CN106223059A - One spins lining adhesion lining cloth and preparation method thereof - Google Patents
One spins lining adhesion lining cloth and preparation method thereof Download PDFInfo
- Publication number
- CN106223059A CN106223059A CN201610610760.3A CN201610610760A CN106223059A CN 106223059 A CN106223059 A CN 106223059A CN 201610610760 A CN201610610760 A CN 201610610760A CN 106223059 A CN106223059 A CN 106223059A
- Authority
- CN
- China
- Prior art keywords
- fabric
- lining
- base fabric
- cloth
- grams per
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides one and spin lining adhesion lining cloth, including base fabric and thermoplastic binder resin, through the described thermoplastic binder resin of the surface of pretreated described base fabric coating point-like.Present invention also offers a kind of described above having and spin the preparation method of lining adhesion lining cloth, comprise the following steps: (1) pretreatment: refine, dye, be dehydrated and open-width, arrange and shape: in the stock tank of collator, add dressing liquid, after making the textile pad dressing liquid after dehydration and open-width, enter back in the baking oven of collator, at a temperature of 180 ~ 200 DEG C, fabric drying is made to shape, wherein, speed 30 ~ 45 ms/min and/or stamp；(2) coating.Technical scheme spins lining adhesion lining cloth and garment material directly bonds described in can making, and simplifies the work flow of clothing, improves production production efficiency, improve the style of clothing, it is achieved that the most generous useful visual effect.
Description
Technical field
The present invention relates to textile processing field, particularly relate to one and spin lining adhesion lining cloth and preparation method thereof.
Background technology
Clothing be machined into industrialization large-scale production after, in order to improve the attractive in appearance of clothing profile, it is ensured that the matter of clothing
Amount, people begin to use dress lining cloth, and the use of clothing Novel lapping cloth has had the history of decades at present.In prior art
Lining cloth be typically all used in the middle of the interlayer of fabric and back boxing, such design not only increases the manufacturing procedure of clothing, and
And reduce the efficiency of production.
Therefore, one can simplify manufacturing procedure and carry high efficiency lining cloth, be those skilled in the art in the urgent need to.
Summary of the invention
Based on above-mentioned background technology, it is an object of the invention to obtain one and spin lining adhesion lining cloth so that it is can kimonos
Dress fabric directly bonds, and simplifies the work flow of clothing, improves production production efficiency, improves the style of clothing, it is achieved
Simple generous useful visual effect.
The technical scheme is that one spins lining adhesion lining cloth, including base fabric and thermoplastic binder resin, pass through
The described thermoplastic binder resin of the surface coating point-like of pretreated described base fabric.
Further, described pretreatment includes refine, dyes, shapes and/or stamp.
After dyeing and finishing sizing or stamp process, coated the thermoplastic of scatterplot shape at base reverse of the cloth by double-dot coating technology
Property binder resin.
Having the basic material spinning base fabric is the Weft knitting fabric for polyester filament.Afterwards through dyeing, sizing or stamp.
In order to embody the concordance of adhesive lining and satinet, base fabric can also stamp the decorative pattern of needs.Stamp can lead to
Cross transfer printing or wire mark realizes.Transfer printing is according to the floral designs determined, first pattern dyestuff or coating is imprinted on
On paper, obtain transfer paper, utilize the high temperature of about 200 DEG C that the dyestuff on calico paper or coating are condensed upon for gas phase by heat sublimation
In base fabric, then permeated by unformed area in fiber macromole, anchor at after cooling inside fabric fibre, formed specific
Floral designs, thus form stamp base fabric.
Further, the decalcomania in base fabric can also be realized by screen printing.Screen printing includes that cylinder prints
Flower and PLATE SCREAM PRINTING etc..The basic principle of its stamp is the part mesh of decorative pattern will not had not to be coated with not according to floral designs, constitute by
The decorative pattern of mesh composition, directly bites on fabric by mill base by decorative pattern mesh, subsequently with the fabric of decorative pattern again through vapour
Steaming, fixation, soap, wash, obtain finished product.
Further, described base fabric preferably employs Weft knitting double-sided cloth, and material is that terylene length is fine.And according to garment material
Thickness, scrim material chooses 30D to 100D dacron elasticity silk, and weft knitting is furnished with preferable agreeableness, is suitable to different
Fabric bonds.
Further, the described thermoplastic binder resin of point-like is random is arranged in described base fabric with interval.
