CN1391004A - Adhesive lining cloth able to be washed and dyed and its making method - Google Patents
Adhesive lining cloth able to be washed and dyed and its making method Download PDFInfo
- Publication number
- CN1391004A CN1391004A CN 02113192 CN02113192A CN1391004A CN 1391004 A CN1391004 A CN 1391004A CN 02113192 CN02113192 CN 02113192 CN 02113192 A CN02113192 A CN 02113192A CN 1391004 A CN1391004 A CN 1391004A
- Authority
- CN
- China
- Prior art keywords
- grams per
- temperature
- base cloth
- per liter
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An adhesive lining cloth whose products can be washed is prepared from basic cloth through heating water to 80-95 deg.C, immersing the cloth in it, adding water and assistant, heating to 90-100 deg.C, refining for 5-15 min, finishing it in finishing liquid, baking, and coating the high-smelting-point (120-130 deg.C) polyamide or copolyamide resin on it in dot array mode.
Description
Technical field
The present invention relates to field of textiles, specifically a kind of manufacture method of binding lining of goods able to be washed and dyed.
Background technology
Along with China's entry into the WTO, the gateway of a country is opened wide to the world by China, and the external world also begins to admit gradually China, the contacts in China and the external world, exchange increasing.
Along with the increase of contacts, China not only is being tending towards synchronously with the world aspect the commercial activity custom, and is also increasing to the influence of culture, language, psychology or the like each side.Wherein clothes, dressing class can be said so and be subjected to that the west is popular to have the greatest impact, and along with the dressing theory in west is more and more deep to our influence, only go in the past a sleek mark in Chinese thousand people dressing scene of the same colour in old film and memory.The variation of clothes, a personalized fashion trend that has become the world today, especially this just shows more obviously on the great market in Growth Development in China.This fashion trend shows as a small amount ofization, miniaturization, the multiple class of production in the production of clothes and lining.
Aspect clothes processing, tackle in the trend of above-mentioned clothes and fashionable dress, wash behind the washing of ready-made clothes, the ready-made clothes and special processing technology such as dye and arise at the historic moment.These and traditional costume process processing method far from each other often have special design effect or unusual color effect, and these provide the broad space of any reverie all for designerss.Reaching special outward appearance and handle effect, the washing of cowboy's series, water mill, sand washing and wash polishing after dying also have dress ornament color change from top to bottom or the like, and be too numerous to enumerate as shirt ready-made clothes washing.
When processing these type of clothes, have many-sided consideration such as better morphological stability, washing size stability and intensity, feel, must select for use various binding linings to come supporting use in order to make clothes.Traditional binding lining is used for this type of dress ornament and adds man-hour, because there is deficiency in each side such as bonding force, washing fastness, uses the back easily to produce problems such as bubbling, come off, causes decrease in yield.
Summary of the invention
The objective of the invention is to seek a kind of binding lining and manufacture method thereof of goods able to be washed and dyed, because the resin that this binding lining uses has fusing point and the bonding strength more much higher than other resins, so binding lining of the present invention is used for above-mentioned clothes and adds man-hour, after the processing technology of going through multiple complexity such as washing, dyeing after washing, non-foaming, do not come off, compare with traditional in the past binding lining, have higher yield rate.
Its main technical schemes is the resin that applies dystectic polyamide-based and copolyamide class on base cloth, and between 130 degree, and melt index MI (in the time of 160 ℃) is 40~15 to the fusing point of this resinoid at 120 degree.
The manufacture method feature of the binding lining of this goods able to be washed and dyed is:
Concise: as in the fluid cylinder of concise machinery, to add entry, after being warming up to 80~95 ℃, fabric is dropped in the fluid cylinder, make water and fabric one cycle rotation in the fluid cylinder that coexists, in this process, add entry to required amount and auxiliary agent, be warming up to 90~100 ℃ of concise temperature then, after concise 5~15 minutes, venting refining liquid takes out behind the adding cold water washing.
Arrangement: in the liquid bath of arrangement machinery, add the dressing liquid that is mixed with by water and auxiliary agent, after making above-mentioned refined fabric soak into dressing liquid, enter again in the mechanical baking oven of arrangement, under 90 ℃~200 ℃ temperature, make the fabric drying typing, 25~40 meters/minute of the speed of a motor vehicle;
Bonding: as to make above-mentioned fabric process coating machine, on fabric, be coated with the dystectic polyamide and the copolyamide resinoid of point-like through arrangement.
