镍织物将被逐渐陶汰，主要是镍金属对人体皮肤产生刺激过敏。但目前含银的纤维织物，其工艺生产方法普遍采用的化学镀银工艺。这种工艺存在镀液污染环境、成本高、附着力差等缺点。
发明内容
为了克服上述技术缺陷，本发明的目的是提供一种镀银纤维织物的制备方法，该方法可连续化生产，成品率高，质量好，成本低、镀层无杂质，其生产的镀银纤维织物屏蔽性能好。
本发明的主要技术方案是：该种镀银纤维织物的制备方法，其步骤为，
1、基体：化纤织物或涤纶无纺布。
所述化纤织物是，涤纶平纹布、涤纶方格布、涤纶针织物、涤纶丝网布，纤维丝单丝直径0.006-0.099mm；规格18dtex/1f-36f至75dtex/1f-36f；所述涤纶无纺布是涤纶无纺布或涤纶压花无纺布，厚度0.04mm-0.50mm、密度18g-250g/m2。
2、上述基材在氮气或氩气的保护下，采用离子镀膜法镀银或不锈钢，温度120℃-164℃或176℃-200℃；真空度1.5×10-1Pa至8×10-5Pa，基材运行速度0.5-1.48米/分钟，银或不锈钢离子密度0.5-1.95克/m或2.55-4克/m2；基材表面电阻率R＝5Ω/CM-1MΩ/CM。
3、采用传统的电镀塑料的技术工艺在基材表面再连续镀镍、铜或银。对于镀镍、铜的基材最后再电镀一层银，材料的表面电阻率为0.006-0.08Ω/cm。
4、然后将上述材料，冲洗、烘干、切边、切割、计量、包装。
本发明与现有的技术相比，具有以下优良的效果。
1、与现有的镀铜镍导电布相比，具有极高的导电性能和柔韧性能，屏蔽效能可达到80DB以上，远高于当前市场的镀铜镍的导电布，可用于高档手机、PDP-TV、LCD-TV和技术含量高的电子技术产品，更加保证信息的安全性、机器的安全性，产品可用于军事保密系统的电子通信设备、仪器，在现代电子战争中可做为电子设备的屏蔽。
2、镀银布、镀银铜布、镀不锈钢银布可作为保健用品，如床上用品、保健服和电磁屏蔽服。
由于镀银纤维不断释放银离子，又因银离子具有非常高的生物活性，极易与其他物质相结合，故具有很强的杀菌功效，并除臭消除人体异味，调节人体体温和湿度，这是镀镍导电布所不具备的。
3、本工艺加工出的涤纶针织物，可进行二次加工，拆拉出单股丝(镀银导电纤维)再与普通的纤维交织成不同屏蔽效果的导电织物，供不同要求的消费者选择，克服了当前的镀铜镍织物存在的板结、硬度高、透气性不好的缺点，更适合电子仪器的电磁屏蔽件和电磁屏蔽服及各种制品，物别是在发达国家对颜料中的镍含量作出限量规定，对服装的镍含量也有严格的规定，镀银纤维织物的研制成功，对屏蔽服及民用屏蔽品的发展将具有划时代的意义。
4、可连续化生产，成品率高，质量好，成本低。与化学镀相比无污染、镀液封闭运行，环保性好。
具体实施方式
结合实例对本发明更进一步说明：
实施例1、镀银导电布的制备，包括如下步骤：
1、基体，涤纶织物，厚度0.082mm、宽1020mm，规格55dtex/24f，经纬线密度230T，纤维丝单丝直径0.008mm。
2、离子镀不锈钢，将基体在氩气保护下用离子镀膜法镀不锈钢，真空室温度164℃，真空度1.1×10-3Pa，基体运行速度1.48米/分钟，不锈钢离子密度1.9克/m2。
3、用当前的塑料电镀技术在上述材料上连续镀铜、银，形成不锈钢-铜-银的膜层结构。
4、然后将上述导电布冲洗、烘干、切边、分割计量包装。
实施例2、涤纶布镀银，步骤与实施例1所不同的是：先在涤纶布表面真空镀银，不再镀铜，则纤维表面形成纯银层，即镀银导电布。
实施例3，涤纶无纺布镀银，步骤如实施例1所不同的是：基体是涤纶无纺布、基体表面镀银离子1.6克/m2。
实施例4，涤纶针织物上镀银，步骤如实施例1所不同的是：基体在真空室内运行速度每分钟1.2米，并且在基体烘干后分拆成单股线(镀银纤维)，再定型包装。
实施例5、镀银导电布的制备，包括如下步骤：
1、基体，涤纶平纹布，厚度0.11mm、宽1020mm，规格70dtex/24f，经纬线密度240T，纤维丝单丝直径0.010mm。
2、离子镀银，将基体在氩气保护下用离子镀膜法镀银，真空室温度180℃，真空度1.3×10-3Pa，基体运行速度1.2米/分钟，银离子密度3克/m2。
3、用当前的塑料电镀技术在上述材料上连续镀铜和银，形成银-铜-银的膜层结构。
4、然后将上述导电布冲洗、烘干、切边、分割计量包装。

Claims (4)

  1. 一种镀银纤维织物的制备方法，步骤如下：
    (1)基体：化纤织物或涤纶无纺布；
    所述化纤织物是，涤纶平纹布、涤纶方格布、涤纶针织物、涤纶丝网布，纤维丝单丝直径0.006-0.099mm；规格18dtex/1f-36f至75dtex/1f-36f；所述涤纶无纺布是涤纶无纺布或涤纶压花无纺布，厚度0.04mm-0.50mm、密度18g-250g/m2；
  2. (2)上述基材在氮气或氩气的保护下，采用离子镀膜法镀银或不锈钢，温度120℃-164℃或176℃-200℃；真空度1.5×10-1Pa至8×10-5pa，基材运行速度0.5-1.48米/分钟，银或不锈钢离子密度0.5-1.95克/m或2.55-4克/m2；基材表面电阻率R＝5Ω/CM-1MΩ/CM；
  3. (3)采用传统的电镀塑料的技术工艺在基材表面再连续镀镍、铜或银；对于镀镍或铜的基材最后再电镀一层银，材料的表面电阻率为0.006-0.08Ω/cm；
  4. (4)然后将上述材料，冲洗、烘干、切边、切割、计量、包装。
CN 200410024079 2004-05-10 2004-05-10 镀银纤维织物的制备方法 Expired - Fee Related CN1276127C (zh)