CN103214195B - 利用聚乙烯热熔胶膜粘接的真空玻璃的封接方法 - Google Patents

利用聚乙烯热熔胶膜粘接的真空玻璃的封接方法 Download PDF

Info

Publication number
CN103214195B
CN103214195B CN201310120879.9A CN201310120879A CN103214195B CN 103214195 B CN103214195 B CN 103214195B CN 201310120879 A CN201310120879 A CN 201310120879A CN 103214195 B CN103214195 B CN 103214195B
Authority
CN
China
Prior art keywords
aluminum alloy
adhesive film
melt adhesive
alloy frame
glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310120879.9A
Other languages
English (en)
Other versions
CN103214195A (zh
Inventor
张百庆
韩立平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Kangling Curing Technology Co Ltd
Original Assignee
Hefei Kangling Curing Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Kangling Curing Technology Co Ltd filed Critical Hefei Kangling Curing Technology Co Ltd
Priority to CN201310120879.9A priority Critical patent/CN103214195B/zh
Publication of CN103214195A publication Critical patent/CN103214195A/zh
Application granted granted Critical
Publication of CN103214195B publication Critical patent/CN103214195B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用聚乙烯热熔胶膜粘接的真空玻璃的封接方法，先制备热熔胶膜，将上、下片平板玻璃裁片，在上、下片玻璃片四周边缘之间夹持铝合金框，铝合金框与上、下玻璃片间围成一个密封的腔体，其中一个铝合金框上开有抽气孔，在铝合框与上、下玻璃片的接合面处放置热熔胶膜条，加压夹紧，送入加热炉中，在110-125℃温度下放置4-5分钟后，取出冷却；再在铝合金框外侧与玻璃片的交接处再涂抹玻璃胶；然后抽真空、填塞抽气孔，在真空玻璃四周装上边框。本发明采用制作的热熔胶膜，用于玻璃片与铝合金框之间的封接，效果好，本发明制作的真空玻璃窗，经过使用二年以上，检验封接部位完好，没有出现脱胶现象，夹层内真空度仍然保持较高水平，夹层内无结露、霉变等情况，保温隔热效果良好。

Description

利用聚乙烯热熔胶膜粘接的真空玻璃的封接方法
技术领域
本发明涉及一种真空玻璃封接方法。
背景技术
由多片玻璃板复合而成的真空玻璃以其优良的隔音、隔热、保温性能受到人们的重视，得以在建筑上大量应用。现有的真空玻璃是在上、下片玻璃之间夹上一圈铝合金框，多是采用粘合剂进行粘接，由于没有专用的粘结剂，导致长时间使用或者经过恶劣环境后，粘接部位易脱落，会出现水汽进入真空玻璃内，夹层内结露、玻璃霉变。
发明内容
针对现有技术存在的不足，本发明的目的在于提供一种利用聚乙烯热熔胶膜粘接的真空玻璃的封接方法，工艺简便、封接可靠、牢固。
本发明的技术方案如下：
一种利用聚乙烯热熔胶膜粘接的真空玻璃的封接方法，其特征在于：包括以下步骤：
（1）、制备热熔胶膜：
所述的热熔膜原料组成的重量份为：
中密度聚乙烯85-90、聚氧甲烯4-6、SG-1聚氯乙烯25-30、改性C5石油树脂10-12、硅烷偶联剂KH5702-3、交联剂TAIC1-2、烟片胶2-3、抗氧剂DSTP1-2、纳米二氧化硅3-4；
制备方法：将各原料置入造粒机的搅拌室内，进行混合搅拌后制成颗粒；将所述的颗粒加入流延机而获得热熔胶膜；并剪成条；
所述的改性C5石油树脂通过以下方法制得：
首先在反应容器中加入30-35份C5石油树脂、2-3份烟片胶、8-10份乙二醇二缩水甘油醚、1-2份纳米砖渣粉末、3-4份明矾粉末，搅拌，在115-120℃下反应2-3小时；
再向反应容器中加入2-3份顺丁烯二酸酐、1-2份乙烯基三甲氧基硅烷，搅拌，在80-90℃条件下反应1-2小时，即得；
（2）、是将上、下片平板玻璃裁片，在上、下片玻璃片四周边缘之间夹持铝合金框，铝合金框与上、下玻璃片间围成一个密封的腔体，其中一个铝合金框上开有抽气孔，在铝合框与上、下玻璃片的接合面处放置热熔胶膜条，加压夹紧，送入加热炉中，在110-125℃温度下放置4-5分钟后，取出冷却；
（3）、再在铝合金框外侧与玻璃片的交接处再涂抹玻璃胶；然后抽真空、填塞抽气孔，在真空玻璃四周装上边框。
本发明采用制作的热熔胶膜，用于玻璃片与铝合金框之间的封接，效果好，本发明制作的真空玻璃窗，经过使用二年以上，检验封接部位完好，没有出现脱胶现象，夹层内真空度仍然保持较高水平，夹层内无结露、霉变等情况，保温隔热效果良好。
具体实施方式
一种利用聚乙烯热熔胶膜粘接的真空玻璃的封接方法，包括以下步骤：
（1）、制备热熔胶膜：
所述的热熔膜原料组成的重量份为：
中密度聚乙烯90、聚氧甲烯6、SG-1聚氯乙烯25、改性C5石油树脂12、硅烷偶联剂KH5702、交联剂TAIC1、烟片胶3、抗氧剂DSTP2、纳米二氧化硅4；
制备方法：将各原料置入造粒机的搅拌室内，进行混合搅拌后制成颗粒；将所述的颗粒加入流延机而获得热熔胶膜；并剪成条；
所述的改性C5石油树脂通过以下方法制得：
首先在反应容器中加入30份（重量，下同）C5石油树脂、3份烟片胶、8份乙二醇二缩水甘油醚、2份纳米砖渣粉末、3份明矾粉末，搅拌，在115-120℃下反应2小时；
再向反应容器中加入2份顺丁烯二酸酐、2份乙烯基三甲氧基硅烷，搅拌，在80-90℃条件下反应1小时，即得；
（2）、是将上、下片平板玻璃裁片，在上、下片玻璃片四周边缘之间夹持铝合金框，铝合金框与上、下玻璃片间围成一个密封的腔体，其中一个铝合金框上开有抽气孔，在铝合框与上、下玻璃片的接合面处放置热熔胶膜条，加压夹紧，送入加热炉中，在110-125℃温度下放置4-5分钟后，取出冷却；
（3）、再在铝合金框外侧与玻璃片的交接处再涂抹玻璃胶；然后抽真空、填塞抽气孔，在真空玻璃四周装上边框。
本发明制作的真空玻璃窗，经过使用二年以上，检验封接部位完好，没有出现脱胶现象，夹层内真空度仍然保持较高水平，夹层内无结露、霉变等情况，保温隔热效果良好。

