CN1328097A - 用于建筑五金制品上的抗菌涂层 - Google Patents
用于建筑五金制品上的抗菌涂层 Download PDFInfo
- Publication number
- CN1328097A CN1328097A CN 01116521 CN01116521A CN1328097A CN 1328097 A CN1328097 A CN 1328097A CN 01116521 CN01116521 CN 01116521 CN 01116521 A CN01116521 A CN 01116521A CN 1328097 A CN1328097 A CN 1328097A
- Authority
- CN
- China
- Prior art keywords
- coating
- antiseptic
- architectural hardware
- hardware member
- cated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
非金属的保护涂层常用于建筑五金构件上。涂层包括透明聚合物表面涂层或者决定构件形状及手感的模压聚合物。在非金属的保护涂层中添加有抗菌剂。涂层可在相当长的时间内维持其抗菌效果,从而具有以下功能:保护聚合物不会由于发霉、真菌、霉菌而发生老化。抗菌剂还可以抑制微生物的生长从而不使细菌繁殖,并可减少由于微生物的生长而产生的难闻气味。
Description
本发明通常涉及用于建筑五金构件上的涂层，特别是用于建筑五金构件上的抗菌涂层。
现有的建筑五金构件，例如门的球形把手、横杆、手柄、出口设施的推门垫板及门推手、栏杆、扶手、生物统计几何读出器等等，通常是在基体芯材表面涂覆一层防腐层制成的。有些建筑五金构件是通过在芯材表面模压可注模树脂形成的，其他的是将芯材去除而整个建筑五金构件均由可模压树脂构成。当使用这样的建筑五金构件时，无论用户使用自己家中的还是公众使用公共设施上的上述构件，细菌及其他传染剂就会通过第一位使用者在扶手、推门垫板等处留存下来并传给下一位使用者的手，进而可能再将细菌及其他带有传染剂传播给下—位使用者。
以上说明了目前的建筑五金构件中存在的公知的缺陷。因此，可以提供一种替换物来直接克服以上提出的一种或更多的缺陷，其优点是显而易见的。从而，提供一种适用的替换物，其所具备的特征将在下文充分公开。
一方面，本发明是这样实现的：提供一种涂覆在建筑五金构件上的涂层，该涂层包括一种包含有一种或多种有机或无机的抗菌剂的聚合底涂层材料。
另一方面，本发明是这样实现的：提供一种有表面涂层的建筑五金构件，该构件包含有一个金属芯的基材及一层含有抗菌剂的防腐蚀的保护涂层。
以上内容及其他的方面可以通过以下的详细描述得以清楚的说明。
本发明涉及一种在建筑五金产品或构件的基体芯材上的非金属聚合覆盖层或涂层中使用的抗菌剂。通常基体芯材为金属芯材，然而，一些建筑五金产品却不使用金属芯材，而是由诸如尼龙的可模压的树脂形成的。对于其外观取决于基体材质的产品，比如：黄铜、铬、黄铜似的涂层、铬似的涂层等，使用透明的防护涂层来保护基础材料。在其他产品中，将含有染色剂的可模压树脂模压在基材上以使基材的外观具有美感。不论是基体芯材上的防护涂层还是在基体芯材上的模压树脂，还是无基体芯材的模压树脂，在每种情况下，其顶涂层都要添加抗菌剂。
本发明的第一个实施例是在覆盖于建筑五金构件金属主体上的透明聚合表层中使用一种抗菌剂。透明聚合涂层保护金属主体，不发生腐蚀、生锈、氧化、变色、着色等。把一种或多种无机的或有机的抗菌剂添加到透明聚合涂层中。容许的透明涂层的一个例子就是H.B.Fuller公司生产的丙烯酸透明涂层1F7066。
本发明的第二个实施例是与可模压树脂全部混合的一种抗菌剂，可模压树脂比如尼龙通常模压在由碳钢制成的基体芯材上。作为选择，这种聚合树脂可被粘合在基体芯材上。在另一个实施例中，建筑五金构件全部是由可模压的树脂构成，不包括下面的基体芯材。也可使用的其他树脂包括有聚丙烯、聚乙烯、聚氯乙烯、苯乙烯、聚氨酯、热塑性聚酯、热塑性合成橡胶、聚碳酸酯和工程塑料。
对于第二个实施例，把普通的原料比如尼龙与浓缩的颜料及抗菌剂混合在一起。原料、浓缩的颜料及抗菌剂的混合物在80℃下干燥3至4个小时以将湿度减少到低于0.1％。当使用基体芯材时，就将基体芯材插入到模型中。混合物处于熔融状态并以大约为200巴的压力被注入到模型中。上述部分保存预定的时间，这个时间由尼龙用量、这部分的大小和所需要的表面光洁度决定，所有这些参数对于聚合树脂模压领域普通专业技术人员来说是已知的。通常尼龙的厚度从1mm的尼龙模压层至41mm的固体尼龙构件之间变动。上述生产方法可被应用于许多种建筑五金构件中，比如卫生洁具、残疾人使用的产品、扶手、栏杆、拉手、手柄、杠杆等。第二个实施例的一个关键要素是抗菌剂与相对厚度的尼龙全部混合(1mm～41mm)，这使得抗菌剂的抗菌效果很少受到刮擦、磨损或磨蚀的影响。
