CN1186153C - 片状锌及锌铝合金粉湿法生产工艺 - Google Patents
片状锌及锌铝合金粉湿法生产工艺 Download PDFInfo
- Publication number
- CN1186153C CN1186153C CN 03124444 CN03124444A CN1186153C CN 1186153 C CN1186153 C CN 1186153C CN 03124444 CN03124444 CN 03124444 CN 03124444 A CN03124444 A CN 03124444A CN 1186153 C CN1186153 C CN 1186153C
- Authority
- CN
- China
- Prior art keywords
- ball milling
- zinc
- allumen
- ball
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种片状锌及锌铝合金粉湿法生产工艺,该工艺包括配料、球磨、抛光、分级、固液分离工序,配料球磨工序是将非片状锌粉或锌铝合金粉原料、溶剂、至少含有一种金属氧化物的助剂及球磨介质,按比例投入转速不低于120r/min的磨机中球磨。本发明大大缩短球磨时间,提高了球磨效率,使能耗降低,同时得到的产品与已有技术相比,具有表面规整,抗氧化性强,径厚比大,遮盖力高,粒度分布窄。
Description
技术领域:
本发明涉及颜料粉的生产工艺,尤其是涉及片状锌及锌铝合金粉湿法生产工艺。
背景技术:
目前,本领域公知的片状锌粉湿法生产工艺通常是:将锌粉原料、溶剂、硬脂酸或硬脂酸盐类成片助剂一起投入转速为每分钟几十转的球磨机(卧式)中进行球磨,球磨后料浆经抛光分级,固液分离得到片状锌粉浆,其中球磨时,为防止加工过程中产品氧化,造成成品品质下降,球磨速度均采用低速,因此球磨时间长,如美国专利US4026710中所述及的工艺,其球磨时间需10小时以上,产品质量虽然较前有所提高,但球磨时间长,效率低,所得成品表面易氧化,产品遮盖力低。
发明内容:
本发明的目的在于提供一种球磨时间短,效率高,产品遮盖力高,表面不易氧化的片状锌及锌铝合金粉湿法生产工艺。
本发明片状锌及锌铝合金粉湿法生产工艺包括配料、球磨、抛光、分级、固液分离工序,其中配料球磨工序是将非片状锌粉或锌铝合金粉原料、溶剂、至少含有一种金属氧化物的助剂及球磨介质,按比例投入转速不低于120r/min的磨机中球磨。
为得到片状锌及锌铝合金粉在固液分离工序之后进行干燥。
所述非片状锌粉或锌铝合金粉原料选取粒度不粗于200目,金属氧化物为SiO2、TiO2、ZnO、Al2O3、Sb2O3、ZrO2、V2O5的一种或几种,其总用量为原料锌粉或锌铝合金粉重量的0.05-10%。
所述金属氧化物总用量为原料锌粉或锌铝合金粉重量的0.5-5%。
所述磨机最好为搅拌球磨机或高能球磨机,球磨转速为120-500r/min,球磨时间为10-240min。
球磨速度最好为150-350r/min,球磨时间为30-180min。
由于本发明助剂至少包含一种金属氧化物,在球磨过程中,金属氧化物包覆于锌粉或锌铝合金粉表面,增加了锌铝或锌铝合金粉的表面抗氧化性,因此可采用大于120r/min的速度高速球磨,时间仅需10-240min,由此大大缩短球磨时间,提高了球磨效率,随之带来的是能耗降低,同时得到的产品与已有技术相比,具有表面规整,抗氧化性强,径厚比大,遮盖力高,粒度分布窄。
具体实施方式:
