CN116752287A - 一种改良型熔喷布的制备方法 - Google Patents
一种改良型熔喷布的制备方法 Download PDFInfo
- Publication number
- CN116752287A CN116752287A CN202310457144.9A CN202310457144A CN116752287A CN 116752287 A CN116752287 A CN 116752287A CN 202310457144 A CN202310457144 A CN 202310457144A CN 116752287 A CN116752287 A CN 116752287A
- Authority
- CN
- China
- Prior art keywords
- melt
- mixture
- blowing
- blown
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及熔喷布技术领域，本发明公开了一种改良型熔喷布的制备方法，包括如下步骤：1、将PP聚合物、电气石母粒、丁香油和檀香油依次添加到搅拌桶中，进行搅拌混合，得到混合料；2、将混合料放入加温筒内进行高温熔化；3、将高温熔化后的混合料加到螺杆挤出机中，进行挤出；4、将高温熔化后的混合料经过熔体过滤器过滤后，进行熔喷纺丝，得到熔喷布。本发明制作而成的口罩，不仅可物理阻挡和静电吸附作用而过滤颗粒物与微生物之外，一定程度上还能起到缓解身体疲劳感、减轻焦虑和镇静安神等功效，解决了现有的口罩功能单一等问题，具有良好的市场前景。
Description
技术领域
本发明涉及熔喷布技术领域，具体为一种改良型熔喷布的制备方法。
背景技术
熔喷布是口罩最核心的材料，熔喷布主要以聚丙烯(PP)为主要原料，纤维直径可以达到1～5微米，空隙多、结构蓬松、抗褶皱能力好，具有独特的毛细结构的超细纤维增加单位面积纤维的数量和表面积，从而使熔喷布具有很好的过滤性、屏蔽性、绝热性和吸油性。
在春季流感多发季外出时均需要佩戴口罩以防病毒感染，目前市场上用于口罩的熔喷法非织造布的作用比较单一，即通过物理阻挡和静电吸附作用而过滤颗粒物与微生物，进而对人体达到保护作用，这两种作用均为物理作用，而没有生理作用，例如，孕妇等特殊人群外出到医院、公园、超市、人员密集场所、大雾天气、雾霾天气等场所时由于长时间的口罩的佩戴，可能会出现身体缺氧而引发一些不良症状，孕妇可能出现心情烦躁而导致的孕期焦虑，产生紧张的情绪。因此，本发明设计一种改良型熔喷布的制备方法以解决现有技术中存在的问题。
发明内容
本发明的目的在于提供一种改良型熔喷布的制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种改良型熔喷布的制备方法，包括如下步骤：S1：将PP聚合物、电气石母粒、丁香油和檀香油依次添加到搅拌桶中，进行搅拌混合，得到混合料；
S2：将混合料放入加温筒内进行高温熔化；
S3：将高温熔化后的混合料加到螺杆挤出机中，进行挤出；
S4：将高温熔化后的混合料经过熔体过滤器过滤后，进行熔喷纺丝，得到熔喷布。
优选的，所述的步骤S1中：搅拌混合时间为60分钟，所述的搅拌桶内PP聚合物、电气石母粒、丁香油和檀香油的含量分别为：PP聚合物：200kg，电气石母粒：8kg，丁香油：100g～150g，檀香油：100g～150g。
优选的，所述的步骤S2中，加热温度为200℃～300℃。
优选的，所述的步骤S4中，熔喷纺丝前经过熔喷泵对过滤后的混合料进行计量，熔喷纺丝工艺为：通过熔喷模头将高温熔化后的混合料均匀的吹散到成型网上，最后收卷切割成型；
所述的熔喷泵温度为：300℃；
所述的熔喷泵转速为50r/min；
所述的熔喷模头温度为260℃。
优选的，所述的熔喷布收卷切割成型前，通过直流驻极器给熔喷布添加静电。
优选的，所述的步骤S4中，所述的熔喷布添加静电后，通过喷雾机对熔喷布进行喷雾，然后再收卷切割成型。
