CN118202501A - 锂二次电池 - Google Patents
锂二次电池 Download PDFInfo
- Publication number
- CN118202501A CN118202501A CN202280071457.4A CN202280071457A CN118202501A CN 118202501 A CN118202501 A CN 118202501A CN 202280071457 A CN202280071457 A CN 202280071457A CN 118202501 A CN118202501 A CN 118202501A
- Authority
- CN
- China
- Prior art keywords
- resin film
- lithium
- negative electrode
- metal layer
- secondary battery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种锂二次电池,其具备:正极;负极;分隔件,其配置在所述正极与所述负极之间;以及非水电解质,其具有锂离子传导性,在所述负极中,在充电时锂金属析出,在放电时所述锂金属溶解,所述负极具有树脂薄膜和与所述树脂薄膜层叠的锂金属层。
Description
技术领域
本公开涉及一种锂二次电池。
背景技术
作为超过锂离子电池的高容量的非水电解质二次电池,锂二次电池(锂金属二次电池)是有希望的。在锂二次电池中,在充电时锂金属在负极析出,在放电时锂金属溶解于非水电解质中而释放锂离子。
然而,在锂二次电池中,在充电时锂金属在负极析出,在放电时锂金属溶解,因此负极的体积变化显著。因此,容易产生电极的压曲、电极的断裂等。
专利文献1提出的阳极电极构造体具备包含铜的集电体。阳极电极构造体还具备形成于集电体上的锂金属膜。阳极电极构造体还具备形成于锂金属膜上的固体电解质界面(SEI)膜堆。在一个实施方式中,集电体110、160中的至少1个包含用金属材料涂覆的聚对苯二甲酸乙二醇酯膜。
现有技术文献
专利文献
专利文献1:日本特表2021-502671号公报
发明内容
发明要解决的问题
如专利文献1那样,在锂二次电池中,集电体一般使用铜。然而,判明了在负极电位低的状态下铜脆化。铜的脆化进一步促进电极的压曲、电极的断裂等,因此锂二次电池的循环特性容易降低。
用于解决问题的方案
本公开的一方面涉及一种锂二次电池,其中,该锂二次电池具备:正极;负极;分隔件,其配置在所述正极与所述负极之间;以及非水电解质,其具有锂离子传导性,在所述负极中,在充电时锂金属析出,在放电时所述锂金属溶解,所述负极具有树脂薄膜和与所述树脂薄膜层叠的锂金属层。
发明的效果
根据本公开,可抑制锂二次电池的循环特性的降低。
将本发明的新的特征记述在所附的权利要求书中,但本发明涉及结构和内容这两者,与本发明的其他目的和特征一起,通过对照附图的以下的详细的说明来更好地理解。
附图说明
图1是示意性地表示本公开的一实施方式的锂二次电池的纵剖视图。
图2是图1中的区域II的放大剖视图。
图3是图1中的区域III的放大剖视图。
具体实施方式
以下,举例对本公开的实施方式进行说明,但本公开并不限定于以下说明的例子。在以下的说明中,有时例示具体的数值、材料等,但只要能够得到本公开的效果,就也可以应用其他数值、材料等。需要说明的是,本公开中特征性的部分以外的构成要素也可以应用公知的二次电池的构成要素。在本说明书中,在“数值A~数值B的范围”的情况下,该范围包括数值A和数值B。“数值A~数值B”的记载能够替换为“数值A以上且数值B以下”。在以下的说明中,在例示了与特定的物性、条件等相关的数值的下限和上限的情况下,只要下限不成为上限以上,就能够将例示的下限的任一个与例示的上限的任一个任意地组合。在例示多种材料的情况下,既可以从其中选择1种单独使用,也可以组合使用2种以上。
