CN1188090A - Colour paving tile and its making method - Google Patents

Colour paving tile and its making method Download PDF

Info

Publication number
CN1188090A
CN1188090A CN97100154A CN97100154A CN1188090A CN 1188090 A CN1188090 A CN 1188090A CN 97100154 A CN97100154 A CN 97100154A CN 97100154 A CN97100154 A CN 97100154A CN 1188090 A CN1188090 A CN 1188090A
Authority
CN
China
Prior art keywords
slag
cement
green
colour
floor tile
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN97100154A
Other languages
Chinese (zh)
Other versions
CN1084310C (en
Inventor
孔祥禄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN97100154A priority Critical patent/CN1084310C/en
Publication of CN1188090A publication Critical patent/CN1188090A/en
Application granted granted Critical
Publication of CN1084310C publication Critical patent/CN1084310C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The present invention relates to a method for making coloured floor tile by using slag produced by arc furnace steel production. It is made up mainly by using pigments of iron oxide, red, orange, yellow, green, black and blue, etc. and adding stock, i. e, pre-slag, cement and water through such processes of stirring and press forming. Said invented floor tile is high in tightness, firm, large in bearing capacity, and its surface colour is non-ageing or non-fading, and eye-catching. Said invention not only effectively utilizes the waste material produced in steel production, but also possesses the action of protecting environment.

Description

A kind of colour floor tile and preparation method thereof
The present invention relates to a kind of colour floor tile and preparation method thereof, the particularly relevant method of utilizing the electric-arc furnace steelmaking slag to make colour floor tile.
Quickening along with Chinese national economy reform progress, the scale of fundamental construction is increasing, house, building and various buildings are rised sheer from level ground like rain the back spring bamboo, be presented in vigorously people in face of, thereupon the highway of pregnant life and surface facility also more and more towards high-grade, sternly require, spacious, generous, luxurious, style, attractive in appearance, practical direction develop.
At present, the road surface facility of China nearly all is asphalt road, cement road or a stone road of the same colour, and asphalt road is afraid of to be exposed to the sun summer, and easily chap winter; Cement road, stone road, they have a common defective, and color is single, some local material source difficulty, the cost height gives people with simple and crude, sense down of low grade.
In addition, along with the development of steel-making cause, the slag that is produced in the steelmaking process also day by day increases, pile up like a mountain for waste residue, and contaminate environment is occupied large stretch of useful ground, these waste steel slags are paid close attention to by everybody always, and people explore always and how to handle steel-making waste residue for many years, so that improve environment.
It is that oxidation sludge and later stage slag are reducing slag that electric-arc furnace steelmaking can be divided into pre-slag, the ratio that pre-slag accounts for slag is big, the raw material of pre-slag is many, iron oxide content is higher in the pre-slag, than great,, be black rigid piece shape because of iron-holder height in its slag, so do raw material brickmaking with pre-slag, solid and stable.
The object of the present invention is to provide a kind of electric-arc furnace steelmaking slag that utilizes is that pre-slag is made colour floor tile and preparation method thereof, made brick density height, solid, supporting power is big, color is eye-catching, this motley paving brick is laid on the road surface, has played the purpose in city, decoration; Make the pre-slag that perplexs environment for a long time find the approach that utilizes in addition, turn waste into wealth, played the effect of environment protection.
A kind of colour floor tile of the present invention, mainly adding the blank compacting by colored lining forms, described colored lining is a ferric oxide, colors such as red, orange, yellow, green, blue or green, indigo plant, described blank by pre-slag, cement, add water and stir compacting and form, it is characterized in that proportioning raw materials (volumetric ratio): cement: pre-slag is 0.8-1.2: 5, and water is 10% of cement and pre-slag gross weight.
A kind of colour floor tile of the present invention, its feature also is described pre-slag, and its particle is divided into two kinds of 5mm ± 1mm and 2-3mm ± 1mm, and the volumetric ratio of these two kinds of pre-slags is: 2: 3.
A kind of colour floor tile goods of the present invention prepare according to following process: 1. aggregate preparation:
With the pre-slag Mechanical Crushing, screening, granularity can be divided into two kinds of 5mm and 2-3mm: 2. blank preparation:
Batching: A, get cement and pre-slag, its volume proportioning is 1: 2: 3, i.e. 1 (cement): 2 (in earlier stage
Solid impurity particle 5mm): 3 (pre-slag particle 2-3mm),
B, water intaking, its weight are 10% of cement and pre-slag gross weight,
Stir: utilize pre-slag to make aggregate, water mixing mud adds water and stirs; 3. body formation:
A, with colored lining croci, colors such as red, orange, yellow, green, blue or green, indigo plant, optional one
Plant even spreading on stock board, thickness is about 10mm,
B, above-mentioned blank is placed in the stock board, cover is real, press forming, and the demoulding, base substrate is bright and clean, and solid colour promptly gets product of the present invention.
Further specify the present invention below in conjunction with embodiment
The scheme of described embodiment, do not limit the present invention, one of skill in the art can make improvements and change according to spirit of the present invention, and described these changes and improvements all should be considered as within the scope of the invention, and scope and spirit of the present invention are limited by claim.
1. aggregate preparation of embodiment 1:
With the pre-slag Mechanical Crushing, screening, granularity can be divided into two kinds of 5mm and 2-3mm; 2. blank preparation:
Batching: A, get 425# cement 10 bucket, particle is pre-slag 20 buckets of 5mm, and particle is 2-3mm's
Pre-slag 30 buckets,
150 kilograms of B, water intakings,
Stir: utilize pre-slag to make aggregate, water mixing mud adds water and stirs; 3. body formation:
A, select colored lining ferric oxide red powder end, and the uniform spreading of difference is on each stock board, thickness is about 10mm, B, the above-mentioned blank that stirs is placed respectively in each stock board, and cover is real, press forming, the demoulding, base substrate is bright and clean, solid colour, promptly get 100 products of the present invention, the surface is red paving brick.1. aggregate preparation of embodiment 2: with the pre-slag Mechanical Crushing, sieve, granularity can be divided into two kinds of 5mm and 2-3mm; 2. blank preparation: batching: A, get 425# cement 8 buckets, particle is pre-slag 16 buckets of 5mm, and particle is 2-3mm's
Pre-slag 24 buckets,
130 kilograms of B, water intakings, stir: utilize pre-slag to make aggregate, water mixing mud adds water and stirs; 3. body formation:
A, select colored lining iron oxide green powder, and respectively uniform spreading on each stock board,
Thickness is about 10mm,
B, the above-mentioned blank that stirs is placed respectively in each stock board, cover is real, press forming,
The demoulding, base substrate is bright and clean, and solid colour promptly gets 80 products of the present invention, and the surface is green
Paving brick.
A kind of colour floor tile of the present invention and preparation method thereof is compared with prior art: A, the present invention have thoroughly solved asphalt surface in the prior art expand with heat and contract with cold distortion, the be full of cracks of rear appearance Etc. phenomenon; B, the present invention have also solved other deficiency in the prior art, and it comprises single, the material of road surface color The source is difficult, cost is high, simple and crude, low-grade, row is transported inconvenience etc. C, since slag composition iron content than great, made brick density height, solid, supporting power are big, it Surface color is not aging, colour-fast, color is eye-catching; D, effectively utilized waste material in the steel-making, made the pre-slag that perplexs for a long time environment find profit With approach, turn waste into wealth, played the effect of environmental protection; E, this motley floor tile are laid on highway and the urban human trade, have played the decoration The purpose in city.

