CN1569716A - 夹金属装饰板的夹层玻璃及其生产工艺 - Google Patents

夹金属装饰板的夹层玻璃及其生产工艺 Download PDF

Info

Publication number
CN1569716A
CN1569716A CN 200410018112 CN200410018112A CN1569716A CN 1569716 A CN1569716 A CN 1569716A CN 200410018112 CN200410018112 CN 200410018112 CN 200410018112 A CN200410018112 A CN 200410018112A CN 1569716 A CN1569716 A CN 1569716A
Authority
CN
China
Prior art keywords
glass
thickness
intermediate coat
temperature
controlled
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200410018112
Other languages
English (en)
Other versions
CN1290788C (zh
Inventor
孙大海
潘伟
张立云
沈国全
胡永康
吕海良
盛强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Yaohua Pilkington Glass Group Co ltd
SHANGHAI YAOPI ENGINEERING GLASS CO LTD
Original Assignee
Yaohua-Pierjindun Glass Co Ltd Shanghai
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yaohua-Pierjindun Glass Co Ltd Shanghai filed Critical Yaohua-Pierjindun Glass Co Ltd Shanghai
Priority to CN 200410018112 priority Critical patent/CN1290788C/zh
Publication of CN1569716A publication Critical patent/CN1569716A/zh
Application granted granted Critical
Publication of CN1290788C publication Critical patent/CN1290788C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本发明采用EVA或SGP作为粘胶中间膜，并采用二次辊压法，或者是真空法生产工艺，生产一种夹金属中间膜玻璃，其玻璃结构是：玻璃板/有面胶粘材料EVA或SGP中间膜/金属装饰薄板/有机胶粘材料EVA或SGP中间膜/玻璃板；二次辊压法的生产工艺过程是：玻璃的外观和尺寸检查→35℃纯水清洗→热风烘干→在一定温湿度的净室内合片→一次加热→一次辊动预压→二次加热→二次辊动预压→质量检验→上高压釜车架→在高压釜中最终成形→产品逐片检验→产品包装。优点是，玻璃、有机中间膜(EVA、SGP)和金属装饰板结合非常牢固。其抗冲击、抗穿透和耐候等性能是普通PVB夹层玻璃的5倍以上，具有优异的安全、抗击飓风、防盗、防爆等性能。

