CN1276127C - 镀银纤维织物的制备方法 - Google Patents
镀银纤维织物的制备方法 Download PDFInfo
- Publication number
- CN1276127C CN1276127C CN 200410024079 CN200410024079A CN1276127C CN 1276127 C CN1276127 C CN 1276127C CN 200410024079 CN200410024079 CN 200410024079 CN 200410024079 A CN200410024079 A CN 200410024079A CN 1276127 C CN1276127 C CN 1276127C
- Authority
- CN
- China
- Prior art keywords
- silver
- matrix
- fabric
- plating
- terylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种镀银纤维织物的制备方法,属于真空镀和电镀技领域。其制备步骤为:基体采用化纤织物或涤纶无纺布;基体在氮气或氩气的保护下,采用离子镀膜法镀银或不锈钢;采用传统的电镀塑料的技术工艺在基材表面再连续镀镍、铜或银;然后将上述材料,冲洗、烘干、切边、计量、切割、包装即完成工序。该方法可连续化生产,成品率高,质量好,成本低、镀层无杂质,其生产的镀银纤维织物屏蔽性能好。广泛用于高档手机、PDP-TV、LCD-TV和技术含量高的电子技术产品,以及军事保密系统的电子通信设备、仪器,在现代电子战争中可做为电子设备的屏蔽。
Description
技术领域
本发明涉及一种对绝缘、阻燃、软体材料(包括涤纶织物、涤纶无纺布)进行导电处理、制备软体电磁屏蔽织物的方法。属于真空镀和电镀技术领域。
背景技术
随着电子技术的发展,电子、电气设备、PDP-TV、LCD-TV及办公自动化系统获得了广泛的应用,由于这些设备的增加,电磁干扰也在增加,电磁环境越来越恶劣,对电子仪器造成的信号失真、失误屡见不鲜,其损失难以估量,同时电磁辐射,对人体健康的影响也越来越严重。当前市场上流行的镀铜镍的导电布,已不能满足电子设备、精密仪器快速发展的需要及人民健康生活的需要。日本、南韩、美国镀铜银导电布、纯镀银导电布、镀银涤纶纤维被广泛采用到PDP-TV、LCD-TV、军用电子产品和高端电子产品中。在这些领域将逐渐取代当前的镀镍导电布,在民用的屏蔽服用制品中,也被广泛采用镀银织物,镀(铜)镍织物将被逐渐陶汰,主要是镍金属对人体皮肤产生刺激过敏。但目前含银的纤维织物,其工艺生产方法普遍采用的化学镀银工艺。这种工艺存在镀液污染环境、成本高、附着力差等缺点。
发明内容
为了克服上述技术缺陷,本发明的目的是提供一种镀银纤维织物的制备方法,该方法可连续化生产,成品率高,质量好,成本低、镀层无杂质,其生产的镀银纤维织物屏蔽性能好。
本发明的主要技术方案是:该种镀银纤维织物的制备方法,其步骤为,
1、基体:化纤织物或涤纶无纺布。
所述化纤织物是,涤纶平纹布、涤纶方格布、涤纶针织物、涤纶丝网布,纤维丝单丝直径0.006-0.099mm;规格18dtex/1f-36f至75dtex/1f-36f;所述涤纶无纺布是涤纶无纺布或涤纶压花无纺布,厚度0.04mm-0.50mm、密度18g-250g/m2。
2、上述基体在氮气或氩气的保护下,采用离子镀膜法施镀,温度120℃-164℃或176℃-200℃;真空度1.5×10-1Pa至8×10-5Pa,基体运行速度0.5-1.48米/分钟,离子密度0.5-1.95克/m2或2.55-4克/m2;基体表面电阻率R=5Ω/cm-1MΩ/cm,所镀物质为银或不锈钢;
3、采用传统的电镀塑料的技术工艺在基体表面再连续镀镍、铜或银。对于镀镍、铜的基体最后再电镀一层银,材料的表面电阻率为0.006-0.08Ω/cm。