另外,本公开包含从所附的权利要求书所记载的多个权利要求中任意选择的2个以上的权利要求所记载的事项的组合。即,只要不产生技术上的矛盾,就能够组合从所附的权利要求书所记载的多个权利要求中任意选择的2个以上的权利要求所记载的事项。
本公开的实施方式涉及使用锂金属作为负极活性物质的锂二次电池(锂金属二次电池)。锂二次电池具备正极、负极、配置于正极与负极之间的分隔件、以及具有锂离子传导性的非水电解质。在锂二次电池的负极中,充电时锂金属析出,放电时该锂金属溶解。
在锂二次电池中,额定容量的例如70%以上通过锂金属的析出和溶解而显现。充电时和放电时的负极中的电子的移动主要基于负极中的锂金属的析出和溶解。具体而言,充电时和放电时的负极中的电子的移动(在其他观点中为电流)的70%~100%(例如80%~100%、90%~100%)是基于锂金属的析出和溶解。即,锂二次电池的负极的充电时和放电时的负极中的电子的移动与主要基于由负极活性物质(石墨等)引起的锂离子的吸藏和释放的负极不同。
在充电时在负极使锂金属析出的电池中,满充电时的负极的开路电位(OCV:OpenCircuit Voltage)相对于锂金属(锂的溶解析出电位)例如为70mV以下。满充电时是指,在将电池的额定容量设为C时,例如将电池充电到0.98×C以上的充电状态(SOC:State ofCharge)为止的状态。满充电时的负极的开路电位(OCV)只要将满充电状态的电池在氩气气氛下分解而取出负极,以锂金属为对电极组装电池单体进行测定即可。电池单体的非水电解质也可以是与分解后的电池中的非水电解质相同的组成。
以下,对二次电池的各构成要素依次进行说明。
[负极]
在本公开的实施方式的锂二次电池中,负极具有树脂薄膜和与树脂薄膜层叠的锂金属层。即,负极是树脂薄膜与锂金属层的层叠体。以下,将这样的负极也称为“负极RL”。
树脂薄膜通常为绝缘体,不具有集电功能,因此锂金属层承担集电功能。也可以在树脂薄膜的表面(特别是与用于将负极和端子电连接的引线或极耳的连接部位)设置铜、镍等基底金属层。在设置基底金属层的情况下,即使在充放电循环时锂金属层减少或者锂金属变化为锂化合物的情况下,也能够抑制集电功能的降低。
锂二次电池在充电时锂金属在负极析出,因此负极的膨胀的程度容易变大。在此,“负极的膨胀”是指,负极的体积与析出的锂金属的体积的合计的体积增加。特别是在锂金属以枝晶状析出的情况下,膨胀量进一步变大。由此,在负极容易产生应力。
另外,在负极使用铜的情况下,铜在负极电位低的状态下脆化。在负极产生的应力与铜的脆化相结合,负极劣化,促进压曲、断裂等。若通过SEM观察铜的断裂部分,则沿着铜的晶界观察到多个晶界裂纹。因而,认为由于晶界裂纹而产生脆性破坏。
另一方面,在负极RL中,树脂薄膜不会像铜那样脆化。另外,树脂薄膜的柔软性高,能够缓和在负极产生的应力,因此对应力的耐性高。因此,作为树脂薄膜与锂金属层的层叠体的负极RL不易劣化,不易产生断裂等。另外,树脂薄膜为轻量,容易提高锂二次电池的能量密度。进而,树脂薄膜在辊运送中不易断裂,处理容易。
树脂薄膜的主面是指树脂薄膜的端面以外的面,是具有2个最大面积的面。锂金属层也可以分别层叠于树脂薄膜的2个主面这两者。锂金属层也具有2个主面。
(第1实施方式)
在第1实施方式中,负极在树脂薄膜的至少一个主面具有与该主面接触的锂金属层。具体而言,锂金属层的一个主面与树脂薄膜的主面接触。与树脂薄膜的主面接触的一侧的锂金属层的主面的整体也可以与树脂薄膜的主面接触。或者,与树脂薄膜的主面接触的一侧的锂金属层的主面的90%以上的面积也可以与树脂薄膜的主面接触。
需要说明的是,在负极RL中,在树脂薄膜与锂金属层之间可以存在不可避免地形成的层。另外,通过锂金属参与的反应而生成的产物视为锂金属层的一部分。另外,容许实质上不产生脆化的影响的程度的铜介于锂金属层与树脂薄膜之间。