The composition of the auxiliary agent in the concise liquid is softener 0.1~0.3 grams per liter, surfactant 0.1~0.3 grams per liter, NaOH 2~10 grams per liters, desizing agent 0.3~0.5 grams per liter in metal ion chelation agent 0.1~0.3 grams per liter, the bath, Yu Weishui.
The composition of the auxiliary agent in the dressing liquid is softener 2~6 grams per liters, antistatic agent 0.5~1.5 grams per liter, bleeding agent 0.1~0.3 grams per liter, Yu Weishui.
When bonding, the mode of utilizing the net tube to shift is coated on prime cement on the base cloth surface with point-like, the spreading powdered resin equably again, absorb unnecessary resin then, the place that prime cement is arranged on the base cloth is stained with or keeps resin, carry out Infrared Heating, temperature again: 180~210 ℃, make prime cement dry and be bonded on the base cloth surface, enter drying room then and make base cloth typing, 100~140 ℃ of drying room temperature, 35~45 meters/minute of process velocities.
When bonding, the mode that also can utilize hot melt to shift, above being covered with the engraved roll of pit, the hopper of adorning powdered resin is arranged, the engraved roll temperature is 30~40 ℃, be useful on the warm-up mill of heating base cloth in the both sides, front and back of engraved roll, the temperature of warm-up mill is 155~185 ℃, engraved roll rotates, powdered resin falls in the pit of engraved roll, exist side by side molten condition, make base cloth paste engraved roll and pass through, resin in the pit just is adhered to the base cloth surface, form the resin of point-like, again through tentering car drying and shaping, temperature of oven is 160~170 ℃.
Warm-up mill has a roller, No. two rollers and No. three rollers, and the temperature of roller~No. three roller is 155~185 ℃.
Before concise back, arrangement, dye earlier: the dye liquor that in the high temperature liquid-flow dyeing machine, adds the preparation of entry and auxiliary agent, wherein the addition of auxiliary agent is DISPERSE DYES 5~20 grams per liters, softener 0.5~1.5 grams per liter in the bath, dispersant 0.3~1 grams per liter, formic acid 0.1~0.3 grams per liter is again under 100~150 ℃ temperature, dyeed through 20~40 minutes;
Soaping after the dyeing: soaped 10~20 minutes in the liquid of soaping of water and soaping agent preparation, temperature is 70~90 ℃, and soaping agent content is 1~3 grams per liter; And then washing: wash in clear water, 10~20 minutes time, temperature is a normal temperature.
The present invention is a kind of binding lining that uses with in the dress ornament process that reaches special feel or outward appearance, color effect design that has ready-made clothes washing or ready-made clothes to wash in technological design to dye, as collar, the cuff of shirt, jacket, jeans etc., take door, pkt. flap etc. and locate all can use.The bubble problem that uses binding lining of the present invention that the more serious collar as shirt of existence in the past, cuff etc. are located diminishes in invisible.Lining cloth between inside and outside two-layer lining plays reinforcement that collar, cuff etc. is located, washable, not deliquescing, wrinkle resistant effect, has used the clothes of this binding lining more attractive in appearance, washablely scalds, easily maintenance, improved the use value of dress ornament.And can enhance productivity widely making in the process of dress ornament.
Because needn't worry between lining and the binding lining problems such as bonding strength, designerss can use ready-made clothes washing and ready-made clothes dyeing technology audaciously, pursuing effects such as unusual color, feel, outward appearance, and needn't worry that the processing aspect could reach requirement.
Binding lining of the present invention applies one deck spot distribution by base cloth and on base cloth, the slurry that has dystectic resin or apply one deck spot distribution on base cloth is spilt one deck then thereon and is had dystectic resin oven dry and form, if single-layer resin, resin can be flattened on base cloth, to improve fixation performance.
Base cloth is generally chosen long fiber material and is made.Mainly be to spin cloth because as do base cloth with nonwoven fabric, after the washing, anti-ly draw, wash each side such as intensity obvious decline is all arranged.
Base cloth makes it possess various performances such as feel, contraction, intensity through refining, dyeing, arrangement processing, applies one deck or bilayer then and has dystectic resin and promptly become finished product.This resin is generally polyamide and copolyamide resinoid.
