CN106666881A - Elastic waist interlining - Google Patents
Elastic waist interlining Download PDFInfo
- Publication number
- CN106666881A CN106666881A CN201611237690.8A CN201611237690A CN106666881A CN 106666881 A CN106666881 A CN 106666881A CN 201611237690 A CN201611237690 A CN 201611237690A CN 106666881 A CN106666881 A CN 106666881A
- Authority
- CN
- China
- Prior art keywords
- base fabric
- elastic waist
- elastic
- double
- served
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an elastic waist interlining which comprises a basic fabric and a double-point coating. The basic fabric is made of a 75D woven full-polyester 2/2 damask, and the double-point coating is made from thermoplastic resin polyamide PA; the basic fabric is preprocessed, the double-point coating is formed on the surface of the basic fabric in a dotted distribution mode, and finally the elastic waist interlining is formed; basic fabric preprocessing includes refining and dyeing, dehydration and scotching and finishing and sizing; the double-point coating is a lining coating formed by coating the surface of the basic fabric with dotted thermoplastic resin through a double-point coating machine, then performing baking and sintering through a baking oven and performing cooling and rolling, wherein the processing speed is 30-40 meters/minutes. By selecting the basic fabric and limiting the double-point coating including a making method of the elastic waist interlining, finally obtained elastic waist interlining can be bonded with an elastic fabric, the problem of lining usage at the waist part of trousers is solved, and the demand for the elastic waist interlining made of the elastic fabric on the market is met.
Description
Technical field
The present invention relates to field of textiles, more particularly to a kind of elastic waist lining.
Background technology
Lining cloth is played very as a kind of textile material for setting off fabric and improving clothing performance to the graceful outward appearance of clothes
Big effect, promotes clothes to have perfect moulding, can make up fabric performance not enough in itself.From the point of view of general, dress lining cloth
It is generally divided into nonwoven and there are two major classes of spinning.Wherein, nonwoven is exactly the cloth not formed by weaving, specifically：First will
Chemical fibre viscose glue forms base fabric by high temperature, high pressure；Then it is coated with one layer of PUR in scrim surfaces by coating machine；Pass through again
Drying is formed the nonwoven lining cloth used by us.The application method of nonwoven lining cloth is that the one side that lining cloth has glue is placed on into fabric
On, then being heated with bonder or flatiron melts the glue on lining cloth, so as to reach the effect being bonded on fabric.Although nonwoven
Lining cloth has cheap, soft advantage, but there is not washable defect.Relatively, having spinning lining cloth then generally needs
Terylene is made into base fabric by weaving first by equipment such as key lever loom and water-jet looms, gluing is yet further passed through afterwards
Formed.Have the advantages that the pulling force that spinning lining cloth has is strong, elastic good, make it have widely application.
At present, with the variation of garment material, elastic fabric is more and more, elastic fabric improve clothes with
With property and comfortableness, the particularly elastic waist of trousers improves retractility.In order to improve the thickness of the waist of trousers, the general waist of trousers has bonding
Lining is used, and in order to keep the retractility of the original fabric of the waist of trousers, it requires that waist lining will also have larger regime of elastic deformation.
Therefore, develop a kind of elastic waist lining adhesion lining cloth be those skilled in the art in the urgent need to.
The content of the invention
It is an object of the invention to provide a kind of elastic waist lining, by selection and the restriction of double-dot coating to base fabric, its
Include its method for preparing, serving as a contrast the elastic waist for finally giving can bond with elastic fabric, solve elastic fabric, especially
It is that waistband uses lining problem, meets the demand that in the market glues lining to the elastic fabric waist of trousers.
The technical scheme is that：
A kind of elastic waist lining, including base fabric and double-dot coating, wherein：
The base fabric washs 2/2 twill entirely using 75D is woven；
The double-dot coating uses thermoplastic polyamide resin PA；
The base fabric is formed in the surface of the base fabric by pretreatment, the double-dot coating in the way of spot distribution, finally
Form the elastic waist lining.
Further, the material warp thread of the base fabric uses the high-elastic dacron elasticity silks of PBT, weft yarn to use low elastic polyester filament.