在负极RL中,锂金属层也可以在树脂薄膜的主面直接粘贴膜状的锂金属而形成。另外,锂金属层也可以通过使用液相法或气相法在树脂薄膜的主面直接堆积锂金属而形成。作为液相法,可列举出电析法。作为气相法,可列举出蒸镀法。但是,负极RL的制造方法或锂金属层的形成方法没有特别限定。
树脂薄膜的主面既可以平滑,也可以粗糙化,还可以进行等离子体处理、电晕处理等。等离子体处理是指通过等离子体照射使树脂薄膜的主面改性的处理。电晕处理是指通过电晕放电照射使树脂薄膜的主面改性的处理。在树脂薄膜的主面平滑的情况下,平滑是指主面的最大高度粗糙度Rz为10μm以下。在树脂薄膜的主面被粗糙化的情况下,主面的最大高度粗糙度Rz超过10μm,也可以为20μm以上。最大高度粗糙度Rz按照JIS B 0601:2013进行测定。
在第1实施方式的一个方式中,负极在树脂薄膜的两个主面分别具有锂金属层,正极和负极隔着分隔件卷绕。在该情况下,锂金属层分别与树脂薄膜的两个主面接触。
(第2实施方式)
在第2实施方式中,负极在树脂薄膜的至少一个主面具有与该主面接触的基底金属层。锂金属层与基底金属层的主面和树脂薄膜的上述主面中的至少一者接触。具体而言,锂金属层的一个主面与基底金属层和树脂薄膜的至少一个主面接触。基底金属层提高负极的集电性。
锂金属层例如也可以与基底金属层和树脂薄膜的两个主面接触。即,基底金属层也可以以仅与树脂薄膜的主面的一部分接触的方式设置。在该情况下,锂金属层能够与基底金属层和树脂薄膜的两个主面接触。例如,也可以在树脂薄膜的主面中的与用于将负极和端子电连接的引线或极耳的连接部位选择性地设置基底金属层。设置基底金属层的面积相对于树脂薄膜的一个主面例如既可以为2%以上且30%以下,也可以为10%以上且20%以下。期望的是,这样的限定的区域包含与引线或极耳的连接部位。
基底金属层也可以相对于树脂薄膜的一个主面设置成例如90%以上的面积。在该情况下,锂金属层能够仅与基底金属层的主面接触。
与树脂薄膜的主面接触的一侧的锂金属层的主面的整体也可以与基底金属层和树脂薄膜的至少一个主面接触。或者,与树脂薄膜的主面接触的一侧的锂金属层的主面的90%以上的面积也可以与基底金属层和树脂薄膜中的至少一个主面接触。
在第2实施方式的一个方式中,负极在树脂薄膜的两个主面分别具有基底金属层和锂金属层,正极和负极隔着分隔件卷绕。在该情况下,配置于树脂薄膜的两个主面的锂金属层也可以分别与基底金属层的主面接触。
基底金属层的厚度例如既可以为2μm以下,也可以为1μm以下。在该情况下,即使在基底金属层包含铜的情况下,也不易受到脆化的影响。但是,从可靠地得到集电性的提高效果的观点出发,期望的是,将基底金属层的厚度设为例如0.05μm以上。
基底金属层例如包含铜、镍、铬、钛、银、金、锡等,在容易确保耐腐蚀性、导电性等方面、难以与锂合金化方面是优选的。
基底金属层例如能够通过蒸镀、溅射等气相法、化学镀法、电镀法、层压法等形成,但其形成方法没有特别限定。
树脂薄膜是指以树脂或有机物为主成分的膜,树脂薄膜的51质量%以上由树脂或有机物构成。树脂薄膜也可以包含无机颗粒这样的无机物。树脂薄膜既可以是拉伸膜,也可以是无孔性膜(无孔的膜),还可以是具有规则排列的多个孔的膜。树脂薄膜既可以具有绝缘性,也可以具有导电性,还可以是非导电性的。树脂薄膜的形态和物性没有特别限定。
树脂薄膜所包含的树脂并无特别限定,例如可列举出聚酯、聚酰胺、聚酰亚胺等。其中,期望的是,具有芳香环或不含氟原子的树脂。树脂在其分子内具有芳香环(例如苯环)的情况下,树脂薄膜与锂金属层的亲和性变高,两者间的粘接力提高。作为聚酯,优选芳香族聚酯,聚对苯二甲酸乙二醇酯、聚对苯二甲酸丁二醇酯等由于廉价而特别优选。作为聚酰亚胺,优选芳香族聚酰亚胺,作为聚酰胺,优选芳香族聚酰胺(芳纶)。
树脂薄膜的拉伸强度例如为100MPa以上,既可以为200MPa以上,也可以为250MPa以上,还可以为300MPa以上。树脂薄膜的拉伸强度的上限没有特别限定,从确保缓和应力的充分的柔软性的观点出发,例如也可以为500MPa以下。