Point-like thermoplastic binder resin of the present invention, it is simply that one by one in point-like, have spaced bonding
Agent.By double-dot coating machine in resin-bonding to base fabric.
Further, described thermoplastic binder resin is copolyamide class and/or copolymerization esters.
Technical scheme also includes that the preparation method of lining adhesion lining cloth is spun in a kind of described above having, including with
Lower step:
(1) pretreatment:
A. refine: carry out refine in High Temperature High Pressure overflow dyeing machine, after being warming up to 85 ~ 90 DEG C, puts into fabric in dye vat,
Make fabric and water together cycle rotation in dye vat, add refining liquid in the process, then heat to refining temperature 100 ~ 120
DEG C, refine 15 ~ 20 minutes, venting refining liquid, takes out after adding cold water washing；
B. dyeing: the fabric after refine is warmed up to 90 DEG C and starts to add dyestuff, is then warmed up to 130 DEG C of insulations 0.4 ~ 0.8 little
Time, adding reduction cleaner after then cooling to 80 DEG C, conventional water wash of lowering the temperature the most again goes out cloth in 15 minutes；
C. dehydration and open-width: the fabric after dyeing is first passed through dehydration equipment and sloughs moisture, then carry out cuing open cloth and open-width, institute
Stating and cuing open cloth is that the fabric of tubular is cutd open into open width；
D. arrange and shape: in the stock tank of collator, adding dressing liquid, make the textile pad dressing liquid after dehydration and open-width
After, enter back in the baking oven of collator, at a temperature of 180 ~ 200 DEG C, make fabric drying shape, wherein, speed 30 ~ 45
M/min；And/or
E. stamp: the fabric after arranging and shaping uses transfer printing, ROTARY SCREAM PRINTING or the mode printing pattern of PLATE SCREAM PRINTING,
Finally give base fabric；
(2) coating: described base fabric is through double-dot coating machine, at the thermoplastic resin of the surface-coated point-like of base fabric, warp the most again
Cross baking oven to bake, sinter, cooling rolling after obtain described in spin lining adhesion lining cloth, wherein, process velocity is 30-40 m/min.
Further, the component of described refining liquid includes metal ion chelation agent, sodium hydroxide, refining agent and water, wherein,
Described metal ion chelation agent, sodium hydroxide and the refining agent content in described refining liquid be respectively 0.1 ~ 0.5 grams per liter, 2 ~
10 grams per liters and refining agent 1 ~ 3 grams per liter.
Specifically, the component in described refining liquid be metal ion chelation agent 0.3 ~ 0.5 grams per liter, wetting softener 0.3 ~
0.5 grams per liter, surfactant 0.1 ~ 0.3 grams per liter, 2 ~ 10 grams per liter sodium hydroxide, desizing agent 0.3 ~ 0.6 grams per liter, remaining is
Water.Dyeing base fabric, dyestuff adds according to the joined pigment proportion of sample.
Further, the component of described dressing liquid includes softening agent, antistatic agent, penetrating agent, acid and water, wherein, described
Softening agent, antistatic agent, penetrating agent and the acid content in described dressing liquid be respectively 10 ~ 20 grams per liters, 0.1 ~ 1.5 grams per liter,
0.1 ~ 0.3 grams per liter and 1 ~ 2 grams per liter.
Specifically, in described dressing liquid component include silicone softening agent 10 ~ 30 grams per liter, antistatic agent 0.5 ~ 1.5 gram/
Liter, waterproofing agent 1 ~ 5 grams per liter, remaining is water.
Further, described sizing is carried out in sizing room, totally 8, described sizing room, and the temperature of each room is: a Room 150 ~
160 DEG C, two 160 ~ 170 DEG C, Room, three 170 ~ 180 DEG C, Room, four 180 ~ 190 DEG C, Room, five 190 ~ 200 DEG C, Room, six 190 ~ 200 DEG C, Room,
Seven 190 ~ 200 DEG C, Room, eight 180 ~ 190 DEG C, Room.
In described stamp, the disperse dyes of application, can distil at a temperature of 180 ~ 200 DEG C and become gas phase dye molecule, Gu
On fiber, and good washing fastness and ironing fastness can be obtained.
