CN1245294C - Production method for ceramic brick with natural concave-convex surface - Google Patents
Production method for ceramic brick with natural concave-convex surface Download PDFInfo
- Publication number
- CN1245294C CN1245294C CN 03126850 CN03126850A CN1245294C CN 1245294 C CN1245294 C CN 1245294C CN 03126850 CN03126850 CN 03126850 CN 03126850 A CN03126850 A CN 03126850A CN 1245294 C CN1245294 C CN 1245294C
- Authority
- CN
- China
- Prior art keywords
- brick
- production method
- ceramic
- natural
- ceramic tiles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a production method for ceramic bricks with natural concave-convex surfaces, which is characterized in that a proper amount water is sprayed at the surface of the dry green brick, and then, the surface of the green brick is baked with a high temperature. Thus, liquid water of the surface is quickly gasified at a high temperature, and irregular damage, breaking up and disengagement are carried out to the shallow surface of the green brick. Then, the breaking up and disengaged blank mud is removed, and natural concave convex graining effect is formed at the surface of the green brick. Finally, the green brick is put in a ceramic brick roller way kiln and is calcinated. The production method is characterized in that the texture of the design and colour patterns of the concave convex surface of the ceramic brick is very natural, the texture is bulged in a stereoscopic mode, and the ceramic brick is like a stone material. Compared with the product by adopting the production method the prior art, the patterns of the product which is formed by the concave convex mould in a pressing way are natural and rich, the stereo perception is strong, and the patterns are not stiff and are full of variation. Simultaneously, the variety and the standard are rich, the ceramic brick has environment protection performance and does not absorb dirt. The ceramic brick belongs to a high-grade decorative material for buildings.
Description
Technical field
The present invention relates to the production method that a kind of surface has the Ceramic Tiles of the concavo-convex textured pattern decoration of nature.
Background technology
As everyone knows, concave-convex brick in the market generally all is building and ornament materials of making a kind of top grade of type through concavo-convex mold pressing, it has advantages such as wear-resistant, anti-skidding, but simultaneously because its pattern texture is limited to male and female mold, so seem stiff stiff, lack naturality and stereo perception, greatly limited consumer's desire to purchase.Can and traditional concavo-convex mold pressing makes the ceramic product of type, is difficult to fundamentally solve consumer's aesthstic desire, reach this requirement of consumer, starting point of the present invention just.
Summary of the invention
The purpose of this invention is to provide the production method that a kind of surface has the Ceramic Tiles of nature Z-Correct bump mapping Z-correct decoration, make the Z-Correct bump mapping Z-correct of brick face natural and tripping, colour image is full of variety, do not have repetition, and solid is true to nature, reaches the decorative effect of lithotome, satisfies consumer's aesthstic desire.
For achieving the above object, production method of the present invention has adopted following steps:
A), spray an amount of water on dried Ceramic Tiles green compact surface;
B), treat that moisture content penetrates into the billet surface appropriate depth after, rapidly high temperature is carried out on its surface and scorches, form billet surface and peel off, burst apart; According to the requirement of concave-convex effect, can carry out executing water and scorching of one or many;
C), the base mud that billet surface is come off is removed;
D), in ceramic roller kiln, burn till formation semi-finished product brick, 1150～1250 ℃ of firing temperatures, firing period 50～80 minutes;
E), the cooling of the semi-finished product brick after burning till after shallow polishing or inferior polishing or do not polish through edging, drying, pick, packing, get product again.
In the above-mentioned steps, the water yield of executing on the natural male and fomale(M﹠F) Ceramic Tiles of this kind green compact surface is 0.1g/cm
2～40g/cm
2It is 400～2500 ℃ that high temperature scorches temperature; It is 0.3～6mm that moisture content infiltrates the brick face degree of depth; The degree of depth of bursting apart 0～6mm.
The present invention has the following advantages:
1, spray water and scorch PROCESS FOR TREATMENT on Ceramic Tiles green compact surface, formed concavo-convex naturally combination with decorative surfaces, expose the pattern and the color of adobe nexine, three-dimensional true to nature.
2, every tile Z-Correct bump mapping Z-correct is never identical, be full of variety, and the color between different aspects clearly shines, abundant naturally, very tool is appreciated sense.
3, the pattern of product, pattern and Z-Correct bump mapping Z-correct can be as required, arbitrarily design, coordination collocation.
The specific embodiment
In the method for the present invention, at first prepare the Ceramic Tiles green compact, preparation Ceramic Tiles green compact adopt existing common method: promptly be pressed into the Ceramic Tiles green compact by prescription weighing, ball milling slurrying, mist projection granulating, press, its concrete whole process flow is: prescription weighing → ball milling slurrying → mist projection granulating → press compression moulding → brick bat drying → execute hydrophone to spray suitable quantity of water (0.1g/cm to the adobe surface
2～40g/cm
2) → conveyer belt carry adobe → moisture content infiltrate the adobe surface 0.3～6mm degree of depth → high temperature scorch district (400～2500 ℃ of temperature) → (spray water and scorch and can carry out repeatedly) → adobe surface burst apart naturally 0～6mm degree of depth → removing adobe surface burst apart thing and reclaim → go into roller kilns by Ceramic Tiles burn till requirement burn till → shallow polishing or Asia are polished or are not polished → edging → drying → packing.In the said process, peel off very naturally, burst apart through the ceramic base surface that Shi Shuihe scorches after the PROCESS FOR TREATMENT, the base mud through billet surface is come off has just formed natural and tripping Z-Correct bump mapping Z-correct after removing, and three-dimensional the color pattern that manifests the base substrate the inside.
Claims (2)
1, a kind of production method of natural male and fomale(M﹠F) Ceramic Tiles is characterized in that, this method comprises the steps:
A), spray an amount of water on dried Ceramic Tiles green compact surface;
B), treat that moisture content penetrates into the billet surface appropriate depth after, rapidly high temperature is carried out on its surface and scorches, form billet surface and peel off, burst apart; According to the requirement of concave-convex effect, can carry out executing water and scorching of one or many;
C), the base mud that billet surface is come off is removed;
D), in ceramic roller kiln, burn till formation semi-finished product brick, 1150～1250 ℃ of firing temperatures, firing period 50～80 minutes;
E), the cooling of the semi-finished product brick after burning till after shallow polishing or industry polishing or do not polish through edging, drying, pick, packing, get product again.
2, the production method of natural male and fomale(M﹠F) Ceramic Tiles according to claim 1 is characterized in that, the water yield is executed by g/cm in described Ceramic Tiles green compact surface
2Meter is 0.1g/cm
2～40g/cm
2It is 400～2500 ℃ that high temperature scorches temperature; It is 0.3～6mm that moisture content infiltrates the brick face degree of depth; The degree of depth of bursting apart 0～6mm.