树脂薄膜的拉伸强度根据将树脂薄膜的试验片在相对于其截面垂直的方向上以一定速度拉伸时的最大载荷,通过下式求出。即,拉伸强度是最大载荷除以初始的截面积而得到的标称应力。拉伸强度通过遵循JIS C 2151的方法进行测定。试验片由树脂薄膜冲裁成预定的形状而制作。试验片的形状为JIS C 2151的试验片类型2。试验片的厚度设为树脂薄膜的厚度。
ρ=Pmax/A0
ρ:拉伸强度(MPa)
Pmax:最大载荷(N)
A0:初始的截面积(mm2)
树脂薄膜的断裂伸长率例如为50%以上,既可以为80%以上,也可以为100%以上,还可以为200%以上。树脂薄膜的断裂伸长率的上限没有特别限定,从确保充分的机械强度的观点出发,例如也可以为400%以下。
树脂薄膜的断裂伸长率根据将树脂薄膜的试验片在相对于其截面垂直的方向上以一定速度拉伸时的断裂时的长度和初始的长度,通过下式求出。断裂伸长率通过遵循JISK 7127的方法来测定。试验片的形状为JIS K 7127的试验片类型2。试验片的厚度设为膜厚度。
断裂伸长率δ(%)=100×(断裂时的长度L-初始的长度Lo)/初始的长度Lo
δ:断裂伸长率(%)
L:断裂时的长度
Lo:初始的长度
锂金属层的厚度只要是在放电时能够确保充分的集电性的厚度即可,在放电深度(DOD:Depth of Discharge)90%以上的放电状态下,例如既可以为1μm以上,也可以为5μm以上。另一方面,从提高锂二次电池的能量密度的观点出发,锂金属层的厚度在放电深度90%以上的放电状态下也可以为40μm以下或30μm以下。需要说明的是,放电深度(DOD)为90%以上的放电状态与将电池的额定容量设为C时的0.1×C以下的充电状态(SOC)同义。
锂金属层作为负极集电体发挥功能。在充电时,非水电解质所包含的锂离子在锂金属层上接受电子而成为锂金属,在锂金属层的表面析出。在锂金属层的表面析出的锂金属通过放电而作为锂离子溶解于非水电解质中。需要说明的是,非水电解质所包含的锂离子既可以源自添加到非水电解质中的锂盐,也可以通过充电从正极活性物质供给,还可以是它们两者。
锂金属层只要是由锂金属和锂合金中的至少一者形成的层即可。锂合金优选包含镁。锂合金中所包含的镁的含有率例如为0.1质量%以上,优选为0.5质量%以上或1质量%以上,也可以为3质量%以上或5质量%以上。在锂合金中的镁的含有率为这样的范围的情况下,抑制锂金属以枝晶状析出的效果提高,并且,容易在锂金属层的表面形成膜质优异的SEI覆膜。因此,能够进一步提高循环特性。锂合金中的镁的含有率例如为30质量%以下,也可以为15质量%以下或10质量%以下。在锂合金中的镁的含有率为这样的范围的情况下,通过锂金属的析出和溶解而得到容量的比例变多,能够得到更高的容量。另外,镁容易固溶于锂中,容易形成稳定的锂合金。
锂合金也可以包含除了锂(第1元素)和镁(第2元素)之外的第3元素。第3元素的例子为铝、铟、钙、铅、氢、钠、铋、铜以及锌。锂合金既可以包含1种第3元素,也可以包含2种以上的第3元素。锂合金中的第3元素的含有率例如为10质量%以下,也可以为1质量%以下或低于0.1质量%。
从提高锂二次电池的能量密度的观点出发,只要确保机械强度,树脂薄膜的厚度越薄越好。树脂薄膜的厚度例如既可以为5μm以上且80μm以下,也可以为5μm以上且30μm以下。
锂金属层和树脂薄膜的厚度也可以通过分别使用扫描型电子显微镜(SEM)测定负极的截面的任意10点的厚度,计算它们的平均值来求出。
负极也可以在树脂薄膜的两个主面具有锂金属层。在该情况下,也可以通过将正极和负极隔着分隔件卷绕而构成电极组。即,锂二次电池也可以具备卷绕型的电极组。通常,卷绕型的电极组在充放电时容易产生应力,容易产生负极的断裂。特别是在卷绕型的电极组的外周侧,有时对负极施加大的拉伸张力。另一方面,负极RL包含断裂伸长率大的树脂薄膜,因此即使在卷绕型的电极组的外周侧对负极施加大的拉伸张力的情况下,也可显著抑制负极的断裂。
[正极]
