CN101292785A - Technique for preparing multifunctional liner of printing sarcenet - Google Patents
Technique for preparing multifunctional liner of printing sarcenet Download PDFInfo
- Publication number
- CN101292785A CN101292785A CNA2008100602227A CN200810060222A CN101292785A CN 101292785 A CN101292785 A CN 101292785A CN A2008100602227 A CNA2008100602227 A CN A2008100602227A CN 200810060222 A CN200810060222 A CN 200810060222A CN 101292785 A CN101292785 A CN 101292785A
- Authority
- CN
- China
- Prior art keywords
- printing
- sarcenet
- polyurethane
- production technology
- base cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production technology of multifunctional liner of printing lining, which sequentially includes the steps of basic fabric weaving, loosening overflow pretreatment, tension-free shaping, printing, color fixing and shaping, gluing, baking, rolling, etc. By adopting the loosening pre-shrinking shaping technology, the invention can cause fiber pores to be tighter, thus generating loose and clean appearance. Dual point coating is conducted by adopting thermosetting-typed hot melt glue of polyurethane and polyamide; the hot melt glue of polyurethane after heating loses cross linking generated by hydrogen bonds in polyurethane molecules and changes into melt viscous fluid, and after cooling, the hot melt glue of polyurethane recovers to the original property; both the polyurethane and the polyamide at the upper layer have good elasticity and strength and comparatively good affinity and can integrate with each other and endure various washing methods. The production technology is applicable to various fiber fabrics without glue seeping and can realize the integration of products with fabrics by ironing. The interlining produced by the technology is light and soft and has good drape property and is applicable to being as the fabrics of upscale wear of women.
Description
[technical field]
The present invention relates to a kind of production technology of functional adhesive lining, especially a kind of production technology of multifunctional liner of printing sarcenet.
[background technology]
The multifunctional liner of printing sarcenet product all is to adopt the rubber-like base cloth at present, after overflow pre-treatment and typing arrangement, selects for use polyester (PES) PUR as prime cement, and face glue selects for use polyamide (PA) to carry out CP90 order two point coating.
When this multifunctional liner of printing sarcenet and soft slim lining were bonding, the strike-through phenomenon very easily took place with the combination of polyamide (PA) in polyester (PES).Thereby influence the feel and the outward appearance of lining.
[summary of the invention]
Purpose of the present invention solves the problems of the prior art exactly, proposes a kind of production technology of multifunctional liner of printing sarcenet, multifunctional liner and lining pressure is scalded promptly be integral, and avoids the generation of strike-through phenomenon.
For achieving the above object, the present invention proposes a kind of production technology of multifunctional liner of printing sarcenet, in turn include the following steps:
Base cloth is weaved: base cloth adopts 50D/48F to close the fibril combination, weaves through full-automatic jet plane;
The pre-treatment of overflow pine formula: the base cloth after weaving carries out loose formula pre-treatment through the HTHP overflow machine;
No tension force typing: adopt the mode of loose formula preshrunk typing that base cloth is carried out the drying typing;
Stamp: base cloth is delivered to printing machine carry out the stamp arrangement;
Fixation typing: stamp is not after there is tension force drying fixation, and the arrangement moulding of washing back;
Point glue: select for use heat curing-type polyurethane (PU) PUR as prime cement, polyamide (PA) carries out the two point coating as face glue;
Bake and batch: after baking under 195 ℃-215 ℃ the temperature, batch.
As preferably, setting nozzle exit pressure in the described overflow pine formula pre-treatment step is 0.2-0.5kg/m
3, temperature is 100 ℃-120 ℃, the holdup time is 30-45 minute.
As preferably, printing machine adopts flat screen printing machine in the described stamp step.
As preferably, cylinder order number is CP90 in the described some glue step, and the speed of a motor vehicle is 40m/min, and the drying room temperature is 170-180 ℃, and the workshop condition temperature is 20-30 ℃.
Beneficial effect of the present invention: the present invention adopts loose formula preshrunk shaping technology can make the fiber pore tightr, thereby produces bulk bright and clean outward appearance.Adopt heat curing-type polyurethane hot melt and polyamide to carry out the two point coating, polyurethane hot melt has lost produced by hydrogen bond action in the polyurethane molecular crosslinked after being heated, become the viscous fluid of fusion, recover original rerum natura after the cooling again, it and upper strata polyamide all have excellent elasticity and intensity, both affinity is preferable, can become one fully, can anti-various washings.Be applicable to the lining of various fibers, the strike-through phenomenon can not take place, this technology can realize fully that product and lining press to scald and promptly be integral.The frivolous softness of the lining cloth of this explained hereafter has good vertical fugacity, and product had not only had the dual-use function effect of adhesive function but also alternative lining silk, the demand of having catered to market.Be fit to high-grade women's dress lining.
Feature of the present invention and advantage will be elaborated in conjunction with the accompanying drawings by embodiment.
[description of drawings]
Fig. 1 is the process chart of the production technology of a kind of multifunctional liner of printing sarcenet of the present invention.
[specific embodiment]
Consult Fig. 1, a kind of production technology of multifunctional liner of printing sarcenet in turn includes the following steps:
Base cloth weaves 1: base cloth adopts 50D/48F to close the fibril combination, weaves through full-automatic jet plane.Overflow pine formula pre-treatment 2: the base cloth after weaving carries out loose formula pre-treatment through the HTHP overflow machine.The setting nozzle exit pressure is 0.2-0.5kg/m
3, temperature is 100 ℃-120 ℃, the holdup time is 30-45 minute.