Further, described stamp specifically includes: put into once arrange fixed base fabric in transfer printing machine, at printing machine
Add the dressing liquid being configured to by water and auxiliary agent in the liquid bath of tool, after making the above-mentioned textile pad arranged, enter back into printing machine
In the baking oven of tool, at a temperature of 150 ~ 200 DEG C, make fabric drying shape, subsequently enter in printing device, at 180 ~ 210 DEG C
At a temperature of make dye sublimation transfer on fabric, the stamp time is 10 ~ 15 seconds, makes transfer paper by high temperature (about 200 DEG C)
On dye sublimation be that gas phase condenses upon fabric face, then to the unformed area of fiber macromole permeate, set after cooling
Inside fabric fibre, form specific floral designs.The pattern of transfer printing is true to nature, and decorative pattern is fine and smooth, clear layer, third dimension
By force.Or the base fabric after arranging is put in circular screen printer, fabric leans on circulation rubber belt track and base fabric is brought into printing device
In, under the normal operation of sizing device, utilize the regulation by scraper angle of the cylinder design, the road junction of scraper and
The inner circle of cylinder is tangent, scraper to mill base to apply pressure, to scrape be auxiliary to complete printing technology, subsequently into color-fixing device,
At a temperature of 160 ~ 200 DEG C, carry out gas steaming, subsequently enter wash mill, carry out soaping, washing, in rear entrance baking oven, 100 ~
Dry at a temperature of 200 DEG C.Or the base fabric after arranging is put in flat screen printing machine, sent by seamless circulating rubber leader
Enter printing device, move under a screen frame, utilize and carry out upper mill base to sizing device, roll net, utilize scraper to scrape, stop 10
Second, carrying net, fabric moves on and moves to, below next screen frame, print another part pattern, readvance, repeat above operation,
Complete overall stamp, subsequently into color-fixing device
Further, described coating uses the mode of cylinder transfer, is coated on scrim surfaces with point-like equably by prime cement, then
Dispense powdered resin on slurry point surface, then absorb Excess resin by pressure-vaccum system, only make the local guarantor having prime cement in base fabric
Stay resin, then carry out Infrared Heating, temperature 160 ~ 180 DEG C, make prime cement be dried and be bonded on scrim surfaces, subsequently into drying room
Base fabric is shaped, and thermoplastic binder resin sinters, melts and is bonded on slurry point and base fabric.
Further, the temperature of described drying room is 160-200 DEG C.
In general, in cylinder and PLATE SCREAM PRINTING, the location of scraper and the control of angle are the keys of this kind stamp,
The problem that the present invention notes also that these routines.
When coating, use double-dot coating mode, so-called two point, it is simply that in the base fabric handled well, first first coat a kind of point
The prime cement of shape, the surface at slurry point sprinkles powdery hot-melt resin the most again, then absorbs Excess resin, makes to have in base fabric prime cement
Place is stained with or retains resin, then carries out Infrared Heating, and temperature 200 ~ 250 DEG C makes prime cement be dried and is bonded to fabric substrate table
On face, fabric is made to shape subsequently into drying room, drying room temperature 180 ~ 200 DEG C, process velocity 30 ~ 45 ms/min.By means of which
The adhesion lining cloth scribbling double-layer resin can be produced.
So-called prime cement is a kind of containing having that acrylate or polyurethane compositions emulsion add water that thickening agent adjusts
Certain viscosity and the colloid of mobility.
The invention have the characteristics that being different from general routine spins lining, breaches adhesive lining and only can be used in clothing sandwich
In.This lining cloth can replace the satinet of portion of garment so that conventional satinet and HOTMELT ADHESIVE PADDING CLOTH (at garment material and
Between satinet, it is bonded together with fabric by PUR) unite two into one so that the processing of clothing more simplifies, and efficiency improves.
Garment language is brief generous.The particularly bonding back boxing of stamp, gives the stronger sensory effects of fabric and three-dimensional feel.
Accompanying drawing explanation
Fig. 1 is coating schematic diagram of the present invention.
Wherein: 1 is baking oven, 2 is powder reclaiming device, and 3 is air compressor, and 4 is dusting device, and 5 is doctor, and 6 is circle
Net, 7 is prime cement, and 8 for supporting bottom roller, and 9 beat cloth rewinder roll for vibrations, and 10 is base fabric, and 11 is slurry point, and 12 is powdery hot-melt resin, and 13 are
It is bonded at the thermoplastic resin on slurry point.In production, base fabric is behind the gap of cylinder and support bottom roller, and slurry is from the mesh of cylinder
Being transferred on cloth cover by doctor blade coating, base fabric moves on, and at dusting device, is spread last layer powdered resin, then warp
After cloth apparatus is beaten in vibrations, making powdery hot-melt resin be sprinkling upon equably in base fabric, the unnecessary powder between slurry point and slurry point can pass through
Retracting device siphons away, and makes powdery hot-melt resin be evenly distributed on slurry point.Bake through baking oven the most again, sinter so that the end
Slurry and thermoplastic resin anchor in base fabric, eventually pass cooling rolling and complete coating processing.