正极例如具备正极集电体和担载于正极集电体的正极合剂层。正极合剂层能够通过将使正极合剂分散于分散介质而成的正极浆料涂布于正极集电体的表面并使其干燥而形成。也可以根据需要对干燥后的涂膜进行压延。正极合剂能够包含正极活性物质作为必须成分,包含粘结剂、导电剂等作为任意成分。正极合剂层既可以仅形成于正极集电体的单面,也可以形成于两面。
正极活性物质是吸藏和释放锂离子而显现容量的材料。作为正极活性物质,例如可列举出含锂过渡金属氧化物、过渡金属氟化物、聚阴离子、氟化聚阴离子、过渡金属硫化物等。其中,从制造成本低、平均放电电压高的方面考虑,优选为含锂过渡金属氧化物。
作为含锂过渡金属氧化物所包含的过渡金属元素,可列举出Sc、Ti、V、Cr、Mn、Fe、Co、Ni、Cu、Y、Zr、W等。含锂过渡金属氧化物既可以包含1种过渡金属元素,也可以包含2种以上。过渡金属元素也可以为Co、Ni和/或Mn。含锂过渡金属氧化物能够根据需要包含1种以上的典型元素。作为典型元素,可列举出Mg、Al、Ca、Zn、Ga、Ge、Sn、Sb、Pb、Bi等。典型元素也可以是Al等。
导电材料例如是碳材料。作为碳材料,可列举出炭黑、乙炔黑、科琴黑、碳纳米管以及石墨等。
作为粘结材料,例如可列举出氟树脂、聚丙烯腈、聚酰亚胺树脂、丙烯酸树脂、聚烯烃树脂、橡胶状聚合物等。作为氟树脂,可列举出聚四氟乙烯、聚偏二氟乙烯等。
正极集电体使用箔、薄膜等。在正极集电体的表面也可以涂布碳材料。作为正极集电体的材质,例如可列举出包含Al、Ti、Fe等的金属材料。金属材料也可以是Al、Al合金、Ti、Ti合金、Fe合金等。Fe合金也可以是不锈钢(SUS)。正极集电体的厚度没有特别限制,例如为5μm以上且30μm以下。
[分隔件]
通常,期望的是在正极与负极之间夹设分隔件。分隔件的离子透过度高,具备适度的机械强度和绝缘性。作为分隔件,能够使用微多孔薄膜、机织布、无纺布等。作为分隔件的材质,优选聚丙烯、聚乙烯等聚烯烃、聚甲基戊烯、聚对苯二甲酸乙二醇酯、聚对苯二甲酸丁二醇酯、芳纶、纤维素等。
分隔件既可以在正极与负极之间夹设1张,也可以夹设多张。在正极与负极之间夹设多张分隔件的情况下,既可以将微多孔薄膜、机织布、无纺布中的1种重叠多张来使用,也可以将微多孔薄膜、机织布、无纺布中的至少2种重叠多张来使用。夹设1张的情况下的分隔件的厚度没有特别限制,优选为5μm~80μm。夹设多张的情况下的分隔件的厚度也没有特别限制,优选为5μm~80μm。
[非水电解质]
具有锂离子传导性的非水电解质既可以是液态电解质(电解液),也可以是凝胶状电解质,还可以是固体电解质。液态电解质(电解液)例如包含非水溶剂和溶解于非水溶剂的锂盐。液态电解质通过使锂盐溶解于非水溶剂来制备。通过锂盐溶解于非水溶剂中,生成锂离子和阴离子。
凝胶状电解质包含锂盐和基质聚合物,或者包含锂盐、非水溶剂以及基质聚合物。作为基质聚合物,例如使用吸收非水溶剂而凝胶化的聚合物材料。作为聚合物材料,可列举出氟树脂、丙烯酸树脂、聚醚树脂等。
固体电解质也可以是无机固体电解质。作为无机固体电解质,例如使用全固体锂离子二次电池等中公知的材料(例如氧化物系固体电解质、硫化物系固体电解质、卤化物系固体电解质等)。
作为锂盐的阴离子,能够使用锂二次电池的非水电解质中利用的公知的阴离子。具体而言,可列举出BF4 -、ClO4 -、PF6 -、CF3SO3 -、CF3CO2 -、酰亚胺类的阴离子、草酸盐络合物的阴离子等。作为酰亚胺类的阴离子,可列举出N(SO2F)2 -、N(SO2CF3)2 -等。草酸盐络合物的阴离子也可以含有硼和/或磷。作为草酸盐络合物的阴离子,可列举出双草酸硼酸根阴离子、BF2(C2O4)-、PF4(C2O4)-、PF2(C2O4)2 -等。非水电解质既可以单独包含1种锂盐,也可以包含2种以上的锂盐。
从抑制锂金属以枝晶状析出的观点出发,非水电解质优选至少包含草酸盐络合物的阴离子。通过草酸盐络合物的阴离子与锂的相互作用,锂金属容易以细小的颗粒状均匀地析出。因此,容易抑制锂金属的局部析出。非水电解质也可以包含草酸盐络合物的阴离子和其他阴离子。其他阴离子也可以为PF6 -和/或酰亚胺类的阴离子。