Further, the pretreatment of the base fabric, including refining and dyeing, dehydration and open-width and arrangement and sizing.
Specifically：
The refining and dyeing：
It is concise --- under the conditions of 85 ~ 90 DEG C, base fabric cycle rotation in water；Refining liquid is added, 100 ~ 120 DEG C are warming up to, it is concise
15 ~ 20 minutes；Refining liquid is excluded, base fabric is rinsed in cold water；
Dyeing --- the base fabric of dyeing will be needed to be warming up to 90 ~ 95 DEG C, add dyestuff；130 ~ 135 DEG C are warming up to, 25-40 is incubated
Minute；80 ~ 85 DEG C are cooled to, reduction cleaner is added；Base fabric washing goes out cloth in 15 minutes.
Dyeed by Overflow dyeing.
Wherein, the refining liquid includes auxiliary agent 1 and water, wherein, the component and each component in the auxiliary agent 1 are in refining liquid
Content be：1 ~ 3 g/l of 0.1 ~ 0.5 g/l of metal ion chelation agent, 2 ~ 10 g/l of NaOH and refining agent.
Wherein, dyestuff is added as needed.
The dehydration and open-width：
Dehydration --- dewater treatment is carried out by dehydration equipment；
Open-width --- open-width is carried out by autoscutch.
The arrangement and sizing：
Arrange --- base fabric is placed in dressing liquid and is processed；
Sizing --- base fabric is placed in baking oven, under the conditions of 180 ~ 200 DEG C, is dried, shaped.
Wherein, the dressing liquid includes auxiliary agent 2 and water, wherein, the component and each component in the auxiliary agent 2 are in dressing liquid
Content be：10 ~ 20 g/l of silicone softening agent, 0.1 ~ 1.5 g/l of antistatic agent, 0.1 ~ 0.3 g/l of bleeding agent and acid 1 ~
2 g/l.
It should be noted that above-mentioned pre-treatment step can as needed carry out selection combination, if for example, need not enter
Row dyeing, then can delete dyeing course；If need not be dehydrated and open-width, this process can be deleted.
Further, the formation of the double-dot coating, including：
Prime cement is equably coated in scrim surfaces in the form of spot distribution by way of cylinder is shifted, slurry point is formed；
The surface for starching point dispenses powdery thermoplastic resin；Then unnecessary powder thermoplastic resin is absorbed by way of pressure-vaccum；Pass through
The mode of infrared heating dries slurry point and is bonded to the surface of base fabric；Base fabric is carried out into secondary sizing in drying room, is made
Powder thermoplastic resin sintered molten is simultaneously bonded in slurry point and base fabric.
Wherein, the temperature of infrared heating is 200 ~ 250 DEG C.
Wherein, drying room temperature when carrying out secondary sizing is 160 ~ 200 DEG C.
Wherein, the powder thermoplastic resin is in point-like, is irregularly layed in the base fabric, as double-dot coating.
Wherein, the number of the cylinder is 25 mesh.
Further, the finished product grammes per square metre of the elastic waist lining is 60g/m2。
The prime cement is preferably to be a kind of emulsion containing acrylate or polyurethane compositions and is added with water and thickener
The colloid with certain viscosity and mobility of adjustment.
It is characteristic of the invention that：The woven thermal smelting adesive lining of general routine is different from, the viscous lining of the elastic fabric waist of trousers is solved
Problem.Base fabric washs 2/2 twill entirely using 75D is woven first, and material warp thread uses the high-elastic dacron elasticity silks of PBT, weft yarn to adopt
With common low elastic polyester filament.The warp-wise elastic extension of product can reach more than 25%.Coating uses 25 mesh cylinders, point-type
Size and density be well suited for waist lining, and fabric bonding after can both ensure the flatness of fabric, can ensure certain viscous again
Close intensity.
Brief description of the drawings
Fig. 1 is the formation process schematic diagram of double-dot coating of the present invention.
Reference：
1 is baking oven, and 2 is powder reclaiming device, and 3 is air compressor, and 4 is dusting device, and 5 is doctor, and 6 is cylinder, and 7 is bottom
Slurry, 8 is support bottom roller, and 9 is that cloth rewinder roll is beaten in vibrations, and 10 is base fabric, and 11 is slurry point, and 12 is powdery hot-melt resin, and 13 is to be bonded at slurry point
On thermoplastic resin.
