CN117002127A - 一种基于荔枝浸渍速冻用包装材料及其制备方法 - Google Patents
一种基于荔枝浸渍速冻用包装材料及其制备方法 Download PDFInfo
- Publication number
- CN117002127A CN117002127A CN202311260220.3A CN202311260220A CN117002127A CN 117002127 A CN117002127 A CN 117002127A CN 202311260220 A CN202311260220 A CN 202311260220A CN 117002127 A CN117002127 A CN 117002127A
- Authority
- CN
- China
- Prior art keywords
- parts
- packaging material
- litchi
- auxiliary agent
- quick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种基于荔枝浸渍速冻用包装材料：包括内层和外层，由聚酯材料、聚丙烯、导热助剂、低温助剂、降解助剂、防霉剂、增塑剂组成。其制备过程为：（1）将内层原料或外层原料按照各自的配比分别加入二个独立的混合釜中，搅拌混合均匀；（2）将步骤（1）中混合后的内层物料或外层物料分别加入二个机筒中进行熔化密炼，温度控制在150℃～230℃之间，同时真空脱水；（3）将步骤（2）中熔化密炼后物料分别通过二台挤出机挤出，通过两层共挤模头流延成膜、冷却铸片、拉伸、热定型、收卷、分切，得到本发明的双层包装材料。本发明制备的包装材料导热性能好，耐低温，同时降解性能好，应用广泛，适用于荔枝浸渍速冻用包装材料。
Description
技术领域
本发明涉及包装材料领域，特别涉及一种基于荔枝浸渍速冻用包装材料及其制备方法。
背景技术
荔枝属亚热带常绿无患子科植物，是我国岭南佳果，色、香、味皆美，有“果王”之美称。然而，由于荔枝果实的结构特殊、代谢旺盛，采摘季节极短暂且集中在炎热的夏天，水分蒸发干耗率高，故变质极快。
目前在荔枝保鲜上主要采用低温冷藏结合药物处理、硫处理结合浸酸护色等技术，此外还有热处理、速冻、同位素辐照等方法，都可在一定程度上延长荔枝果实的货架期，但效果都不理想。低温保鲜的保鲜期较短；化学保鲜和辐照保鲜存在残留污染，有安全、卫生方面的问题；速冻保鲜解冻后果皮更易褐变，失去天然色泽，裂果率高；热处理单独使用的效果有限等；浸渍速冻保鲜荔枝的方法为一种较好的选择，通过分选、浸渍、预冷、包装、速冻、冻藏实现对荔枝的保鲜。
在荔枝浸渍速冻保鲜过程中，需要用到包装材料对荔枝进行包装，然后再进行速冻，速冻过程中因为温度极低，所以对包装材料的要求很高，既要有好的传热洗漱，又需要耐低温，现有的材料大都性能不太适合。
发明内容
本发明的目的提供一种基于荔枝浸渍速冻用包装材料及其制备方法，制造方法简单，工艺过程容易控制，制备的包装材料导热性能好，耐低温，同时降解性能好，应用广泛，适用于荔枝浸渍速冻用包装材料。
为实现上述目的，第一方面，本发明提供一种基于荔枝浸渍速冻用包装材料，包括内层、和外层
所述内层由以下质量份数的物质组成：
聚酯材料50~100份
聚丙烯15~30份
导热助剂1~3份
低温助剂8~15份
降解助剂4~15份
防霉剂1~2份
增塑剂1~3份
所述外层由以下质量份数的物质组成：
聚酯材料50~100份
聚丙烯31~50份
导热助剂1~3份
低温助剂8~15份
降解助剂2~5份
防霉剂1~2份
增塑剂4~6份
外层材料和内层材料相比，在外层材料中，增加了聚丙烯和增塑剂的用量，同时降低了降解助剂的用量，使得外层材料的韧性更高，强度更高，整体包装材料更耐用。
优选地，所述导热助剂为导热硅脂、石墨烯、纳米碳纤维中的一种。采用导热助剂制备的包装材料，导热性能更佳，使得荔枝内部的热量可以更快的传递到冷媒中，加速荔枝降温，提高保鲜效果。