Detailed description of the invention
The invention provides one and spin lining adhesion lining cloth, including base fabric and thermoplastic binder resin, through pretreatment
After described base fabric surface coating point-like described thermoplastic binder resin.
Preferably, described pretreatment includes refine, dyes, shapes and/or stamp.
After dyeing and finishing sizing or stamp process, coated the thermoplastic of scatterplot shape at base reverse of the cloth by double-dot coating technology
Property binder resin.
Having the basic material spinning base fabric is the Weft knitting fabric for polyester filament.Afterwards through dyeing, sizing or stamp.
In order to embody the concordance of adhesive lining and satinet, base fabric can also stamp the decorative pattern of needs.Stamp can lead to
Cross transfer printing or wire mark realizes.Transfer printing is according to the floral designs determined, first pattern dyestuff or coating is imprinted on
On paper, obtain transfer paper, utilize the high temperature of about 200 DEG C that the dyestuff on calico paper or coating are condensed upon for gas phase by heat sublimation
In base fabric, then permeated by unformed area in fiber macromole, anchor at after cooling inside fabric fibre, formed specific
Floral designs, thus form stamp base fabric.
Preferably, the decalcomania in base fabric can also be realized by screen printing.Screen printing includes ROTARY SCREAM PRINTING
With PLATE SCREAM PRINTING etc..The basic principle of its stamp is to be coated with not according to floral designs by the part mesh not having decorative pattern, constitutes by net
Eye composition decorative pattern, directly mill base is bitten on fabric by decorative pattern mesh, subsequently with decorative pattern fabric again through decatize,
Fixation, soap, wash, obtain finished product.
Preferably, described base fabric preferably employs Weft knitting double-sided cloth, and material is that terylene length is fine.And according to garment material
Thickness, scrim material chooses 30D to 100D dacron elasticity silk, and weft knitting is furnished with preferable agreeableness, is suitable to and different faces
Material bonding.
Preferably, the described thermoplastic binder resin of point-like is random is arranged in described base fabric with interval.
Point-like thermoplastic binder resin of the present invention, it is simply that one by one in point-like, have spaced bonding
Agent.By double-dot coating machine in resin-bonding to base fabric.
Preferably, described thermoplastic binder resin is copolyamide class and/or copolymerization esters.
Present invention also offers a kind of described above having and spin the preparation method of lining adhesion lining cloth, comprise the following steps:
(1) pretreatment:
A. refine: carry out refine in High Temperature High Pressure overflow dyeing machine, after being warming up to 85 ~ 90 DEG C, puts into fabric in dye vat,
Make fabric and water together cycle rotation in dye vat, add refining liquid in the process, then heat to refining temperature 100 ~ 120
DEG C, refine 15 ~ 20 minutes, venting refining liquid, takes out after adding cold water washing；
B. dyeing: the fabric after refine is warmed up to 90 DEG C and starts to add dyestuff, is then warmed up to 130 DEG C of insulations 0.4 ~ 0.8 little
Time, adding reduction cleaner after then cooling to 80 DEG C, conventional water wash of lowering the temperature the most again goes out cloth in 15 minutes；
C. dehydration and open-width: the fabric after dyeing is first passed through dehydration equipment and sloughs moisture, then carry out cuing open cloth and open-width, institute
Stating and cuing open cloth is that the fabric of tubular is cutd open into open width；
D. arrange and shape: in the stock tank of collator, adding dressing liquid, make the textile pad dressing liquid after dehydration and open-width
After, enter back in the baking oven of collator, at a temperature of 180 ~ 200 DEG C, make fabric drying shape, wherein, speed 30 ~ 45
M/min；And/or
E. stamp: the fabric after arranging and shaping uses transfer printing, ROTARY SCREAM PRINTING or the mode printing pattern of PLATE SCREAM PRINTING,
Finally give base fabric；
(2) coating: described base fabric is through double-dot coating machine, at the thermoplastic resin of the surface-coated point-like of base fabric, warp the most again
Cross baking oven to bake, sinter, cooling rolling after obtain described in spin lining adhesion lining cloth, wherein, process velocity is 30-40 m/min.
