CN1207358C - 防红外热效应涂料及其制备方法 - Google Patents

防红外热效应涂料及其制备方法 Download PDF

Info

Publication number
CN1207358C
CN1207358C CN 02130636 CN02130636A CN1207358C CN 1207358 C CN1207358 C CN 1207358C CN 02130636 CN02130636 CN 02130636 CN 02130636 A CN02130636 A CN 02130636A CN 1207358 C CN1207358 C CN 1207358C
Authority
CN
China
Prior art keywords
infrared heat
methacrylic acid
heat proof
proof paint
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 02130636
Other languages
English (en)
Other versions
CN1482189A (zh
Inventor
陈居正
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 02130636 priority Critical patent/CN1207358C/zh
Publication of CN1482189A publication Critical patent/CN1482189A/zh
Application granted granted Critical
Publication of CN1207358C publication Critical patent/CN1207358C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种防红外热效应涂料,其所述防红外热效应涂料的组份及重量百分比为:基料聚丙烯酸酯30-60%、颜填料甲基丙烯酸锌皂20-60%、交联剂0-20%、辅料0-20%及有机溶剂10-40%。其制备方法包括下列工序:先由甲基丙烯酸与氧化锌进行皂化反应,制成甲基丙烯酸锌皂,待用;按组份及重量份称重计量;将甲基丙烯酸锌皂和/或辅料和/或部分替代颜填料进行混合、研磨制成色浆;制成的色浆再配以基料、交联剂及溶剂进行调和;调和后进行过滤、包装,即得成品。该发明工艺简单、操作容易、原料丰富、价格便宜、适用范围广,它能有效地防止红外热效应,具有良好的大气稳定性和耐化学性。

Description

防红外热效应涂料及其制备方法
技术领域
本发明涉及一种化工涂料,具体是一种适用于涂覆各种物体的防红外热效应涂料及其制备方法。
背景技术
温室效应是当今人类共同关注的问题,由温室效应造成的影响和破坏给全球带来了不可估量的巨大损失,全球变暖、大气温度升高、日益频繁的热带飓风、海平面升高而造成耕田减少以及农业、渔业和水源方面遭受的损失高达三、四千亿美元。因而有关专家指出,必须加大努力,减少二氧化碳和其他与造成温室效应有关的气体污染,采取各种积极有效措施,控制破坏环境导致温室效应。
发明内容
本发明的目的在于提供一种能防止太阳光红外热效应威胁及由红外热效应可能产生的各种破坏性的防红外热效应涂料。
本发明的另一个目的在于提供一种热塑型、热固型、溶剂型及水溶性防红外热效应涂料的制备方法。
本发明的目的是按以下技术方案实现的:一种防红外热效应涂料,其特征在于所述防红外热效应涂料的组份及重量百分比为:基料聚丙烯酸酯30-60%、颜填料甲基丙烯酸锌皂20-60%、交联剂0-20%、辅料0-20%及有机溶剂10-40%。
上述中:
所述聚丙烯酸酯为聚甲基丙烯酸甲酯、聚甲基丙烯酸丁酯、聚丙烯酸、聚丙烯酸丁酯或聚甲基丙烯酸羟乙酯;
所述颜填料甲基丙烯酸锌皂由甲基丙烯酸与氧化锌进行皂化反应制成;
所述颜填料甲基丙烯酸锌皂由氧化锌、钛白粉、硅灰石粉、轻钙、方解石、滑石粉替代或部分替代;
所述交联剂为异氰酸酯多聚体;
所述辅料为己二异氰酸酯、三聚氰胺甲醛或硝酸纤维素;
所述溶剂为醋酸丁酯、甲苯、乙醇、丙二醇乙醚醋酸酯或蒸馏水;
所述防红外热效应涂料的制备方法,包括下列工序:1)由2摩尔的甲基丙烯酸与1摩尔的氧化锌在反应罐中进行皂化反应,制成甲基丙烯酸锌皂,待用;2)按组份及重量百分比称重计量;3)将甲基丙烯酸锌皂和/或辅料和/或部分替代颜填料在混合罐中进行混合,然后通过研磨机进行研磨制成色浆;4)制成的色浆再配以基料、溶剂投入调漆器中进行调和;5)调和后进入过滤器进行过滤;6)最后进入灌装机进行包装,即得成品。
本发明的涂料防红外热效应和不易受紫外线破坏成膜物的原理为:①采用不吸收红外线的甲基丙烯酸锌皂、方解石(广西柳江产)、硅灰石(安徽广德产)等矿石粉为颜填料,参与构成不产生热效应并成为紫外线猝灭剂的成膜物质;②采用耐光、耐候性好的聚丙烯酸酯类为基料,配合使用少量CAB及硝酸纤维素提高流平性能和改善溶剂释放性能。
本发明的优点是:工艺简单、操作容易、原料丰富、价格便宜、适用范围广,它能有效地防止红外热效应,具有良好的大气稳定性和耐化学性,使用寿命可达13年以上。
具体实施方式
下面结合实施例详述本发明。
实施例1.
首先由2摩尔的甲基丙烯酸与1摩尔的氧化锌在反应罐中进行皂化反应,制成甲基丙烯酸锌皂,留作下面待用。
其制备工序包括:1)按组份及重量百分比称取基料聚甲基丙烯酸甲酯45份、颜填料甲基丙烯酸锌皂20份与钛白粉11份、辅料己二异氰酸酯4份及溶剂醋酸丁酯20份;2)将上述颜填料甲基丙烯酸锌皂与钛白粉及辅料己二异氰酸酯放在混合罐中进行混合,然后通过研磨机进行研磨制成色浆;3)制成的色浆再配以基料聚甲基丙烯酸甲酯及溶剂醋酸丁酯投入调漆器中进行调和;4)调和后进入过滤器进行过滤;5)最后进入灌装机进行包装,即得热塑型涂料成品。
实施例2.
其制备工序包括:1)按组份及重量百分比称取基料聚甲基丙烯酸丁酯56份、颜填料甲基丙烯酸锌皂4份、钛白粉6份及硅灰石粉10.5份、辅料硝酸纤维素11.5份及溶剂乙醇12份;下面工序同实施例1.即得热塑型涂料成品。
实施例3.
其制备工序包括:1)按组份及重量百分比称取基料聚甲基丙烯酸羟乙酯60份、颜填料甲基丙烯酸锌皂13份与钛白粉8份、辅料己二异氰酸酯10份及溶剂丙二醇乙醚醋酸酯9份;下面工序同实施例1.即得乳液型涂料成品。
实施例4.
其制备工序包括:1)按组份及重量百分比称取基料聚甲基丙烯酸羟乙酯31份、颜填料甲基丙烯酸锌皂10份与方解石粉11份、辅料三聚氰胺甲醛15份、硝酸纤维素4.5、交联剂异氰酸酯多聚体16份及溶剂醋酸丁酯12.5份;下面工序同实施例1.即得烘烤交联固化型涂料成品。
实施例5.
其制备工序包括:1)按组份及重量百分比称取基料聚甲基丙烯酸甲酯33.6份、颜填料甲基丙烯酸锌皂39份与钛白粉13份、辅料己二异氰酸酯4份及溶剂醋酸丁酯10.4份;下面工序同实施例1.即得乳液型涂料成品。
实施例6.
其制备工序包括:1)按组份及重量百分比称取基料聚丙烯酸丁酯30.2份、颜填料甲基丙烯酸锌皂40份、钛白粉11份及滑石粉7.8份及溶剂蒸馏水11份;下面工序同实施例1.即得水溶性涂料成品。

