CN1212441A - 片式多层瓷介电容器钯银内电极浆料 - Google Patents

片式多层瓷介电容器钯银内电极浆料 Download PDF

Info

Publication number
CN1212441A
CN1212441A CN 97117285 CN97117285A CN1212441A CN 1212441 A CN1212441 A CN 1212441A CN 97117285 CN97117285 CN 97117285 CN 97117285 A CN97117285 A CN 97117285A CN 1212441 A CN1212441 A CN 1212441A
Authority
CN
China
Prior art keywords
palladium
silver
ceramic capacitor
percentage
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 97117285
Other languages
English (en)
Inventor
孟淑缓
梁力平
庞溥生
陈锦清
刘会冲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Zhaoqing Fenghua Electronic Engineering Development Co Ltd
Original Assignee
Guangdong Zhaoqing Fenghua Electronic Engineering Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Zhaoqing Fenghua Electronic Engineering Development Co Ltd filed Critical Guangdong Zhaoqing Fenghua Electronic Engineering Development Co Ltd
Priority to CN 97117285 priority Critical patent/CN1212441A/zh
Publication of CN1212441A publication Critical patent/CN1212441A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种片式多层瓷介电容器钯银内电极浆料,它与现有技术相比,具有性能好和成本低兼备的优点,用它做成的片式多层瓷介电容器内电极,具有连续、平滑、均匀、致密、银层薄和单位面积银浆消耗量少等特征,而且电气性能一致性好,内部物理结构好,缺陷率低,产品命中率高。整体技术指标达到甚至超过国外同类产品的最好水平。

Description

片式多层瓷介电容器钯银内电极浆料
本发明涉及一种电容器钯银内电极浆料，特别是片式多层瓷介电容器钯银内电极浆料。
随着电子产品小型化、薄型化、轻量化及表面安装技术(SMT)的发展，电子元件正朝着片式化发展，八十年代以来，我国引进了十六条片式多层瓷介电容器(MLC)生产线，生产能力已达三十亿只/年以上。这些生产线所需的大量的钯银内电极浆料，都需从国外进口。国外以美国杜邦公司的6010 3/7钯银内电极浆料最为成熟，但价格较昂贵；而国内北京有色院的同类产品价格较低，但在平均细度、电容量分布、缺陷率及稳定性等重要指标上与进口产品有较大距离，无法满足MLC引进生产线的要求。
本发明的目的是提供一种片式多层瓷介电容器钯银内电极浆料，它采用国产原材料，大大降低成本，具有良好的流动性、触变性、均匀性和粘性，技术指标达到甚至超过美国杜邦公司同类产品水平，可替代进口。
本发明是这样实现的：它的配方组成(重量百分比)为：
3/7钯银金属粉           35～65％
乙基纤维素EC            1～10％
有机溶剂                30～57％
氧化物添加剂            0～20％
其中：3/7钯银金属粉的组成(重量百分比)为：
Pd    30％
Ag    70％
有机溶剂的组成(重量百分比)为：
松节油                 35～70％
松油醇                 10～33％
蓖麻油                 0.5～6.5％
烃类溶剂               15～20％
流平剂                 1.5～2.5％
触变剂                 1.2～1.8％
消泡剂                 0.5～1.5％
本发明与现有技术相比，具有性能好和成本低兼备的优点，用它做成的片式多层瓷介电容器内电及，具有连续、平滑、均匀、致密、银层薄和单位面积银浆消耗量少等特征，而且电气性能一致性好，内部物理结构好，缺陷率低，产品命中率高。
下面结合实施例对本发明作进一步描述。
本发明的最佳实施例配方组成(重量百分比)为：
3/7钯银金属粉              40～60％
乙基纤维素EC               2～8％
有机溶剂                   35～55％
氧化物添加剂               0.5～17％
其中：3/7钯银金属粉的组成(重量百分比)为：
Pd    30％
Ag    70％
有机溶剂的组成(重量百分比)为：
松节油                    55～65％
松油醇                    10～13％
蓖麻油                    5～6.5％
烃类溶剂                  16. 5～19％
流平剂                  1.5～2.3％
触变剂                  1.3～1.6％
消泡剂                  0.8～1.2％
在本实施例中，要求3/7钯银金属粉的技术指标为：
粒度分布：              0.1～2.0μm
摇实比：                1.5～4.0g/ml
比表面积：              1.0～3.0m2/g
形貌：球形或近球形无团限聚
在本实施例中，本发明的技术指标如下：
粘度(KCPS/25℃)         20～30
干燥温度(℃)            30～50
平均细度(μm)           6
烧结温度(℃)            1140
电容量分布              集中
缺陷率(％)              2～3

Claims (2)

1、一种片式多层瓷介电容器钯银内电极浆料，其特征是其配方组成(重量百分比)为：
3/7钯银金属粉     35～65％
乙基纤维素EC      1～10％
有机溶剂          30～57％
氧化物添加剂      0～20％
其中：3/7钯银金属粉的组成(重量百分比)为：
Pd    30％
Ag    70％
有机溶剂的组成(重量百分比)为：
松节油            35～70％
松油醇            10～33％
蓖麻油            0.5～6.5％
烃类溶剂          15～20％
流平剂            1.5～2.5％
触变剂            1.2～1.8％
消泡剂            0.5～1.5％
2、根据权利要求1所述的片式多层瓷介电容器钯银内电极浆料，其特征是其配方组成(重量百分比)为：
3/7钯银金属粉     40～60％
乙基纤维素EC      2～8％
有机溶剂          35～55％
氧化物添加剂      0.5～17％
其中：3/7钯银金属粉的组成(重量百分比)为：
Pd    30％
Ag    70％
有机溶剂的组成(重量百分比)为：
松节油               55～65％
松油醇               10～13％
蓖麻油               5～6.5％
烃类溶剂             16.5～19％
流平剂               1.5～2.3％
触变剂               1.3～1.6％
消泡剂               0.8～1.2％
CN 97117285 1997-09-19 1997-09-19 片式多层瓷介电容器钯银内电极浆料 Pending CN1212441A (zh)