Description

夹金属装饰板的夹层玻璃及其生产工艺
技术领域
本发明涉及一种采用辊压法或真空法生产的新型夹层玻璃产品，属于建筑材料技术领域。
背景技术
夹层玻璃作为一种安全玻璃已逐步被人们熟识和了解。普通夹层玻璃仅仅是将二片或更多片玻璃通过有机胶粘材料(中间膜)粘结在一起，起到安全、隔音和过滤紫外线的作用。通常使用的有机胶粘材料是PVB(聚乙烯醇缩丁醛)中间膜。
PVB(聚乙烯醇缩丁醛)中间膜是普通夹层玻璃最常用的有机胶粘材料，因其成本相对低、工艺成熟、产品性能稳定、粘结强度高、使用寿命长等特点，而被广泛地应用于建筑幕墙、护栏、门窗等领域。普通夹层玻璃的组成比较简单，即：
玻璃板+有机胶粘材料(PVB中间膜)+玻璃板
然而，PVB中间膜的性能虽好，但只能够和玻璃粘结，不能与金属粘结，因此PVB中间膜不可能用于“夹金属装饰板夹层玻璃”的设计和制作。
发明内容
为了解决夹金属装饰板夹层玻璃生产中的粘结问题，本发明采用EVA(聚乙烯醋酸乙脂)或SGP(商品名称为SentryGlas Plus，乙烯与甲基丙烯酸的共聚物)，作为有机胶粘中间膜，并采用二次辊压法，或者是真空法生产工艺，该玻璃线路构成是：
玻璃板/有机胶粘材料EVA或SGP中间膜/金属装饰板/有机胶粘材料EVA或SGP中间膜/玻璃板；
玻璃板的厚度为2mm～19mm；玻璃板可以是普通优质浮法玻璃、钢化或钢化热浸的热反射膜玻璃、低辐射膜(Low-e)玻璃等；玻璃板上可钻孔或不钻孔；玻璃钻孔的孔径不小于玻璃的标准厚度；
EVA中间膜的厚度为0.4～2.4mm；SGP中间膜的厚度为0.76mm～10.16mm；
金属装饰板的厚度为0.1mm～4mm，可以是冲孔网板或丝网的各种不锈钢、普通碳钢、镀锌钢、彩钢板、铝合金、铜合金等各类金属材料；用穿孔板时，穿孔板的开孔率可为20％～85％，孔径为1mm～100mm，孔心距为2mm～110mm，孔的排列为正方形、矩形、四边形或三角形。装饰板上的图形和图案可任意选择。
该玻璃的生产工艺采用二次辊压法，或者是真空法，二次辊压法的工艺过程是：
玻璃的外观和尺寸检查→35℃纯水清洗→热风烘干→在一定温湿度的净室内合片→一次加热→一次辊动预压→二次加热→二次辊动预压→质量检验→上高压釜车架→在高压釜中最终成形→产品逐片检验→产品包装；
其中：一次辊压工艺是：玻璃板面温度控制在30℃～60℃之间，辊压间隙控制在比夹胶玻璃总厚度小1～3mm之间，预压加热炉的温度控制在200℃～260℃之间，要求炉温加热元件温度控制在较低的温度400℃，玻璃线速度控制在比相同厚度正常夹胶玻璃快1.5～2.5倍的基础上，根据环境温度、相对湿度不同进行调整；
二次辊压工艺是：玻璃板面温度控制在65℃～90℃之间，辊压间隙控制在比夹胶玻璃总厚度小1～3mm之间。预压加热炉的温度控制在250℃～360℃之间，要求炉温加热元件温度控制在较高的温度700℃，玻璃线速度控制在比相同厚度正常夹胶玻璃快0.5～1.0倍的基础上，根据环境温度、相对湿度不同进行调整；
真空法的工艺过程是：
玻璃的外观和尺寸检查→35℃纯水清洗→热风烘干→在一定温湿度的净室内合片→真空预压(真空环或真空袋)→质量检验→上高压釜车架→在高压釜中最终成形→产品逐片检验→产品包装；
其中：抽真空保温温度：90～140℃，根据玻璃厚度、中间膜厚度、中间膜材料进行调整，保温时间控制在30分钟到60分钟之间；根据玻璃厚度、中间膜厚度、中间膜材料进行调整；真空度控制在30托以下。
本发明的优点是，
1、该结构具有外观简练、美观、多样化、个性化、安全和节能等特点。
2、该结构的夹层玻璃可以控制阳光能量进入室内。通过改变金属装饰板的材质和类型，改变孔的直径和疏密程度，调节太阳光透过和反射比例，达到良好的节能效果。
3、该结构中玻璃、有机中间膜(EVA、SGP)和金属装饰板结合非常牢固。其抗冲击、抗穿透和耐侯等性能是普通PVB夹层玻璃的5倍以上，具有优异的安全、抗击飓风、防盗、防爆等性能。
4、该结构具有良好的隔音和吸音能力。
5、该结构具有良好的防紫外线、耐侯性和化学稳定性。
6、该结构产品具有玻璃和金属两种色泽，是良好的装饰材料，适用于建筑外立面的围护和室内的装饰装潢。
附图说明
附图是本发明夹金属装饰板的夹层玻璃结构图。
具体实施方式
实例1：
申请人上海耀华皮尔金顿玻璃股份有限公司(简称：“SYP”)在生产“东方艺术中心”项目的“夹金属穿孔板的SGP夹层玻璃”过程中，采用二次辊压工艺方法，在工艺上，采用二对压辊，二次预压，压辊间隙根据玻璃总厚度-2mm的方式控制，上片清洗机工艺及水质、合片室工艺及环境控制情况与普通PVB夹层玻璃的生产基本保持一致。
下片段控制情况如下：
  1#炉表温℃   2#炉表温℃   玻璃线速度(m/min)   玻璃表面温度℃
  第一次辊压   230～250   290～310   2.5   35～55
第二次辊压   230～250   290～310     1.0     70～85
在生产过程中，根据夹层玻璃出预压段后的表面图案，可对上述工艺控制参数做部分调整。产品在高压釜中的最终成形参照普通PVB夹层玻璃程序。
实例2：
在生产“东方艺术中心”的异形“夹金属穿孔板的SGP夹层玻璃”过程中(不规则四边形、三角形等)，采用了真空法工艺，工艺上采用了硅橡胶真空环或尼龙真空袋作为密封材料，显著提高了真空法预压的密封度，确保残留在中间膜和金属板间的气体被真空排出。
真空法预压的时间、温度和真空度制度：
1、升温过程：在60分钟内将温度从室温升至125～130℃；真空度始终控制在30托以下。
2、保温温度：125～130℃；保温时间：45分钟；真空度控制在30托以下。
3、降温过程：将设备关闭，玻璃随设备自然降温至室温。
产品在高压釜中的最终成形参照普通PVB夹层玻璃程序。
两种工艺方法各有千秋，适用的产品类型也不同。以下是两者的对比：
    二次辊压法     真空法
  工艺流程     复杂     简单
  工艺控制     难     易
  设备要求     高     低
  自动化程度     高     低
产品类型     平面夹层玻璃   平面或曲面夹层玻璃
产量     高   低