优选地，所述低温助剂为己二酸二辛酯、丁二酸二辛酯，月桂二酸二丁酯中的一种。采用低温助剂制备的包装材料，耐低温性能更佳，在-30℃以下使用依然保持很好的性能，不会变脆，老化。
优选地，所述降解助剂为碳酸钙粉、氧化铝粉、壳聚糖中的一种。采用降解助剂制备的包装材料，使用完成后，在大自然中可以降解，降低对环境的污染。
优选地，所述防霉剂为柠檬酸、漂白粉、孟宗竹提取物中的一种。采用防霉剂制备的包装材料，可以使得荔枝在储存过程中保存时间更长。
优选地，所述增塑剂为邻苯二甲酸酯、磷酸三辛酯，2-（4-乙基苯甲酰）苯甲酸乙酯中的一种。采用2-（4-乙基苯甲酰）苯甲酸乙酯时，效果更好。
优选地，所述降解助剂粒径在1~15微米之间。降解助剂粒径在1~15微米之间有助于本发明包装材料使用后的降解。
第二方面，本发明提出了一种上述包装材料的制备方法，包括以下步骤：
（1）将内层原料或外层原料按照各自的配比分别加入二个独立的混合釜中，搅拌混合均匀；
（2）将步骤（1）中混合后的内层物料或外层物料分别加入二个机筒中进行熔化密炼，温度控制在150℃～230℃之间，同时真空脱水；
（3）将步骤（2）中熔化密炼后物料分别通过二台挤出机挤出，通过两层共挤模头流延成膜、冷却铸片、拉伸、热定型、收卷、分切，得到本发明的双层包装材料。
优选地，步骤（3）中拉伸比为1.3~1.5，拉伸温度73~78℃，热定型温度180~220℃。通过拉伸，控制恰当的拉伸比，进一步调整了材料的性能，其导热性和可降解性进一步提升，且强度在可接受范围内。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整的描述，显然，所描述的实施例仅仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例1
一种基于荔枝浸渍速冻用包装材料，包括内层、和外层，
所述内层由以下质量份数的物质组成：
聚酯材料50份
聚丙烯15份
石墨烯1份
己二酸二辛酯8份
氧化铝粉4份，粒径在1~15微米之间
柠檬酸1份
邻苯二甲酸酯1份
所述外层由以下质量份数的物质组成：
聚酯材料50份
聚丙烯32份
石墨烯1份
己二酸二辛酯8份
氧化铝粉2份，粒径在1~15微米之间
柠檬酸1份
邻苯二甲酸酯4份
上述的包装材料的制备方法，包括以下步骤：
（1）将内层原料或外层原料按照各自的配比分别加入二个独立的混合釜中，搅拌混合均匀；
（2）将步骤（1）中混合后的内层物料或外层物料分别加入二个机筒中进行熔化密炼，温度控制在150℃～200℃之间，同时真空脱水；
（3）将步骤（2）中熔化密炼后物料分别通过二台挤出机挤出，通过两层共挤模头流延成膜、冷却铸片、拉伸、热定型、收卷、分切，得到本发明的双层包装材料，其中拉伸比为1.3~1.5，拉伸温度73~78℃，热定型温度180~220℃。
实施例2
一种基于荔枝浸渍速冻用包装材料，包括内层、和外层，
所述内层由以下质量份数的物质组成：
聚酯材料80份
聚丙烯20份
导热硅脂2份
月桂二酸二丁酯10份
碳酸钙粉8份，粒径在1~15微米之间
孟宗竹提取物2份
2-（4-乙基苯甲酰）苯甲酸乙酯3份
所述外层由以下质量份数的物质组成：
聚酯材料80份
聚丙烯40份
导热硅脂2份
月桂二酸二丁酯10份
碳酸钙粉4份，粒径在1~15微米之间
孟宗竹提取物2份
2-（4-乙基苯甲酰）苯甲酸乙酯6份
上述的包装材料的制备方法，包括以下步骤：
（1）将内层原料或外层原料按照各自的配比分别加入二个独立的混合釜中，搅拌混合均匀；
（2）将步骤（1）中混合后的内层物料或外层物料分别加入二个机筒中进行熔化密炼，温度控制在180℃～220℃之间，同时真空脱水；
（3）将步骤（2）中熔化密炼后物料分别通过二台挤出机挤出，通过两层共挤模头流延成膜、冷却铸片、拉伸、热定型、收卷、分切，得到本发明的双层包装材料，其中拉伸比为1.3~1.5，拉伸温度73~78℃，热定型温度180~220℃。
