CN110846906A - Novel woven tape bonding lining cloth material and production process - Google Patents
Novel woven tape bonding lining cloth material and production process Download PDFInfo
- Publication number
- CN110846906A CN110846906A CN201911047864.8A CN201911047864A CN110846906A CN 110846906 A CN110846906 A CN 110846906A CN 201911047864 A CN201911047864 A CN 201911047864A CN 110846906 A CN110846906 A CN 110846906A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- lining cloth
- woven tape
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel woven tape bonding lining cloth material and a production process thereof, wherein the novel woven tape bonding lining cloth material comprises the following raw materials in parts by weight: the coating comprises, by weight, 50-60 parts of base material fibers, 30-40 parts of coating slurry and the balance of deionized water, wherein the base material fibers consist of 40-50 parts of polyester fibers, 10-20 parts of polybutylene terephthalate (PBT) fibers, 5-10 parts of polyamide 66 fibers and 10-20 parts of polyurethane fibers, and the coating slurry consists of 25-40 parts of hot melt adhesive powder, 25-40 parts of dispersing agents, 1-5 parts of thickening agents, 1-3 parts of stabilizing agents, 1-3 parts of photocatalysts, 1-3 parts of defoaming agents and the balance of water. This novel meshbelt bonding lining cloth new material and production technology can realize taking the synthetic fiber that elasticity is strong as the base stock fibre through adopting, has increased meshbelt bonding lining cloth's elasticity greatly, simultaneously through adding photocatalyst in the coating, makes meshbelt bonding lining cloth under the shining of external ultraviolet ray light, can release hydroxyl and carry out germicidal treatment to the cloth surface.
Description
Technical Field
The invention relates to the technical field of textile materials, in particular to a novel woven tape bonding lining cloth material and a production process thereof.
Background
The lining cloth of the clothes is a large variety of auxiliary materials of the clothes, and plays a role of a framework on the clothes, if a house is built, reinforced concrete is needed to be used as the framework, and the lining cloth is needed to be used as the framework when the clothes are manufactured, the costume can form beautiful styles of shapes, colors and colors by the functions of shaping, reinforcing and shape keeping of the lining cloth, the lining cloth takes woven fabrics, knitted fabrics and non-woven fabrics as non-base cloth, adopts (or does not adopt) thermoplastic macromolecular compounds, and carries out special finishing processing by special machinery, the special clothing accessories which are used for the inner layer of the clothing to play the roles of reinforcement, stiffness and smoothness and the like and are bonded (or not bonded) with the fabric, the lining cloth is the fabric on the outer surface and the lining material on the inner surface of the clothing, the lining cloth is arranged in the middle of the clothing, therefore, the lining cloth can not be directly seen in general, but the position needing to form stiff, full hand feeling, smooth transition and reinforcement is covered with the lining cloth, wherein the woven tape adhesive lining cloth is most widely used.
Most of the existing woven tape adhesive padding cloth is directly processed by adopting polyester fiber as a base material, and then the base material is coated by using a functional coating, so that the woven tape adhesive padding cloth is obtained, however, the elasticity of the woven tape adhesive padding cloth is limited, the woven tape adhesive padding cloth can only be applied to the production of clothes with lower elasticity requirements, and the processing of the clothes with higher elasticity requirements is limited, for example, the production of mountaineering clothes or fitness clothes and the like is realized, the elasticity of the existing woven tape adhesive padding cloth is insufficient after the existing woven tape adhesive padding cloth is used, the clothes are easy to tear, meanwhile, the existing woven tape adhesive padding cloth does not have a self-cleaning function, dirt or bacteria are dissolved on the woven tape adhesive padding cloth, the bacteria breeding is serious, and the threat to.