Further, in one embodiment, there is the preparation method spinning lining adhesion lining cloth, including following step described in a kind of
Rapid:
(1) pretreatment:
A. refine: carry out refine in High Temperature High Pressure overflow dyeing machine, after being warming up to 85 ~ 90 DEG C, puts into fabric in dye vat,
Make fabric and water together cycle rotation in dye vat, add refining liquid in the process, then heat to refining temperature 100 ~ 120
DEG C, refine 15 ~ 20 minutes, venting refining liquid, takes out after adding cold water washing；Preferably refining temperature 110 ± 5 DEG C, refine 15 ~ 20
Minute.
B. dyeing: the fabric after refine is warmed up to 90 DEG C and starts to add dyestuff, is then warmed up to 130 DEG C of insulations 0.4 ~ 0.8
Hour, adding reduction cleaner after then cooling to 80 DEG C, conventional water wash of lowering the temperature the most again goes out cloth in 15 minutes；It is preferably insulation 0.5
Hour
C. dehydration and open-width: the fabric after dyeing is first passed through dehydration equipment and sloughs moisture, then carry out cuing open cloth and open-width, institute
Stating and cuing open cloth is that the fabric of tubular is cutd open into open width；
D. arrange and shape: in the stock tank of collator, adding dressing liquid, make the textile pad dressing liquid after dehydration and open-width
After, enter back in the baking oven of collator, at a temperature of 180 ~ 200 DEG C, make fabric drying shape, wherein, speed 30 ~ 45
M/min, preferably 190 ± 5 DEG C；With
E. stamp: the fabric after arranging and shaping uses transfer printing, ROTARY SCREAM PRINTING or the mode printing pattern of PLATE SCREAM PRINTING,
Finally give base fabric；
(2) coating: described base fabric is through double-dot coating machine, at the thermoplastic resin of the surface-coated point-like of base fabric, warp the most again
Cross baking oven to bake, sinter, cooling rolling after obtain described in spin lining adhesion lining cloth, wherein, process velocity is 30-40 m/min.
Further, the component of described refining liquid includes metal ion chelation agent, sodium hydroxide, refining agent and water, wherein,
Described metal ion chelation agent, sodium hydroxide and the refining agent content in described refining liquid be respectively 0.1 ~ 0.5 grams per liter, 2 ~
10 grams per liters and refining agent 1 ~ 3 grams per liter.
Specifically, alternatively, the component in described refining liquid is soft in being metal ion chelation agent 0.3 ~ 0.5 grams per liter, bath
Agent 0.3 ~ 0.5 grams per liter, surfactant 0.1 ~ 0.3 grams per liter, 2 ~ 10 grams per liter sodium hydroxide, desizing agent 0.3 ~ 0.6 grams per liter, its
Yu Weishui.Dyeing base fabric, dyestuff adds according to the joined pigment proportion of sample.
Further, the component of described dressing liquid includes softening agent, antistatic agent, penetrating agent, acid and water, wherein, described
Softening agent, antistatic agent, penetrating agent and the acid content in described dressing liquid be respectively 10 ~ 20 grams per liters, 0.1 ~ 1.5 grams per liter,
0.1 ~ 0.3 grams per liter and 1 ~ 2 grams per liter.
Specifically, alternatively, in described dressing liquid component include silicone softening agent 10 ~ 30 grams per liter, antistatic agent 0.5 ~
1.5 grams per liters, waterproofing agent 1 ~ 5 grams per liter, remaining is water.
Further, described sizing is carried out in sizing room, totally 8, described sizing room, and the temperature of each room is: a Room 150 ~
160 DEG C, two 160 ~ 170 DEG C, Room, three 170 ~ 180 DEG C, Room, four 180 ~ 190 DEG C, Room, five 190 ~ 200 DEG C, Room, six 190 ~ 200 DEG C, Room,
Seven 190 ~ 200 DEG C, Room, eight 180 ~ 190 DEG C, Room.
Preferably, described sizing is carried out in sizing room, totally 8, described sizing room, and the temperature of each room is: 154 DEG C, a Room, and two
166 DEG C, room, three 173 DEG C, Room, four 19 DEG C, Room, five 198 DEG C, Room, six 195 DEG C, Room, seven 200 DEG C, Room, eight 188 DEG C, Room.Certainly, above
The scope of lower floating 1 DEG C is to allow.
In described stamp, the disperse dyes of application, can distil at a temperature of 180 ~ 200 DEG C and become gas phase dye molecule, Gu
On fiber, and good washing fastness and ironing fastness can be obtained.