实施例3
一种基于荔枝浸渍速冻用包装材料，包括内层、和外层，
所述内层由以下质量份数的物质组成：
聚酯材料100份
聚丙烯30份
纳米碳纤维3份
丁二酸二辛酯15份
壳聚糖15份，粒径在1~15微米之间
漂白粉2份
磷酸三辛酯3份
所述外层由以下质量份数的物质组成：
聚酯材料100份
聚丙烯50份
纳米碳纤维3份
丁二酸二辛酯15份
壳聚糖4份，粒径在1~15微米之间
漂白粉2份
磷酸三辛酯6份
上述的包装材料的制备方法，包括以下步骤：
（1）将内层原料或外层原料按照各自的配比分别加入二个独立的混合釜中，搅拌混合均匀；
（2）将步骤（1）中混合后的内层物料或外层物料分别加入二个机筒中进行熔化密炼，温度控制在180℃～220℃之间，同时真空脱水；
（3）将步骤（2）中熔化密炼后物料分别通过二台挤出机挤出，通过两层共挤模头流延成膜、冷却铸片、拉伸、热定型、收卷、分切，得到本发明的双层包装材料，其中拉伸比为1.3~1.5，拉伸温度73~78℃，热定型温度180~220℃。
对比例1
去掉实施例3中的导热助剂纳米碳纤维，其他同实施例3，不再赘述。
对比例2
去掉实施例2中的低温助剂月桂二酸二丁酯，其他同实施例2，不再赘述。
对比例3
去掉实施例2中降解助剂碳酸钙粉，其他同实施例2，不再赘述。
对比例4
去掉实施例2中防霉剂孟宗竹提取物，其他同实施例2，不再赘述，使用结果表明，采用防霉剂的包装袋，包装荔枝的保存时间更久。
对以上实施例和对比例制得的包装材料进行性能测试，测试结果见表1。
表1性能测试结果
由上表数据可以看出，对比例1中去掉导热助剂纳米碳纤维，导热系数明显降低；对比例2中去掉低温助剂月桂二酸二丁酯，断裂伸长率降低，特别是低温下降低更明显；对比例3中去掉降解助剂碳酸钙粉，分解率明显降低。
Claims (9)
1.一种基于荔枝浸渍速冻用包装材料，其特征在于，包括内层、和外层，
所述内层由以下质量份数的物质组成：
聚酯材料50~100份
聚丙烯15~30份
导热助剂1~3份
低温助剂8~15份
降解助剂4~15份
防霉剂1~2份
增塑剂1~3份
所述外层由以下质量份数的物质组成：
聚酯材料50~100份
聚丙烯31~50份
导热助剂1~3份
低温助剂8~15份
降解助剂2~5份
防霉剂1~2份
增塑剂4~6份。
2.根据权利要求1所述的基于荔枝浸渍速冻用包装材料，其特征在于，所述导热助剂为导热硅脂、石墨烯、纳米碳纤维中的一种。
3.根据权利要求1所述的基于荔枝浸渍速冻用包装材料，其特征在于，所述低温助剂为己二酸二辛酯、丁二酸二辛酯，月桂二酸二丁酯中的一种。
4.根据权利要求1所述的基于荔枝浸渍速冻用包装材料，其特征在于，所述降解助剂为碳酸钙粉、氧化铝粉、壳聚糖中的一种。
5.根据权利要求1所述的基于荔枝浸渍速冻用包装材料，其特征在于，所述防霉剂为柠檬酸、漂白粉、孟宗竹提取物中的一种。
6.根据权利要求1所述的基于荔枝浸渍速冻用包装材料，其特征在于，所述增塑剂为邻苯二甲酸酯、磷酸三辛酯，2-（4-乙基苯甲酰）苯甲酸乙酯中的一种。
7.根据权利要求4所述的基于荔枝浸渍速冻用包装材料，其特征在于，所述降解助剂粒径在1~15微米之间。
8.一种权利要求1~7中任一项权利要求所述的包装材料的制备方法，包括以下步骤：
（1）将内层原料或外层原料按照各自的配比分别加入二个独立的混合釜中，搅拌混合均匀；
（2）将步骤（1）中混合后的内层物料或外层物料分别加入二个机筒中进行熔化密炼，温度控制在150℃～230℃之间，同时真空脱水；
（3）将步骤（2）中熔化密炼后物料分别通过二台挤出机挤出，通过两层共挤模头流延成膜、冷却铸片、拉伸、热定型、收卷、分切，得到本发明的双层包装材料。
9.根据权利要求8所述的制备方法，其特征在于，步骤（3）中拉伸比为1.3~1.5，拉伸温度73~78℃，热定型温度180~220℃。