作为非水溶剂,可列举出酯化合物、醚化合物、腈化合物、酰胺化合物等。这些化合物包含卤素取代物等。作为卤素取代物,可列举出氟化物等。非水电解质既可以单独包含这些非水溶剂,也可以包含2种以上。
非水溶剂也可以包含醚化合物作为主成分。需要说明的是,主成分是指,非水溶剂中的醚化合物的含量为50质量%以上,也可以为80质量%以上。另外,非水溶剂中的醚化合物的含量既可以为95质量%以下,也可以为100质量%以下。关于非水溶剂中的醚化合物的含量范围,也可以为将上述的上限和下限任意组合的范围。
认为醚化合物的稳定性(特别是耐还原性)优异,负极表面的分解物的生成受到抑制,因此负极的膨胀受到抑制。
作为醚化合物,可列举出环状醚、链状醚等。作为环状醚,可列举出1,3-二氧戊环、4-甲基-1,3-二氧戊环、四氢呋喃、2-甲基四氢呋喃等。作为链状醚,可列举出1,2-二甲氧基乙烷、二乙醚、乙基乙烯基醚、甲基苯醚、苄基乙醚、二苯醚、二苄醚、1,2-二乙氧基乙烷、二乙二醇二甲醚、1,1,2,2-四氟乙基-2,2,2-三氟乙醚、1,1,2,2-四氟乙基-2,2,3,3-四氟丙醚等。其中,优选1,2-二甲氧基乙烷、1,1,2,2-四氟乙基-2,2,2-三氟乙醚等。它们既可以单独使用,也可以组合使用2种以上。
作为酯化合物,例如可列举出碳酸酯、羧酸酯等。作为环状碳酸酯,可列举出碳酸亚乙酯、碳酸亚丙酯等。作为链状碳酸酯,可列举出碳酸二甲酯(DMC)、碳酸甲乙酯(EMC)、碳酸二乙酯等。作为环状羧酸酯,可列举出γ-丁内酯、γ-戊内酯等。作为链状羧酸酯,可列举出乙酸乙酯、丙酸甲酯、氟丙酸甲酯等。它们既可以单独使用,也可以组合使用2种以上。
非水电解质(例如电解液)中的锂盐的浓度例如为0.5mol/L以上且3.5mol/L以下。也可以将非水电解质中的阴离子的浓度设为0.5mol/L以上且3.5mol/L以下。另外,也可以将非水电解质中的草酸盐络合物的阴离子的浓度设为0.05mol/L以上且1mol/L以下。
非水电解质也可以包含添加剂。添加剂也可以在负极上形成覆膜。通过在负极上形成源自添加剂的覆膜,容易进一步抑制枝晶的生成。作为添加剂,例如可列举出碳酸亚乙烯酯、氟代碳酸亚乙酯(FEC)、碳酸乙烯基乙酯(VEC)等。
[锂二次电池]
以下,以具备卷绕型的电极组的圆筒形电池为例,参照附图对本公开的锂二次电池的结构进行说明。但是,本公开并不限定于以下的结构。
图1是示意性地表示本公开的实施方式的锂二次电池的一例的纵剖视图。图2是将由图1的区域II包围的部分(包含正极的一部分)放大的图。图3是将由图1的区域III包围的部分(包含负极的一部分)放大的图。需要说明的是,各图是示意性地表示的图,各构成构件的尺寸(例如,厚度)的比率等与实际不同。
锂二次电池10具备圆筒形的电池外壳、收纳于电池外壳内的卷绕型的电极组14以及未图示的非水电解质。电极组14通过将带状的正极11和带状的负极12以分隔件13介于正极11与负极12之间的方式卷绕而构成。
负极12由树脂薄膜和锂金属层构成。负极12经由负极引线20与兼作负极端子的外壳主体15电连接。负极引线20的一端部例如与负极12的长度方向的端部连接,另一端部焊接于外壳主体15的内底面。
正极11具备正极集电体30和正极合剂层31,经由正极引线19与兼作正极端子的盖子26电连接。正极引线19的一端部例如与正极11的长度方向的中央附近连接。从正极11延伸出的正极引线19通过形成于绝缘板17的未图示的贯通孔而延伸至过滤器22。正极引线19的另一端部焊接于过滤器22的电极组14侧的面。
电池外壳由作为有底圆筒形的金属制容器的外壳主体15和将外壳主体15的开口部封口的封口体16构成。在外壳主体15与封口体16之间配置有垫片27,由此确保电池外壳的密闭性。在外壳主体15内,在电极组14的卷绕轴方向的两端部分别配置有绝缘板17、18。