Specific embodiment
The invention provides a kind of elastic waist lining, including base fabric and double-dot coating, wherein：
The base fabric washs 2/2 twill entirely using 75D is woven；
The double-dot coating uses thermoplastic polyamide resin PA；
The base fabric is formed in the surface of the base fabric by pretreatment, the double-dot coating in the way of spot distribution, finally
Form the elastic waist lining.
In one embodiment, the material warp thread of the base fabric uses the high-elastic dacron elasticity silks of PBT, and weft yarn is low using terylene
Elater.
In one embodiment, the pretreatment of the base fabric, including refining and dyeing, dehydration and open-width and arrangement and fixed
Type.
In a specific embodiment, the step of pretreating process is：
The refining and dyeing：
It is concise --- under the conditions of 85 ~ 90 DEG C, base fabric cycle rotation in water；Refining liquid is added, 100 ~ 120 DEG C are warming up to, it is concise
15 ~ 20 minutes；Refining liquid is excluded, base fabric is rinsed in cold water；
Dyeing --- the base fabric of dyeing will be needed to be warming up to 90 ~ 95 DEG C, add dyestuff；130 ~ 135 DEG C are warming up to, 25-40 is incubated
Minute；80 ~ 85 DEG C are cooled to, reduction cleaner is added；Base fabric washing goes out cloth in 15 minutes.
Dyeed by Overflow dyeing.
Wherein, the refining liquid includes auxiliary agent 1 and water, wherein, the component and each component in the auxiliary agent 1 are in refining liquid
Content be：1 ~ 3 g/l of 0.1 ~ 0.5 g/l of metal ion chelation agent, 2 ~ 10 g/l of NaOH and refining agent.
Wherein, dyestuff is added as needed.
The dehydration and open-width：
Dehydration --- dewater treatment is carried out by dehydration equipment；
Open-width --- open-width is carried out by autoscutch.
The arrangement and sizing：
Arrange --- base fabric is placed in dressing liquid and is processed；
Sizing --- base fabric is placed in baking oven, under the conditions of 180 ~ 200 DEG C, is dried, shaped.
Wherein, the dressing liquid includes auxiliary agent 2 and water, wherein, the component and each component in the auxiliary agent 2 are in dressing liquid
Content be：10 ~ 20 g/l of silicone softening agent, 0.1 ~ 1.5 g/l of antistatic agent, 0.1 ~ 0.3 g/l of bleeding agent and acid 1 ~
2 g/l.
It should be noted that above-mentioned pre-treatment step can as needed carry out selection combination, if for example, need not enter
Row dyeing, then can delete dyeing course；If need not be dehydrated and open-width, this process can be deleted.
In one embodiment, the formation of the double-dot coating, including：
Prime cement is equably coated in scrim surfaces in the form of spot distribution by way of cylinder is shifted, slurry point is formed；
The surface for starching point dispenses powdery thermoplastic resin；Then unnecessary powder thermoplastic resin is absorbed by way of pressure-vaccum；Pass through
The mode of infrared heating dries slurry point and is bonded to the surface of base fabric；Base fabric is carried out into secondary sizing in drying room, is made
Powder thermoplastic resin sintered molten is simultaneously bonded in slurry point and base fabric.
Wherein, the temperature of infrared heating is 200 ~ 250 DEG C.
Wherein, drying room temperature when carrying out secondary sizing is 160 ~ 200 DEG C.
Wherein, the powder thermoplastic resin is in point-like, is irregularly layed in the base fabric, as double-dot coating.
Wherein, the number of the cylinder is 25 mesh.
Wherein, the prime cement be preferably be a kind of emulsion containing acrylate or polyurethane compositions and be added with water and
The colloid with certain viscosity and mobility of thickener adjustment.