Claims (1)

1.一种利用聚乙烯热熔胶膜粘接的真空玻璃的封接方法，其特征在于：包括以下步骤：
（1）、制备热熔胶膜：所述的热熔膜原料组成的重量份为：中密度聚乙烯85-90、聚氧甲烯4-6、SG-1聚氯乙烯25-30、改性C5石油树脂10-12、硅烷偶联剂KH5702-3、交联剂TAIC1-2、烟片胶2-3、抗氧剂DSTP1-2、纳米二氧化硅3-4；制备方法：将各原料置入造粒机的搅拌室内，进行混合搅拌后制成颗粒；将所述的颗粒加入流延机而获得热熔胶膜；并剪成条；所述的改性C5石油树脂由以下重量份原料制成：C5石油树脂30-35、烟片胶2-3、乙二醇二缩水甘油醚8-10、纳米砖渣粉末1-2、明矾粉末3-4、顺丁烯二酸酐2-3、乙烯基三甲氧基硅烷1-2，所述的改性C5石油树脂通过以下方法制得：首先在反应容器中加入C5石油树脂、烟片胶、乙二醇二缩水甘油醚、纳米砖渣粉末、明矾粉末，搅拌，在115-120℃下反应2-3小时；再向反应容器中加入顺丁烯二酸酐、乙烯基三甲氧基硅烷，搅拌，在80-90℃条件下反应1-2小时，即得；
（2）、是将上、下片平板玻璃裁片，在上、下片玻璃片四周边缘之间夹持铝合金框，铝合金框与上、下玻璃片间围成一个密封的腔体，其中一个铝合金框上开有抽气孔，在铝合金框与上、下玻璃片的接合面处放置热熔胶膜条，加压夹紧，送入加热炉中，在110-125℃温度下放置4-5分钟后，取出冷却；
（3）、再在铝合金框外侧与玻璃片的交接处再涂抹玻璃胶；然后抽真空、填塞抽气孔，在真空玻璃四周装上边框。
CN201310120879.9A 2013-04-09 2013-04-09 利用聚乙烯热熔胶膜粘接的真空玻璃的封接方法 Expired - Fee Related CN103214195B (zh)