外壳主体15例如具有将外壳主体15的侧壁局部地从外侧冲压而形成的台阶部21。台阶部21也可以在外壳主体15的侧壁沿着外壳主体15的周向形成为环状。在该情况下,封口体16被台阶部21的开口部侧的面支承。
封口体16具备过滤器22、下阀芯23、绝缘构件24、上阀芯25以及盖子26。在封口体16中,这些构件以该顺序层叠。封口体16以盖子26位于外壳主体15的外侧、过滤器22位于外壳主体15的内侧的方式安装于外壳主体15的开口部。构成封口体16的上述各构件例如是圆板形状或环形状。下阀芯23和上阀芯25在各自的中央部相互连接,并且在各自的周缘部之间夹设有绝缘构件24。过滤器22和下阀芯23在各自的周缘部相互连接。上阀芯25和盖子26在各自的周缘部相互连接。即,除了绝缘构件24之外的各构件相互电连接。
在下阀芯23形成有未图示的通气孔。因此,当电池外壳的内压由于异常发热等而上升时,上阀芯25向盖子26侧膨胀,从下阀芯23离开。由此,下阀芯23与上阀芯25的电连接被切断。当内压进一步上升时,上阀芯25断裂,气体从形成于盖子26的未图示的开口部排出。
在图示例中,对圆筒形的锂二次电池进行了说明,但不限于该情况,能够应用本实施方式。锂二次电池的形状根据其用途等,除了圆筒形以外,还能够从硬币型、方型、片型、扁平型等各种形状中适当选择。另外,在图示例中示出卷绕型的电极组,但电极组的形态也没有特别限定,也可以是通过将正极和负极隔着分隔件层叠而构成的层叠型的电极组。另外,关于锂二次电池的电极组和非水电解质以外的结构,能够没有特别限制地利用公知的结构。
<实施例>
以下,基于实施例和比较例对本公开的锂二次电池进行具体说明。本公开并不限定于以下的实施例。
《实施例1~21》
(1)正极的制作
将含有Li、Ni、Co以及Al的含锂过渡金属氧化物(NCA;正极活性物质)、乙炔黑(AB;导电材料)以及聚偏二氟乙烯(PVdF;粘结材料)以NCA:AB:PVdF=95:2.5:2.5的质量比混合,进而适量添加N-甲基-2-吡咯烷酮(NMP)并搅拌,制备正极合剂浆料。接下来,将得到的正极合剂浆料涂布于作为正极集电体发挥功能的Al箔(厚度15μm)的两面后,进行干燥,使用辊对正极合剂的涂膜进行压延。最后,将得到的正极集电体与正极合剂层的层叠体切断成预定的电极尺寸,制作在正极集电体的两面具备正极合剂层(厚度65μm)的正极。
(2)负极的制作
准备具有表1、表2所示的厚度、拉伸强度、断裂伸长率以及材质的树脂薄膜。在非活性气体气氛中,在树脂薄膜的两面压接锂箔(厚度5μm或30μm),制作具备层叠于树脂薄膜的两面的锂金属层(锂合金箔)的负极。
仅E6使用除了锂以外还包含5质量%的镁的锂合金箔(厚度30μm)。
表1中的缩写如以下所示。
PET:聚对苯二甲酸乙二醇酯
PBT:聚对苯二甲酸丁二醇酯
PE:聚乙烯
PP:聚丙烯
PI:聚酰亚胺
PA:聚酰胺
在E13、E14中,对树脂薄膜的表面实施电晕处理。电晕放电密度为10W/cm2。
在E1~E11中,使用混炼有二氧化硅填料的树脂薄膜。将树脂薄膜中的二氧化硅填料的含有率示于表1。
在E5~E21中,通过真空蒸镀的方法在树脂薄膜的两面形成铜、铬、银或镍的基底金属层(厚度为0.2μm或1μm)。
(3)非水电解质的制备
分别在非水溶剂中以成为1摩尔/L的浓度溶解LiPF6,并且以成为0.1摩尔/L的浓度溶解LiBF2(C2O4),制备液体的非水电解质。非水溶剂使用1,2-二甲氧基乙烷与1,2,2,2-四氟乙基-2,2,2-三氟乙醚的混合溶剂。
(4)电池的制作
在上述得到的正极上安装Al制的极耳。在上述得到的负极的锂金属层上安装Ni制的极耳。在非活性气体气氛中,使分隔件介于正极与负极之间,将正极和负极卷绕成螺旋状,制作卷绕型的电极组。分隔件使用2种聚乙烯制的微多孔薄膜(厚度15μm的分隔件A或厚度30μm的分隔件B)。在将2张重叠使用的情况下(E4~E21、R1),使分隔件B与正极的两面相邻地配置。将得到的电极组收纳于由具备Al层的层压片形成的袋状的外壳体,向收纳有电极组的外壳体注入上述非水电解质后,将外壳体密封,制作锂二次电池。在表1、表2中,E1~E21是实施例1~21的电池。