If the colloid that the double-deck bonding slurry that then uses is formed as the copolymer and the water of polyacrylic acid and polyacrylate.
Using method:
In the process of using binding lining processing shirt of the present invention, jacket, casual pants etc., in advance this clothing collar, cuff etc. are located lining and passed through hot calendering bonding together, together carry out cutting then, be sewn into ready-made clothes with the binding lining of selecting that can cooperate with this lining.According to the ready-made clothes design ready-made clothes is washed at last, add medicines such as softener in the aqueous solution as required and handle, reach feel, the appearance requirement of expectation by washing; Perhaps according to the ready-made clothes design ready-made clothes is dyeed, washing removes the color effect of removal floating color to obtain designing then.
So use binding lining of the present invention, not only can reach the feel and the three-dimensional color effect of the special washing of expected design, and problems such as foaming, bonding intensity be not enough have been eliminated, can play reinforcement that collar, cuff etc. is located, washable, not deliquescing, wrinkle resistant effect by refining, dyeing, arrangement processing simultaneously, use the clothes of this binding lining more attractive in appearance, washablely scald, easily maintenance, improved the use value of clothes.
Processing method:
Base cloth difference then processing method is also different, because the material different performance is different, the process route of design has certainly than big-difference.
Refining:
This type of base cloth is generally long fiber, is formed by long fiber terylene or nylon textile, owing to do not contain cotton, so there are not field trashes such as glue, cotton wax, seed coat, a need be removed the secondary inclusion thing and get final product in refining process.Simultaneously because long stapled particularity, long stapled grey cloth must be carried out boiling-off under lax state, when removing impurity, also to add medicines such as NaOH, H2O2 and the corrosion of long stapled fiber be attenuated so that removes gloss and acquisition is easily dyed, characteristic such as soft, flexible.
Dyeing: dyestuff is adhered to or be bonded to fiber or enter fibrous inside, make fabric obtain attractive in appearance, even, firm color, and with require sample identical.
In order to keep long fiber fabric better elastic, long stapled dyeing continues to adopt High Temperature High Pressure liquid-flow dyeing machine or high-temperature high-pressure liquid stream jet dyeing machine down with lax state, with DISPERSE DYES or ACID DYES or dispersion/direct dyeing.
Arrangement: utilize the technology of the method for physics or chemistry to the processing of grey cloth enforcement sense organ.
Make after refining, the dyeing the lax fully and grey cloth tentering that shrinks to certain fabric width, the typing of heating then.In this process,, make grey cloth after arrangement processing, not only have smooth outward appearance, and had certain elasticity, anti-static ability by adding softener, antistatic additive infiltration grey cloth, oven dry, and the feel that has design to need.
Bonding:
Way that shifts with hot melt or slurry coating method make thermoplastic resin polyamide-based resin or copolyamide resinoid scatter and be bonded to processing technology on the base cloth equably.Concrete grammar is exactly as shown in Figure 2: the A roller is inner heating, is uniform-distribution with the upper glue roller of pit on the surface.When the A roller rotates, the polyamide-based resin of the powdery in the hopper 14 falls in the pit and melted by heating, adheres to cooling on the grey cloth 10, looks to have or not arts demand again, whether decision utilizes pressure roller D1, D2 to flatten on grey cloth 10 resin 15 of powder point-like, comes out to be finished product.
Perhaps as shown in Figure 1: the slurry that applies one deck spot distribution on base cloth is spilt one deck then thereon and is had dystectic copolyamide resinoid oven dry and form.1 is baking oven among the figure, and 2 is retracting device, and 3 is air pump, and 4 is dusting device, and 5 is scraper plate, and 6 are the net tube, and 7 is resin slurry, and 8 is cylinder, and 9 is device of excitation, and 10 is base cloth, and 11 is the point-like slurry, and 12 is powdered resin, and 13 for being bonded at the resin on the point-like slurry.Base cloth is through cylinder and after netting between tube, slurry comes out from the mesh of net tube, becomes point-like to be bonded on the base cloth, and base cloth continues reach, at the dusting device place, sprinkled one deck powdered resin, then, after the vibrating device vibration, make powdered resin be sprinkling upon on the base cloth equably, behind air pump and retracting device, the unnecessary powdered resin between the point-like slurry is absorbed again, made powdered resin become point-like to be uniformly distributed in the base cloth surface.