优选的，所述的步骤S4中，所述的喷雾机内添加喷雾剂，所述的喷雾剂包括10wt％～15wt％的植物香油、75wt％的双脱醛乙醇和10wt％～15wt％的水。
与现有技术相比，本发明的有益效果如下：
1.本发明通过在制备熔喷布的时候添加丁香油和檀香油，在吸入微量的气味后一定程度上可以缓解肺热症状，具有较强杀菌能力，同时在一定程度上还可以预防传染病发生，并且可以改善失眠症状而檀香的味道能够缓解身体的疲劳感，减轻焦虑、紧张的情绪，镇静安神；
2.本发明通过在制备熔喷布的时候添加兰花香油，在吸入微量的气味后可以起到改善神经衰弱症状，促进睡眠的一定作用；当添加满天星香油，在吸入微量的气味后由于满天星香油的味道比较宜人，能够很好地释放自身的精神压力；当添加茉莉花香油，在吸入微量的气味后具有提神醒脑、改善心情的作用，可以帮助提高睡眠质量以及缓解孕期焦虑；
3.本发明制作而成的口罩，不仅可物理阻挡和静电吸附作用而过滤颗粒物与微生物之外，一定程度上还能起到缓解身体疲劳感、减轻焦虑和镇静安神等功效，解决了现有的口罩功能单一等问题，具有良好的市场前景。
附图说明
图1为本发明的工作流程示意图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供的三种实施例：
实施例1：
本发明包括如下步骤：
S1：将PP聚合物、电气石母粒、丁香油和檀香油依次添加到搅拌桶中，进行搅拌混合，得到混合料；
S2：将混合料放入加温筒内进行高温熔化；
S3：将高温熔化后的混合料加到螺杆挤出机中，进行挤出；
S4：将高温熔化后的混合料经过熔体过滤器过滤后，进行熔喷纺丝，得到熔喷布。
在本实施的步骤S1中：搅拌混合时间为60分钟，搅拌桶内PP聚合物、电气石母粒、丁香油和檀香油的含量分别为：PP聚合物：200kg，电气石母粒：8kg，丁香油：120g，檀香油：120g。其中丁香油可以缓解肺热症状，具有较强杀菌能力，在一定程度上还可以预防传染病发生，并且可以改善失眠症状；而檀香油，檀香的味道能够缓解身体的疲劳感，减轻焦虑、紧张的情绪，镇静安神。
在本实施的步骤S2中，加热温度为260℃。
在本实施的步骤S4中，熔喷纺丝前经过熔喷泵对过滤后的混合料进行计量，熔喷纺丝工艺为：通过熔喷模头将高温熔化后的混合料均匀的吹散到成型网上，最后收卷切割成型；
在本实施中：熔喷泵温度为：300℃；
在本实施中：熔喷泵转速为50r/min；且熔喷泵的型号为：RT-500；
在本实施中：熔喷模头温度为260℃。
在本实施中：熔喷布收卷切割成型前，通过直流驻极器给熔喷布添加静电，且直流驻极器的型号为：TRC2025E。
在本实施中：熔喷布添加静电后，通过喷雾机对熔喷布进行喷雾，然后再收卷切割成型。
在本实施中：喷雾机内添加喷雾剂，喷雾剂包括10wt％的兰花香油、75wt％的双脱醛乙醇和15wt％的水。兰花香油可以起到改善神经衰弱症状，促进睡眠的一定作用。
实施例2：
本发明包括如下步骤：
S1：将PP聚合物、电气石母粒、丁香油和檀香油依次添加到搅拌桶中，进行搅拌混合，得到混合料；
S2：将混合料放入加温筒内进行高温熔化；
S3：将高温熔化后的混合料加到螺杆挤出机中，进行挤出；
S4：将高温熔化后的混合料经过熔体过滤器过滤后，进行熔喷纺丝，得到熔喷布。
在本实施的步骤S1中：搅拌混合时间为60分钟，搅拌桶内PP聚合物、电气石母粒、丁香油和檀香油的含量分别为：PP聚合物：200kg，电气石母粒：8kg，丁香油：150g，檀香油：150g。其中丁香油可以缓解肺热症状，具有较强杀菌能力，在一定程度上还可以预防传染病发生，并且可以改善失眠症状；而檀香油，檀香的味道能够缓解身体的疲劳感，减轻焦虑、紧张的情绪，镇静安神。
在本实施的步骤S2中，加热温度为220℃。
在本实施的步骤S4中，熔喷纺丝前经过熔喷泵对过滤后的混合料进行计量，熔喷纺丝工艺为：通过熔喷模头将高温熔化后的混合料均匀的吹散到成型网上，最后收卷切割成型；