[评价]
对于得到的各电池,在25℃的环境下进行充放电循环试验。充放电在以下的条件下进行。在充电与放电之间进行20分钟的休止。
(充电)
以10mA进行恒流充电直至电压成为4.1V,之后,以4.1V进行恒压充电直至电流成为1mA。
(放电)
以10mA进行恒流放电直至电压成为3V。
反复进行充放电直至100次循环,测定100次循环时的放电容量。将评价结果示于表1、表2。需要说明的是,在表1、表2中,各电池的100次循环时的放电容量表示为将电池E1的100次循环时的放电容量设为100时的相对值。
[表1]
[表2]
《比较例1》
作为负极,使用电解铜箔(厚度12μm)代替树脂薄膜与锂金属层的层叠体,除此以外,与实施例4同样地制作锂二次电池,进行评价。将结果以上述相对值示于表2。
电池E1~E21与电池R1相比,100次循环时的放电容量高,循环特性提高。将100次循环后的各电池分解,对负极进行SEM观察,结果确认了在R1中发生了铜箔的断裂。另一方面,在E1~E21中未确认到负极的断裂、压曲。
产业上的可利用性
本公开的锂二次电池能够用于移动电话、智能手机、平板终端那样的电子设备、包括混合动力设备、插电式混合动力设备的电动汽车、与太阳能电池组合的家庭用蓄电池等。
关于目前的优选实施方式对本发明进行了说明,但不应限定性地解释这样的公开。通过阅读上述公开,各种变形和改变对于属于本发明的技术领域的本领域技术人员来说是显而易见的。因而,所附的权利要求书应解释为,在不脱离本发明的真正的精神和范围的情况下包括所有的变形和改变。
附图标记说明
10、锂二次电池;11、正极;12、负极;13、分隔件;14、电极组;15、外壳主体;16、封口体;17、18、绝缘板;19、正极引线;20、负极引线;21、台阶部;22、过滤器;23、下阀芯;24、绝缘构件;25、上阀芯;26、盖子;27、垫片;30、正极集电体;31、正极合剂层;40、树脂薄膜;41、锂金属层。
Claims (12)
1.一种锂二次电池,其具备:
正极;
负极;
分隔件,其配置在所述正极与所述负极之间;以及
非水电解质,其具有锂离子传导性,
在所述负极中,在充电时锂金属析出,在放电时所述锂金属溶解,
所述负极具有树脂薄膜和与所述树脂薄膜层叠的锂金属层。
2.根据权利要求1所述的锂二次电池,其中,所述负极在所述树脂薄膜的至少一个主面具有所述锂金属层,
所述锂金属层与所述树脂薄膜的所述主面接触。
3.根据权利要求2所述的锂二次电池,其中,所述负极在所述树脂薄膜的两个所述主面分别具有所述锂金属层,
所述正极和所述负极隔着所述分隔件卷绕。
4.根据权利要求1所述的锂二次电池,其中,所述负极在所述树脂薄膜的至少一个主面具有基底金属层,
所述基底金属层与所述树脂薄膜的所述主面接触,
所述锂金属层与所述基底金属层的主面和所述树脂薄膜的所述主面中的至少一者接触。
5.根据权利要求4所述的锂二次电池,其中,所述负极在所述树脂薄膜的两个所述主面分别具有所述基底金属层和所述锂金属层,所述正极和所述负极隔着所述分隔件卷绕。
6.根据权利要求4或5所述的锂二次电池,其中,所述基底金属层的厚度为2μm以下。
7.根据权利要求1~6中任一项所述的锂二次电池,其中,所述树脂薄膜的拉伸强度为100MPa以上。
8.根据权利要求1~7中任一项所述的锂二次电池,其中,所述树脂薄膜的断裂伸长率为50%以上。
9.根据权利要求1~8中任一项所述的锂二次电池,其中,在放电深度为90%以上的放电状态下,所述锂金属层的厚度为40μm以下。
10.根据权利要求1~9中任一项所述的锂二次电池,其中,所述树脂薄膜的厚度为5μm以上且80μm以下。
11.根据权利要求1~10中任一项所述的锂二次电池,其中,所述树脂薄膜所包含的树脂具有芳香环。
12.根据权利要求1~11中任一项所述的锂二次电池,其中,所述锂金属层包含镁。