Characteristic feature of an invention:
Design philosophy: present invention is directed to traditional ready-made clothes washing or ready-made clothes of being used for and wash the deficiency of dying the binding lining that processing technology uses and the new product of developing.Traditional binding lining easily produces problems such as bubbling, come off because bonding force is not enough, binding lining of the present invention has improved the bonding force of binding lining, the finished product bonding force can reach more than the 1000 gram/square inches, and more traditional bonding force 500~600 gram/square inches double.Can be used as ready-made clothes washing or ready-made clothes and wash the specialty binding lining that dyes processing.
Purposes: can be used for that all need after ready-made clothes washing or the dress must frequent washing, and requires non-foamingly after the washing, can keep special feel and relief dress ornament.
Resin with high melting point: add man-hour in washing of finished products such as the shirt that uses binding lining of the present invention, jacket, casual pants or finished product dyeing, for using the part of binding lining, fully firm as easily the bubble lining of part such as the collar of shirt, jacket, cuff with combining of binding lining, select this high-melting point polyamide and copolyamide resinoid especially as adhesive.
Description of drawings
Fig. 1 is the bonding schematic diagram of double-layer resin.
Fig. 2 is the hot melt transition diagram.
The specific embodiment
Embodiment one
1, former base: T32432, former base specification: 50D/48F
*50D/48F, density: 76
*61, form: T:100%, fabric width: 147 centimetres.
2, concise: as in the fluid cylinder of concise machinery, to add the concise liquid that is mixed with by water and auxiliary agent, base cloth is dropped in the fluid cylinder, make concise liquid and base cloth one cycle rotation in the fluid cylinder that coexists, be warming up to 80 degree then, the concise liquid of venting after concise 10 minutes takes out behind the adding cold water washing.The addition of auxiliary agent is in concise liquid: metal ion chela and agent 0.1 grams per liter, and softener 0.15 grams per liter in the bath, surfactant 0.1 grams per liter, NaOH 3 grams per liters, desizing agent 0.3 grams per liter, all the other in the scouring agent are water.
3, dyeing: add the dye liquor of entry and auxiliary agent preparation in the high temperature liquid-flow dyeing machine, wherein the addition of auxiliary agent is: DISPERSE DYES 5 grams per liters, and softener 1.0 grams per liters, dispersant 0.4 grams per liter, formic acid 0.1 grams per liter carries out dyeing in 40 minutes after being warming up to 100 degree.Soap after the dyeing, the time is 10 minutes, and adding soaping agent is 1 grams per liter.
Open-width on request in scutcher again after the dyeing, and in dryer, dry.
4, arrangement: in the liquid bath of arrangement machinery, add entry and the dressing liquid that auxiliary agent is mixed with, make to enter in the collator tool oven dry behind the base cloth padding finishing liquid and finalize the design.Setting machine has nine Room, and temperature is respectively 100 to 190 degree, and 25 meters/minute of speed are finished the width of cloth: 123 centimetres, and density 90
*70, degree of stretching: 15
*20, auxiliary component is softener 2 grams per liters in the dressing liquid, antistatic agent 0.5 grams per liter, bleeding agent 0.1 grams per liter.
5, bonding: the mode of utilizing the net tube to shift, prime cement is coated on the base cloth surface with point-like equably, the resin of spreading powdery is again absorbed uncoated unnecessary resin to the slurry place then, the place that prime cement is arranged on the base cloth is stained with or keeps resin, carry out Infrared Heating again, temperature: 180 degree, make prime cement dry and be bonded on the base cloth surface, enter typing in the drying room then, the drying room temperature is 100 degree, 35 meters/minute of process velocities.
Embodiment two
1, former base: YT31131, former base specification: 50D/36F
*50D/36F, density: 65
*58, form: T:100%, fabric width: 127 centimetres.
2, concise: as in the fluid cylinder of concise machinery, to add the concise liquid that is mixed with by water and auxiliary agent, base cloth is dropped in the fluid cylinder, make concise liquid and base cloth one cycle rotation in the fluid cylinder that coexists, be warming up to 85 degree then, the concise liquid of venting after concise 15 minutes takes out behind the adding cold water washing.The addition of auxiliary agent is in concise liquid: metal ion chela and agent 0.15 grams per liter, and softener 0.1 grams per liter in the bath, surfactant 0.15 grams per liter, NaOH 4 grams per liters, desizing agent 0.4 grams per liter, all the other in the scouring agent are water.
