CN1313550C - 用于反射光线的丙烯酸树脂涂料及制造方法 - Google Patents
用于反射光线的丙烯酸树脂涂料及制造方法 Download PDFInfo
- Publication number
- CN1313550C CN1313550C CNB2004100479120A CN200410047912A CN1313550C CN 1313550 C CN1313550 C CN 1313550C CN B2004100479120 A CNB2004100479120 A CN B2004100479120A CN 200410047912 A CN200410047912 A CN 200410047912A CN 1313550 C CN1313550 C CN 1313550C
- Authority
- CN
- China
- Prior art keywords
- weight part
- liquid
- solution
- dimethylbenzene
- acrylic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种用于反射光线的丙烯酸树脂涂料及制造方法。由丙烯酸树脂、二甲苯和丙酮及异佛尔酮混合溶剂、有机硅酮溶液、超细二氧化硅粉、钛白粉、甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、氟碳改性硅氧烷溶液组成A液,由六亚甲基二异氰酸酯聚异氰酸酯、二甲苯和甲氧基乙酸丙酯混合溶液组成B液,使用时将两组分混合。该涂料成本低、施工方便,其涂层具有优良的防晒隔热性能,对太阳光的辐射率为0.90。可用于石油化工储罐外表面及屋顶的防日晒涂层。
Description
技术领域
本发明涉及一种用于反射光线的丙烯酸树脂涂料及制造方法,用于石油化工储罐外表面及建筑物屋顶表面的防日晒涂层。
技术背景
现有的合成树脂涂料,涂敷于石油化工储罐外表面,其涂层对太阳光的反射能力差,尤其是对太阳光中的红外线反射率低,造成在日晒下石油化工储罐内部温度升高、带来危险;现有的屋顶表面,由于日晒使室内温度升高,给生活带来不便,对节能不利。
发明内容
本发明要解决的技术问题:避免上述现有技术中的不足之处而提供一种制造方法简单、成本低、施工方便、其涂层具有优良隔热性能、对太阳光反射率高的用于反射光线的丙烯酸树脂涂料及制造方法。
本发明采用的技术方案
本发明的一种用于反射光线的丙烯酸树脂涂料,其特征是由A液和B液组成,其中A液是由1重量份丙烯酸树脂、0.1~0.4重量份的二甲苯和丙酮及异佛尔酮混合溶剂、0.002~0.01重量份有机硅酮溶液、0.005~0.01重量份颗粒直径为1~100nm超细二氧化硅粉、0.1~0.4重量份钛白粉、0.005~0.01重量份甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、0.002~0.01重量份γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、0.01~0.05重量份氟碳改性硅氧烷溶液;其中B液是由1重量份六亚甲基二异氰酸酯聚异氰酸酯0.5~1重量份二甲苯和0.5~1重量份甲氧基乙酸丙酯的混合溶液组成,使用时由1重量份A液与0.06~0.1重量份B液混合而成。
较优的用于反射光线的丙烯酸树脂涂料,其特征是特征是由A液和B液组成,其中A液由1重量份丙烯酸树脂、0.25重量份的二甲苯和丙酮及异佛尔酮的混合溶剂、0.025重量份有机硅酮溶液、0.007重量份颗粒直径为1~100nm超细二氧化硅粉、0.35重量份钛白粉、0.007重量份甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、0.004重量份γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、0.025重量份氟碳改性硅氧烷溶液,B液是1重量份由六亚甲基二异氰酸酯聚异氰酸酯1重量份二甲苯和1重量份甲氧基乙酸丙酯混合溶液组成,使用时由1重量份A液和0.1重量份B液组成。