Claims (5)

1、一种夹金属装饰板的夹层玻璃，其特征在于：该夹层玻璃结构是：玻璃板/有机胶粘材料EVA或SGP中间膜/金属装饰薄板/有机胶粘材料EVA或SGP中间膜/玻璃板。
2、按权利要求1所述的夹金属装饰板的夹层玻璃，其特征在于：玻璃板的厚度为2mm～19mm；玻璃板可以是普通优质浮法玻璃、钢化或钢化热浸的热反射膜玻璃、低辐射膜(Low-e)玻璃等；玻璃板上可钻孔或不钻孔；玻璃钻孔的孔径不小于玻璃的标准厚度。
3、按权利要求1所述的夹金属装饰板的夹层玻璃，其特征在于：EVA中间膜的厚度为0.4～2.4mm；SGP中间膜的厚度为0.76mm～10.16mm。
4、按权利要求1所述的夹金属装饰板的夹层玻璃，其特征在于：金属装饰板的厚度为0.1mm～4mm，可以是冲孔网板或丝网的各种不锈钢、普通碳钢、镀锌钢、彩钢板、铝合金、铜合金等各类金属材料；用穿孔板时，穿孔板的开孔率可为20％～85％，孔径为1mm～100mm，孔心距为2mm～110mm，孔的排列为正方形、矩形、四边形或三角形。装饰板上的图形和图案可任意选择。
5、一种夹金属装饰板的夹层玻璃生产工艺，其特征在于：该玻璃的生产工艺采用二次辊压法，或者是真空法，二次辊压法的工艺过程是：玻璃的外观和尺寸检查→35℃纯水清洗→热风烘干→在一定温湿度的净室内合片→一次加热→一次辊动预压→二次加热→二次辊动预压→质量检验→上高压釜车架→在高压釜中最终成形→产品逐片检验→产品包装；
其中：一次辊压工艺是：玻璃板面温度控制在30℃～60℃之间，辊压间隙控制在比夹胶玻璃总厚度小1～3mm之间，预压加热炉的温度控制在200℃～260℃之间，要求炉温加热元件温度控制在较低的温度400℃，玻璃线速度控制在比相同厚度正常夹胶玻璃快1.5～2.5倍的基础上，根据环境温度、相对湿度不同进行调整；
二次辊压工艺是：玻璃板面温度控制在65℃～90℃之间，辊压间隙控制在比夹胶玻璃总厚度小1～3mm之间。预压加热炉的温度控制在250℃～360℃之间，要求炉温加热元件温度控制在较低的温度700℃，玻璃线速度控制在比相同厚度正常夹胶玻璃快0.5～1.0倍的基础上，根据环境温度、相对湿度不同进行调整；
真空法的工艺过程是：
玻璃的外观和尺寸检查→35℃纯水清洗→热风烘干→在一定温湿度的净室内合片→真空预压(真空环或真空袋)→质量检验→上高压釜车架→在高压釜中最终成形→产品逐片检验→产品包装；
其中：抽真空保温温度：90～140℃，根据玻璃厚度、中间膜厚度、中间膜材料进行调整，保温时间控制在30分钟到60分钟之间；根据玻璃厚度、中间膜厚度、中间膜材料进行调整；真空度控制在30托以下。
CN 200410018112 2004-05-08 2004-05-08 夹金属装饰板的夹层玻璃生产工艺 Expired - Lifetime CN1290788C (zh)