此外，第二层聚合树脂可以模压或粘合在第一层树脂之上。在这种情况下，抗菌剂应当被包含在第二层或表面层中。在这种情况下，第一层聚合物通常保证总体的形状、结构或一些其他的特性比如构件的强度。第二层聚合物可保证构件的辅助特性，也就是“柔软的”触感、构件的不同色彩或特殊质地。当使用两层树脂时，使用或者不必使用基体芯材均可。
对每一个实施例而言，都可以使用有机的或无机的抗菌剂。当添加到透明涂层中时，容许的抗菌剂浓度为0.1～10w％。若对透明涂层的透明度有特别严格的要求，优选浓度为0.25～1w％。当用在可模压的聚合树脂中时，容许的抗菌剂浓度为0.5～10w％，其优选范围为1～3w％。
可采用的无机抗菌剂的实例包括载银的TiO2或ZnO，其中在TiO2或ZnO的芯材分子外涂覆一层金属银。两种可采用的产品是杜邦公司生产的MicrofreeφZ200，该产品的ZnO芯材表面涂覆有金属银，同样由杜邦公司生产的MicrofreeφT558，该产品的ZnO芯材表面涂覆有银、氧化铜和硅酸锌的混合物。对这两种Microfreeφ产品而言，银具有抗菌的作用，氧化铜及硅酸锌具有抗真菌的作用。其他可采用的抗菌剂是含有银、铜、铂、钯、锡、铋、铱、锑、金或锌的无机混合物。
可接受的有机抗菌剂的实例包括Microban Products Company，Huntersville，North Carolina，US生产的Microbanφ，2，4，4-三氯-2-羟基二苯醚，商业有售的由Ciba-Geigy公司生产的“Triclosan”或“Irgasan DP300”以及3，4，4″－三氯对称二苯脲，N－(4－氯苯基－N－3，4－二氯苯基)脲，商业有售的由NipaHardwicke公司生产的“Triclocarban”或者“NipaguardTCC”。
Claims (30)
1、一种建筑五金构件涂层，包括：
含有一种或多种有机或无机抗菌剂的聚合底涂层材料。
2、根据权利要求1所述的涂层，其中底涂层材料为透明材料。
3、根据权利要求1所述的涂层，其中底涂层为可注模树脂。
4、根据权利要求3所述的涂层，其中的树脂为尼龙。
5、根据权利要求4所述的涂层，其中还包括染色剂。
6、一种涂覆有涂层的建筑五金构件，包括：
基体金属芯材；
含有抗菌剂的防腐蚀保护涂层。
7、根据权利要求6所述的涂覆有涂层的建筑五金构件，其中保护涂层为透明的涂层。
8、根据权利要求6所述的涂覆有涂层的建筑五金构件，其中保护涂层为可注模树脂。
9、根据权利要求8所述的涂覆有涂层的建筑五金构件，其中的树脂为尼龙。
10、根据权利要求8所述的涂覆有涂层的建筑五金构件，其中的树脂还包括染色剂。
11、根据权利要求6所述的涂覆有涂层的建筑五金构件，其中还包括另外的聚合涂层。
12、根据权利要求6所述的涂覆有涂层的建筑五金构件，其中另外的聚合涂层是涂在防腐层上面的。
13、根据权利要求6至12中任意一项所述的涂覆有涂层的建筑五金构件，其中抗菌剂包括一种或多种载有银的无机化合物。
14、根据权利要求13所述的涂覆有涂层的建筑五金构件，其中抗菌剂包括一种或多种选自由TiO2和ZnO组成的组合中的无机化合物。
15、根据权利要求6至12中任意一项所述的涂覆有涂层的建筑五金构件，其中抗菌剂为包括银、钯、铂、锡、锑、铋、铱、金、锌、铜中的一种或多种无机化合物。
16、根据权利要求6至12中任意一项所述的涂覆有涂层的建筑五金构件，其中抗菌剂为3，4，4″－三氯对称二苯脲，N－(4－氯苯基－N－3，4－二氯苯基)脲。
17、根据权利要求6至12中任意一项所述的涂覆有涂层的建筑五金构件，其中抗菌剂为2，4，4－三氯－2－羟基二苯醚。
18、根据权利要求6至12中任意一项所述的涂覆有涂层的建筑五金构件，其中抗菌剂的浓度至少为0.1W％。
19、根据权利要求6至12中任意一项所述的涂覆有涂层的建筑五金构件，其中抗菌剂的浓度为0.1W％至10W％。
20、根据权利要求6至12中任意一项所述的涂覆有涂层的建筑五金构件，其中抗菌剂的浓度为1W％至3W％。
21、根据权利要求7所述的涂覆有涂层的建筑五金构件，其中抗菌剂的浓度为0.25W％至1W％。
22、—种建筑五金构件，包括：
尼龙芯材；以及
与尼龙芯材整体进行混合的一种或多种有机或无机抗菌剂。
23、根据权利要求22所述的建筑五金构件，其中尼龙芯材中还包括染色剂。
24、根据权利要求22或23中任意一项所述的建筑五金构件，其中抗菌剂为包括银、钯、铂、锡、锑、铋、铱、金、锌、铜中的一种或多种的无机混合物。
25、根据权利要求22或23中任意一项所述的建筑五金构件，其中抗菌剂为2，4，4－三氯－2－羟基二苯醚。
26、根据权利要求22或23中任意一项所述的建筑五金构件，其中抗菌剂为3，4，4″－三氯对称二苯脲，N－(4－氯苯基－N－3，4－二氯苯基)脲。
27、根据权利要求22或23中任意一项所述的建筑五金构件，其中抗菌剂的浓度为1w％至3w％。
28、一种涂覆有涂层的建筑五金构件，包括：
基体金属芯材；及模压在基体金属芯材外的尼龙树脂，该树脂含有2，4，4-三氯-2-羟基二苯醚抗菌剂。
29、根据权利要求28所述的涂覆有涂层的建筑五金构件，其中抗菌剂浓度至少为0.5w％。
30、根据权利要求29所述的涂覆有涂层的建筑五金构件，其中抗菌剂的浓度为1w％至3w％。