In one embodiment, the finished product grammes per square metre of the elastic waist lining is 60g/m2。
The present invention be about the table in woven 75D twills on the ground, using double-dot coating technology apply be covered with hot melt adhesive tree
Fat and formed elastic waist lining, to meet the demand that the in the market elastic fabric waist of trousers glues lining
In a specific embodiment, a kind of elastic waist lining, including base fabric and double-dot coating, wherein：The base fabric uses 75D machines
Knit and wash 2/2 twill entirely；The double-dot coating uses thermoplastic polyamide resin PA；The base fabric is described double by pretreatment
Point coating is formed in the surface of the base fabric in the way of spot distribution, ultimately forms the elastic waist lining；
The pretreatment includes：
（1）Refining, dyeing：Refined in HTHP overflow dyeing machine, after being warming up to 85 ~ 90 DEG C, fabric（That is base fabric）Throw
Enter in dye vat, fabric and water is together rotated in dye vat interior circulation, a certain amount of water and auxiliary agent 1 are added in the process（It is i.e. smart
Refining liquid）, 100 ~ 120 DEG C of refining temperature is then heated to, refine 15 ~ 20 minutes, venting refining liquid, taken after adding cold water washing
Go out；Need the base fabric of dyeing to be warmed up to 90 ° to start plus dyestuff, be then warmed up to or so 130 ° of insulation half an hour, then cool to
80 degree plus reduction cleaner, finally wash 15 minutes in the conventional water of cooling and go out cloth；Wherein, the component and each group in the auxiliary agent 1
Content point in refining liquid is：0.1 ~ 0.5 g/l of metal ion chelation agent, 2 ~ 10 g/l of NaOH and refining agent 1 ~ 3
G/l；The dyestuff is added as needed；
（2）Dehydration, open-width：The above-mentioned base fabric for refining will first pass through dehydration equipment and slough moisture, then on autoscutch
Carry out open-width；
（3）Arrange, shape：The dressing liquid being configured to by water and auxiliary agent 2 is added in the stock tank of collator, make above-mentioned dehydration,
After the base fabric padding finishing liquid that open-width is crossed, enter back into the baking oven of collator, under 180 ~ 200 DEG C of temperature conditionss, make base
Cloth drying, sizing；Wherein, speed is 30 ~ 45 ms/min, content of the component and each component in the auxiliary agent 2 in dressing liquid
For：1 ~ 2 gram of 10 ~ 20 g/l of silicone softening agent, 0.1 ~ 1.5 g/l of antistatic agent, 0.1 ~ 0.3 g/l of bleeding agent and acid/
Rise.
The double-dot coating is to pass through：
By base fabric by double-dot coating machine, the thermoplastic resin of point-like is coated on the surface of base fabric, then baked by baking oven again,
Sintering, cooling winding completes lining cloth coating；Wherein, process velocity is 30 ~ 40 ms/min.
Preferably, it is necessary to the base fabric of dyeing, is carried out according to Overflow dyeing.
Preferably, the baking oven in type-approval process（Shape room）8 are had, the temperature of each room is：One Room 150 ~ 160
DEG C, two 160 ~ 170 DEG C of Room, three 170 ~ 180 DEG C of Room, four 180 ~ 190 DEG C of Room, five 190 ~ 200 DEG C of Room, six 190 ~ 200 DEG C of Room, seven Room
190 ~ 200 DEG C, eight 180 ~ 190 DEG C of Room.
Preferably, when using two point mode coating, the mode shifted using cylinder（The mesh number of cylinder selects 25 mesh）, will
Prime cement is uniformly coated on scrim surfaces with point-like, then dispenses powdered resin on slurry point surface, is then inhaled by pressure-vaccum system
Except Excess resin, only make to have in base fabric the place of prime cement to retain resin, then carry out infrared heating, 200 ~ 250 DEG C of temperature makes prime cement
Dry and be bonded on scrim surfaces, subsequently into drying room so that base fabric is shaped, thermoplastic resin sintered molten is simultaneously bonded to slurry point
On base fabric.160 ~ 200 DEG C of drying room temperature, 30 ~ 40 ms/min of speed.
Base fabric first passes through dyeing and finishing setting process, then coats the corresponding of scatterplot shape in base reverse of the cloth by double-dot coating technology
Thermoplastic resin.