在本实施中：熔喷泵温度为：300℃；
在本实施中：熔喷泵转速为50r/min；且熔喷泵的型号为：RT-500；
在本实施中：熔喷模头温度为260℃。
在本实施中：熔喷布收卷切割成型前，通过直流驻极器给熔喷布添加静电，且直流驻极器的型号为：TRC2025E。
在本实施中：熔喷布添加静电后，通过喷雾机对熔喷布进行喷雾，然后再收卷切割成型。
在本实施中：喷雾机内添加喷雾剂，喷雾剂包括15wt％的满天星香油、75wt％的双脱醛乙醇和10wt％的水。满天星香油的味道比较宜人，能够很好地释放自身的精神压力。
实施例3：
本发明包括如下步骤：
S1：将PP聚合物、电气石母粒、丁香油和檀香油依次添加到搅拌桶中，进行搅拌混合，得到混合料；
S2：将混合料放入加温筒内进行高温熔化；
S3：将高温熔化后的混合料加到螺杆挤出机中，进行挤出；
S4：将高温熔化后的混合料经过熔体过滤器过滤后，进行熔喷纺丝，得到熔喷布。
在本实施的步骤S1中：搅拌混合时间为60分钟，搅拌桶内PP聚合物、电气石母粒、丁香油和檀香油的含量分别为：PP聚合物：200kg，电气石母粒：8kg，丁香油：140g，檀香油：140g。
在本实施的步骤S2中，加热温度为245℃。
在本实施的步骤S4中，熔喷纺丝前经过熔喷泵对过滤后的混合料进行计量，熔喷纺丝工艺为：通过熔喷模头将高温熔化后的混合料均匀的吹散到成型网上，最后收卷切割成型；
在本实施中：熔喷泵温度为：300℃；
在本实施中：熔喷泵转速为50r/min；且熔喷泵的型号为：RT-500；
在本实施中：熔喷模头温度为260℃。
在本实施中：熔喷布收卷切割成型前，通过直流驻极器给熔喷布添加静电，且直流驻极器的型号为：TRC2025E。
在本实施中：熔喷布添加静电后，通过喷雾机对熔喷布进行喷雾，然后再收卷切割成型。
在本实施中：喷雾机内添加喷雾剂，喷雾剂包括12wt％的茉莉花香油、75wt％的双脱醛乙醇和13wt％的水。茉莉花香油具有提神醒脑、改善心情的作用，可以帮助提高睡眠质量以及缓解孕期焦虑。
尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (7)
1.一种改良型熔喷布的制备方法，其特征在于：包括如下步骤：S1：将PP聚合物、电气石母粒、丁香油和檀香油依次添加到搅拌桶中，进行搅拌混合，得到混合料；
S2：将混合料放入加温筒内进行高温熔化；
S3：将高温熔化后的混合料加到螺杆挤出机中，进行挤出；
S4：将高温熔化后的混合料经过熔体过滤器过滤后，进行熔喷纺丝，得到熔喷布。
2.根据权利要求1所述的一种改良型熔喷布的制备方法，其特征在于：所述的步骤S1中：搅拌混合时间为60分钟，所述的搅拌桶内PP聚合物、电气石母粒、丁香油和檀香油的含量分别为：PP聚合物：200kg，电气石母粒：8kg，丁香油：100g～150g，檀香油：100g～150g。
3.根据权利要求1所述的一种改良型熔喷布的制备方法，其特征在于：所述的步骤S2中，加热温度为200℃～300℃。
4.根据权利要求1所述的一种改良型熔喷布的制备方法，其特征在于：所述的步骤S4中，熔喷纺丝前经过熔喷泵对过滤后的混合料进行计量，熔喷纺丝工艺为：通过熔喷模头将高温熔化后的混合料均匀的吹散到成型网上，最后收卷切割成型；
所述的熔喷泵温度为：300℃；
所述的熔喷泵转速为50r/min；
所述的熔喷模头温度为260℃。
5.根据权利要求4所述的一种改良型熔喷布的制备方法，其特征在于：所述的熔喷布收卷切割成型前，通过直流驻极器给熔喷布添加静电。
6.根据权利要求5所述的一种改良型熔喷布的制备方法，其特征在于：所述的步骤S4中，所述的熔喷布添加静电后，通过喷雾机对熔喷布进行喷雾，然后再收卷切割成型。
7.根据权利要求6所述的一种改良型熔喷布的制备方法，其特征在于：所述的步骤S4中，所述的喷雾机内添加喷雾剂，所述的喷雾剂包括10wt％～15wt％的植物香油、75wt％的双脱醛乙醇和10wt％～15wt％的水。