用于反射光线的丙烯酸树脂涂料的制造方法,其特征是在1重量份丙烯酸树脂中加入0.1~0.4重量份的二甲苯和丙酮及异佛尔酮混合溶剂,加入0.005~0.01重量份颗粒直径为1~100nm超细二氧化硅粉,再加入0.002~0.01重量份有机硅酮溶液,将其加热控制在25℃,高速搅拌1h,在搅拌下加入0.1~0.4重量份钛白粉,然后用砂磨机研磨1.5h,之后加入0.005~0.01重量份甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、0.002~0.01重量份γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、0.01~0.05重量份氟碳改性硅氧烷溶液,混合均匀制成A液;由1重量份六亚甲基二异氰酸酯聚异氰酸酯、0.5~1重量份二甲苯和0.5~1重量份甲氧基乙酸丙酯混合溶液制成B液,使用时由1重量份A液与0.06~0.1重量份B液混合而成。
较优的用于反射光线的丙烯酸树脂涂料的制造方法,其特征是在1重量份丙烯酸树脂中加入0.25重量份的二甲苯和丙酮及异佛尔酮混合溶剂,加入0.007重量份颗粒直径为1~100nm超细二氧化硅粉,再加入0.0025重量份有机硅酮溶液,将其加热控制在25℃,高速搅拌1h,在搅拌下加入0.35重量份钛白粉,然后用砂磨机研磨1.5h,之后加入0.007重量份甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、0.004重量份γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、0.025重量份氟碳改性硅氧烷溶液,混合均匀,制成A液;由1重量份六亚甲基二异氰酸酯聚异氰酸酯1重量份二甲苯和1重量份甲氧基乙酸丙酯混合溶液制成B液,使用时由1重量份A液与0.1重量份B液混合而成。
本发明的用于反射光线的丙烯酸树脂涂料A液由丙烯酸树脂、二甲苯和丙酮及异佛尔酮混合溶剂、有机硅酮溶液、超细二氧化硅粉、钛白粉、甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、氟碳改性硅氧烷溶液组成,B液由六亚甲基二异氰酸酯聚异氰酸酯、二甲苯和甲氧基乙酸丙酯混合溶液组成,使用时A液与B液组成涂料。使用的颗粒直径为1~100nm超细二氧化硅粉,有助于降低涂层对光线的吸收能力、即对光线具有强的反射能力。使用的二甲苯和丙酮及异佛尔酮混合溶剂有助于使超细二氧化硅粉与树脂充分混合分散,其中三者按相等重量份配料。使用的钛白粉有助于反射光线。使用的有机硅酮溶液有助于消除涂料中的气泡,使涂层平清。使用的甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液助于改善涂料的触变性和施工性,提高涂料的储存稳定性。使用的氟碳改性硅氧烷溶液,有助于提高涂层的光泽从而提高涂层的对光线的反射能力。
本发明与现有技术相比的有益效果
1、本发明的用于反射光线的丙烯酸树脂涂料,涂料成本低、施工方便、其涂层具有优良的防晒隔热性能、对太阳光线有极强的反射能力,其辐射率为0.90。涂层具有优良的耐候性、耐洗刷性、耐沾污性。可用于石油化工钢储罐外表面的防晒隔热涂层、建筑物屋顶及外墙表面的防日晒涂层。
2、本发明的隔热反射涂料的制造方法,工艺简单,无须特殊设备,性能价格比好,成本低。
具体实施方式1
本发明的用于反射光线的丙烯酸树脂涂料的制造方法。在1重量份丙烯酸树脂中加入0.25重量份的二甲苯和丙酮及异佛尔酮混合溶剂,其中三者按相等重量份混合,加入0.007重量份颗粒直径为1~100nm超细二氧化硅粉,再加入0.0025重量份有机硅酮溶液,将其加热控制在25℃,高速搅拌1h,在搅拌下加入0.35重量份钛白粉,然后用砂磨机研磨1.5h,之后加入0.007重量份甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、0.004重量份γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、0.025重量份氟碳改性硅氧烷溶液,混合均匀制成A液;由六亚甲基二异氰酸酯聚异氰酸酯、二甲苯和甲氧基乙酸丙酯混合溶液制成B液,其中三者按等重量份混合,使用时由1重量份A液与0.1重量份B液混合而成。
