CN101586324A - Pervious environment protection encarpus brick and method for producing the same - Google Patents
Pervious environment protection encarpus brick and method for producing the same Download PDFInfo
- Publication number
- CN101586324A CN101586324A CNA2009100395683A CN200910039568A CN101586324A CN 101586324 A CN101586324 A CN 101586324A CN A2009100395683 A CNA2009100395683 A CN A2009100395683A CN 200910039568 A CN200910039568 A CN 200910039568A CN 101586324 A CN101586324 A CN 101586324A
- Authority
- CN
- China
- Prior art keywords
- environment protection
- lining
- bed material
- water
- encarpus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a pervious environment protection encarpus brick and a method for producing the same, including a plus material and a bottom material, wherein the plus material is composed of emery sand, common silicates P.O42.5 grade cement, pigment and water, and the bottom material is composed of refined pisolite, common silicates P.O42.5 grade cement and water. The encarpus brick of the invention has an elegance and beautiful appearance, is ecological, environment protection, pervious, ventilated, radiating and skidproof, and may be used for laying for metro roads, large-sized parks, sports gymnasium, high-grade buildings, speedway service zone, plaza, shipside, parking grounds, district roads and the like, and is worthy to employ and popularize extensively.
Description
Technical field
The invention provides a kind of pervious environment protection encarpus brick and preparation method thereof, be specifically related to a kind of be used for floor file novel and can seep water, keep azulejo that surrounding enviroment water and soil do not run off and preparation method thereof fast.
Background technology
At present, along with improving constantly of people's living standard, people are also more and more higher to the requirement of shelter surrounding enviroment, traditional floor file azulejo, do not have the water-permeable and air permeable heat sinking function, rainwater can not cause soil erosion with brick body rapid osmotic to underground, can't replenish underground water effectively, unfavorable to the green plants growth of periphery; And how traditional floor file azulejo is because surperficial forming with the fine sand compacting, the rainy day descendant walks in the above and slips easily, traffic is exerted an influence, the blemish in an otherwise perfect thing so seem,, the conserve water and soil pervious environment protection encarpus brick that run off anti-skidding at the ventilative heat radiation of a kind of novel water permeable of traditional azulejo existing problems development is very necessary.
Summary of the invention
The present invention is in order to overcome the deficiency that above prior art exists, and provides that a kind of production technology is simple, permeable, ventilative, heat radiation, anti-skidding, environmental protection, the pervious environment protection encarpus brick that conserves water and soil and do not run off.
Another object of the present invention is to provide a kind of preparation method of pervious environment protection encarpus brick.
Purpose of the present invention realizes by following technical scheme: comprise a lining and a bed material, it is characterized in that described lining is made up of class g cement, pigment and water such as diamond dust, normal silicate P.O42.5, bed material is made up of class g cements such as refining Guamishi, normal silicate P.O42.5 and water, and each weight percentages of components is:
Lining: diamond dust 68%-75%
Class g cement 20%-26% such as normal silicate P.O42.5
Pigment 0.7%-1%
Water 4%-5%
Bed material: refining Guamishi 78%-80%
Class g cement 15%-17% such as normal silicate P.O42.5
Water 4%-5%
The color that it is characterized in that the diamond dust in the described lining is red, orange, yellow, green, blue or green, blue or purple.
It is characterized in that described diamond dust diameter is 1.25mm～2.5mm.
It is characterized in that class g cements such as described normal silicate P.O42.5 are ash concrete or white cement.
It is characterized in that described refining Guamishi diameter 5mm～12mm.
It is characterized in that described pigment is iron oxide pigment.
The preparation method of above-mentioned pervious environment protection encarpus brick is characterized in that may further comprise the steps:
(1) preparation lining: by described ratio with the mixing of class g cements such as diamond dust, normal silicate P.O42.5, pigment after, put into the lining mixer and add water and stir into thick;
(2) preparation bed material: after will making with extra care Guamishi, normal silicate P.O42..5 grade cement mixing in described ratio, put into the bed material mixer and add water and stir into thick;
(3) evenly bed material is layered in the former frame of die forming machine, formpiston presses down and shakes 2 seconds to 3 seconds in advance, then lining evenly is layered on above the bed material, and formpiston presses down the demoulding after main the shaking 5 seconds-6 seconds, is sent to finished product by chain transfer then and stacks the place.