Disclosure of Invention
Technical problem to be solved
Aiming at the defects of the prior art, the invention provides a novel woven tape adhesive lining cloth material and a production process thereof, which solve the problems that the elasticity of the existing woven tape adhesive lining cloth is relatively limited, the existing woven tape adhesive lining cloth can only be applied to the production of certain clothes with lower elasticity requirements, and for the production of certain clothes with higher elasticity requirements, such as mountaineering clothes or body-building clothes and the like, the elasticity of the existing woven tape adhesive lining cloth is not enough after the existing woven tape adhesive lining cloth is used, so that the clothes are easy to tear, meanwhile, the existing woven tape adhesive lining cloth does not have a self-cleaning function, dirt or bacteria are dissolved on the woven tape adhesive lining cloth, the bacteria are seriously bred, and the threat to the health of people is caused.
(II) technical scheme
In order to achieve the purpose, the invention is realized by the following technical scheme: a novel woven tape bonding lining cloth material comprises the following raw materials in parts by weight: 50-60 parts of base material fiber, 30-40 parts of coating slurry and the balance of deionized water, wherein the base material fiber consists of 40-50 parts of polyester fiber, 10-20 parts of polybutylene terephthalate (PBT) fiber, 5-10 parts of polyamide 66 fiber and 10-20 parts of polyurethane fiber, and the coating slurry consists of 25-40 parts of hot melt adhesive powder, 25-40 parts of dispersing agent, 1-5 parts of thickening agent, 1-3 parts of stabilizing agent, 1-3 parts of photocatalyst, 1-3 parts of defoaming agent and the balance of water.
Preferably, the raw materials comprise the following components in parts by weight: 55 parts of base material fiber, 35 parts of coating slurry and the balance of deionized water, wherein the base material fiber consists of 45 parts of polyester fiber, 15 parts of polybutylene terephthalate (PBT) fiber, 7 parts of polyamide 66 fiber and 15 parts of polyurethane fiber, and the coating slurry consists of 35 parts of hot melt adhesive powder, 30 parts of dispersing agent, 3 parts of thickening agent, 2 parts of stabilizing agent, 2 parts of photocatalyst, 2 parts of defoaming agent and the balance of water.
Preferably, the raw materials comprise the following components in parts by weight: the coating comprises 50 parts of base material fiber, 30 parts of coating slurry and the balance of deionized water, wherein the base material fiber comprises 40 parts of polyester fiber, 10 parts of polybutylene terephthalate (PBT) fiber, 5 parts of polyamide 66 fiber and 10 parts of polyurethane fiber, and the coating slurry comprises 25 parts of hot melt adhesive powder, 25 parts of dispersing agent, 1 part of thickening agent, 1 part of stabilizing agent, 1 part of photocatalyst, 1 part of defoaming agent and the balance of water.
Preferably, the raw materials comprise the following components in parts by weight: the coating comprises 60 parts of base material fiber, 40 parts of coating slurry and the balance of deionized water, wherein the base material fiber comprises 50 parts of polyester fiber, 20 parts of polybutylene terephthalate (PBT) fiber, 10 parts of polyamide 66 fiber and 20 parts of polyurethane fiber, and the coating slurry comprises 40 parts of hot melt adhesive powder, 40 parts of dispersing agent, 5 parts of thickening agent, 3 parts of stabilizing agent, 3 parts of photocatalyst, 3 parts of defoaming agent and the balance of water.
Preferably, the hot melt adhesive powder is a copolyamide powder.
Preferably, the photocatalyst is one or more of titanium dioxide, zinc oxide or tin oxide in combination.
Preferably, the dispersant is an anionic polyacrylamide.