In coating, using double-dot coating mode, so-called two point exactly first first coats a kind of point in the base fabric handled well
The prime cement of shape, then sprinkles powdery hot-melt resin on the surface of slurry point again, then absorbs Excess resin by pressure-vaccum system, makes base
The place for having prime cement on cloth is stained with or retains resin, then carries out infrared heating, 200 ~ 250 DEG C of temperature, prime cement is dried and set
In on fabric substrate surface, fabric is set to shape subsequently into drying room, 160 ~ 200 DEG C of drying room temperature, 30 ~ 45 ms/min of process velocity.
The adhesion lining cloth for scribbling double-layer resin can be produced by means of which.
According to shown in Fig. 1, wherein, 1 is baking oven, and 2 is powder reclaiming device, and 3 is air compressor, and 4 is dusting device, and 5 are
Doctor, 6 is cylinder, and 7 is prime cement, and 8 is support bottom roller, and 9 beat cloth rewinder roll for vibrations, and 10 is base fabric, and 11 is slurry point, and 12 is powdery heat
Cladding resin, 13 is the thermoplastic resin being bonded on slurry point.
Base fabric is by behind the gap of cylinder 6 and support bottom roller 8, slurry is scraped from the mesh of cylinder 6 by doctor 5 in production
Painting is transferred on cloth cover, and base fabric 10 moves on, and at dusting device, is spread last layer powdered resin, then plays cloth through vibrations
After device, powdery hot-melt resin is set equably to be sprinkling upon in base fabric, the unnecessary powder between slurry point and slurry point can be by retracting device
Siphon away, powdery hot-melt resin is evenly distributed on slurry point.Then baked by baking oven again, sintered so that prime cement and hot melt
Resin is anchored in base fabric, is eventually passed cooling winding and is completed coating processing.
In another specific embodiment, 75D/36F POLYESTER HIGH ELASTIC YARNs, woven 2/2 twill, finished product target grammes per square metre
60g/ m2Elastic waist lining, specifically：
Refining：The composition of auxiliary agent 1 in refining liquid is metal ion chelation agent 0.3 g/l, 5 g/l NaOH, refining agents 3
G/l, remaining is water, is warming up to 85 degree by fabric input overflow cylinder, fabric and water is together rotated in dye vat interior circulation, so
After be warming up to 100 DEG C of refining temperature, refine 15 minutes, venting refining liquid, taken out after adding cold water washing；
Sizing：The composition of auxiliary agent 2 in sizing dressing liquid is 20 g/l of silicone softening agent, 0.5 g/l of antistatic agent, waterproofing agent
5 g/l, remaining is water, make it is above-mentioned through refining base fabric dehydration, after open-width by after forming machine padding finishing liquid, entering back into
In the baking oven of collator, at a temperature of 190 DEG C, fabric drying is set to shape, 45 ms/min of speed；
Coating：Using double-dot coating mode, first pass through cylinder and prime cement is coated in base fabric, the surface then put in slurry again sprinkles poly-
Acid amides PA thermoplastic resins, then the Excess resin by the absorption of pressure-vaccum system between points, makes the place for having prime cement in base fabric
Resin is stained with and retained, then carries out infrared heating, 200 DEG C of temperature makes prime cement dry and be bonded on fabric substrate surface, then
Fabric is set to shape into drying room, 180 ~ 200 DEG C of drying room temperature, 35 ms/min of process velocity, then through the lower machine of supercooling winding.
To finally be prepared in the above embodiment of the present invention elastic waist lining A1, with the market buy it is similar serve as a contrast into
The bonding Comparison study of the row waist of trousers, it is found that the present invention solves the problems, such as that the elastic fabric waist of trousers glues lining, specifically：Base fabric is adopted first
2/2 twill is washed entirely with 75D is woven, and material warp thread uses the high-elastic dacron elasticity silks of PBT, weft yarn to use common polyester low stretch
Silk, so that the warp-wise elastic extension of product can reach more than 25%；Secondly, coating use 25 mesh cylinders, point-type it is big
Small and density is well suited for waist and serves as a contrast, and can both ensure the flatness of fabric after fabric bonding, can ensure that certain bonding is strong again
Degree.