Further, described stamp specifically includes: put into once arrange fixed base fabric in transfer printing machine, at printing machine
Add the dressing liquid being configured to by water and auxiliary agent in the liquid bath of tool, after making the above-mentioned textile pad arranged, enter back into printing machine
In the baking oven of tool, at a temperature of 150 ~ 200 DEG C, make fabric drying shape, subsequently enter in printing device, at 180 ~ 210 DEG C
At a temperature of make dye sublimation transfer on fabric, the stamp time is 10 ~ 15 seconds, makes transfer paper by high temperature (about 200 DEG C)
On dye sublimation be that gas phase condenses upon fabric face, then to the unformed area of fiber macromole permeate, set after cooling
Inside fabric fibre, form specific floral designs.The pattern of transfer printing is true to nature, and decorative pattern is fine and smooth, clear layer, third dimension
By force.Or the base fabric after arranging is put in circular screen printer, fabric leans on circulation rubber belt track and base fabric is brought into printing device
In, under the normal operation of sizing device, utilize the regulation by scraper angle of the cylinder design, the road junction of scraper and
The inner circle of cylinder is tangent, scraper to mill base to apply pressure, to scrape be auxiliary to complete printing technology, subsequently into color-fixing device,
At a temperature of 160 ~ 200 DEG C, carry out gas steaming, subsequently enter wash mill, carry out soaping, washing, in rear entrance baking oven, 100 ~
Dry at a temperature of 200 DEG C.Or the base fabric after arranging is put in flat screen printing machine, sent by seamless circulating rubber leader
Enter printing device, move under a screen frame, utilize and carry out upper mill base to sizing device, roll net, utilize scraper to scrape, stop 10
Second, carrying net, fabric moves on and moves to, below next screen frame, print another part pattern, readvance, repeat above operation,
Complete overall stamp, subsequently into color-fixing device
Further, described coating uses the mode of cylinder transfer, is coated on scrim surfaces with point-like equably by prime cement, then
Dispense powdered resin on slurry point surface, then absorb Excess resin by pressure-vaccum system, only make the local guarantor having prime cement in base fabric
Stay resin, then carry out Infrared Heating, temperature 160 ~ 180 DEG C, make prime cement be dried and be bonded on scrim surfaces, subsequently into drying room
Base fabric is shaped, and thermoplastic binder resin sinters, melts and is bonded on slurry point and base fabric.
Further, the temperature of described drying room is 160-200 DEG C.
In general, in cylinder and PLATE SCREAM PRINTING, the location of scraper and the control of angle are the keys of this kind stamp,
The problem that the present invention notes also that these routines.
When coating, use double-dot coating mode, so-called two point, it is simply that in the base fabric handled well, first first coat a kind of point
The prime cement of shape, the surface at slurry point sprinkles powdery hot-melt resin the most again, then absorbs Excess resin, makes to have in base fabric prime cement
Place is stained with or retains resin, then carries out Infrared Heating, and temperature 200 ~ 250 DEG C makes prime cement be dried and is bonded to fabric substrate table
On face, fabric is made to shape subsequently into drying room, drying room temperature 180 ~ 200 DEG C, process velocity 30 ~ 45 ms/min.By means of which
The adhesion lining cloth scribbling double-layer resin can be produced.
So-called prime cement is a kind of containing having that acrylate or polyurethane compositions emulsion add water that thickening agent adjusts
Certain viscosity and the colloid of mobility.
Below in conjunction with example, the present invention will be described.The present invention is not limited to lifted example.Need the lining cloth of stamp
In addition to increasing revenue stamp process, other operation is identical.
Embodiment 1
50D/48F long fibre low elastic polyester filament, weft knitting rib-loop double-sided cloth, finished product target grammes per square metre 100g/m2。
Refine: the auxiliary component in refining liquid is metal ion chelation agent 0.3 grams per liter, wetting softener 0.3 grams per liter, table
Face activating agent 0.1 grams per liter, 5 grams per liter sodium hydroxide, desizing agent 0.3 grams per liter, remaining is water.It is warming up to 85 degree put into by fabric
In overflow cylinder, make fabric and water together cycle rotation in dye vat, then heat to refining temperature 100 DEG C, refine 15 minutes, row
Remove refining liquid, take out after adding cold water washing.