3, dyeing: add the dye liquor of entry and auxiliary agent preparation in the high temperature liquid-flow dyeing machine, wherein the addition of auxiliary agent is: DISPERSE DYES 8 grams per liters, and softener 0.5 grams per liter, dispersant 0.3 grams per liter, formic acid 0.2 grams per liter carries out dyeing in 25 minutes after being warming up to 120 degree.Soap after the dyeing, the time is 15 minutes, and adding soaping agent is 1.5 grams per liters.
Open-width on request in scutcher again after the dyeing, and in dryer, dry.
4, arrangement: in the liquid bath of arrangement machinery, add entry and the dressing liquid that auxiliary agent is mixed with, make to enter in the collator tool oven dry behind the base cloth padding finishing liquid and finalize the design.Setting machine has nine Room, and temperature is respectively 100 to 190 degree, and 40 meters/minute of speed are finished the width of cloth: 113 centimetres, and density 72
*71, degree of stretching: 18
*15, auxiliary component is softener 3 grams per liters in the dressing liquid, antistatic agent 0.8 grams per liter, bleeding agent 0.2 grams per liter.
5, bonding: the mode of utilizing the net tube to shift, prime cement is coated on the base cloth surface with point-like equably, the resin of spreading powdery is again absorbed uncoated unnecessary resin to the slurry place then, the place that prime cement is arranged on the base cloth is stained with or keeps resin, carry out Infrared Heating again, temperature: 200 degree, make prime cement dry and be bonded on the base cloth surface, enter typing in the drying room then, the drying room temperature is 130 degree, 40 meters/minute of process velocities.
Embodiment three
1, former base: T32412, former base specification: 75D
*75D, density: 45
*37, form: T:100%, fabric width: 142 centimetres.
2, refining: in the fluid cylinder of concise machinery, add the concise liquid that is mixed with by water and auxiliary agent, base cloth is dropped in the fluid cylinder, make concise liquid and base cloth one cycle rotation in the fluid cylinder that coexists, be warming up to 90 degree then, the concise liquid of venting after concise 15 minutes takes out behind the adding cold water washing.The addition of auxiliary agent is in concise liquid: metal ion chela and agent 0.2 grams per liter, and softener 0.2 grams per liter in the bath, surfactant 0.2 grams per liter, NaOH 5 grams per liters, desizing agent 0.5 grams per liter, all the other in the scouring agent are water.
3, dyeing: add the dye liquor of entry and auxiliary agent preparation in the high temperature liquid-flow dyeing machine, wherein the addition of auxiliary agent is: DISPERSE DYES 10 grams per liters, and softener 1.5 grams per liters, dispersant 0.5 grams per liter, formic acid 0.15 grams per liter carries out dyeing in 30 minutes after being warming up to 130 degree.Soap after the dyeing, the time is 20 minutes, and adding soaping agent is 2 grams per liters.
Open-width on request in scutcher again after the dyeing, and in dryer, dry.
4, arrangement: in the liquid bath of arrangement machinery, add entry and the dressing liquid that auxiliary agent is mixed with, make to enter in the collator tool oven dry behind the base cloth padding finishing liquid and finalize the design.Setting machine has nine Room, and temperature is respectively 100 to 190 degree, and 30 meters/minute of speed are finished the width of cloth: 123 centimetres, and density 53
*44, degree of stretching: 15
*20, auxiliary component is softener 4 grams per liters in the dressing liquid, antistatic agent 1.0 grams per liters, bleeding agent 0.3 grams per liter.
5, bonding: the mode of utilizing the net tube to shift, prime cement is coated on the base cloth surface with point-like equably, the resin of spreading powdery is again absorbed uncoated unnecessary resin to the slurry place then, the place that prime cement is arranged on the base cloth is stained with or keeps resin, carry out Infrared Heating again, temperature: 210 degree, make prime cement dry and be bonded on the base cloth surface, enter typing in the drying room then, the drying room temperature is 140 degree, 45 meters/minute of process velocities.