The invention also discloses a production process of the novel woven tape adhesive lining cloth material, which specifically comprises the following steps:
s1, preparation of a mixture of base fibers: firstly, respectively measuring required polyester fibers, polybutylene terephthalate (PBT) fibers, polyamide 66 fibers and polyurethane fibers by using weighing equipment, then sequentially pouring all fiber materials into mixing and stirring equipment, then adding deionized water in corresponding weight ratio, stirring for 1-2 hours by using the stirring equipment at the rotating speed of 700-;
s2, preparation of coating slurry: respectively measuring required hot melt adhesive powder, a dispersing agent, a thickening agent, a stabilizing agent, a photocatalyst and a defoaming agent by using weighing equipment, then adding the measured components into mixing and stirring equipment, simultaneously adding water in corresponding weight parts, and stirring for 1-2 hours by using the stirring equipment at the rotating speed of 700-;
s3, weaving base cloth: weaving the base material fiber obtained in the step S1 by using an air jet loom through warp and weft to obtain a base layer woven fabric;
s4, forming of the woven tape adhesive lining cloth: coating the coating slurry obtained in the step S2 on the base layer woven cloth woven in the step S3 through dispensing coating equipment, then carrying out hot air drying treatment through hot air drying equipment, and then carrying out cooling treatment through cooling equipment to enable the coating to be rapidly melted and solidified on the base layer woven cloth, so that woven tape adhesive lining cloth is obtained;
s5, processing of the woven tape adhesive lining cloth finished product: and (4) cutting and forming the woven tape adhesive lining cloth obtained in the step (S4) by using cutting equipment, cleaning for 2-3 times by using cleaning equipment, thoroughly cleaning impurities on the surface of the cloth, drying, and finally rolling and packaging the dried cloth by using a round roller to obtain a woven tape adhesive lining cloth finished product.
(III) advantageous effects
The invention provides a novel woven tape bonding lining cloth material and a production process thereof. Compared with the prior art, the method has the following beneficial effects: the novel woven tape bonding lining cloth material and the production process comprise the following raw materials in parts by weight: 50-60 parts of base material fiber, 30-40 parts of coating slurry and the balance of deionized water, wherein the base material fiber consists of 40-50 parts of polyester fiber, 10-20 parts of polybutylene terephthalate (PBT) fiber, 5-10 parts of polyamide 66 fiber and 10-20 parts of polyurethane fiber, and the coating slurry consists of 25-40 parts of hot melt adhesive powder, 25-40 parts of dispersing agent, 1-5 parts of thickening agent, 1-3 parts of stabilizing agent, 1-3 parts of photocatalyst, 1-3 parts of defoaming agent and the balance of water, so that the elasticity of the woven tape bonding lining cloth is greatly increased by adopting synthetic fiber with strong elasticity as the base material fiber, the woven tape bonding lining cloth can be applied to the production of clothes with lower elasticity requirement, can be well applied to the processing of clothes with higher elasticity requirement, and can avoid the insufficient elasticity of the woven tape bonding lining cloth after being used, the condition that the clothing is torn is made to occur, and meanwhile, the photocatalyst is added into the coating layer, so that the mesh belt adhesive lining cloth can release hydroxyl to sterilize the surface of the cloth under the irradiation of external ultraviolet light, the mesh belt adhesive lining cloth has a self-cleaning function, the problem that dirt or bacteria are dissolved on the mesh belt adhesive lining cloth and the bacteria are seriously bred is well solved, and the health of people is guaranteed to be free from threats.