Because the thin silk that easily colludes of fabric, in process, not only equipment has been proposed very high requirement, and technical recipe and flow process are also very crucial.By utilization computer on the HTHP overflow machine is accurately controlled temperature, time, nozzle exit pressure, make cloth cover smooth, bright and clean, do not have and to collude silk.
No tension force typing 3: adopt the mode of loose formula preshrunk typing that base cloth is carried out the drying typing.Adopt loose formula preshrunk shaping technology to be applicable to the drying typing of such ultrathin microfibre stockinette, can make the fiber pore tightr, thereby produce bulk bright and clean outward appearance.
Stamp 4: base cloth is delivered to printing machine carry out the stamp arrangement.Printing machine adopts flat screen printing machine.Wear the cloth route by reasonable introduction,, suitably regulate entering printing roller degree of tightness before, make base cloth and selvage guide obtain the elongation of uniformity by the friction of selvage guide roller and tension-adjusting gear and fabric.Under same speed, condition, enter printing system, can obtain the colored type of setting with tension force.
Fixation typing 5: stamp is not after there is tension force drying fixation, and the arrangement moulding of washing back.
Point glue 6: select for use heat curing-type polyurethane (PU) as prime cement, polyamide carries out the two point coating as face glue.The parameter of some glue is: cylinder order number is CP90, and the speed of a motor vehicle is 40m/min, and the drying room temperature is 170-180 ℃, and the workshop condition temperature is 20-30 ℃.Select for use heat curing-type polyurethane (PU) PUR as prime cement, face glue selects for use polyamide (PA) to carry out CP90 order two point coating.Compare with the system of other types, have the excellent comprehensive performance, its main cause is that polyurethane hot melt has lost produced by hydrogen bond action in the polyurethane molecular crosslinked after being heated, and becomes the viscous fluid of fusion, recovers original rerum natura after the cooling again.It and upper strata PA PUR all have excellent elasticity and intensity, and both affinity is preferable, can become one fully, so can anti-various washings.Be applicable to the lining of various fibers, the strike-through phenomenon can not take place, this system can realize fully that product and lining press to scald and promptly be integral, the adhesive function but also the thick dual-use function of alternative lining that have not only had adhesive lining.Clothes need not to add lining fabric, have both reduced the clothing making operation, and are attractive and durable again, add the bonding intensity of its extra-heavy, just in time cooperate the changeable trend of fashionable dress style, style and materials now.The frivolous softness of this lining cloth has good vertical fugacity, and product had not only had the dual-use function effect of adhesive function but also alternative lining silk, the demand of having catered to market.Be fit to high-grade women's dress lining.This top grade adhesive lining both had the good wearability of " light, thin, gentle, very, suitable ", not only anti-dry-cleaning is arranged again but also water-fastly wash, the superior quality level of dimensionally stable.
Bake and batch 7: after baking under 195 ℃-215 ℃ the temperature, batch.
Technical target of the product is as shown in Table 1:
Table one:
| Project | Technical indicator |
| Separation strength is not less than | ≥15N/5×10cm |
| Xeothermic appearance change is not less than (%) | Warp-wise :-1.5% broadwise :-1.0% |
| The hydro-thermal appearance change is not less than (%) | Warp-wise :-2.5% broadwise :-1.5% |
| Do, wash change in size, be not less than | 4 grades |
| Discharge free formaldehyde (mg/kg) | ≤50ppm |
| PH value | 4-9 |
| Anti-dry friction | 3 |
| Can decompose fragrant dyestuff | Do not have |
The foregoing description is to explanation of the present invention, is not limitation of the invention, and any scheme after simple transformation on the basis of the present invention all belongs to protection scope of the present invention.
Claims (4)
1. the production technology of a multifunctional liner of printing sarcenet is characterized in that: in turn include the following steps:
Base cloth is weaved (1): base cloth adopts 50D/48F to close the fibril combination, weaves through full-automatic jet plane;
The formula pre-treatment (2) of overflow pine: the base cloth after weaving carries out loose formula pre-treatment through the HTHP overflow machine;
No tension force typing (3): adopt the mode of loose formula preshrunk typing that base cloth is carried out the drying typing;
Stamp (4): base cloth is delivered to printing machine carry out the stamp arrangement;
Fixation typing (5): stamp is not after there is tension force drying fixation, and the arrangement moulding of washing back;
Point glue (6): select for use heat curing-type polyurethane (PU) PUR as prime cement, polyamide (PA) carries out the two point coating as face glue;
Bake and batch (7): after baking under 195 ℃-215 ℃ the temperature, batch.
2. the production technology of a kind of multifunctional liner of printing sarcenet as claimed in claim 1 is characterized in that: setting nozzle exit pressure in described overflow pine formula pre-treatment (2) step is 0.2-0.5kg/m
3, temperature is 100 ℃-120 ℃, the holdup time is 30-45 minute.
3. the production technology of a kind of multifunctional liner of printing sarcenet as claimed in claim 1 is characterized in that: printing machine employing flat screen printing machine in described stamp (4) step.
4. as the production technology of claim 1 or 2 or 3 described a kind of multifunctional liner of printing sarcenet, it is characterized in that: cylinder order number is CP90 in described glue (6) step, and the speed of a motor vehicle is 40m/min, and the drying room temperature is 170-180 ℃, and the workshop condition temperature is 20-30 ℃.