Embodiment four
1, former base: T32432, former base specification: 50D/48F
*50D/48F, density: 76
*61, form: T:100%, fabric width: 147 centimetres.
2, concise: as in the fluid cylinder of concise machinery, to add the concise liquid that is mixed with by water and auxiliary agent, base cloth is dropped in the fluid cylinder, make concise liquid and base cloth one cycle rotation in the fluid cylinder that coexists, be warming up to 90 degree then, the concise liquid of venting after concise 10 minutes takes out behind the adding cold water washing.The addition of auxiliary agent is in concise liquid: metal ion chela and agent 0.3 grams per liter, and softener 0.3 grams per liter in the bath, surfactant 0.3 grams per liter, NaOH 10 grams per liters, desizing agent 0.35 grams per liter, all the other in the scouring agent are water.
3, dyeing: add the dye liquor of entry and auxiliary agent preparation in the high temperature liquid-flow dyeing machine, wherein the addition of auxiliary agent is: DISPERSE DYES 20 grams per liters, and softener 1.0 grams per liters, dispersant 0.5 grams per liter, formic acid 0.1 grams per liter carries out dyeing in 30 minutes after being warming up to 125 degree.Soap after the dyeing, the time is 20 minutes, and adding soaping agent is 3 grams per liters.
Open-width on request in scutcher again after the dyeing, and in dryer, dry.
4, arrangement: in the liquid bath of arrangement machinery, add entry and the dressing liquid that auxiliary agent is mixed with, make to enter in the collator tool oven dry behind the base cloth padding finishing liquid and finalize the design.Setting machine has nine Room, and temperature is respectively 100 to 190 degree, and 30 meters/minute of speed are finished the width of cloth: 123 centimetres, and density 90
*70, degree of stretching: 15
*20, auxiliary component is softener 4 grams per liters in the dressing liquid, antistatic agent 1.0 grams per liters, bleeding agent 0.3 grams per liter.
5, bonding: as to make above-mentioned fabric process coating machine, on fabric, be coated with the polyamide and the copolyamide resinoid of point-like through arrangement.
Above being covered with the engraved roll of pit, the hopper of adorning powdered resin is arranged, the engraved roll temperature is 30 degree, be useful on the warm-up mill of heating base cloth in the both sides, front and back of engraved roll, engraved roll rotates, and powdered resin just falls in the pit of engraved roll, becomes molten condition when powdered resin contact base cloth immediately, after making base cloth paste engraved roll to pass through, resin in the pit just is adhered to the base cloth surface, forms the resin of point-like, and temperature of oven is 160 degree.Warm-up mill has a roller, No. two rollers and No. three rollers, and the temperature of roller~No. three roller is 155 degree, 165 degree, 175 degree.Bonding finishing enters tentering in the stenter, and the stenter temperature is 160 degree, 16 meters/minute of process velocities.
Embodiment five
1, former base: T32432, former base specification: 50D/48F
*50D/48F, density: 76
*61, form: T:100%, fabric width: 147 centimetres.
2, concise: as in the fluid cylinder of concise machinery, to add entry, after being warming up to 92 degree, fabric is dropped in the fluid cylinder, make water and fabric one cycle rotation in the fluid cylinder that coexists, in this process, add entry to required amount and auxiliary agent, be warming up to concise temperature 97 degree then, after concise 8 minutes, venting refining liquid takes out behind the adding cold water washing.The composition of the auxiliary agent in the concise liquid is softener 0.15 grams per liter, surfactant 0.15 grams per liter, NaOH 2 grams per liters, desizing agent 0.4 grams per liter in metal ion chelation agent 0.15 grams per liter, the bath, Yu Weishui.
3, dyeing: the dye liquor that in the high temperature liquid-flow dyeing machine, adds the preparation of entry and auxiliary agent, wherein the addition of auxiliary agent is DISPERSE DYES 10 grams per liters, softener 1.5 grams per liters in the bath, dispersant 1 grams per liter, formic acid 0.3 grams per liter, again 150 the degree temperature under, through 20 minutes dyeing; Soaping after the dyeing: soaped 15 minutes in the liquid of soaping of water and soaping agent preparation, temperature is 85 degree, and soaping agent content is 3 grams per liters; And then washing: wash in clear water, 15 minutes time, temperature is a normal temperature.