Specific embodiment of the invention has been described in detail above, but it is intended only as example, and the present invention is not limited
It is formed on particular embodiments described above.To those skilled in the art, any equivalent modifications carried out to the present invention and
Replacement is also all among scope of the invention.Therefore, the impartial conversion made without departing from the spirit and scope of the invention and
Modification, all should be contained within the scope of the invention.
Claims (10)
1. a kind of elastic waist is served as a contrast, it is characterised in that including base fabric and double-dot coating, wherein：
The base fabric washs 2/2 twill entirely using 75D is woven；
The double-dot coating uses thermoplastic polyamide resin PA；
The base fabric is formed in the surface of the base fabric by pretreatment, the double-dot coating in the way of spot distribution, finally
Form the elastic waist lining.
2. elastic waist according to claim 1 is served as a contrast, it is characterised in that the material warp thread of the base fabric is washed using PBT is high-elastic
Synthetic fibre elastic filament, weft yarn uses low elastic polyester filament.
3. elastic waist according to claim 1 is served as a contrast, it is characterised in that the finished product grammes per square metre of the elastic waist lining is 60g/m2。
4. elastic waist according to claim 1 is served as a contrast, it is characterised in that the pretreatment of the base fabric, including refine and dye,
Dehydration and open-width and arrangement and sizing.
5. elastic waist according to claim 1 is served as a contrast, it is characterised in that the refining and dyeing：
It is concise --- under the conditions of 85 ~ 90 DEG C, base fabric cycle rotation in water；Refining liquid is added, 100 ~ 120 DEG C are warming up to, it is concise
15 ~ 20 minutes；Refining liquid is excluded, base fabric is rinsed in cold water；
Dyeing --- the base fabric of dyeing will be needed to be warming up to 90 ~ 95 DEG C, add dyestuff；130 ~ 135 DEG C are warming up to, 25-40 is incubated
Minute；80 ~ 85 DEG C are cooled to, reduction cleaner is added；Base fabric washing goes out cloth in 15 minutes；
The refining liquid includes auxiliary agent 1 and water, wherein, the content of component and each component in the auxiliary agent 1 in refining liquid is：
1 ~ 3 g/l of 0.1 ~ 0.5 g/l of metal ion chelation agent, 2 ~ 10 g/l of NaOH and refining agent.
6. elastic waist according to claim 1 is served as a contrast, it is characterised in that the arrangement and sizing：
Arrange --- base fabric is placed in dressing liquid and is processed；
Sizing --- base fabric is placed in baking oven, under the conditions of 180 ~ 200 DEG C, is dried, shaped；
Wherein, the dressing liquid includes auxiliary agent 2 and water, wherein, component and each component the containing in dressing liquid in the auxiliary agent 2
Measure and be：1 ~ 2 gram of 10 ~ 20 g/l of silicone softening agent, 0.1 ~ 1.5 g/l of antistatic agent, 0.1 ~ 0.3 g/l of bleeding agent and acid/
Rise.
7. elastic waist according to claim 1 is served as a contrast, it is characterised in that the formation of the double-dot coating, including：By cylinder
Prime cement is equably coated in scrim surfaces by the mode of transfer in the form of spot distribution, forms slurry point；Spread on the surface of slurry point
Cloth powder thermoplastic resin；Then unnecessary powder thermoplastic resin is absorbed by way of pressure-vaccum；By infrared heating
Mode dries slurry point and is bonded to the surface of base fabric；Base fabric is carried out into secondary sizing in drying room, makes powder thermoplastic tree
Fat sintered molten is simultaneously bonded in slurry point and base fabric.
8. elastic waist according to claim 7 is served as a contrast, it is characterised in that the temperature of infrared heating is 200 ~ 250 DEG C；Carry out
Drying room temperature during secondary sizing is 160 ~ 200 DEG C.
9. elastic waist according to claim 7 is served as a contrast, it is characterised in that the number of the cylinder is 25 mesh.
10. elastic waist according to claim 7 is served as a contrast, it is characterised in that the prime cement is a kind of containing acrylate or poly-
The emulsion of urethane composition is simultaneously added with the colloid with certain viscosity and mobility that water and thickener are adjusted.