(4) for stacking finished bricks in heaps, pitched the workshop natural air drying 28 hours to 30 hours by fork truck, packaging and warehousing then, maintenance can be dispatched from the factory in 8 days to 10 days.
It is characterized in that described step (3) is lining storehouse and the bed material storehouse that the lining that will stir and bed material are put into forming machine respectively, is finished automatically by forming machine.
It is characterized in that described fabric thickness is 5mm～10mm.
The present invention compares than prior art, has the following advantages and beneficial effect:
(1) pervious environment protection encarpus brick of the present invention, ecological, environmental protective, with its unique pervious function, can make natural precipitation see through the face of land well, effectively recharge groundwater is given full play to the advantage that soil is regulated city temperature and humidity, effectively solves problems such as street floating dust, eliminate " heat island effect ", safeguard the urban surface ecological homeostasis;
(2) the present invention can guarantee that the rainy day road surface do not have ponding, and because its rough surface can improve vehicle ' and pedestrian's safety and comfortableness;
(3) preparation method of the present invention is simple, productivity ratio is high, pollution-free, its bending and compressive strength and anti-wear performance are suitable with the Common Concrete Pavement brick, the laying in places such as town road, large-scale park, stadiums, senior building, Expressway Service, square, harbour, parking lot, sub-district road be can be widely used in, extensively utilization and popularization are worth.
(4) the present invention can produce the azulejo of multiple abnormity as required, for example: shades of colour, all size and different shape, its color is various, and outward appearance is beautiful.Through testing repeatedly and checking, the key technical indexes intensity, anti-folding, immersion, light fastness, freeze proof, abrasion resistance, permeability rate are " the permeable brick standard of JC/T945-2005 " above national sector standard all, and of the present invention being extensive use of will have positive social benefit.
The specific embodiment
Below in conjunction with embodiment, to the detailed description further of the present invention's do, but embodiments of the present invention are not limited thereto.
Embodiment one
With the 230*115*60cm pervious environment protection encarpus brick of producing 10 square metres of redness is that example is elaborated.
Prepared pervious environment protection encarpus brick, each component and percentage by weight thereof are:
Lining: White gold emery 70.92%
Normal silicate P.O42.5 grade white cement 23.64%
Red Lockwood mars pigment 0.71%
Water 4.73%
Bed material: selected Guamishi 79.37%
Normal silicate P.O42.5 grade ash concrete 15.87%
Water 4.76%
Its preparation method is as follows:
(1) preparation lining: diameter is 3 kilograms of 300 kilograms of White gold emery, Lockwood mars pigments, 100 kilograms of normal silicate P.O42.5 grade white cements, 20 kilograms in the water of 2.5mm, puts into the lining mixer and stirs into thick;
(2) preparation bed material: diameter is 1000 kilograms of high-quality Guamishis, 200 kilograms of normal silicate P.O42.5 grade ash concretes, 60 kilograms in the water of 10mm, puts into the bed material mixer and stirs into thick;
(3) lining, the bed material that stir are put into the lining storehouse and the bed material storehouse of the 230*115*60cm mould molding machine that has installed respectively, start forming machine, forming machine evenly is layered on bed material in the former frame of mould (below the former frame supporting plate being arranged), formpiston presses down and shakes in advance about 2 seconds, formpiston promotes, forming machine evenly is layered on (the fabric thickness layer is at 8mm) above the bed material with lining then, and formpiston presses down the demoulding after main the shaking 5 seconds, and the plate brick that chain transfer will press is sent to the finished product place and piled up.
(4) for stacking finished bricks in heaps, pitched the workshop natural air drying 28 hours by fork truck, packaging and warehousing then, maintenance can be dispatched from the factory in 8 days to 10 days.
Embodiment two
Prepared litchi surface encaustic brick, each component and percentage by weight thereof are:
Lining: White gold emery 71%
Normal silicate P.O42.5 grade white cement 23%
Red sea this mars pigment 1% of name
Water 5%
Bed material: selected Guamishi 79%
Normal silicate P.O42.5 grade ash concrete 16%
Water 5%
Its preparation method is as follows:
(1) gets lining and bed material according to the above ratio ready.