4, arrangement: in the liquid bath of arrangement machinery, add the dressing liquid that is mixed with by water and auxiliary agent, after making above-mentioned refined fabric soak into dressing liquid, enter again in the baking oven of arrangement machinery, wherein the temperature of Room 1~9 is 90 degree~200 degree, make the fabric drying typing, 35 meters/minute of the speed of a motor vehicle are finished the width of cloth: 123cm, density: 90
*70, degree of stretching: 15
*20; The composition of the auxiliary agent in the dressing liquid is softener 5 grams per liters, antistatic agent 1.5 grams per liters, bleeding agent 0.3 grams per liter, Yu Weishui.
5, bonding: as to make above-mentioned fabric process coating machine, on fabric, be coated with the polyamide and the copolyamide resinoid of point-like through arrangement.
Above being covered with the engraved roll of pit, the hopper of adorning powdered resin is arranged, the engraved roll temperature is 38 degree, be useful on the warm-up mill of heating base cloth in the both sides, front and back of engraved roll, engraved roll rotates, and powdered resin falls in the pit of engraved roll, exist side by side molten condition, making base cloth paste engraved roll passes through, resin in the pit just is adhered to the base cloth surface, forms the resin of point-like, and temperature of oven is 160 degree.Warm-up mill has a roller, No. two rollers and No. three rollers, and the temperature of roller~No. three roller is 160 degree, 170 degree, 185 degree.Bonding finishing enters tentering in the stenter, tentering car temperature: 170 degree, speed: 18 meters/minute.
Embodiment six
1, former base: T32432, former base specification: 50D/48F
*50D/48F, density: 76
*61, form: T:100%, fabric width: 147 centimetres.
2, concise: as in the fluid cylinder of concise machinery, to add entry, after being warming up to 90 degree, fabric is dropped in the fluid cylinder, make water and fabric one cycle rotation in the fluid cylinder that coexists, in this process, add entry to required amount and auxiliary agent, be warming up to concise temperature 95 degree then, after concise 10 minutes, venting refining liquid takes out behind the adding cold water washing.The composition of the auxiliary agent in the concise liquid is softener 0.2 grams per liter, surfactant 0.2 grams per liter, NaOH 5 grams per liters, desizing agent 0.5 grams per liter in metal ion chelation agent 0.2 grams per liter, the bath, Yu Weishui.
3, dyeing: the dye liquor that in the high temperature liquid-flow dyeing machine, adds the preparation of entry and auxiliary agent, wherein the addition of auxiliary agent is DISPERSE DYES 15 grams per liters, softener 1.0 grams per liters in the bath, dispersant 0.8 grams per liter, formic acid 0.2 grams per liter, again 140 the degree temperature under, through 35 minutes dyeing; Soaping after the dyeing: soaped 18 minutes in the liquid of soaping of water and soaping agent preparation, temperature is 80 degree, and soaping agent content is 2 grams per liters; And then washing: wash in clear water, 15 minutes time, temperature is a normal temperature.
4, arrangement: in the liquid bath of arrangement machinery, add the dressing liquid that is mixed with by water and auxiliary agent, after making above-mentioned refined fabric soak into dressing liquid, enter again in the baking oven of arrangement machinery, wherein the temperature of Room 1~9 is 90 degree~200 degree, make the fabric drying typing, 40 meters/minute of the speed of a motor vehicle are finished the width of cloth: 123cm, density: 90
*70, degree of stretching: 15
*20; The composition of the auxiliary agent in the dressing liquid is softener 6 grams per liters, antistatic agent 1.0 grams per liters, bleeding agent 0.2 grams per liter, Yu Weishui.
5, bonding: as to make above-mentioned fabric process coating machine, on fabric, be coated with the polyamide and the copolyamide resinoid of point-like through arrangement.
Above being covered with the engraved roll of pit, the hopper of adorning powdered resin is arranged, the engraved roll temperature is 40 degree, be useful on the warm-up mill of heating base cloth in the both sides, front and back of engraved roll, engraved roll rotates, and powdered resin falls in the pit of engraved roll, exist side by side molten condition, making base cloth paste engraved roll passes through, resin in the pit just is adhered to the base cloth surface, forms the resin of point-like, and temperature of oven is 170 degree.Warm-up mill has a roller, No. two rollers and No. three rollers, and the temperature of roller~No. three roller is 165 degree, 175 degree, 185 degree.Bonding finishing enters tentering in the stenter, tentering car temperature: 170 degree, speed: 20 meters/minute.