涂料硬化后所形成的涂层试验表明,涂层对太阳光的辐射率为0.90。
所用原料为市售品。
Claims (4)
1、一种用于反射光线的丙烯酸树脂涂料,其特征是由A液和B液组成,其中A液是由1重量份丙烯酸树脂、0.1~0.4重量份按相等重量份混合的二甲苯和丙酮及异佛尔酮的混合溶剂、0.002~0.01重量份有机硅酮溶液、0.005~0.01重量份颗粒直径为1~100nm超细二氧化硅粉、0.1~0.4重量份钛白粉、0.005~0.01重量份甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、0.002~0.01重量份γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、0.01~0.05重量份氟碳改性硅氧烷溶液组成;其中B液是由1重量份六亚甲基二异氰酸酯聚异氰酸酯、0.5~1重量份二甲苯和0.5~1重量份的甲氧基乙酸丙酯混合溶液组成,使用时由1重量份A液与0.06~0.1重量份B液组成。
2、根据权利要求1所述的用于反射光线的丙烯酸树脂涂料,其特征是A液由1重量份丙烯酸树脂、0.25重量份按相等重量份混合的二甲苯和丙酮及异佛尔酮混合溶剂、0.0025重量份有机硅酮溶液、0.007重量份颗粒直径为1~100nm超细二氧化硅粉、0.35重量份钛白粉、0.007重量份甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、0.004重量份γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、0.025重量份氟碳改性硅氧烷溶液组成;B液是由1重量份六亚甲基二异氰酸酯聚异氰酸酯、1重量份二甲苯和1重量份甲氧基乙酸丙酯混合溶液组成,使用时由1重量份A液和0.1重量份B液组成。
3、一种如权利要求1所述的用于反射光线的丙烯酸树脂涂料的制造方法,其特征是在1重量份丙烯酸树脂中加入0.1~0.4重量份按相等重量份混合的二甲苯和丙酮及异佛尔酮混合溶剂,加入0.005~0.01重量份颗粒直径为1~100nm超细二氧化硅粉,再加入0.002~0.01重量份有机硅酮溶液,将其加热控制在25℃,高速搅拌1h,在搅拌下加入0.1~0.4重量份钛白粉,然后用砂磨机研磨1.5h,之后加入0.005~0.01重量份甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、0.002~0.01重量份γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、0.01~0.05重量份氟碳改性硅氧烷溶液,混合均匀,制成A液;由1重量份六亚甲基二异氰酸酯聚异氰酸酯、0.5~1重量份二甲苯和0.5~1重量份甲氧基乙酸丙酯混合溶液制成B液,使用时由1重量份A液与0.06~0.1重量份B液混合而成。
4、根据权利要求3所述的用于反射光线的丙烯酸树脂涂料的制造方法,其特征是在1重量份丙烯酸树脂中加入0.25重量份按相等重量份混合的二甲苯和丙酮及异佛尔酮混合溶剂,加入0.007重量份颗粒直径为1~100nm超细二氧化硅粉,再加入0.0025重量份有机硅酮溶液,将其加热控制在25℃,高速搅拌1h,在搅拌下加入0.35重量份钛白粉,然后用砂磨机研磨1.5h,之后加入0.007重量份甲基(N-β-氨乙基γ-氨丙基)二甲氧基硅烷溶液、0.004重量份γ-甲基丙烯酰氧基丙基三甲氧基硅烷溶液、0.025重量份氟碳改性硅氧烷溶液,混合均匀,制成A液;由1重量份六亚甲基二异氰酸酯聚异氰酸酯、1重量份二甲苯和1重量份甲氧基乙酸丙酯混合溶液制成B液,使用时由1重量份A液与0.1重量份B液混合而成。