Claims (3)

1, a kind of colour floor tile, mainly adding the blank compacting by colored lining forms, described colored lining is a ferric oxide, colors such as red, orange, yellow, green, blue or green, indigo plant, described blank by pre-slag, cement, add water and stir compacting and form, it is characterized in that proportioning raw materials (volumetric ratio): cement: pre-slag is 0.8-1.2: 5, and water is 10% of cement and pre-slag gross weight.
2, according to the colour floor tile of claim 1, its feature also is described pre-slag, and its particle is divided into two kinds of 5mm ± 1mm and 2-3mm=1mm, and the volumetric ratio of these two kinds of pre-slags is: 2: 3.
3, a kind of preparation method of colour floor tile is characterized in that according to following process preparation: 1. aggregate preparation:
With the pre-slag Mechanical Crushing, screening, granularity can be divided into two kinds of 5mm and 2-3mm: 2. blank preparation:
Batching: A, get cement and pre-slag, its volume proportioning is 1: 2: 3, and promptly cement 1: particle is
The pre-slag 2 of 5mm: particle is the pre-slag 3 of 2-3mm,
B, water intaking, its weight are 10% of cement and pre-slag gross weight,
Stir: utilize pre-slag to make aggregate, water mixing mud adds water and stirs; 3. body formation:
A, with colored lining croci, colors such as red, orange, yellow, green, blue or green, indigo plant, optional one
Plant even spreading on stock board, thickness is about 10mm,
B, above-mentioned blank is placed in the stock board, cover is real, press forming, and the demoulding, base substrate is bright and clean,
Solid colour promptly gets product of the present invention.
CN97100154A 1997-01-13 1997-01-13 Colour paving tile and its making method Expired - Fee Related CN1084310C (en)