Claims (10)
1, a kind of binding lining of goods able to be washed and dyed is characterized in that applying dystectic polyamide and copolyamide resinoid on base cloth, the fusing point of this resinoid is between 120 degree are spent to 130, and melt index MI is 40~15.
2, a kind of manufacture method of binding lining of goods able to be washed and dyed is characterized in that:
Concise: as in the fluid cylinder of concise machinery, to add entry, after being warming up to 80~95 ℃, fabric is dropped in the fluid cylinder, make water and fabric one cycle rotation in the fluid cylinder that coexists, in this process, add entry to required amount and auxiliary agent, be warming up to 90~100 ℃ of concise temperature then, after concise 5~15 minutes, venting refining liquid takes out behind the adding cold water washing.
Arrangement: in the liquid bath of arrangement machinery, add the dressing liquid that is mixed with by water and auxiliary agent, after making above-mentioned refined fabric soak into dressing liquid, enter again in the mechanical baking oven of arrangement, under 90 ℃~200 ℃ temperature, make the fabric drying typing, 25~40 meters/minute of the speed of a motor vehicle;
Bonding: as to make above-mentioned fabric process coating machine, on fabric, be coated with the polyamide and the copolyamide resinoid of point-like through arrangement.
3, method according to claim 2, the composition that it is characterized in that the auxiliary agent in the concise liquid is softener 0.1~0.3 grams per liter, surfactant 0.1~0.3 grams per liter, NaOH 2~10 grams per liters, desizing agent 0.3~0.5 grams per liter in metal ion chelation agent 0.1~0.3 grams per liter, the bath, Yu Weishui.
4, method according to claim 2, the composition that it is characterized in that the auxiliary agent in the dressing liquid are softener 2~6 grams per liters, antistatic agent 0.5~1.5 grams per liter, bleeding agent 0.1~0.3 grams per liter, Yu Weishui.
5, method according to claim 2 is characterized in that when bonding, the mode of utilizing the net tube to shift, prime cement is coated on the base cloth base cloth surface with point-like equably, the spreading powdered resin is absorbed unnecessary resin then again, the place that prime cement is arranged on the base cloth is stained with or keeps resin, carry out Infrared Heating again, temperature: 180~210 ℃, make prime cement dry and be bonded on the base cloth surface, enter drying room then and make the base cloth typing, 100~140 ℃ of drying room temperature, 35~45 meters/minute of process velocities.
6, method according to claim 2, it is characterized in that: when bonding, above being covered with the engraved roll of pit, the hopper of adorning powdered resin is arranged, the engraved roll temperature is 30~40 ℃, be useful on the warm-up mill of heating base cloth in the both sides, front and back of engraved roll, the temperature of warm-up mill is 155~185 ℃, engraved roll rotates, powdered resin falls in the pit of engraved roll, exist side by side molten condition, make base cloth paste engraved roll and pass through, resin in the pit just is adhered to the base cloth surface, form the resin of point-like, temperature of oven is 160~170 ℃, 15~20 meters/minute of process velocities.
7, method according to claim 6 it is characterized in that warm-up mill has a roller, No. two rollers and No. three rollers, and the temperature of roller~No. three roller is 155~185 ℃.
8,, it is characterized in that after being coated with the point-like resin on the base cloth, flattening on base cloth again according to claim 2 or 6 described methods.
9, method according to claim 2, it is characterized in that before concise back, arrangement, dyeing earlier: the dye liquor that in the high temperature liquid-flow dyeing machine, adds the preparation of entry and auxiliary agent, wherein the addition of auxiliary agent is DISPERSE DYES 5~20 grams per liters, softener 0.5~1.5 grams per liter in the bath, dispersant 0.3~1 grams per liter, formic acid 0.1~0.3 grams per liter, again under 100~150 ℃ temperature, through 20~40 minutes dyeing.
10, method according to claim 9 is characterized in that soaping after the dyeing: soaped 10~20 minutes in the liquid of soaping of water and soaping agent preparation, temperature is 70~90 ℃, and soaping agent content is 1~3 grams per liter; And then washing: wash in clear water, 10~20 minutes time, temperature is a normal temperature.