Drawings
FIG. 1 is a flow chart of the production process of the present invention.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Referring to fig. 1, the embodiment of the present invention provides three technical solutions: a novel mesh belt bonding lining cloth material and a production process specifically comprise the following embodiments:
example 1
S1, preparation of a mixture of base fibers: firstly, respectively weighing 45 parts of polyester fiber, 15 parts of polybutylene terephthalate (PBT) fiber, 7 parts of polyamide 66 fiber and 15 parts of polyurethane fiber by weighing equipment, then sequentially pouring all fiber materials into mixing and stirring equipment, adding deionized water in corresponding weight ratio, stirring for 1.5 hours by the stirring equipment at the rotating speed of 750 r/min and the temperature of 27 ℃ until the mixture is pasty, then transferring the pasty mixture into fiber drawing equipment, and sequentially performing extrusion molding, wire drawing, drying and forming processes to obtain base material fiber;
s2, preparation of coating slurry: respectively weighing 35 parts of required hot melt adhesive powder, 30 parts of dispersing agent, 3 parts of thickening agent, 2 parts of stabilizing agent, 2 parts of photocatalyst and 2 parts of defoaming agent by using weighing equipment, adding the weighed components into mixing and stirring equipment, simultaneously adding water in corresponding weight ratio, and stirring for 1.5 hours by using the stirring equipment at the rotating speed of 750r \ min until the mixture is pasty, so as to obtain coating slurry, wherein the hot melt adhesive powder is copolyamide powder, the photocatalyst is a composition of titanium dioxide, zinc oxide and tin oxide, and the dispersing agent is anionic polyacrylamide;
s3, weaving base cloth: weaving 55 parts of the base material fiber obtained in the step S1 by using an air jet loom through warp and weft yarns to obtain a base layer woven fabric;
s4, forming of the woven tape adhesive lining cloth: coating the 35 parts of coating slurry obtained in the step S2 on the base layer woven cloth in the step S3 through dispensing coating equipment, then carrying out hot air drying treatment through hot air drying equipment, and then carrying out cooling treatment through cooling equipment to enable the coating to be rapidly melted and solidified on the base layer woven cloth, so that the woven tape adhesive lining cloth is obtained;
s5, processing of the woven tape adhesive lining cloth finished product: and (4) cutting and forming the woven tape adhesive lining cloth obtained in the step (S4) by using cutting equipment, cleaning for 2 times by using cleaning equipment, thoroughly cleaning impurities on the surface of the cloth, drying, and finally rolling and packaging the dried cloth by using a round roller to obtain a woven tape adhesive lining cloth finished product.
Example 2
S1, preparation of a mixture of base fibers: firstly, respectively weighing 40 parts of polyester fiber, 10 parts of polybutylene terephthalate (PBT) fiber, 5 parts of polyamide 66 fiber and 10 parts of polyurethane fiber by weighing equipment, then sequentially pouring all fiber materials into mixing and stirring equipment, then adding deionized water in corresponding weight ratio, stirring for 1h by the stirring equipment at the rotating speed of 700 r/min and the temperature of 25 ℃ until the mixture is pasty, then transferring the pasty mixture into fiber drawing equipment, and sequentially performing extrusion molding, wire drawing, drying and forming processes to obtain base material fiber;
s2, preparation of coating slurry: respectively measuring 25 parts of hot melt adhesive powder, 25 parts of dispersing agent, 1 part of thickening agent, 1 part of stabilizing agent, 1 part of photocatalyst and 1 part of defoaming agent by using weighing equipment, adding the measured components into mixing and stirring equipment, simultaneously adding water in corresponding weight ratio, and stirring for 1h at the rotating speed of 700 r/min by using the stirring equipment until the mixture is pasty, thereby obtaining coating slurry, wherein the hot melt adhesive powder is copolyamide powder, the photocatalyst is titanium dioxide, and the dispersing agent is anionic polyacrylamide;
s3, weaving base cloth: weaving 50 parts of the base material fiber obtained in the step S1 by using an air jet loom through warp and weft yarns to obtain a base layer woven fabric;
s4, forming of the woven tape adhesive lining cloth: coating the 30 parts of coating slurry obtained in the step S2 on the base layer woven cloth in the step S3 through dispensing coating equipment, then carrying out hot air drying treatment through hot air drying equipment, and then carrying out cooling treatment through cooling equipment to enable the coating to be rapidly melted and solidified on the base layer woven cloth, so that the woven tape adhesive lining cloth is obtained;
s5, processing of the woven tape adhesive lining cloth finished product: and (4) cutting and forming the woven tape adhesive lining cloth obtained in the step (S4) by using cutting equipment, cleaning for 2 times by using cleaning equipment, thoroughly cleaning impurities on the surface of the cloth, drying, and finally rolling and packaging the dried cloth by using a round roller to obtain a woven tape adhesive lining cloth finished product.