Claims (4)

1.一种防红外热效应涂料,其特征在于所述防红外热效应涂料的组份及重量百分比为:
基料:聚丙烯酸酯或聚甲基丙烯酸甲酯或聚甲基丙烯酸丁酯或聚甲基丙烯
      酸羟乙酯                                          30-60%:
颜填料:甲基丙烯酸锌皂                                  20-60%;
交联剂:异氰酸酯多聚体                                  0-20%;
辅料:己二异氰酸酯、三聚氰胺甲醛或硝酸纤维素            0-20%;
溶剂:蒸馏水、醋酸丁酯、甲苯、乙醇或丙二醇乙醚醋酸酯    10-40%。
2.根据权利要求1所述的防红外热效应涂料,其特征在于聚丙烯酸酯为聚丙烯酸丁酯。
3.根据权利要求2所述的防红外热效应涂料,其特征在于所述颜填料甲基丙烯酸锌皂由甲基丙烯酸与氧化锌进行皂化反应制成。
4.一种如权利要求1所述防红外热效应涂料的制备方法,其特征在于包括下列工序:1)由2摩尔的甲基丙烯酸与1摩尔的氧化锌在反应罐中进行皂化反应,制成甲基丙烯酸锌皂,待用;2)按组份及重量百分比称重计量;3)将甲基丙烯酸锌皂和辅料在混合罐中进行混合,然后通过研磨机进行研磨制成色浆;4)制成的色浆再配以基料、交联剂及溶剂投入调漆器中进行调和;5)调和后进入过滤器进行过滤;6)最后进入灌装机进行包装,即得成品。
CN 02130636 2002-09-10 2002-09-10 防红外热效应涂料及其制备方法 Expired - Fee Related CN1207358C (zh)