Sizing: the auxiliary component in sizing dressing liquid is silicone softening agent 20 grams per liter, antistatic agent 0.5 grams per liter, prevents
Water preparation 5 grams per liter, remaining is water.After making the above-mentioned base fabric dehydration through refine, open-width after forming machine padding finishing liquid, then
Enter in the baking oven of collator, at a temperature of 190 DEG C, make fabric drying shape, speed 45 meters.
Stamp: the base fabric once arranging sizing is put in transfer printing machine, addition 5 grams in the liquid bath of Printing Machinery/
Rise stabilizer remaining be water, after making above-mentioned fabrics pad, enter back in the baking oven of Printing Machinery, at a temperature of 150 DEG C, make
Fabric drying is shaped, and subsequently enters in printing device, makes dye sublimation transfer on fabric, during stamp at a temperature of 200 DEG C
Between be 10 seconds, anchor at after cooling inside fabric fibre, form specific floral designs.
Coating: use double-dot coating mode, first passes through cylinder and coats prime cement in base fabric, the most again on the surface of slurry point
Sprinkle powdery hot-melt resin, then absorb Excess resin, make in base fabric, have the place of prime cement to be stained with or retain resin, then carry out red
External heat, temperature 200 DEG C, make prime cement be dried and be bonded on fabric substrate surface, making fabric shape subsequently into drying room, drying room
Temperature 193 DEG C, process velocity 35 ms/min.It is then passed through cooling down machine under rolling.
Embodiment 2
50D/48F long fibre low elastic polyester filament, weft knitting rib-loop double-sided cloth, finished product target grammes per square metre 100g/m2。
Refine: the auxiliary component in refining liquid is metal ion chelation agent 0.2 grams per liter, wetting softener 0.5 grams per liter, table
Face activating agent 0.2 grams per liter, 5 grams per liter sodium hydroxide, desizing agent 0.4 grams per liter, remaining is water.It is warming up to 85 degree put into by fabric
In overflow cylinder, make fabric and water together cycle rotation in dye vat, then heat to refining temperature 110 DEG C, refine 15 minutes, row
Remove refining liquid, take out after adding cold water washing.
Sizing: the auxiliary component in sizing dressing liquid is silicone softening agent 28 grams per liter, antistatic agent 0.9 grams per liter, prevents
Water preparation 4 grams per liter, remaining is water.After making the above-mentioned base fabric dehydration through refine, open-width after forming machine padding finishing liquid, then
Enter in the baking oven of collator, at a temperature of 190 DEG C, make fabric drying shape, speed 45 meters.
Stamp: the base fabric once arranging sizing is put in transfer printing machine, adds 4.5 in the liquid bath of Printing Machinery
The stabilizer of grams per liter remaining be water, after making above-mentioned fabrics pad, enter back in the baking oven of Printing Machinery, the temperature of 150 DEG C
Under, make fabric drying shape, subsequently enter in printing device, make dye sublimation transfer on fabric at a temperature of 200 DEG C, print
Taking time is 10 seconds, anchors at after cooling inside fabric fibre, forms specific floral designs.
Coating: use double-dot coating mode, first passes through cylinder and coats prime cement in base fabric, the most again on the surface of slurry point
Sprinkle powdery hot-melt resin, then absorb Excess resin, make in base fabric, have the place of prime cement to be stained with or retain resin, then carry out red
External heat, temperature 200 DEG C, make prime cement be dried and be bonded on fabric substrate surface, making fabric shape subsequently into drying room, drying room
Temperature 190 DEG C, process velocity 40 ms/min.It is then passed through cooling down machine under rolling.
It should be noted that of the present invention spin lining adhesion lining cloth use include base fabric and thermoplastic binder resin etc.
Material, includes pretreatment, material, coating method, coated form and braiding etc. by limiting further so that finally give
Described have spin lining adhesion lining cloth there is prominent feature, including application simple and flexible, convenient later maintenance, need not arrest
Mud is in the restriction of carrying out washing treatment mode, the most right, has the preparation method spinning lining adhesion lining cloth, wherein, sternly described in correspondence
The temperature range that lattice limit is necessary technical characteristic, and the actual temp point limited is preferred technical characteristic, above-mentioned enforcement
Although technical scheme is not limited by example 1 and embodiment 2, but is preferred embodiment.
Being described in detail the specific embodiment of the present invention above, but it is intended only as example, the present invention does not limit
It is formed on particular embodiments described above.To those skilled in the art, any equivalent modifications that the present invention is carried out and
Substitute the most all among scope of the invention.Therefore, the impartial conversion made without departing from the spirit and scope of the invention and
Amendment, all should contain within the scope of the invention.