Example 3
S1, preparation of a mixture of base fibers: firstly, respectively weighing 50 parts of polyester fiber, 20 parts of polybutylene terephthalate (PBT) fiber, 10 parts of polyamide 66 fiber and 20 parts of polyurethane fiber by weighing equipment, then sequentially pouring all fiber materials into mixing and stirring equipment, then adding deionized water in corresponding weight ratio, stirring for 2 hours by the stirring equipment at the rotating speed of 800 r/min and the temperature of 30 ℃ until the mixture is pasty, then transferring the pasty mixture into fiber drawing equipment, and sequentially performing extrusion molding, wire drawing, drying and forming processes to obtain base material fiber;
s2, preparation of coating slurry: respectively measuring 40 parts of required hot melt adhesive powder, 40 parts of required dispersing agent, 5 parts of required thickening agent, 3 parts of required stabilizing agent, 3 parts of required photocatalyst and 3 parts of required defoaming agent by using weighing equipment, then adding the measured components into mixing and stirring equipment, simultaneously adding water in corresponding weight ratio parts, and stirring for 2 hours at the rotating speed of 800 r/min by using the stirring equipment until the mixture is pasty, so that coating slurry is obtained, wherein the hot melt adhesive powder is copolyamide powder, the photocatalyst is tin oxide, and the dispersing agent is anionic polyacrylamide;
s3, weaving base cloth: weaving 60 parts of the base material fiber obtained in the step S1 by using an air jet loom through warp and weft yarns to obtain a base layer woven fabric;
s4, forming of the woven tape adhesive lining cloth: coating the 40 parts of coating slurry obtained in the step S2 on the base layer woven cloth in the step S3 through dispensing coating equipment, then carrying out hot air drying treatment through hot air drying equipment, and then carrying out cooling treatment through cooling equipment to enable the coating to be rapidly melted and solidified on the base layer woven cloth, so that the woven tape adhesive lining cloth is obtained;
s5, processing of the woven tape adhesive lining cloth finished product: and (4) cutting and forming the woven tape adhesive lining cloth obtained in the step (S4) by using cutting equipment, cleaning for 3 times by using cleaning equipment, thoroughly cleaning impurities on the surface of the cloth, drying, and finally rolling and packaging the dried cloth by using a round roller to obtain a woven tape adhesive lining cloth finished product.
It is noted that, herein, relational terms such as first and second, and the like may be used solely to distinguish one entity or action from another entity or action without necessarily requiring or implying any actual such relationship or order between such entities or actions. Also, the terms "comprises," "comprising," or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (8)
1. The utility model provides a novel meshbelt bonding lining cloth new material which characterized in that: the raw materials comprise the following components in parts by weight: 50-60 parts of base material fiber, 30-40 parts of coating slurry and the balance of deionized water, wherein the base material fiber consists of 40-50 parts of polyester fiber, 10-20 parts of polybutylene terephthalate (PBT) fiber, 5-10 parts of polyamide 66 fiber and 10-20 parts of polyurethane fiber, and the coating slurry consists of 25-40 parts of hot melt adhesive powder, 25-40 parts of dispersing agent, 1-5 parts of thickening agent, 1-3 parts of stabilizing agent, 1-3 parts of photocatalyst, 1-3 parts of defoaming agent and the balance of water.
2. The novel mesh belt bonding lining cloth material as claimed in claim 1, is characterized in that: the raw materials comprise the following components in parts by weight: 55 parts of base material fiber, 35 parts of coating slurry and the balance of deionized water, wherein the base material fiber consists of 45 parts of polyester fiber, 15 parts of polybutylene terephthalate (PBT) fiber, 7 parts of polyamide 66 fiber and 15 parts of polyurethane fiber, and the coating slurry consists of 35 parts of hot melt adhesive powder, 30 parts of dispersing agent, 3 parts of thickening agent, 2 parts of stabilizing agent, 2 parts of photocatalyst, 2 parts of defoaming agent and the balance of water.