4、然后将上述材料,冲洗、烘干、切边、切割、计量、包装。
本发明与现有的技术相比,具有以下优良的效果。
1、与现有的镀铜镍导电布相比,具有极高的导电性能和柔韧性能,屏蔽效能可达到80DB以上,远高于当前市场的镀铜镍的导电布,可用于高档手机、PDP-TV、LCD-TV和技术含量高的电子技术产品,更加保证信息的安全性、机器的安全性,产品可用于军事保密系统的电子通信设备、仪器,在现代电子战争中可做为电子设备的屏蔽。
2、镀银布、镀银铜布、镀不锈钢银布可作为保健用品,如床上用品、保健服和电磁屏蔽服。
由于镀银纤维不断释放银离子,又因银离子具有非常高的生物活性,极易与其他物质相结合,故具有很强的杀菌功效,并除臭消除人体异味,调节人体体温和湿度,这是镀镍导电布所不具备的。
3、本工艺加工出的涤纶针织物,可进行二次加工,拆拉出单股丝(镀银导电纤维)再与普通的纤维交织成不同屏蔽效果的导电织物,供不同要求的消费者选择,克服了当前的镀铜镍织物存在的板结、硬度高、透气性不好的缺点,更适合电子仪器的电磁屏蔽件和电磁屏蔽服及各种制品,物别是在发达国家对颜料中的镍含量作出限量规定,对服装的镍含量也有严格的规定,镀银纤维织物的研制成功,对屏蔽服及民用屏蔽品的发展将具有划时代的意义。
4、可连续化生产,成品率高,质量好,成本低。与化学镀相比无污染、镀液封闭运行,环保性好。
具体实施方式
结合实例对本发明更进一步说明:
实施例1、镀银导电布的制备,包括如下步骤:
1、基体,涤纶织物,厚度0.082mm、宽1020mm,规格55dtex/24f,经纬线密度230T,纤维丝单丝直径0.008mm。
2、离子镀不锈钢,将基体在氩气保护下用离子镀膜法镀不锈钢,真空室温度164℃,真空度1.1×10-3Pa,基体运行速度1.48米/分钟,不锈钢离子密度1.9克/m2 。
3、用当前的塑料电镀技术在上述基体上连续镀铜、银,形成不锈钢-铜-银的膜层结构。
4、然后将上述导电布冲洗、烘干、切边、分割计量包装。
实施例2、涤纶布镀银,步骤与实施例1所不同的是:先在涤纶布表面真空镀银,不再镀铜,则纤维表面形成纯银层,即镀银导电布。
实施例3,涤纶无纺布镀银,步骤如实施例1所不同的是:基体是涤纶无纺布、基体表面镀银离子1.6克/m2。
实施例4,涤纶针织物上镀银,步骤如实施例1所不同的是:基体在真空室内运行速度每分钟1.2米,并且在基体烘干后分拆成单股线(镀银纤维),再定型包装。
实施例5、镀银导电布的制备,包括如下步骤:
1、基体,涤纶平纹布,厚度0.11mm、宽1020mm,规格70dtex/24f,经纬线密度240T,纤维丝单丝直径0.010mm。
2、离子镀银,将基体在氩气保护下用离子镀膜法镀银,真空室温度180℃,真空度1.3×10-3Pa,基体运行速度1.2米/分钟,银离子密度3克/m2。
3、用当前的塑料电镀技术在上述材料上连续镀铜和银,形成银-铜-银的膜层结构。
4、然后将上述导电布冲洗、烘干、切边、分割计量包装。
Claims (1)
1.一种镀银纤维织物的制备方法,步骤如下:
(1)基体:化纤织物或涤纶无纺布;
所述化纤织物是,涤纶平纹布、涤纶方格布、涤纶针织物、涤纶丝网布,纤维丝单丝直径0.006-0.099mm;规格18dtex/1f-36f至75dtex/1f-36f;所述涤纶无纺布是涤纶无纺布或涤纶压花无纺布,厚度0.04mm-0.50mm、密度18g-250g/m2;
(2)上述基体在氮气或氩气的保护下,采用离子镀膜法施镀,温度120℃-164℃或176℃-200℃;真空度1.5×10-1Pa至8×10-5Pa,基体运行速度0.5-1.48米/分钟,离子密度0.5-1.95克/m2或2.55-4克/m2;基体表面电阻率R=5Ω/cm-1MΩ/cm,所镀物质为银或不锈钢;
(3)采用传统的电镀塑料的技术工艺在基体表面再连续镀镍、铜或银;对于镀镍或铜的基体最后再电镀一层银,材料的表面电阻率为0.006-0.08Ω/cm;
(4)然后将上述材料,冲洗、烘干、切边、切割、计量、包装。