Claims (10)
1. one kind is spun lining adhesion lining cloth, it is characterised in that include base fabric and thermoplastic binder resin, through pretreated
The described thermoplastic binder resin of the surface coating point-like of described base fabric.
The most according to claim 1 spin lining adhesion lining cloth, it is characterised in that described pretreatment include refine, dyeing,
Sizing and/or stamp.
The most according to claim 1 spin lining adhesion lining cloth, it is characterised in that described base fabric uses Weft knitting two-sided
Cloth, material is that terylene length is fine.
The most according to claim 1 spin lining adhesion lining cloth, it is characterised in that the described thermoplastic binder resin of point-like
Random it is arranged in interval in described base fabric.
The most according to claim 1 spin lining adhesion lining cloth, it is characterised in that described thermoplastic binder resin is copolymerization
Amide-type and/or copolymerization esters.
6. having as described in any one in claim 1-5 spins the preparation method of lining adhesion lining cloth, it is characterised in that
Comprise the following steps:
(1) pretreatment:
A. refine: carry out refine in High Temperature High Pressure overflow dyeing machine, after being warming up to 85 ~ 90 DEG C, puts into fabric in dye vat,
Make fabric and water together cycle rotation in dye vat, add refining liquid in the process, then heat to refining temperature 100 ~ 120
DEG C, refine 15 ~ 20 minutes, venting refining liquid, takes out after adding cold water washing；
B. dyeing: the fabric after refine is warmed up to 90 DEG C and starts to add dyestuff, is then warmed up to 130 DEG C of insulations 0.4 ~ 0.8 little
Time, adding reduction cleaner after then cooling to 80 DEG C, conventional water wash of lowering the temperature the most again goes out cloth in 15 minutes；
C. dehydration and open-width: the fabric after dyeing is first passed through dehydration equipment and sloughs moisture, then carry out cuing open cloth and open-width, institute
Stating and cuing open cloth is that the fabric of tubular is cutd open into open width；
D. arrange and shape: in the stock tank of collator, adding dressing liquid, make the textile pad dressing liquid after dehydration and open-width
After, enter back in the baking oven of collator, at a temperature of 180 ~ 200 DEG C, make fabric drying shape, wherein, speed 30 ~ 45
M/min；And/or
E. stamp: the fabric after arranging and shaping uses transfer printing, ROTARY SCREAM PRINTING or the mode printing pattern of PLATE SCREAM PRINTING,
Finally give base fabric；
(2) coating: described base fabric is through coating machine, at the thermoplastic resin of the surface-coated point-like of base fabric, the most again through overbaking
Case bakes, sinters, cooling rolling after obtain described in spin lining adhesion lining cloth, wherein, process velocity is 30-40 m/min.
The most according to claim 6 have the preparation method spinning lining adhesion lining cloth, it is characterised in that the group of described refining liquid
Divide and include metal ion chelation agent, sodium hydroxide, refining agent and water, wherein, described metal ion chelation agent, sodium hydroxide and essence
Refining agent content in described refining liquid is respectively 0.1 ~ 0.5 grams per liter, 2 ~ 10 grams per liters and refining agent 1 ~ 3 grams per liter.
The most according to claim 6 have the preparation method spinning lining adhesion lining cloth, it is characterised in that the group of described dressing liquid
Dividing and include softening agent, antistatic agent, penetrating agent, acid and water, wherein, described softening agent, antistatic agent, penetrating agent and acid are described
Content in dressing liquid is respectively 10 ~ 20 grams per liters, 0.1 ~ 1.5 grams per liter, 0.1 ~ 0.3 grams per liter and 1 ~ 2 grams per liter.
The most according to claim 6 have the preparation method spinning lining adhesion lining cloth, it is characterised in that described coating uses circle
The mode of net transfer, is coated on scrim surfaces with point-like equably by prime cement, then dispenses powdered resin, then on slurry point surface
Absorb Excess resin by pressure-vaccum system, only make in base fabric, have the local of prime cement to retain resin, then carry out Infrared Heating, temperature
160 ~ 180 DEG C, make prime cement be dried and be bonded on scrim surfaces, subsequently into drying room, base fabric being shaped, thermoplastic bonded tree
Fat sinters, melts and is bonded on slurry point and base fabric.
The most according to claim 9 have the preparation method spinning lining adhesion lining cloth, it is characterised in that the temperature of described drying room
Degree is for 160-200 DEG C.