3. The novel mesh belt bonding lining cloth material as claimed in claim 1, is characterized in that: the raw materials comprise the following components in parts by weight: the coating comprises 50 parts of base material fiber, 30 parts of coating slurry and the balance of deionized water, wherein the base material fiber comprises 40 parts of polyester fiber, 10 parts of polybutylene terephthalate (PBT) fiber, 5 parts of polyamide 66 fiber and 10 parts of polyurethane fiber, and the coating slurry comprises 25 parts of hot melt adhesive powder, 25 parts of dispersing agent, 1 part of thickening agent, 1 part of stabilizing agent, 1 part of photocatalyst, 1 part of defoaming agent and the balance of water.
4. The novel mesh belt bonding lining cloth material as claimed in claim 1, is characterized in that: the raw materials comprise the following components in parts by weight: the coating comprises 60 parts of base material fiber, 40 parts of coating slurry and the balance of deionized water, wherein the base material fiber comprises 50 parts of polyester fiber, 20 parts of polybutylene terephthalate (PBT) fiber, 10 parts of polyamide 66 fiber and 20 parts of polyurethane fiber, and the coating slurry comprises 40 parts of hot melt adhesive powder, 40 parts of dispersing agent, 5 parts of thickening agent, 3 parts of stabilizing agent, 3 parts of photocatalyst, 3 parts of defoaming agent and the balance of water.
5. The novel woven tape adhesive lining cloth material as claimed in any one of claims 1 to 4, is characterized in that: the hot melt adhesive powder is copolyamide powder.
6. The novel woven tape adhesive lining cloth material as claimed in any one of claims 1 to 4, is characterized in that: the photocatalyst is one or the combination of titanium dioxide, zinc oxide or tin oxide.
7. The novel woven tape adhesive lining cloth material as claimed in any one of claims 1 to 4, is characterized in that: the dispersant is anionic polyacrylamide.
8. A production process of a novel woven tape bonding lining cloth material is characterized in that: the method specifically comprises the following steps:
s1, preparation of a mixture of base fibers: firstly, respectively measuring required polyester fibers, polybutylene terephthalate (PBT) fibers, polyamide 66 fibers and polyurethane fibers by using weighing equipment, then sequentially pouring all fiber materials into mixing and stirring equipment, then adding deionized water in corresponding weight ratio, stirring for 1-2 hours by using the stirring equipment at the rotating speed of 700-;
s2, preparation of coating slurry: respectively measuring required hot melt adhesive powder, a dispersing agent, a thickening agent, a stabilizing agent, a photocatalyst and a defoaming agent by using weighing equipment, then adding the measured components into mixing and stirring equipment, simultaneously adding water in corresponding weight parts, and stirring for 1-2 hours by using the stirring equipment at the rotating speed of 700-;
s3, weaving base cloth: weaving the base material fiber obtained in the step S1 by using an air jet loom through warp and weft to obtain a base layer woven fabric;
s4, forming of the woven tape adhesive lining cloth: coating the coating slurry obtained in the step S2 on the base layer woven cloth woven in the step S3 through dispensing coating equipment, then carrying out hot air drying treatment through hot air drying equipment, and then carrying out cooling treatment through cooling equipment to enable the coating to be rapidly melted and solidified on the base layer woven cloth, so that woven tape adhesive lining cloth is obtained;
s5, processing of the woven tape adhesive lining cloth finished product: and (4) cutting and forming the woven tape adhesive lining cloth obtained in the step (S4) by using cutting equipment, cleaning for 2-3 times by using cleaning equipment, thoroughly cleaning impurities on the surface of the cloth, drying, and finally rolling and packaging the dried cloth by using a round roller to obtain a woven tape adhesive lining cloth finished product.