(2) lining, the bed material that stir are put into the lining storehouse and the bed material storehouse of the 230*115*60cm mould molding machine that has installed respectively, start forming machine, forming machine evenly is layered on bed material in the former frame of mould (below the former frame supporting plate being arranged), formpiston presses down and shakes in advance about 3 seconds, formpiston promotes, forming machine evenly is layered on (the fabric thickness layer is at 8mm) above the bed material with lining then, and formpiston presses down the demoulding after main the shaking 6 seconds, and the plate brick that chain transfer will press is sent to the finished product place and piled up.
(3) for stacking finished bricks in heaps, pitched the workshop natural air drying 30 hours by fork truck, packaging and warehousing then, maintenance can be dispatched from the factory in 8 days to 10 days.
Its preparation method and example one difference be, constituent content is according to the aforementioned proportion adjustment in each step, and formpiston presses down and shakes 3 seconds in advance in the step (2), and formpiston presses down the demoulding after main the shaking 6 seconds, and natural air drying is 30 hours in the step (3).
Embodiment three
According to the color of customer demand, the smart hard rock rice of lining employing different colours can be prepared into the pervious environment protection encarpus brick of different colours, and lining does not re-use pigment.Prepared pervious environment protection encarpus brick, each component and percentage by weight thereof are:
Lining: mosaic gold emery 71.63%
Normal silicate P.O42.5 grade white cement 23.64%
Water 4.73%
Bed material: selected Guamishi 79.37%
Normal silicate P.O42.5 grade ash concrete 15.87%
Water 4.76%
The preparation method is identical with embodiment one, no longer describes in detail.
The above-mentioned specific embodiment is the preferred embodiments of the present invention; can not limit claim of the present invention; other any change or other equivalent substitute mode that does not deviate from technical scheme of the present invention and made is included within protection scope of the present invention.
Claims (9)
1, a kind of pervious environment protection encarpus brick, mainly constitute by lining and bed material, it is characterized in that, described lining is made up of class g cement, pigment and water such as diamond dust, normal silicate P.O42.5, bed material is made up of class g cements such as refining Guamishi, normal silicate P.O42.5 and water, and each weight percentages of components is:
Lining: diamond dust 68%～75%
Class g cements 20%～26% such as normal silicate P.O42.5
Pigment 0.7%～1%
Water 4%～5%
Bed material: refining Guamishi 78%～80%
Class g cements 15%～17% such as normal silicate P.O42.5
Water 4%～5%.
2, pervious environment protection encarpus brick according to claim 1, the color that it is characterized in that the diamond dust in the described lining is red, orange, yellow, green, blue or green, blue or purple.
3, pervious environment protection encarpus brick according to claim 1 and 2, the diameter that it is characterized in that described diamond dust is 1.25mm～2.5mm.
4, pervious environment protection encarpus brick according to claim 1 is characterized in that class g cements such as described normal silicate P.O42.5 are ash concrete or white cement.
5, pervious environment protection encarpus brick according to claim 1, the diameter that it is characterized in that described refining Guamishi is 5mm～12mm.
6, pervious environment protection encarpus brick according to claim 1 is characterized in that, described pigment is iron oxide.
7, a kind of preparation method of pervious environment protection encarpus brick may further comprise the steps:
(1) preparation lining: by described ratio with the mixing of class g cements such as diamond dust, normal silicate P.O42.5, pigment after, put into the lining mixer and add water and stir into thick;
(2) preparation bed material: after will making with extra care Guamishi, normal silicate P.O42.5 grade cement mixing in described ratio, put into the bed material mixer and add water and stir into thick;
(3) evenly bed material is layered in the former frame of die forming machine, formpiston presses down and shakes 2 seconds to 3 seconds in advance, then lining evenly is layered on above the bed material, and formpiston presses down the demoulding after main the shaking 5 seconds-6 seconds, is sent to finished product by chain transfer then and stacks the place;
(4) for stacking finished bricks in heaps, transported to the workshop natural air drying 28 hours to 30 hours by fork truck, packaging and warehousing then, maintenance can be dispatched from the factory in 8 days to 10 days.
8, the preparation method of pervious environment protection brick according to claim 7 is characterized in that, described step (3) is lining storehouse and the bed material storehouse that the lining that will stir and bed material are put into forming machine respectively, is finished automatically by forming machine.
9, the preparation method of pervious environment protection encarpus brick according to claim 7 is characterized in that described fabric thickness is 5mm～10mm.