本发明具体实施时,其原料锌粉或锌铝合金粉为气化,冷凝或雾化法制得的非片状锌粉或锌铝合金粉,粒度不粗于200目,溶剂为溶剂油、亚麻油、松香水或其它高沸点溶剂,助剂包括硬脂酸、硬脂酸盐以及SiO2、TiO2、ZnO、Al2O3、Sb2O3、ZrO2、V2O5等金属氧化物中的一种或几种。溶剂用量为锌或锌铝合金粉的重量的30-300%,硬脂酸、硬脂酸盐为锌或锌铝合金粉重量的1-40%,最好为2-10%,金属氧化物用量为锌或锌铝合金粉重量的0.05-10%,如0.1、0.3、3、4、5、6、7、8、9,最好为0.5-5%,如1、1.5。采用的球磨机为搅拌磨机或其它高能磨机,运转速度不低于120r/min,选择范围为120-500r/min,最好为150-350r/min,如190、240、250、290r/min。球磨介质为钢球,直径为3-16mm,最好为4.5-12mm,其与原料锌粉或锌铝合金粉的比例为1∶0.5至1∶40,最好为1∶5至1∶20。
实施例1:取400目锌粉原料100kg,200#溶剂油200kg,氧化锌4kg、硬脂酸4kg、钢球2000kg及其它助剂投入球磨机中,以210-230r/min,如220r/min的转速球磨120min后用200kg溶剂稀释出料,将料浆投入抛光机中进行抛光,抛光后的料浆经分级、固液分离后制得片状锌及锌铝合金粉浆。
实施例2:取500目锌粉原料100kg,200#溶剂油200kg,氧化锌4kg、硬脂酸4kg、钢球2000kg及其它助剂投入球磨机中,以220r/min的转速球磨120min后用200kg溶剂稀释出料,将浆投入抛光机中进行抛光,抛光后的料浆经分级、固液分离、干燥后制得片状锌及锌铝合金粉。
按照上述两个实施例的生产工序,下列3-10个实施方式的工艺参数各有不同(未在表中列出的参数同实施例1或2),见下表:
实施例序号 | 原料名称 | 粒度(目) | 氧化物名称 | 氧化物用量(kg) | 球磨速度(r/min) | 球磨时间(min) |
3 | 锌 | 200 | TiO2 | 1 | 320-340 | 60 |
4 | 锌 | 325 | SiO2 | 2 | 300-320 | 60 |
5 | 锌 | 400 | ZrO2 | 2.5 | 280-300 | 90 |
6 | 锌 | 500 | Al2O3 | 3.5 | 260-280 | 120 |
7 | 锌 | 600 | V2O5 | 4 | 240-260 | 120 |
8 | 锌 | 700 | Sb2O3 | 4.5 | 220-240 | 120 |
9 | 锌 | 800 | ZrO2 | 5 | 180-220 | 150 |
10 | 锌铝合金粉 | 400 | SiO2 | 4 | 200-240 | 120 |
Claims (7)
1、一种片状锌及锌铝合金粉湿法生产工艺,包括配料、球磨、抛光、分级、固液分离工序,其特征在于:配料球磨工序是将非片状锌粉或锌铝合金粉原料、溶剂、至少含有一种金属氧化物的助剂及球磨介质,按比例投入转速不低于120r/min的磨机中球磨。
2、根据权利要求1所述的片状锌及锌铝合金粉湿法生产工艺,其特征在于:在固液分离工序之后进行干燥。
3、根据权利要求1或2所述的片状锌及锌铝合金粉湿法生产工艺,其特征在于:所述非片状锌粉或锌铝合金粉原料选取粒度不粗于200目,金属氧化物为SiO2、TiO2、ZnO、Al2O3、Sb2O3、ZrO2、V2O5中的一种或几种,其总用量为原料锌粉或锌铝合金粉重量的0.05-10%。
4、根据权利要求3所述的片状锌及锌铝合金粉湿法生产工艺,其特征在于:所述金属氧化物总用量为原料锌粉或锌铝合金粉重量的0.5-5%。
5、根据权利要求1或2所述的片状锌及锌铝合金粉湿法生产工艺,其特征在于:所述磨机为搅拌球磨机或高能球磨机,球磨转速为120-500r/min,球磨时间为10-240min。
6、根据权利要求3所述的片状锌及锌铝合金粉湿法生产工艺,其特征在于:所述磨机为搅拌球磨机或高能球磨机,球磨转速为120-500r/min,球磨时间为10-240min。
7、根据权利要求4所述的片状锌及锌铝合金粉湿法生产工艺,其特征在于:球磨速度为150-350r/min,球磨时间为30-180min。